Development of ZTA (80% Al2O3/20% ZrO2) pre-sintered blocks for milling in CAD/CAM systems.

The present work aims to develop a production method of pre-sintered zirconia-toughened-alumina (ZTA) composite blocks for machining in a computer-aided design and computer-aided manufacturing (CAD-CAM) system. The ZTA composite comprised of 80% Al2O3 and 20% ZrO2 was synthesized, uniaxially and isostatically pressed to generate machinable CAD-CAM blocks. Fourteen green-body blocks were prepared and pre-sintered at 1000 °C. After cooling and holder gluing, a stereolithography (STL) file was designed and uploaded to manufacture disk-shaped specimens projected to comply with ISO 6872:2015. Seventy specimens were produced through machining of the blocks, samples were sintered at 1600 °C and two-sided polished. Half of the samples were subjected to accelerated autoclave hydrothermal aging (20h at 134 °C and 2.2 bar). Immediate and aged samples were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). Optical and mechanical properties were assessed by reflectance tests and by biaxial flexural strength test, Vickers indentation and fracture toughness, respectively. Samples produced by machining presented high density and smooth surfaces at SEM evaluation with few microstructural defects. XRD evaluation depicted characteristic peaks of alpha alumina and tetragonal zirconia and autoclave aging had no effect on the crystalline spectra of the composite. Optical and mechanical evaluations demonstrated a high masking ability for the composite and a characteristic strength of 464 MPa and Weibull modulus of 17, with no significant alterations after aging. The milled composite exhibited a hardness of 17.61 GPa and fracture toughness of 5.63 MPa m1/2, which remained unaltered after aging. The synthesis of ZTA blocks for CAD-CAM was successful and allowed for the milling of disk-shaped specimens using the grinding method of the CAD-CAM system. ZTA composite properties were unaffected by hydrothermal autoclave aging and present a promising alternative for the manufacture of infrastructures of fixed dental prostheses.

Effects of different primers and colouring solutions on orthodontic bonding: shear bond strength and colour change.

OBJECTIVES: This in vitro study evaluated the effect of different colouring solutions and primer systems used in the bonding of brackets on enamel colour change and bond strength. MATERIALS AND METHODS: 120 premolar teeth were divided into four main groups; brackets were bonded with 37% orthophosphoric acid + Transbond XT Primer in Group 1, 3 M Single Bond Universal in Group 2, Transbond Plus SEP in Group 3, and G-Premio Bond in Group 4. Each group was divided into three subgroups, and the teeth were placed in a cup containing coffee and tea mixture, in a cup containing cola and in distilled water. A bond strength test was applied to all teeth. Colour measurements of all teeth were performed at 2 different times: before bonding and after the bond strength test. RESULTS: The average bond strength of the 37% orthophosphoric acid group was higher than that of the other groups. The effect of primer and solution groups on colour change was statistically significant (p = 0.001 and p = 0.023, respectively). CONCLUSIONS: In this study, the bond strength was clinically sufficient in all primer groups. The highest colour change was observed when the tea-coffee solution and Transbond Plus SEP primer were used. CLINICAL RELEVANCE: This study has identified enamel discoloration and bond strength from different colouring solutions and primer systems used for bonding braces, which can be used to inform clinicians and patients to achieve better treatment results.

Assessment of the color stability of two silicone elastomers for maxillofacial prostheses upon exposure to cold beverages.

PURPOSE: This study investigated the color stability of different commercially available silicone materials for facial prostheses upon exposure to everyday beverages. It was hypothesized that the beverages would not alter the color of the silicone under conditions simulating daily exposure. METHODS: Sixty specimens were fabricated using two materials - VST-50 and Silfy - and exposed to commercially available cold mineral water, tea, or coffee. Specimen color was evaluated on days 1 and 15. The color was measured with a spectrophotometer based on CIELab system and color differences were calculated as ΔE. Statistical analysis was performed using the Kruskal-Wallis test and Mann-Whitney U test. RESULTS: The mean ΔE values after 15 days of exposure to mineral water, cold green tea, and coffee were 1.016, 3.480, and 3.636 for VST-50 and 0.440, 0.798, and 1.425 for Silfy, respectively. Both materials showed significant differences in color, and VST-50 showed a greater color change than Silfy, especially for coffee. CONCLUSION: Pigmented silicone elastomers have low color stability, leading to an overall color change in silicone prostheses when exposed to pigmented beverages. Color changes in such prostheses can be mitigated by selecting materials with better color stability to extend their longevity.

The use of mouthwash containing trimetaphosphate as an adjunct therapy to fluoridated toothpaste reduces enamel demineralization.

INTRODUCTION: The decline in dental caries has been attributed to the widespread use of fluoride (F). Two forms of presentation are fluoridated toothpaste (FT) and mouthwash (MW), widely used by the population. MATERIALS AND METHODS: This study aimed to evaluate in vitro the effects of combining FT and MW, whether supplemented with sodium trimetaphosphate (TMP) or not, on dental enamel demineralization. Bovine enamel blocks (n = 60) were selected based on initial surface hardness (SHi) and divided into 5 experimental groups (n = 12 each): I) Placebo Toothpaste (without F/TMP); II) 1100 ppm F Toothpaste (FT); III) 1100F associated with a MW at 100 ppm F (FT + MW 100F); IV) 1100F associated with a MW at 225 ppm F (FT + MW 250F); and V) 1100F associated with a MW at 100 ppm F supplemented with 0.4 % TMP (FT + MW 100F-TMP). The blocks were treated twice a day, undergoing 5 pH cycles over 7 days. Thus, the percentage change in surface hardness (%SH), integrated subsurface hardness loss (ΔKHN), and the concentration of F, phosphorus (P), and calcium (Ca) in the enamel were determined. The data were submitted to ANOVA and Student-Newman-Keuls test (p < 0.001). RESULTS: The 1100F group was statistically inferior to the groups associated with MW for %SH, ΔKHN, and the concentration of P and Ca in the enamel (p < 0.001). Blocks treated with FT + MW 225F and FT + MW 100F-TMP showed significantly lower %SH compared to the other groups (p < 0.001). The FT + MW 100F - TMP group exhibited the lowest depth mineral loss (ΔKHN), and higher concentration de P in enamel (p < 0.001). CONCLUSION: The adjunct use of MW with FT produces a greater protective effect in inhibiting enamel demineralization, and the supplementation of TMP to the MW with 100F provides a superior effect compared to MW with 225F. CLINICAL SIGNIFICANCE: This combination of treatments could be regarded as one of several alternative fluoride supplements for subjects at elevated risk of caries.

Exploring the role of flavonoids in caries-affected dentin adhesion: A comprehensive scoping review.

OBJECTIVES: The aim of this scoping review was to evaluate the available scientific evidence regarding the use of flavonoids in the treatment of caries-affected dentin focusing on bonding to dentin. METHODS: A comprehensive literature search was performed in five databases from March 2022 and updated in April 2023: PubMed, EMBASE, Scopus, Web of Science, and Scielo. Additionally, the references of included studies were manually searched. Gray literature was excluded from the review. STUDY SELECTION: Inclusion criteria included in vitro, in situ, and in vivo studies (animal or human) published in English. Abstracts, reviews, case reports, book chapters, doctoral dissertations, guidelines, and studies using pure plant extracts were excluded. Data collected from the selected studies were summarized and subjected to narrative and descriptive analysis. Out of the 91 studies identified, only 16 studies met the inclusion criteria. RESULTS: The review analyzed eight different flavonoids (hesperidin, galardin, proanthocyanidin, genipin, quercetin, naringin, epigallocatechin-3-gallate, and other catechins subtypes) used as pretreatment or loaded into adhesive systems, primers, and phosphoric acid. The use of flavonoids improved the mechanical properties of the materials and modified the biological properties of the dentin, reducing collagen loss by the inhibition of proteolytic activity of matrix metalloproteinases (MMPs). CONCLUSIONS: Based on the findings of this scoping review, it can be concluded that the use of flavonoids as pretreatment or incorporation into dental materials preserves collagen in the hybrid layer, inhibiting the MMPs activities, modifying the collagen fibrils of the dentin matrix and improving the mechanical properties of the dental adhesive systems. Therefore, it represents a promising approach for promoting dentin biomodification. This can result in more stable bonding of adhesive restorations to caries-affected dentin.

Statistical analysis of VEXLPE wear against alumina produced by a new 200-station, multidirectional pin-on-disk device.

With low wear rates shown by contemporary bearing materials of total hip prostheses, the standard deviation of wear rate is relatively high. Therefore, large sample sizes are needed for an adequate power of test. Because wear tests take a long time, it is practical to test several samples simultaneously. A new high-capacity, multidirectional wear test device, called the SuperCTPOD-200, was introduced. A 3 million-cycle wear test with an unprecedented sample size of 200 was performed for VEXLPE. The duration of the test was 6 weeks. The wear factor was normally distributed with a mean ± SD of 1.64 × 10-7 mm3/Nm ± 0.22 × 10-7 mm3/Nm (n = 200). The observation that SD was 13.1% of the mean can be useful in power analyses of future tests with other highly cross-linked polyethylenes. Burnishing was the most typical feature on the worn pins, which was in agreement with clinical findings on retrieved acetabular liners. The present study emphasizes statistics that often plays a minor role only in wear studies.

INFLUENCE OF AGING, BEVERAGES, AND MOUTH WASH SOLUTIONS ON THE MICROSTRUCTURAL AND COLOR STABILITY OF DIFFERENT DENTAL CERAMICS: AN IN VITRO STUDY.

Рurроse - to evaluate the influence of aging, beverages, and mouthwash solutions on the microstructural and color stability of three CAD/CAM ceramic materials. In total, 87 specimens (7×5×1.5 mm) were prepared from 3 CAD/CAM ceramic groups, Lithium Disilicate glass ceramic (IPS e.max CAD), Extra translucent zirconia (VITA YZ), and Resin Nanoceramic (Cerasmart 270). All the materials were A2 or equivalent shades. After hydrothermal aging in distilled water at 5 C to 55 C for (10.000 cycles). The samples were randomly allocated into 3 groups (n=27) and immersion (staining) for one week in 3 different solutions coffee, green tea, and chlorhexidine. The baseline measurements of ceramic discs were recorded for color change and 2 samples of each group sent for SEM (microstructure) images before aging and staining. The second measurement was recorded after 10000 thermocycling and immersion in staining agents for 7 days. Statistical analysis were performed with an independent Kruskal-wallis test . The significant level was set at P≤0.05. ∆E values for lithium Disilicate after immersion in coffee, green tea and chlorhexidine gluconate were 3.167, 1.847 and 2.022, respectively. corresponding ∆E values for VITA XT were 3.438, 4.201 and 2.267. meanwhile Cerasmart shows more sensitivity for staining than LD and VITA of 4.454, 2.926 and 2.933. Within limitation of this study lithium disilicate showed the best color stability with values less than perception threshold. VITA and Cerasmart show higher sensitivity for staining with VITA more affected by green tea (Higher than clinically accepted threshold) and Cerasmart more affected by coffee (higher than clinically accepted threshold).

Effect of Polymerization Unit, Polishing, and Coffee Thermocycling on the Color and Translucency of Additively Manufactured Resins Used for Definitive Prostheses.

PURPOSE: To evaluate the effect of polymerization unit, polishing, and coffee thermocycling on the color and translucency of additively manufactured polyurethane-based resins with different viscosities. In addition, their color behavior was compared with the color of the shade tab throughout the fabrication steps and aging. MATERIALS AND METHODS: Disk-shaped specimens (Ø10 × 2 mm) were fabricated from polyurethane-based resins with different viscosities (Tera Harz TC-80DP and C&B permanent; n = 30 per material). Baseline color coordinates were measured after cleaning. The specimens in each resin group were divided into three subgroups (n = 10 per subgroup) to be polymerized with different polymerization units (Otoflash G171 [FLN], Wash and Cure 2.0 [CLED1], and P Cure [CLED2]), polished, and subjected to coffee thermocycling. Color coordinates were remeasured after each process. Color differences (ΔE00) and relative translucency parameter (RTP) values were calculated. Data were statistically analyzed (α = .05). RESULTS: Time points and polymerization units affected the ΔE00 for each material (P ≤ .049). ΔE00 of each polymerization unit pair had significant differences within and among different time points within each material (P ≤ .024). ΔE00 (when compared with the shade tab) and RTP were mostly affected by polymerization units and time points within both materials (P ≤ .042). CONCLUSIONS: Tested polymerization units, polishing, and coffee thermocycling affected the color difference and translucency of tested resins. Color differences ranged from moderately unacceptable to extremely unacceptable, and the differences in translucency values mostly ranged from perceptible to unacceptable, according to previous thresholds. In addition, tested resin-polymerization unit pairs had unacceptable color differences when compared to the shade tab. CLED1 may enable higher color stability for tested resins.

The Effect of Different Ageing Protocols on the Shear Bond Strength of the Ceromer Indirect Composite on Two Different Substructure Materials.

BACKROUND: The evolution of restorative materials in prosthodontics has led to the emergence of indirect composite resins, including ceromers, as alternatives to traditional metal-ceramic restorations. However, research gaps exist regarding the impact of ageing protocols on the bond strength of ceromer composites to different metal substructures, necessitating further investigation in this area. AIM: This study aimed to determine the effect of five different ageing protocols on the shear bond strength (SBS) of ceromer indirect composites on two different substructures. METHODS: In this in vitro study, 120 metallic discs (10 × 2 mm) were cast from cobalt-chromium (Co-Cr) alloy (n = 60) and spark erosion treated from grade V titanium (n = 60). Each sample was sandblasted. The M.L. primer (Shofu, Germany) and layers of opaque were applied to the surface following the manufacturer's instructions. A special jig (6 × 2 mm) was placed on each disc. The ceromer was condensed in it and light-cured separately for 90 s. Following polishing, specimens were separated into five ageing groups: distilled water (as a control), thermal cycling, tea, coffee, and gastric acid immersion. All samples were placed in 37°C incubation for 28 days for distilled water, coffee, and tea, and 7 days for gastric acid immersion and thermal cycling for 5000 cycles (5-55°C). A universal test machine was used to measure the SBS. The samples were evaluated for failure modes using stereomicroscopy. Data were analyzed using one-way analysis of variance (ANOVA) (P < 0.05). RESULTS: According to one-way ANOVA, the mean SBS (MPa) between the two groups was compared in each ageing protocol, and there were no significant differences between the Co-Cr-C and Ti-C groups (P > 0.05). The most frequent mode of failure in all groups was mixed. CONCLUSIONS: Applying the ageing protocols, the type of substructure material had no significant effect on the SBS of the ceromer indirect composite except for tea immersion.

Effect of aging and bleaching on the color stability and surface roughness of a recently introduced single-shade composite resin.

OBJECTIVES: To assess the effects of aging and bleaching procedures on the color stability and surface roughness of a new single-shade composite versus multi-shade composite resins. METHODS: A single-shade composite resin (Charisma Diamond One, CDO) and 3 multi-shade composite resins (Tetric NCeram, Filtek Z350 XT, Clearfil Majesty Posterior) were tested. Thirty specimens of each material were subjected to one of the aging procedures respectively: immersion in distilled water (12 days/37 °C), immersion in coffee (12 days/37 °C), or water thermocycling (10,000 cycles/5-55 °C). All specimens underwent in-office bleaching after aging. Kruskal-Wallis tests and analysis of variance were used for statistical analysis (α=0.05). RESULTS: All materials exhibited a change of color (ΔE00), translucency (RTP), whiteness (WID) and surface roughness parameters (Sa,Sv) after aging and bleaching procedures. CDO showed the highest ΔE00 among all resins with the highest RTP value, regardless of the aging procedures. Immersion in coffee led to the significantly highest ∆E00 values and lowest RTP values for nearly all resins. Positive ΔWID1 (WID(bleaching)-WID(baseline)) values were found in distilled water immersion and thermocycling groups, while negative ΔWID1 values were found in the coffee immersion group for all materials. Besides, positive ΔWID2 (WID(bleaching)-WID(aging)) values were found in all aging groups for nearly all materials. All materials showed an increasing trend in Sa and Sv after bleaching. CONCLUSIONS: CDO showed more pronounced discoloration than multi-shade composite resins. Although the whiteness of all resins increased after bleaching, none was completely restored in the coffee immersion group. Bleaching significantly increased the surface roughness of all materials. CLINICAL SIGNIFICANCE: Charisma Diamond One is more susceptible to discoloration, which may affect its long-term success rate. Bleaching could partially reduce the color change of the composite resins but did not return them completely to their original state. The roughness of the resins increased after bleaching, prompting dentists to repolish them after bleaching.

Topographical and crystalline change on surface by sandblasting improve flexural and shear bond strength of niobia-modified yttria-stabilized tetragonal zirconia polycrystal.

This study aimed to investigate the effects of sandblasting on the physical properties and bond strength of two types of translucent zirconia: niobium-oxide-containing yttria-stabilized tetragonal zirconia polycrystals ((Y, Nb)-TZP) and 5 mol% yttria-partially stabilized zirconia (5Y-PSZ). Fully sintered disc specimens were either sandblasted with 125 µm alumina particles or left as-sintered. Surface roughness, crystal phase compositions, and surface morphology were explored. Biaxial flexural strength (n=10) and shear bond strength (SBS) (n=12) were evaluated, including thermocycling conditions. Results indicated a decrease in flexural strength of 5Y-PSZ from 601 to 303 MPa upon sandblasting, while (Y, Nb)-TZP improved from 458 to 544 MPa. Both materials significantly increased SBS after sandblasting (p<0.001). After thermocycling, (Y, Nb)-TZP maintained superior SBS (14.3 MPa) compared to 5Y-PSZ (11.3 MPa) (p<0.001). The study concludes that (Y, Nb)-TZP is preferable for sandblasting applications, particularly for achieving durable bonding without compromising flexural strength.

Two-Photon-Excited FLIM of NAD(P)H and FAD-Metabolic Activity of Fibroblasts for the Diagnostics of Osteoimplant Survival.

Bioinert materials such as the zirconium dioxide and aluminum oxide are widely used in surgery and dentistry due to the absence of cytotoxicity of the materials in relation to the surrounding cells of the body. However, little attention has been paid to the study of metabolic processes occurring at the implant-cell interface. The metabolic activity of mouse 3T3 fibroblasts incubated on yttrium-stabilized zirconium ceramics cured with aluminum oxide (ATZ) and stabilized zirconium ceramics (Y-TZP) was analyzed based on the ratio of the free/bound forms of cofactors NAD(P)H and FAD obtained using two-photon microscopy. The results show that fibroblasts incubated on ceramics demonstrate a shift towards the free form of NAD(P)H, which is observed during the glycolysis process, which, according to our assumptions, is related to the porosity of the surface of ceramic structures. Consequently, despite the high viability and good proliferation of fibroblasts assessed using an MTT test and a scanning electron microscope, the cells are in a state of hypoxia during incubation on ceramic structures. The FLIM results obtained in this work can be used as additional information for scientists who are interested in manufacturing osteoimplants.

Influence of casein phosphopeptide-amorphous calcium phosphate on the surface topography and composition of nickel-titanium archwires during orthodontic treatment with fixed appliances.

PURPOSE: To investigate the surface topography and nickel content of nickel-titanium (NiTi) archwires exposed to either routine oral hygiene or a prophylactic regimen with casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) during orthodontic treatment. METHODS: This in vivo study involved 40 orthodontic patients with fixed appliances, who were randomly assigned to either a routine oral hygiene group or a CPP-ACP supplementary regimen group. Twenty new NiTi archwires served as controls. All archwires underwent scanning electron microscopy and energy-dispersive spectroscopy to evaluate their surface topography and elemental composition. The nickel content was quantified as a percentage of total weight and the Ni/Ti ratio, and statistical comparisons were made using pairwise tests. RESULTS: Wires exposed to fluoride toothpaste showed signs of pitting corrosion, deep grooves, and corrosion debris. In contrast, wires exposed to supplementary CPP-ACP exhibited smooth surface areas interspersed with microdefects and deposits. Statistically significant differences in nickel content were found between the new and retrieved archwires, as well as between wires exposed to routine oral hygiene and CPP-ACP (P < 0.001). The archwires exposed to CPP-ACP had the lowest nickel content (P < 0.001). CONCLUSION: The use of CPP-ACP holds promise for application as a safe anticariogenic agent with possible protective properties during orthodontic treatment.

Sandwich hydrogel to realize cartilage-mimetic structures and performances from polyvinyl alcohol, chitosan and sodium hyaluronate.

Developing artificial substitutes that mimic the structures and performances of natural cartilage is of great importance. However, it is challenging to integrate the high strength, excellent biocompatibility, low coefficient of friction, long-term wear resistance, outstanding swelling resistance, and osseointegration potential into one material. Herein, a sandwich hydrogel with cartilage-mimetic structures and performances was prepared to achieve this goal. The precursor hydrogel was obtained by freezing-thawing the mixture of poly vinyl alcohol, chitosan and deionized water three cycles, accompanied by soaking in sodium hyaluronate solution. The top of the precursor hydrogel was hydrophobically modified with lauroyl chloride and then loaded with lecithin, while the bottom was mineralized with hydroxyapatite. Due to the multiple linkages (crystalline domains, hydrogen bonds, and ionic interactions), the compressive stress was 71 MPa. Owing to the synergy of the hydrophobic modification and lecithin, the coefficient of friction was 0.01. Additionally, no wear trace was observed after 50,000 wear cycles. Remarkably, hydroxyapatite enabled the hydrogel osseointegration potential. The swelling ratio of the hydrogel was 0.06 g/g after soaking in simulated synovial fluid for 7 days. Since raw materials were non-toxic, the cell viability was 100 %. All of the above merits make it an ideal material for cartilage replacement.

Comparison of light transmittance and color changes between polyurethane and copolyester retainer materials after staining and destaining.

BACKGROUND: Retainers are the only effective approach to prevent orthodontic relapse. The aim of this study was to compare the changes in color and light-transmittance of rough and smooth thermoformed polyurethane and copolymer retainer samples after staining in different solutions and destaining with different approaches. METHODS: Four hundred copolyester (Essix® ACE) and 400 polyurethane (Zendura®) samples with different surface textures, smooth and rough, were stained in 4 different solutions (n = 100 per solution) over 28 days. Each of the four groups of 100 stained samples of each material was subdivided into 5 groups of 20 samples and subjected to different destaining solutions. Light transmittance and color changes were evaluated using a spectrometer and a spectrophotometer. Mean differences were compared using a two-way analysis of variance (ANOVA) and posthoc multiple comparison tests at P = 0.05. RESULTS: No significant differences in light transmittance were found between both untreated materials. Both materials were stained in a similar fashion and showed no significant differences between two materials after staining. Coffee and tea stained both materials more significantly than wine, but there was a significant difference of changes of color and light transmittance between rough and smooth surfaces during the destaining in coffee- and tea-stained samples of copolyester material. All destaining solutions were effective at removing all stains on the samples. The surface roughness of the material plays a significant role in the ability of the materials to be destained, demonstrating a more significant greater effect on cleaning rough samples for improvements in light-transmittance and greater changes in color. CONCLUSIONS: This study concluded that the surface of materials plays a significant role in the material destaining and staining. In addition, the different polymers used for retainer fabrication exhibited different responses during the destaining process depending on types of stains.

Effect of the use of bromelain associated with bioactive glass-ceramic on dentin/adhesive interface.

OBJECTIVES: To evaluate the effect of bromelain associated with Biosilicate on the bond strength (BS) of a universal adhesive system to sound (SD) and caries-affected dentin (CAD), and on the proteolytic activity. MATERIALS AND METHODS: Cavities were prepared in 360 molars, half submitted to cariogenic challenge. Teeth were separated into groups (n=20): Control-No treatment; CHX-0.12% chlorhexidine; NaOCl-5% sodium hypochlorite; Br5%-5% bromelain; Br10%-10% bromelain; Bio-10% Biosilicate; NaOClBio-NaOCl+Bio; Br5%Bio-Br5%+Bio; Br10%Bio-Br10%+Bio. Following treatments, the adhesive system was applied, and cavities were restored. Samples were sectioned into sticks and stored at 37 °C for 24 h, 6 months, and 1 year. Microtensile BS (2-way ANOVA, Bonferroni's test, α=0.05), fracture patterns (SEM), and adhesive interfaces (TEM) were evaluated. Bacterial collagenase assay and in situ zymography were performed. RESULTS: In CAD, Br10% presented higher BS (p=0.0208) than Br5%Bio. Br5% presented higher BS (p=0.0033) after 6 months than after 24 h; and association of treatments, higher BS (p<0.05) after aging than after 24 h. Mixed fractures were the most prevalent. Association of treatments promoted a more uniform hybrid layer with embedded Bio particles. Experimental groups presented lower (p<0.0001) relative fluorescence units than Control. Bromelain, associated or not with Bio, showed collagenolytic degradation. CONCLUSIONS: Bromelain associated with Biosilicate did not affect the BS to SD. In CAD, Br5%Bio decreased immediate BS but had no long-term influence. This association decreased the proteolytic activity. CLINICAL RELEVANCE: Bromelain and Biosilicate may enhance the longevity of adhesive restorations by inhibiting endogenous proteases.

Radiotherapy in the head and neck region influences the chemical and mechanical properties of intraradicular dentin.

OBJECTIVES: To investigate the chemical and mechanical properties of intraradicular dentin submitted to radiotherapy. MATERIALS AND METHODS: Sixteen mandibular incisors were divided into two groups (n = 8): non-irradiated and irradiated. The irradiated teeth were obtained from head and neck radiotherapy patients, with a total dose ranging from 70.2 to 72 Gy divided into 1.8 Gy daily. After sample preparation, intraradicular dentin slices of each root third were evaluated by Raman spectroscopy, energy dispersive spectroscopy and Knoop microhardness test. Data were analyzed by Two-way ANOVA and Tukey's test (α = 0.05). RESULTS: In Raman spectroscopy, carbonate and amide III showed a significant difference for irradiation and third (carbonate p = 0.021 and p < 0.001; amide III p < 0.001 and p = 0.001, respectively). For amide I, there was a significant difference for third (p < 0.001). For carbonate/mineral ratio, there was a significant difference for irradiation (p = 0.0016) and third (p < 0.001), with the irradiated middle third showing the lowest values. For amide I/amide III ratio, there was a significant difference for irradiation (p = 0.005) in the cervical third. In energy dispersive spectroscopy, carbon (p = 0.004; p = 0.020), phosphorus (p < 0.001; p = 0.009) and calcium (p = 0.008; p = 0.007) showed differences for irradiation and third, with the irradiated groups presenting lower values in cervical and middle thirds. For calcium/phosphorus ratio, there was a significant difference for irradiation (p < 0.001) in cervical and middle thirds. Regarding microhardness, there was a significant difference for irradiation (p < 0.001), with all irradiated groups showing lower microhardness values. CONCLUSIONS: The radiotherapy altered the chemical and mechanical properties of intraradicular dentin, mainly in the cervical and middle root thirds.

Effect of Tea Tree Oil Addition to Denture Liners Against Candida albicans and Bond Strength to Acrylic Denture Bases.

PURPOSE: To evaluate the effect of adding tea tree oil to denture liners on Candida albicans and bond strength to the acrylic denture base. MATERIALS AND METHODS: Disc-shaped specimens were fabricated from silicone-based resilient liner (Tokuyama, Molloplast), acrylic-based hard liner (GC Reline), and acrylic-based soft liner (Visco-gel). Tea tree oil (TTO) was incorporated into the liners at varying concentrations (0% [control], 2%, 5%, 8%). C albicans were counted by viable colony count, and optical density (OD) was measured with a spectrophotometer. The tensile strength to heat polymerized acrylic denture base was measured in a universal testing machine. The compliance of the data to the distribution of normality was evaluated using the Shapiro Wilk test. Two-way ANOVA, Bonferroni correction, and paired sample t test were performed (α = .05). RESULTS: The addition of TTO into liners provided a significant decrease in the OD values (P < .001). The control groups of the liners presented the highest colony counts, whereas increasing TTO decreased the results (P < .01). According to tensile bond strength test, 8% TTO addition resulted in a significant decrease for Tokuyama (P < .01) and Molloplast liners (P < .05), while 2% TTO resulted in significance for GC Reline (P < .001). CONCLUSIONS: Denture liners containing increasing percentages of TTO presented lower amounts of C albicans colonies and decreased bond strength to the denture bases. When using TTO for its antifungal properties, the amount added should be carefully selected because the tensile bond strength may be affected.

Effect of coffee thermocycling on the surface roughness and stainability of denture base materials with different chemical compositions manufactured with additive and subtractive technologies.

OBJECTIVE: To evaluate the effect of coffee thermocycling (CTC) on the surface roughness (Ra ) and stainability of denture base materials with different chemical compositions fabricated by using additive and subtractive manufacturing. MATERIALS AND METHODS: Disk-shaped specimens were additively (FREEPRINT denture, AM) or subtractively (G-CAM, GSM and M-PM, SM) fabricated from three pink denture base materials in different chemical compositions (n = 10). Ra was measured before and after polishing, while color coordinates were measured after polishing. Specimens were subjected to CTC (5000 cycles) and measurements were repeated. Color differences (ΔE00 ) after CTC were calculated. Ra among different time intervals within materials was evaluated by using repeated measures analysis of variance (ANOVA), while 1-way ANOVA was used to evaluate the Ra of different materials within each time interval and the ΔE00 values. Color coordinates within each material were compared by using paired samples t-tests (α = 0.05). RESULTS: Ra before polishing was the highest for all materials (p < 0.001), while SM had its lowest Ra after CTC and AM had its lowest Ra after polishing (p ≤ 0.008). Before polishing, AM had the highest Ra among the materials (p < 0.001). After polishing, SM had higher Ra than AM (p < 0.001). After CTC, GSM had the lowest Ra (p ≤ 0.048). SM had the lowest (p ≤ 0.031) and AM had the highest (p < 0.001) ΔE00 . CTC decreased the a* and b* values of SM and AM (p ≤ 0.017), and increased the L* values of AM (p < 0.001). CONCLUSIONS: Polishing significantly reduced the surface roughness of all materials. CTC did not increase the surface roughness of materials above the clinically acceptable threshold. Only AM had perceptible color change when previously reported threshold values for denture base materials were considered. CLINICAL SIGNIFICANCE: Tested denture base materials may have similar surface stability after coffee thermocycling. However, subtractively manufactured denture base materials may have improved color stability when subjected to long-term coffee consumption.

Comparison of retention of monolithic zirconia crowns with alumina airborne-particle abraded and nonabraded intaglio using three different cements: A clinical simulation.

STATEMENT OF PROBLEM: The necessity of roughening the intaglio surface of zirconia crowns to achieve adequate retention is unclear. PURPOSE: The purpose of this clinical simulation study was to evaluate the retention of airborne-particle-abraded and nonabraded monolithic zirconia crowns using 3 different cement types. MATERIAL AND METHODS: Extracted human molars were used and prepared with a 10-degree taper. Impressions were made of the prepared teeth with a polyvinyl siloxane (PVS) material, and dies were made with Type 4 gypsum. Each die was scanned with a NobelProcera 1G Scanner, and the standard tessellation language (STL) files were transferred electronically to the Nobel Biocare production site, where a bar was added virtually on top of each crown and parameters were set for milling. Seventy-two Procera zirconia crowns were generated, of which half were airborne-particle abraded on the intaglio surface with 50-µm alumina particles at 400 to 500 kPa for 15 seconds. The other 36 received no intaglio treatment other than cleaning. Both groups of 36 crowns were divided into 3 subgroups of 12 specimens. The area of each preparation was calculated using a computer-aided design software program. The specimens were distributed to attain similar mean surface areas among the cementation groups. The crowns were cemented onto the specimen with a controlled force of 196 N. The 3 cements used were self-adhesive, modified resin RelyX Unicem Aplicap, resin-modified glass ionomer RelyX Luting, and a composite resin, Panavia F2.0 with ED Primer A & B. All specimens were thermocycled (5 °C to 55 °C) for 5000 cycles and then removed axially with a universal testing machine (Instron Model 5585H) at a crosshead speed of 0.5 mm/min. The removal force was recorded, and stress of dislodgement was calculated for each crown. A 2-way analysis of variance was used for statistical analyses. The type of failure was analyzed with the chi-squared test of association for independent samples (α=.05 for all tests). RESULTS: The mean dislodging force for crowns with airborne-particle abraded intaglio was 5.4 MPa, which was statistically greater than the mean of 3.2 MPa for nonabraded specimens (P<.001). No significant differences related to the dislodging stresses were detected among the 3 cements (P=.109). The mode of failure was similar whether abraded or not, with 50% of specimens retaining cement in the crown after separation. CONCLUSIONS: Alumina airborne-particle abrasion of the intaglio of zirconia to create surface roughness is beneficial in retaining the crowns, regardless of the cement type. The nonabraded crowns demonstrated significantly lower retentive stress with crown removal. The principal mode of failure was similar whether the zirconia intaglio was airborne-particle abraded or not. The most common mode of failure (>50% of specimens) was at least three-fourths of the cement remaining within the crown.