Agregado trióxido mineral y cemento pórtland expuestos a irrigantes endodóncicos: pH, conductividad y solubilidad / Mineral trioxide aggregate and portland cement exposed to endodontic irrigants: pH, conductivity, and solubility
Endodoncia (Madr.)
; 36(1): 10-21, ene.-abr. 2018. tab
Article
em Es
| IBECS
| ID: ibc-172440
Biblioteca responsável:
ES1.1
Localização: BNCS
RESUMEN
Objetivo:
El objetivo de este estudio fue determinar, el pH, la conductividad y la solubilidad al someter el agregado trióxido mineral (MTA) y el cemento Pórtland (CP) a diferentes irrigantes utilizados en endodoncia. Material yMétodos:
Se estudiaron un total de 210 muestras, 105 de cemento ProRoot MTA(R) blanco y 105 de CP blanco. Se seleccionaron los siguientes irrigantes hipoclorito sódico al 2,5% y al 5%, ácido cítrico al 10% y al 20%, clorhexidina al 2%, EDTA al 17%, y suero fisiológico como control. Se expusieron 15 muestras de MTA y 15 de CP a cada tipo de irrigante. Se midieron los resultados a 1, 5, 15, 30 y 60 minutos.Resultados:
La mayoría de cambios del pH y la conductividad fueron de pequeña magnitud, aunque estadísticamente significativos. Destacan la alcalinización del suero fisiológico y la acidificación del hipoclorito sódico. Con MTA disminuye la conductividad en hipoclorito sódico y aumenta la conductividad en EDTA. Con CP hubo una mayor pérdida de conductividad del hipoclorito sódico y del ácido cítrico. Todas las muestras disminuyeron el peso considerablemente después de la exposición a cualquiera de los irrigantes, y en general ésta fue mayor para el CP que el MTA.Conclusiones:
El contacto del material de reparación con los irrigantes utilizados habitualmente en endodoncia altera poco el pH y la conductividad pero aumenta marcadamente su solubilidad. Estos cambios afectan menos al MTA que al CPABSTRACT
Objective. The aim of this study was to determine changes to pH, conductivity, and solubility when mineral trioxide aggregate (MTA) and Portland cement (PC) are exposed to different endodontic irrigants. Methods. The study included a total of 210 samples, 105 white ProRoot MTA® cement and 105 white PC cement. The following irrigants were tested 2.5% and 5% sodium hypochlorite, 10% and 20% citric acid, 2% chlorhexidine, 17% ethylenediamine tetra-acetic acid (EDTA), and physiological serum as a control. Fifteen samples of each material were exposed to each irrigant. PH, conductivity, and solubility were measured at baseline and after 1, 5, 15, 30 and 60 minutes exposure to irrigants. Results. Most changes in pH and conductivity were of small magnitude, although statistically significant. For MTA and PC physical serum produced alkalinization, while sodium hypochlorite produced acidification. MTA lost conductivity when exposed to sodium hypochlorite but this increased with exposure to EDTA. PC underwent greater losses of conductivity when exposed to sodium hypochlorite and citric acid. All samples decreased in weight significantly after exposure to any of the irrigants, and the loss was generally greater for PC than MTA. Conclusions. When repair materials are exposed to the irrigants normally used in endodontics, pH levels and conductivity alter slightly, while solubility increases markedly. These effects were greater for PC than MTA
Buscar no Google
Base de dados:
IBECS
Métodos Terapêuticos e Terapias MTCI:
Plantas_medicinales
Assunto principal:
Cimentos Dentários
Idioma:
Es
Revista:
Endodoncia (Madr.)
Ano de publicação:
2018
Tipo de documento:
Article