How to improve root canal filling in teeth subjected to radiation therapy for cancer.

The aim of this study was to evaluate the influence of radiation therapy on root canal sealer push-out bond strength (BS) to dentin and the sealer/dentin interface after different final irrigation solutions (NaOCl, EDTA, and chitosan). Sixty-four maxillary canines were distributed into two groups (n=30): non-irradiated and irradiated with 60 Gy. Canals were prepared with Reciproc-R50 and subdivided (n=10) for final irrigation (NaOCl, EDTA, chitosan) and filled. Three dentin slices were obtained from each root third. The first slice of each third was selected for BS evaluation, and the failure mode was determined by stereomicroscopy. SEM analysis of the sealer-dentin interface was performed in the remaining slices. Two-way ANOVA and Tukey's tests (α=0.05) were used. Lower BS (P<0.0001) was obtained after irradiation (2.07±0.79 MPa), regardless of the final irrigation solution used. The NaOCl group (P<0.001) had the lowest BS in the irradiated (1.68±0.72) and non-irradiated (2.39±0.89) groups, whereas the EDTA (irradiated: 2.14±0.77 and non-irradiated: 3.92±1.54) and chitosan (irradiated: 2.37±0.73 and non-irradiated: 3.51±1.47) groups demonstrated a higher BS (P<0.05). The highest values were observed in the coronal third (3.17±1.38) when compared to the middle (2.74±1.36) and apical ones (2.09±0.97)(P<0.0001). There were more cohesive failures and more gaps in irradiated specimens, regardless of the final solution. The present study showed that radiation was associated with a decrease in BS, regardless of the final solution used, whereas chitosan increased BS in teeth subjected to radiation therapy.

Evaluation of chemical and morphological changes in radicular dentin after different final surface treatments.

The aim of this study was to evaluate the chemical and morphological effects of different lasers as a final surface treatment for endodontic therapy through energy dispersive X-ray spectroscopy (EDS) and scanning electron microscopy (SEM) respectively. Twenty-five maxillary canines were selected and instrumented with K3 system. Roots were randomly distributed into five groups (n = 5) according to the surface treatment: GI (distilled water), GII (NaOCl + EDTA), GIII (NaOCl + EDTA + 980 nm diode laser), GIV (NaOCl + EDTA+ 1,064 nm Nd:YAG laser), and GV (NaOCl + EDTA+ 2,780 nm Er, Cr:YSGG laser). Lasers were applied for 20 s and samples were bisected, exposing the treated surface and then subjected to elements quantification by EDS and morphological evaluation by scanning electron microscope (SEM). EDS data were submitted to ANOVA-two way, and SEM scores were submitted to two-way Kruskal-Wallis and Dunn's tests. The EDS analysis showed no difference for the chemical elements and Ca/P ratio between groups (p > .05). Statistical analysis showed more intense results for GV and less intense results for GI (p < .05). The GIII showed an amorphous organic matrix surface, while GV provided greater removal of intertubular dentin forming craters, and GIV promoted dentin fusion. The EDS method used in this study was not able to verify any chemical changes in root canal dentin; Nd:YAG, Er, Cr:YSGG, and 980 nm diode laser were capable of modifying the dentin morphology, correlating characteristics features for each one, which are essential clinical knowledge to establish the correct indication for each case. RESEARCH HIGHLIGHTS: EDS was not able to verify any chemical changes in root canal dentin after 980 nm diode, Nd:YAG and Er;Cr:YSGG laser treatments Nd:YAG, Er, Cr:YSGG, and 980 nm diode laser modified dentin morphology, correlating characteristics features for each one.

Physical properties of root cementum: Part 27. Effect of low-level laser therapy on the repair of orthodontically induced inflammatory root resorption: A double-blind, split-mouth, randomized controlled clinical trial.

INTRODUCTION: The purpose of this 2-arm-parallel split-mouth trial was to investigate the effect of low-level laser therapy (LLLT) on the repair of orthodontically induced inflammatory root resorption (OIIRR). METHODS: Twenty patients were included in this study, with 1 side randomly assigned to receive LLLT, and the other side served as a sham. Eligibility criteria included need for bilateral maxillary first premolar extractions as part of fixed appliance treatment. OIIRR was generated by applying 150 g of buccal tipping force on the maxillary first premolars for 4 weeks. After the active force was removed, the teeth were retained for 6 weeks. LLLT commenced with weekly laser applications using a continuous beam 660-nm, 75-mW aluminum-gallium-indium-phosphorus laser with 1/e2 spot size of 0.260 cm2, power density of 0.245 W/cm2, and fluence of 3.6 J/cm2. Contact application was used at 8 points buccally and palatally above the mucosa over each tooth root for 15 seconds with a total treatment time of 2 minutes. After 6 weeks, the maxillary first premolars were extracted and scanned with microcomputed tomography for primary outcome OIIRR calculations. Subgroup analysis included assessment per root surface, per vertical third, and sites of heaviest compressive forces (buccal-cervical and palato-apical). Randomization was generated using www.randomization.com, and allocation was concealed in sequentially numbered, opaque, sealed envelopes. Blinding was used for treatment and outcome assessments. Two-tailed paired t tests were used to determine whether there were any statistically significant differences in total crater volumes of the laser vs the sham treated teeth. RESULTS: Total crater volumes were 0.746 mm3 for the laser treated teeth and 0.779 mm3 for the sham. There was a mean difference of 0.033 ± 0.39 mm3 (95% CI, -0.21 to 0.148 mm3) greater resorption crater volume in the sham group compared with the laser group; this was not statistically significant (P = 0.705). No harm was observed. CONCLUSIONS: No significant difference was found between LLLT and sham control groups in OIIRR repair.

[Root canals dentinal wall structure after photodynamic exposure]. / Izuchenie struktury stenki kornevykh kanalov zubov posle fotodinamicheskogo vozdeistviia.

The aim of the study was to assess root canal dentinal walls structure after photodynamic exposure with the use of 0.5% photoditazine. A root canal dentin of 46 single root intact teeth removed for orthodontic indications was examined by scanning electron microscope JEOL JSM-6510 (Japan). Microphotographs of the root canal wall were obtained in the orifice, central and apical parts under×2000 magnification. It was found that photoactivation of 0.5% gel photoditazine by a light source, laser or diode, with a wavelength of 635-660 nm and a power of 150-200 mW is an effective technique for removing the smear layer of the root canal wall, which facilitates the maximum opening of the dentinal tubules to a depth of 2-3 µm. The best result (the maximum number of open dentinal tubules, the absence of a smear layer) is observed with 3 min photoditazine exposure and 2 min of laser exposure. The method can be proposed as an alternative supplement to the conventional root canals irrigation.

Effects of corticopuncture (CP) and low-level laser therapy (LLLT) on the rate of tooth movement and root resorption in rats using micro-CT evaluation.

The aim of this study was to compare the rate of tooth displacement, quantity of root resorption, and alveolar bone changes in five groups: corticopuncture (CP), low-level laser therapy (LLLT), CP combined with LLLT (CP + LLLT), control (C), and negative control (NC). A total of 60 half-maxilla from 30 male Wistar rats (10 weeks old) were divided randomly into five groups: three (CP, LLLT, and CP + LLLT) test groups with different stimulation for accelerated-tooth-movement (ATM), one control (C) group, and one negative control (NC) group with no tooth movement. Nickel-titanium coil springs with 50 g of force were tied from the upper left and right first molars to micro-implants placed behind the maxillary incisors. For the CP and CP + LLLT groups, two perforations in the palate and one mesially to the molars were performed. For the LLLT and CP + LLLT groups, GaAlAs diode laser was applied every other day for 14 days (810 nm, 100 mW, 15 s). The tooth displacements were measured directly from the rat's mouth and indirectly from microcomputer (micro-CT) tomographic images. Bone responses at the tension and compression sites and root resorption were analyzed from micro-CT images. The resulting alveolar bone responses were evaluated by measuring bone mineral density (BMD), bone volume fraction (BV/TV), and trabecular thickness (TbTh). Root resorption crater volumes were measured on both compression and tension sides of mesial and distal buccal roots. The tooth displacement in the CP + LLLT group was the greatest when measured clinically, followed by the CP, LLLT, and control groups (C and NC), respectively (p <0.05). The tooth movements measured from micro-CT images showed statistically higher displacement in the CP and CP + LLLT groups compared to the LLLT and control groups. The BMD, BV/TV, and TbTh values were lower at the compression side and higher at the tension side for all three test groups compared to the control group. The root resorption crater volume of the distal buccal root was higher in the control group, followed by CP, LLLT, and CP + LLLT, mostly at the compression site. Combining corticopuncture and low-level laser therapy (CP + LLLT) produced more tooth displacement and less root resorption at the compression side. The combined technique also promoted higher alveolar bone formation at the tension side.

How to improve root canal filling in teeth subjected to radiation therapy for cancer

Abstract The aim of this study was to evaluate the influence of radiation therapy on root canal sealer push-out bond strength (BS) to dentin and the sealer/dentin interface after different final irrigation solutions (NaOCl, EDTA, and chitosan). Sixty-four maxillary canines were distributed into two groups (n=30): non-irradiated and irradiated with 60 Gy. Canals were prepared with Reciproc-R50 and subdivided (n=10) for final irrigation (NaOCl, EDTA, chitosan) and filled. Three dentin slices were obtained from each root third. The first slice of each third was selected for BS evaluation, and the failure mode was determined by stereomicroscopy. SEM analysis of the sealer-dentin interface was performed in the remaining slices. Two-way ANOVA and Tukey's tests (α=0.05) were used. Lower BS (P<0.0001) was obtained after irradiation (2.07±0.79 MPa), regardless of the final irrigation solution used. The NaOCl group (P<0.001) had the lowest BS in the irradiated (1.68±0.72) and non-irradiated (2.39±0.89) groups, whereas the EDTA (irradiated: 2.14±0.77 and non-irradiated: 3.92±1.54) and chitosan (irradiated: 2.37±0.73 and non-irradiated: 3.51±1.47) groups demonstrated a higher BS (P<0.05). The highest values were observed in the coronal third (3.17±1.38) when compared to the middle (2.74±1.36) and apical ones (2.09±0.97)(P<0.0001). There were more cohesive failures and more gaps in irradiated specimens, regardless of the final solution. The present study showed that radiation was associated with a decrease in BS, regardless of the final solution used, whereas chitosan increased BS in teeth subjected to radiation therapy.

Influence of root dentin treatment on the push-out bond strength of fibre-reinforced posts

This study evaluates the influence of root dentin treatment with NaOCl alone and combined with EDTA, with and without ultrasound activation, on the push-out bond strength (BS) of fiber-reinforced posts in weakened roots, cemented with RelyX or Panavia. The root canals of 42 maxillary canines were instrumented with Reciproc and 2.5% NaOCl. In the coronal 12mm of all canals, experimental weakening of the roots was produced by reducing dentin thickness with 2.44mm diameter diamond burs. The roots were assigned to 3 groups (n = 14) according to root dentin treatment: 2.5% NaOCl; 2.5% NaOCl + 17% EDTA; and 2.5% NaOCl + 17% EDTA, with solutions agitated using passive ultrasonic irrigation. After cementation of the fiber-reinforced posts the roots were divided in thirds. The first slice of each third was used for the push-out BS test, the second slice for confocal laser scanning microscopy and dentin microhardness (Knoop) analysis. Data were analysed by a two-way ANOVA and Tukey test (a = 0.05). NaOCl + EDTA provided highest BS values than NaOCl (p < 0.0001). Specimens cemented with Panavia presented significantly higher BS than those with RelyX in the three root thirds (p < 0.0001). The highest BS values occurred in the cervical third (p < 0.001). Ultrasound-activated NaOCl + EDTA promoted the greatest reduction in dentin microhardness, followed by NaOCl/EDTA and NaOCl. Ultrasonic activation of NaOCl and EDTA reduced root dentin microhardness, but did not improve the push-out BS of resin-based cements. Panavia presented higher BS than RelyX. RelyX was not influenced by the root dentin treatment protocols.

Biostimulation with diode laser positively regulates cementoblast functions, in vitro.

The aim of this study was to evaluate the effects of diode laser biostimulation on cementoblasts (OCCM.30). A total of 40 root plates were obtained from healthy third molar teeth and assigned to the following two groups: (1) control group and (2) laser-treated group. Root plates were placed into the cell culture inserts, and OCCM.30 cells were seeded onto root plates. Cells were irradiated with a low level of diode laser (power: 0.3 W in continuous wave, 60 s/cm2). Proliferation and mineralized tissue-associated gene's and BMP's messenger RNA (mRNA) expressions of cementoblasts were evaluated. Total RNAs were isolated on day 3 and integrin-binding sialoprotein (Ibsp), bone gamma-carboxyglutamate protein (Bglap), Type I collagen (Col1a1), osteoblastic transcription factor, runt-related transcription factor (Runx2), and Bone Morphogenetic Protein (BMP)-2, 3, 4, 6, and 7 mRNA expressions were determined using quantitative RT-PCR. von Kossa staining was performed to evaluate biomineralization of OCCM.30 cells. In the proliferation experiment, while there was no significant difference until 96 h, laser irradiation retarded the decrease in cell proliferation trend after 96 h compared to the untreated control group. Statistically significant increase in Ibsp, Bglap, and BMP-2,3,6,7 mRNA expressions were noted in the laser groups when compared to the untreated control group (p < 0.05). Laser irradiation induced mineralized nodule formation of cementoblasts. The results of this study reveal that the biostimulation setting of diode laser modulates the behavior of cementoblasts inducing mineralized tissue-associated gene's mRNA expressions and mineralization. Therefore, biostimulation can be used during regenerative periodontal therapies to trigger cells with periodontal attachment apparatus.

Temperature Development on the External Root Surface During Laser-Assisted Endodontic Treatment Applying a Microchopped Mode of a 980 nm Diode Laser.

OBJECTIVE: The aim of this article was to investigate the temperature increase of the external root surface during laser-assisted endodontic treatment using a diode laser (980 nm) in a microchopped mode. METHODS: Ten freshly extracted, human maxillary incisors with mature apices were collected, prepared to size F4 at working length (ProTaper; Dentsply Maillefer, Ballaigues, Switzerland), mounted to a holder, and irradiated (using spiral movements in coronal direction) with a diode laser (GENTLEray 980 Classic Plus; KaVo, Biberach, Germany) with a 200 µm fiber in four different treatment groups: Group 1 (control group) was irradiated in six cycles of 5-sec irradiation/20-sec pause with 2.5 W in the pulse mode. Groups 2 to 4 were irradiated at six cycles of 5-sec irradiation/20-sec pause in the microchopped mode (Group 2-1.6 W; Group 3-2.0 W; Group 4-2.5 W). The applied mode was 25 ms on/25 ms off. Within the on period, the laser delivered an intermittent sequence of energy complexes and the maximum output was equal to the nominated output of the device (12 W). Canals were kept moist by sterile saline irrigation in between irradiations, and temperature changes were continuously measured using a thermal imaging camera. Recordings were analyzed by a mixed model (analysis of variance [ANOVA] for repeated measurements). RESULTS: The highest mean of temperature rise, 1.94°C ± 1.07°C, was measured in Group 4, followed by Group 3 (1.74°C ± 1.22°C) and Group 2 (1.58°C ± 1.18°C). The lowest increase occurred in Group 1 (1.06°C ± 1.20°C). There was a significant difference (p = 0.041) between the groups. Significant differences were found between Groups 1 and 4 (p = 0.007) and 1 and 2 (p = 0.035). In addition, a marginally significant difference between Groups 1 and 2 (p = 0.052) was noted. There was no significant difference between Groups 2, 3, and 4. Despite the low mean values reported, the highest temperature increase (+5.7°C) was measured in one of the specimens of treatment Group 2 at the middle third. CONCLUSIONS: Under the conditions used and within the limitations of the study, the microchopped diode laser irradiation is a safe possible treatment option in laser-assisted endodontic treatment, concerning the temperature elevation on the external root surface.

Low-level laser therapy effectiveness in accelerating orthodontic tooth movement: A randomized controlled clinical trial.

OBJECTIVE: To evaluate the effectiveness of low-level laser therapy (LLLT) in accelerating orthodontic tooth movement of crowded maxillary incisors. MATERIALS AND METHODS: This two-arm, parallel-group, randomized controlled trial involved 26 patients with severe to extreme maxillary incisors irregularity according to Little's irregularity index, indicating two first premolars extraction. Patients were randomly assigned to either the laser group or the control group (13 each). Following premolars extraction, orthodontic treatment with fixed appliances was initiated for both groups. Immediately after insertion of the first archwire, patients in the laser group received a LLL dose from an 830-nm wavelength Ga-Al-As semiconductor laser device with energy of 2 J/point. The laser was applied to each maxillary incisor's root at four points (two buccal, two palatal). Application was repeated on days 3, 7, 14, and then every 15 days starting from the second month until the end of the leveling and alignment stage. Alignment progress was evaluated on the study casts taken before inserting the first archwire (T0), after 1 month of treatment commencement (T1), after 2 months (T2), and at the end of the leveling and alignment stage (T3). The outcome measures were the overall time needed for leveling and alignment and the leveling and alignment improvement percentage. RESULTS: A statistically significant difference was found between the two groups in the overall treatment time (P < .001) and the leveling and alignment improvement percentage at T1 (P = .004) and T2; (P = .001). CONCLUSION: LLLT is an effective method for accelerating orthodontic tooth movement.

Influence of root dentin treatment on the push-out bond strength of fibre-reinforced posts

Abstract This study evaluates the influence of root dentin treatment with NaOCl alone and combined with EDTA, with and without ultrasound activation, on the push-out bond strength (BS) of fiber-reinforced posts in weakened roots, cemented with RelyX or Panavia. The root canals of 42 maxillary canines were instrumented with Reciproc and 2.5% NaOCl. In the coronal 12mm of all canals, experimental weakening of the roots was produced by reducing dentin thickness with 2.44mm diameter diamond burs. The roots were assigned to 3 groups (n = 14) according to root dentin treatment: 2.5% NaOCl; 2.5% NaOCl + 17% EDTA; and 2.5% NaOCl + 17% EDTA, with solutions agitated using passive ultrasonic irrigation. After cementation of the fiber-reinforced posts the roots were divided in thirds. The first slice of each third was used for the push-out BS test, the second slice for confocal laser scanning microscopy and dentin microhardness (Knoop) analysis. Data were analysed by a two-way ANOVA and Tukey test (a = 0.05). NaOCl + EDTA provided highest BS values than NaOCl (p < 0.0001). Specimens cemented with Panavia presented significantly higher BS than those with RelyX in the three root thirds (p < 0.0001). The highest BS values occurred in the cervical third (p < 0.001). Ultrasound-activated NaOCl + EDTA promoted the greatest reduction in dentin microhardness, followed by NaOCl/EDTA and NaOCl. Ultrasonic activation of NaOCl and EDTA reduced root dentin microhardness, but did not improve the push-out BS of resin-based cements. Panavia presented higher BS than RelyX. RelyX was not influenced by the root dentin treatment protocols.

Effect of Nd:YAG (1064-nm) and Diode Laser (980-nm) EDTA Agitation on Root Dentin Ultrastructure Properties.

OBJECTIVE: The purpose of this study was to analyze the effects of agitation of 17% ethylenediaminetetraacetic acid (EDTA) with 1064 nm Nd:YAG and 980 nm diode laser on root dentin microhardness and superficial roughness (with confocal laser scanning microscopy [CLSM]). BACKGROUND DATA: Root canal irrigants are used in an attempt to minimize the negative effects of smear layer. MATERIALS AND METHODS: Twenty-five bovine roots were sectioned longitudinally and divided into five groups (n=10 each): (1) deionized water, (2) 17% EDTA, (3) 17% EDTA with 60 sec manual agitation, (4) 17% EDTA with 50 sec diode laser (2 W) agitation, and (5) 17% EDTA with 50 sec Nd:YAG (1.5 W) laser agitation. Microhardness and superficial roughness values were calculated before and after the procedures at the cervical, middle, and apical root thirds. Microhardness was statistically analyzed using two way ANOVA, paired t test, and Tukey's tests (α=0.05). Roughness was statistically analyzed using Kruskal-Wallis, paired t test, and Student-Newman-Keuls tests (α=0.05%). RESULTS: Statistically significant differences in microhardness and roughness were observed between the deionized water group and others. EDTA with 1064 nm Nd:YAG or 980 nm diode laser presented the lowest microhardness and the highest roughness values and was significantly different from EDTA with manual agitation and EDTA only (p<0.05). However, there were no differences in microhardness or dentin roughness between the root thirds (p>0.05). CLSM analysis showed that the control samples exhibited smoother surfaces than that of the EDTA groups. CONCLUSIONS: Nd:YAG 1064 nm and 980-nm diode laser EDTA agitation caused greater reduction in microhardness and increased roughness of root dentin than EDTA only or EDTA with manual agitation.

Effect of low-level laser therapy on dental root cementum remodeling in rats.

OBJECTIVE: To investigate the amount of the cementum layer formed over the rat's dental root surfaces by daily application of low-level laser therapy (LLLT) for 2 weeks. METHODS: Twelve female Sprague-Dawley (SD) rats were divided into two groups: six rats received daily LLLT (Ga-Al-As, 830 nm), and six rats received no treatment (control). The treatment lasted 2 weeks. In vivo Micro-CT imaging analyzed the root's hard tissue volumetric changes. The cementum thickness was evaluated histologically. RESULTS: Total cementum thicknesses in the LLLT group increased significantly (p = 0.015) compared to the control group. This significant increase in the cementum thickness, verified histologically, was not detectable during in vivo Micro-CT imaging, which showed no significant difference between the groups regarding the root hard tissues volumetric changes over the 2-week evaluation period. CONCLUSION: Two weeks of daily application of LLLT significantly increased rat's dental root cementum thickness as determined histologically. However, in vivo Micro-CT imaging failed to accurately reveal this cementum growth as it was not possible to differentiate dentinal changes.

The effect of low-level laser therapy (810 nm) on root development of immature permanent teeth in dogs.

Traumatic injuries and dental caries can be a big challenge to immature teeth. In these cases, the main purpose of treatment is to maintain the pulp vitality. The purpose of this study was to investigate the effect of low-level laser therapy on accelerating the rate of dentinogenesis in pulpotomy of immature permanent teeth (apexogenesis). Three dogs, 4-6 months old, were used in this study. One jaw in each dog was randomly assigned to laser irradiation group. All selected teeth were pulpotomized with mineral trioxide aggregate (MTA) and restored with amalgam. In the laser group, the Ga-Al-As laser (810 nm, 0.3 W, 4 J/cm(2), 9 s) was used on buccal and lingual gingiva of each tooth in 48 h intervals for 2 weeks. In order to observe the newly formed dentine, tetracycline was injected on the 1st, 3rd, 7th, and 14th day after the operation. Then, ground sections of teeth were observed under a fluorescence microscope. The data was analyzed with Generalized Estimating Equations (GEE) test. The mean distance between the lines of tetracycline formed on the 1st and 14th day was significantly higher in the laser group (P = 0.005). Within the limitation of this study, irradiation of Ga-Al-As laser (810 nm) can accelerate the rate of dentinogenesis in apexogenesis of immature permanent teeth with MTA in dogs.

Connective tissue graft associated or not with low laser therapy to treat gingival recession: randomized clinical trial.

BACKGROUND: To evaluate the treatment of gingival recession with a connective tissue graft (CTG) alone or in combination with low-level laser therapy (CTG + L). METHODS: Forty patients presenting 40 Miller Class I and II gingival recessions were included. The defects were randomly assigned to receive either CTG (n = 20) or CTG + L (n = 20). A diode laser (660 nm) was applied to the test sites immediately after surgery and every other day for 7 days (eight applications). RESULTS: The mean percentage of root coverage was 91.9% for the test group and 89.48% for the control group after 6 months (p > 0.05). The test group presented more complete root coverage (n = 13, 65%) than the control group (n = 7, 35%) (p = 0.04). Dentine sensitivity decreased significantly after 6 months in both groups (p < 0.001). The two groups showed improvement in aesthetics at the end of treatment. CONCLUSIONS: Low-level laser therapy may increase the percentage of complete root coverage when associated with CTG.

The combined use of Er,Cr:YSGG laser and fluoride to prevent root dentin demineralization.

UNLABELLED: The use of erbium lasers to prevent caries in enamel has shown positive results. However, it is not known if Er,Cr:YSGG laser can also be used to increase acid resistance of root dentine, which is another dental tissue susceptible to the action of cariogenic bacteria. OBJECTIVE: To analyze the effects of the Er,Cr:YSGG laser (λ=2.78 µm, 20 Hz) irradiation associated with 2% neutral sodium fluoride (NaF) to prevent root dentin demineralization. MATERIAL AND METHODS: One hundred human root dentin samples were divided into 10 groups (G) and treated as follows: G1: no treatment; G2: NaF; G3: laser (4.64 J/cm2) with water cooling (WC=5.4 mL/min); G4: laser (4.64 J/cm2) without WC; G5: laser (8.92 J/cm2) with WC; G6: laser (8.92 J/cm2) without WC; G7: laser (4.64 J/cm2) with WC and NaF; G8: laser (4.64 J/cm2) without WC and NaF; G9: laser (8.92 J/cm2) with WC and NaF; G10: laser (8.92 J/cm2) without WC and NaF. The NaF gel was applied alone or after 4 min of irradiation. After 14 days of acid challenge, the samples were sectioned and the Knoop microhardness (KHN) test was done at different depths (30, 60, 90 and 120 µm) from the outer dentin surface. Data were analyzed by one-way ANOVA and Fisher's test (α=5%). RESULTS: The results showed that G8 and G10 presented higher KHN than the G1 for the depths of 30 and 60 µm, indicating an increase of the acid resistance of the dentin in up to 35% (p<0.05). CONCLUSIONS: The use of Er,Cr:YSGG laser irradiation at 4.64 J/ cm2 and 8.92 J/cm2 without water cooling and associated with 2% NaF can increase the acid resistance of human root dentin.

The combined use of Er, Cr: YSGG laser and fluoride to prevent root dentin demineralization

The use of erbium lasers to prevent caries in enamel has shown positive results. However, it is not known if Er,Cr:YSGG laser can also be used to increase acid resistance of root dentine, which is another dental tissue susceptible to the action of cariogenic bacteria. Objective: To analyze the effects of the Er,Cr:YSGG laser (λ=2.78 μm, 20 Hz) irradiation associated with 2% neutral sodium fluoride (NaF) to prevent root dentin demineralization. Material and Methods: One hundred human root dentin samples were divided into 10 groups (G) and treated as follows: G1: no treatment; G2: NaF; G3: laser (4.64 J/cm2) with water cooling (WC=5.4 mL/min); G4: laser (4.64 J/cm2) without WC; G5: laser (8.92 J/cm2) with WC; G6: laser (8.92 J/cm2) without WC; G7: laser (4.64 J/cm2) with WC and NaF; G8: laser (4.64 J/cm2) without WC and NaF; G9: laser (8.92 J/cm2) with WC and NaF; G10: laser (8.92 J/cm2) without WC and NaF. The NaF gel was applied alone or after 4 min of irradiation. After 14 days of acid challenge, the samples were sectioned and the Knoop microhardness (KHN) test was done at different depths (30, 60, 90 and 120 μm) from the outer dentin surface. Data were analyzed by one-way ANOVA and Fisher’s test (α=5%). Results: The results showed that G8 and G10 presented higher KHN than the G1 for the depths of 30 and 60 μm, indicating an increase of the acid resistance of the dentin in up to 35% (p<0.05). Conclusions: The use of Er,Cr:YSGG laser irradiation at 4.64 J/ cm2 and 8.92 J/cm2 without water cooling and associated with 2% NaF can increase the acid resistance of human root dentin. .

Platelet-rich plasma, low-level laser therapy, or their combination promotes periodontal regeneration in fenestration defects: a preliminary in vivo study.

BACKGROUND: This study histomorphometrically analyzes the influence of platelet-rich plasma (PRP), low-level laser therapy (LLLT), or their combination on the healing of periodontal fenestration defects (PFDs) in rats. METHODS: PFDs were surgically created in the mandibles of 80 rats. The animals were randomly divided into four groups: 1) C (control) and 2) PRP, defects were filled with blood clot or PRP, respectively; 3) LLLT and 4) PRP/LLLT, defects received laser irradiation, were filled with blood clot or PRP, respectively, and then irradiated again. Animals were euthanized at either 10 or 30 days post-surgery. Percentage of new bone (NB), density of newly formed bone (DNB), new cementum (NC), and extension of remaining defect (ERD) were histomorphometrically evaluated. Data were statistically analyzed (analysis of variance; Tukey test, P <0.05). RESULTS: At 10 days, group PRP presented ERD significantly lower than group C. At 30 days, group PRP presented NB and DNB significantly greater than group C. Groups LLLT, PRP, and PRP/LLLT showed significant NC formation at 30 days, with collagen fibers inserted obliquely or perpendicularly to the root surface. NC formation was not observed in any group C specimen. CONCLUSIONS: LLLT, PRP, or their combination all promoted NC formation with a functional periodontal ligament. The combination PRP/LLLT did not show additional positive effects compared to the use of either therapy alone.

A comparative study of temperature elevation on human teeth root surfaces during Nd:YAG laser irradiation in root canals.

The purpose of this study was to evaluate the temperatures on the root surfaces during Nd:YAG laser irradiation in root canals using pulse durations of 180 and 320 µs. Thirty extracted human teeth were used in this study. The teeth were enlarged up to ISO 40 (multi-rooted) or up to ISO 60 (single-rooted) by conventional technique using K-files. Then the teeth were placed into a water bath with a constant temperature of 37 °C and then irradiated with an Nd:YAG laser having an output power of 1.5 W, a frequency of 15 Hz, using an optic fiber of 200 µm diameter. The temperature on the root surface was measured by means of attaching thermocouples in three areas (coronal, mesial, and apical regions) of the root canals. The thermographic study showed that the average temperature elevation for both pulse durations on the root surfaces was less than 9 °C. There was no significant difference in the observed temperatures in coronal and mesial areas. Though a higher increase of temperature was observed in the apical region when the pulse length of the Nd:YAG laser was 320 µs. The results of the study showed that the temperature rises during Nd:YAG laser irradiation with parameters used in this study minimal to cause damage on bone and periodontal tissues. Moreover, it was suggested that in order to have lower temperature in the apical region, an Nd:YAG laser with a pulse length of 180 µs is preferred than one with a pulse length of 320 µs.

Estudo histomorfométrico da ação do laser de baixa potência na reabsorção radicular ortodonticamente induzida em ratos / Histomorphometric study of low-level laser action on orthodontic induced root resorption

A reabsorção radicular inflamatória induzida pela movimentação dentária é uma consequência da lesão dos cementoblastos devido à aplicação da força sobre o dente deixando a raiz exposta à ação dos osteoclastos. Estudos vêm sendo feitos a fim de se desenvolver um meio de evitar, controlar ou reduzir este tipo de reabsorção. A fototerapia com laser tem demonstrado efetividade como agente antiinflamatório e, considerando a origem inflamatória desta patologia este estudo se propôs a avaliar a ação do laser sobre as reabsorções radiculares. Para isto realizou-se uma análise histomorfométrica da raiz disto-vestibular dos primeiros molares superiores de ratos após a indução da sua movimentação mecânica, sendo irradiados ou não com laser de baixa potência. Para a fototerapia foi utilizado um laser diodo, calibrado com comprimento de onda de 808 nm, potência de saída de 100mW, energia total de 2,1J ou 96J e área de 0,0028cm2. A aplicação foi contínua, pontual e com contato. Foram utilizados 54 ratos Wistar, machos, com aproximadamente 80 dias, pesando entre 280±40g. Para a movimentação utilizou- se uma mola fechada super-elástica, com força constante, pré-calibrada em 25g. Os espécimes foram irradiados a cada 48 horas conforme o grupo a que pertenciam. O sacrifício se procedeu no sétimo ou décimo dia após o início da movimentação. O exame histológico foi realizado com cortes de 6 μm corados em HE. Os resultados revelaram que, com as dosimetrias estudadas, o laser de baixa potência, não teve efeito estatisticamente significante sobre as reabsorções radiculares. Concluindo-se que não há diferença na área reabsorvida, espessura ou extensão da reabsorçãoradicular entre os grupos controle e experimental.

Inflammatory root resorption induced by tooth movement is a consequence of the cementoblasts injury due to application of force on the tooth leaving the root exposed to the action of osteoclasts. Studies have been made to develop a means of preventing, controlling or reducing this kind of resorption. Phototherapy by laser has demonstrated effectiveness as an antiinflammatory and considering the inflammatory origin of this pathology this study evaluated the effects of laser on root resorption. For this we carried out a histomorphometric analysis of maxillary first molars distobuccal root of rats after being moved, irradiated or not with low-level laser. Order to phototherapy it was used a diode laser, calibrated with a wavelength of 808 nm, output power of 100mW, 2.1J or 96J of energy and area of 0.0028 cm2. The application was continuous, punctual and with contact. It was used 54 male Wistar rats, approximately 80 days, weighing 280 ± 40g. For tooth movement, it was used a super elastic closed spring, with pre-calibrated and constant force of 25g. The specimens were irradiated every 48 hours depending on the group they belonged to. The sacrifice was made in the seventh or tenth day after the onset of movement. Histological examination was performed with sections of 6 μm stained with HE. The results revealed that, considering the dosimetry studied, low-level laser, has no effect statistically significant on the root resorption. Concluding it does not have difference in the root reabsorption area, thickness or extension, between the control and the experimental groups.