RESUMEN
A sequence of dye-sensitized solar cells is proposed, utilizing TiO2@Zn/Al-layered double hydroxide (LDH) as their starting materials, in which Ruthenizer N719 was used as a photon absorber. The anticipated system was turned into sheet-like TiO2@mixed metal oxide (MMO) via post-processing treatment. The crystal quality indicated a relation to power conversion efficiency (PCE); this was combined with a comparable morphology profile. In detail, the optimum DSSC device exhibited average sheet-like thickness and a dye loading amount of 43.11 nm and 4.28 ×10-3 mM/cm-2, respectively. Concurrently, a considerable PCE enhancement of the optimum DSSC device (TiO2@MMO-550°) was attained compared to pristine MMO (0.91%), which could be due to boosted electron transfer efficiency. Of the fabricated devices, DSSC fabricated at 550° exhibited the highest PCE (1.91%), with a 35.6% enhancement compared to that obtained at 450°, as a result of its increased open-circuit voltage (3.29 mA/cm2) and short-circuit current (0.81 V). The proposed work delivers an enhanced efficiency as compared to similar geometries.
RESUMEN
In this manuscript, a series of dye-sensitized solar cells (DSSCs) were fabricated as a function of post-processing temperature based on mesoporous CuO@Zn(Al)O-mixed metal oxides (MMO) in conjunction with dye N719 as the main light absorber; the proposed CuO@Zn(Al)O geometry was, in turn, attained using Zn/Al-layered double hydroxide (LDH) as a precursor via combination of co-precipitation and hydrothermal techniques. In particular, the dye loading amount onto the deposited mesoporous materials was anticipated via regression equation-based UV-Vis technique analysis, which evidently demonstrated a robust correlation along with the fabricated DSSCs power conversion efficiency. In detail, of the DSSCs assembled, CuO@MMO-550 exhibited short-circuit current (JSC) and open-circuit voltage (VOC) of 3.42 (mA/cm2) and 0.67 (V) which result in significant fill factor and power conversion efficiency of 0.55% and 1.24%, respectively. This could mainly be due to the relatively high surface area of 51.27 (m2/g) which in turn validates considerable dye loading amount of 0.246 (mM/cm-2).
RESUMEN
The share of wind-based electricity generation is gradually increasing in the world energy market. Wind energy can reduce dependency on fossil fuels, as the result being attributed to a decrease in global warming. This paper discusses and reviews the basic principle parameters that affect the performance of wind turbines. An overview presents the introduction and the background of energy consumption, following the order of the elaboration of wind turbines, including mathematical models, categories of wind turbines were critically discussed. Moreover, it also focuses on materials that are commonly considered for wind turbine manufacturing, and the process used to recycle them. The scale of recycling methods for fiberglass and thermoplastic is presented in the respective section. Various parameters that reduce the function of wind turbines are explained in depth. This review also discusses various environmental impacts of wind turbines. Future research studies are suggested in the conclusion section.
RESUMEN
In the present study, cylindrical ABS P400 polymer parts (diameter 6.5 mm) to be used as die-sinking EDM (electric discharge machining) novel electrodes were fabricated using a fused deposition modeling (FDM) process. To meet the conductivity requirement in EDM, ABS parts were metallized using an innovative method that comprised putting aluminum-charcoal (Al-C) on them followed by their copper electroplating. Real-time EDM of the mild steel workpiece was performed using novel electrodes, and machining performance of the electrodes, measured in terms of dimensional accuracy, i.e., change in diameter (ΔD) and change in depth (ΔH) of the cavity, under varying levels of three EDM factors, i.e., current (I), pulse on time (Ton), and pulse off time (Toff), was investigated. Machining results were analyzed using analysis of variance (ANOVA), perturbation graphs, and 3D surface plots. The optimal setting of the EDM parameters for minimizing ΔD and ΔH was determined using the desirability function approach. The suitability of the novel electrodes for EDM was ascertained by comparing their machining results with those of solid copper (SC) electrodes and electrodes fabricated by FDM and metallized using the electro-deposition method (FDM-EM), already reported in the literature, under similar machining conditions. From the results, it was found that ΔD and ΔH were less when EDM was performed using novel electrodes.