Postoperative sensitivity of composites using novel Bacillus subtilis nanofortified adhesives: a triple-blind study.

NANOTECHNOLOGY: is the art and science of dealing with nanoscale particles. This has transformed contemporary dental practices through myriad contributions to biomaterial science. Titanium dioxide nanoparticles procured from Bacillus subtilis, an eco-friendly and biogenic source, can significantly magnify the physiochemical attributes of dental materials. However, postoperative sensitivity is a major drawback of composite restorations. The incorporation of these nanoparticles into dental adhesives can greatly benefit clinical dentistry by resolving this issue. This trial aimed to evaluate the effectiveness of a novel titanium dioxide nanofortified adhesive on the postoperative sensitivity of composite restorations. METHODS: This triple-blind, parallel-group randomized controlled trial was conducted at the Department of Operative Dentistry and Endodontics, School of Dentistry, Islamabad, from May 15, 2023, to November 25, 2023. Participants (n = 60) with Class I and II primary carious lesions with a minimum cavity depth of 3-5 mm were randomly assigned to two groups (n = 30). After obtaining informed consent, the restorative procedure was accomplished using a minimally invasive approach and etch-and-rinse adhesive strategy. In group A, a nanofortified adhesive was used for composite restoration, whereas in group B, an adhesive without nanoparticles was used. Postoperative sensitivity was evaluated using the Visual Analog Scale (VAS) score at follow-up periods: of one day, one week, two weeks and one month. A Chi-square test was used to compare postoperative sensitivity between the two groups. The level of significance was set at p < 0.05. RESULTS: A noteworthy association was observed between sensitivity and the group variable at all four evaluation periods: after one day (p = 0.002), 1 week (p = 0.002), 2 weeks (p = 0.007) and one month. In conclusion, participants who underwent restorative intervention using titanium dioxide nanoreinforced adhesives reported a notable reduction in sensitivity at all time intervals. Hence, the occurrence and severity of postoperative sensitivity are significantly reduced using Bacillus subtilis-procured nanofortified adhesives as compared to conventional adhesives without nanoparticles. TRIAL REGISTRATION: This trial was retrospectively registered at ClinicalTrials.gov (ID: NCT06242184) on 03/02/2024. All procedures involving human participants were performed in conformance with this protocol.

Clinical Efficacy of a Novel Titania Nanoparticle-Reinforced Bonding Agent in Reducing Post-Restorative Sensitivity: A randomized clinical trial.

Objective: To evaluate the clinical efficacy of novel titania-nanoparticle reinforced bonding agent on post-restorative sensitivity in patients. Methods: This triple-blinded, randomized clinical trial included participants (n = 60) having Class- I and II cavitations with a minimum cavity depth of 3mm at Department of Operative Dentistry & Endodontics, School of Dentistry, Shaheed Zulfiqar Ali Bhutto Medical University, Islamabad from January 5, 2023, to June 20, 2023. They were randomly assigned into two groups A and B (n = 30). After informed consent, restorative intervention was accomplished using an etch-and-rinse adhesive strategy. In Group-A, titania-nanoparticle-incorporated bonding agent was used for composite restoration, while in Group-B, bonding agent without nanoparticles was used. The primary outcome was assessed using Visual Analogue Scale mean score. Participants were instructed to rate their sensitivity status at follow-ups: 24 hours, one week, and one month. Mann-Whitney U test was employed to compare sensitivity between the two groups. Results: According to results of this trial, a significant difference was observed between two groups after 24 hours (p = 0.004) and one week (p = 0.002). However, no discernible difference was observed after one month (p = 0.643). Conclusion: Post-restorative sensitivity in patients with composite restorations was reduced using titania-reinforced bonding agents as compared to bonding agents without nanoparticles. This shows that inclusion of titania nanoparticles into adhesive dentistry could be beneficial in resolving post-restorative sensitivity occurring with composite restorations.