Development of ZTA (80% Al2O3/20% ZrO2) pre-sintered blocks for milling in CAD/CAM systems.

The present work aims to develop a production method of pre-sintered zirconia-toughened-alumina (ZTA) composite blocks for machining in a computer-aided design and computer-aided manufacturing (CAD-CAM) system. The ZTA composite comprised of 80% Al2O3 and 20% ZrO2 was synthesized, uniaxially and isostatically pressed to generate machinable CAD-CAM blocks. Fourteen green-body blocks were prepared and pre-sintered at 1000 °C. After cooling and holder gluing, a stereolithography (STL) file was designed and uploaded to manufacture disk-shaped specimens projected to comply with ISO 6872:2015. Seventy specimens were produced through machining of the blocks, samples were sintered at 1600 °C and two-sided polished. Half of the samples were subjected to accelerated autoclave hydrothermal aging (20h at 134 °C and 2.2 bar). Immediate and aged samples were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). Optical and mechanical properties were assessed by reflectance tests and by biaxial flexural strength test, Vickers indentation and fracture toughness, respectively. Samples produced by machining presented high density and smooth surfaces at SEM evaluation with few microstructural defects. XRD evaluation depicted characteristic peaks of alpha alumina and tetragonal zirconia and autoclave aging had no effect on the crystalline spectra of the composite. Optical and mechanical evaluations demonstrated a high masking ability for the composite and a characteristic strength of 464 MPa and Weibull modulus of 17, with no significant alterations after aging. The milled composite exhibited a hardness of 17.61 GPa and fracture toughness of 5.63 MPa m1/2, which remained unaltered after aging. The synthesis of ZTA blocks for CAD-CAM was successful and allowed for the milling of disk-shaped specimens using the grinding method of the CAD-CAM system. ZTA composite properties were unaffected by hydrothermal autoclave aging and present a promising alternative for the manufacture of infrastructures of fixed dental prostheses.

Prefabricated shouldered abutments enable successful restoration of molar crowns on implants.

PURPOSE: This retrospective study evaluated the effect of selected clinical and patient factors on survival, success, and peri-implant bone level changes of locking taper implants supporting molar crowns on Bicon's prefabricated shouldered abutments. METHODS: A total of 234 patients, who received 274 single molar crowns supported by locking taper implants were included in this retrospective study. Kaplan-Meier survival analysis was used to assess overall implant survival, prostheses survival, and success. Crowns were either monolithic (resin based) or bilayered (milled fiber-reinforced composite coping veneered with indirect composite). Early and late changes in marginal bone levels were plotted and analyzed with equivalence testing to compare the effects of different factors on crestal bone levels. RESULTS: At 9.5 years after implant surgery, the implant survival probability was 94.2%, the probability of prosthesis survival was 91.4%, and the probability of prosthetic success was 90.4%. Neither the use of different crown materials, nor the choice of monolithic versus bilayered crown construction, significantly affected the probability of prosthetic success. Marginal bone levels, on average, trended downwards towards the top of the implant within the first 2 years after functional loading, and remained stable on average, since then. Factors affecting bone levels included the use of nonsteroidal anti-inflammatory drugs, which precluded early implant bone loss; and subcrestal implant placement, which was linked to significantly higher long-term bone levels. CONCLUSION: The implant and abutment system studied resulted in high implant and prosthetic survival rates, regardless of prosthetic material used, with stable bone levels over time.

In silico nonlinear dynamic finite-element analysis for biaxial flexural strength testing of CAD/CAM materials.

PURPOSE: The aim of this study was to establish and assess the validity of in silico models of biaxial flexural strength (BFS) tests to reflect in vitro physical properties obtained from two commercially available computer-aided design/computer-aided manufacturing (CAD/CAM) ceramic blocks and one CAD/CAM resin composite block. METHODS: In vitro three-point bending and BFS tests were conducted for three CAD/CAM materials (n = 10): Katana Zirconia ST10 (raw material: super-translucent multilayered zirconia, ST10; Kuraray Noritake Dental, Niigata, Japan), Katana Zirconia HT10 (raw material: highly translucent multilayered zirconia, HT10; Kuraray Noritake Dental), and Katana Avencia N (AN; Kuraray Noritake Dental). Densities, flexural moduli, and fracture strains were obtained from the in vitro three-point bending test and used as an input for an in silico nonlinear finite element analysis. The maximum principal stress (MPS) distribution was obtained from an in silico BFS analysis. RESULTS: The elastic moduli of AN, HT10, and ST10 were 6.513, 40.039, and 32.600 GPa, respectively. The in silico fracture pattern of ST10 observed after the in silico evaluation was similar to the fracture pattern observed after the in vitro testing. The MPS was registered in the center of the tensile surface for all three specimens. The projections of the supporting balls were in the form of a triple asymmetry. CONCLUSIONS: The in silico approach established in this study provided an acceptable reflection of in vitro physical properties, and will be useful to assess biaxial flexural properties of CAD/CAM materials without wastage of materials.

Hydrofluoric acid concentration and etching time affect differently the microstructure and surface properties of pressed lithium disilicate glass ceramics.

OBJECTIVE: To evaluate the effect of different hydrofluoric acid concentrations and etching times on the surface, chemical composition and microstructure of lithium disilicate. MATERIAL AND METHODS: Ninety specimens of pressed lithium disilicate (LDS) were obtained (IPS e.max Press, Rosetta SP and LiSi Press). The specimens of each material were divided in two groups according to the hydrofluoric acid concentration: 5% and 10% (n = 15/group), and subdivided according to the etching time: 20, 40 and 60 s (n = 5/group). Crystalline evaluations and chemical composition were performed through x-ray diffraction (XRD) and energy-dispersive x-ray spectroscopy (EDS), respectively. Microstructural analyses were performed by scanning electron microscope (SEM), surface roughness (Ra), and material thickness removal evaluation. Thickness removal and Ra data were analyzed by ANOVA and Tukey test (p < 0.05). RESULTS: XRD demonstrated characteristic peaks of lithium disilicate crystals, lithium phosphate and of a vitreous phase for all materials. EDS identified different compositions and SEM confirmed different surface responses to acid etching protocols. Material and etching time influenced Ra and material thickness removal (p < 0.05). CONCLUSION: Hydrofluoric acid concentration and etching time affect the surface characteristics of LDS differently. LiSi Press presented higher resistance to hydrofluoric acid etching compared to e.max Press and Rosetta SP. CLINICAL SIGNIFICANCE: Applying the appropriate etching protocol is pivotal to avoid excessive material removal and to prevent jeopardize the mechanical and optical properties of the material.

Ultrathin lithium disilicate and translucent zirconia crowns for posterior teeth: Survival and failure modes.

PURPOSE: To evaluate the reliability and failure modes of ultrathin (0.5 mm) lithium disilicate, translucent and ultra-translucent zirconia crowns for posterior teeth restorations. MATERIALS AND METHODS: Fifty-four mandibular first molar crowns of three ceramic materials: (1) Lithium disilicate (e.max CAD, Ivoclar Vivadent), (2) 3Y-TZP (Zirconn Translucent, Vipi), and (3) 5Y-PSZ (Cercon XT, Dentsply Sirona), with 0.5 mm of thickness were milled and cemented onto composite resin abutments. Eighteen samples of each group were tested under mouth-motion step-stress accelerated life testing in a humid environment using mild, moderate, and aggressive profiles. Data was subjected to Weibull statistics. Use level curves were plotted and reliability was calculated for a given mission of 100,000 cycles at 100, 200, and 300 N. Fractographic analyses of representative samples were performed in scanning electron microscope. RESULTS: Beta (ß) values suggest that failures were dictated by material's strength for lithium disilicate and by fatigue damage accumulation for both zirconias. No significant differences were detected in Weibull modulus and characteristic strength among groups. At a given mission of 100,000 cycles at 100 N, lithium disilicate presented higher reliability (98% CB: 95-99) regarding 3Y-TZP and 5Y-PSZ groups (84% CB: 65%-93% and 79% CB: 37&-94%, respectively). At 200 N, lithium disilicate reliability (82% CB: 66%-91%) was higher than 5Y-PSZ (20% CB: 4%-44%) and not significantly different from 3Y-TZP (54% CB: 32%-72%). Furthermore, at 300 N no significant differences in reliability were detected among groups, with a notable reduction in the reliability of all materials. Fractographic analyses showed that crack initiated at the interface between the composite core and the ceramic crowns due to tensile stress generated at the intaglio surface. CONCLUSIONS: Ultrathin lithium disilicate crowns demonstrated higher reliability relative to zirconia crowns at functional loads. Lithium disilicate and zirconia crown's reliability decreased significantly for missions at higher loads and similar failure modes were observed regardless of crown material. The indication of 0.5 mm thickness crowns in high-load bearing regions must be carefully evaluated. CLINICAL SIGNIFICANCE: Ultraconservative lithium disilicate and zirconia crowns of 0.5 mm thickness may be indicated in anterior restorations and pre-molars. Their clinical indication in high-load requirement regions must be carefully evaluated.

Minimally processed recycled yttria-stabilized tetragonal zirconia for dental applications: Effect of sintering temperature on glass infiltration.

This study aimed to develop a recycling process for the remnants of milled 3Y-TZP and enhance their properties using glass infiltration. 3Y-TZP powder was gathered from the vacuum system of CAD-CAM milling equipment, calcined and sieved (x < 75 µm). One hundred twenty discs were fabricated and pre-sintered at 1000 °C/h. These specimens were then divided into four groups, categorized by glass infiltration (non-infiltrated [Zr] or glass-infiltrated [Zr-G]) and sintering temperature (1450 °C [Zr-1450] or 1550 °C [Zr-1550]/2h). After sintering, the specimens were characterized by X-Ray Diffraction (XRD), relative density measurement, and scanning electron microscopy and energy dispersive spectroscopy (SEM-EDS). The biaxial flexural strength test was performed according to the ISO 6872 and followed by fractographic analysis. Subsequent results were analyzed using Weibull statistics. Relative density values of the sintered specimens from Zr-1450 and Zr-1550 groups were 86.7 ± 1.5% and 92.2 ± 1.7%, respectively. Particle size distribution revealed particles within the range of 0.1-100 µm. XRD analysis highlighted the presence of the ZrO2-tetragonal in both the Zr-1450 and Zr-1550 groups. Glass infiltration, however, led to the formation of the ZrO2-monoclinic of 9.84% (Zr-1450-G) and 18.34% (Zr-1550-G). SEM micrographs demonstrated similar microstructural characteristics for Zr-1450 and Zr-1550, whereas the glass-infiltrated groups exhibited comparable infiltration patterns. The highest characteristic strength was observed in the glass-infiltrated groups. Fractographic analyses suggested that fracture origins were related to defects on the tensile side, which propagated to the compression side of the samples. Both the sintering temperature and glass infiltration significantly influenced the mechanical properties of the 3Y-TZP recycled.

A Narrative Review on Polycrystalline Ceramics for Dental Applications and Proposed Update of a Classification System.

Dental zirconias have been broadly utilized in dentistry due to their high mechanical properties and biocompatibility. Although initially introduced in dentistry as an infrastructure material, the high rate of technical complications related to veneered porcelain has led to significant efforts to improve the optical properties of dental zirconias, allowing for its monolithic indication. Modifications in the composition, processing methods/parameters, and the increase in the yttrium content and cubic phase have been presented as viable options to improve zirconias' translucency. However, concerns regarding the hydrothermal stability of partially stabilized zirconia and the trade-off observed between optical and mechanical properties resulting from the increased cubic content remain issues of concern. While the significant developments in polycrystalline ceramics have led to a wide diversity of zirconia materials with different compositions, properties, and clinical indications, the implementation of strong, esthetic, and sufficiently stable materials for long-span fixed dental prostheses has not been completely achieved. Alternatives, including advanced polycrystalline composites, functionally graded structures, and nanosized zirconia, have been proposed as promising pathways to obtain high-strength, hydrothermally stable biomaterials. Considering the evolution of zirconia ceramics in dentistry, this manuscript aims to present a critical perspective as well as an update to previous classifications of dental restorative ceramics, focusing on polycrystalline ceramics, their properties, indications, and performance.

3D Printing Applications for Craniomaxillofacial Reconstruction: A Sweeping Review.

The field of craniomaxillofacial (CMF) surgery is rich in pathological diversity and broad in the ages that it treats. Moreover, the CMF skeleton is a complex confluence of sensory organs and hard and soft tissue with load-bearing demands that can change within millimeters. Computer-aided design (CAD) and additive manufacturing (AM) create extraordinary opportunities to repair the infinite array of craniomaxillofacial defects that exist because of the aforementioned circumstances. 3D printed scaffolds have the potential to serve as a comparable if not superior alternative to the "gold standard" autologous graft. In vitro and in vivo studies continue to investigate the optimal 3D printed scaffold design and composition to foster bone regeneration that is suited to the unique biological and mechanical environment of each CMF defect. Furthermore, 3D printed fixation devices serve as a patient-specific alternative to those that are available off-the-shelf with an opportunity to reduce operative time and optimize fit. Similar benefits have been found to apply to 3D printed anatomical models and surgical guides for preoperative or intraoperative use. Creation and implementation of these devices requires extensive preclinical and clinical research, novel manufacturing capabilities, and strict regulatory oversight. Researchers, manufacturers, CMF surgeons, and the United States Food and Drug Administration (FDA) are working in tandem to further the development of such technology within their respective domains, all with a mutual goal to deliver safe, effective, cost-efficient, and patient-specific CMF care. This manuscript reviews FDA regulatory status, 3D printing techniques, biomaterials, and sterilization procedures suitable for 3D printed devices of the craniomaxillofacial skeleton. It also seeks to discuss recent clinical applications, economic feasibility, and future directions of this novel technology. By reviewing the current state of 3D printing in CMF surgery, we hope to gain a better understanding of its impact and in turn identify opportunities to further the development of patient-specific surgical care.

Reliability and Failure Mode of Ti-Base Abutments Supported by Narrow/Wide Implant Systems.

To assess the reliability and failure modes of Ti-base abutments supported by narrow and wide-diameter implant systems. Narrow (Ø3.5 × 10 mm) and wide (Ø5 × 10 mm) implant systems of two different manufacturers with internal conical connections (16°) and their respective Ti-base abutments (3.5 and 4.5 mm) were evaluated. Ti-base abutments were torqued to the implants, standardized metallic maxillary incisor crowns were cemented, and step stress accelerated life testing of eighteen assemblies per group was performed in three loading profiles: mild, moderate, and aggressive until fracture or suspension. Reliability for missions of 100,000 cycles at 100 and 150 N was calculated, and fractographic analysis was performed. For missions at 100 N for 100,000 cycles, both narrow and wide implant systems exhibited a high probability of survival (≥99%, CI: 94-100%) without significant differences. At 150 N, wide-diameter implants presented higher reliability (≥99%, CI: 99-100%) compared to narrow implants (86%, CI: 61-95%), with no significant differences among manufacturers. Failure mode predominantly involved Ti-base abutment fractures at the abutment platform. Ti-base abutments supported by narrow and wide implant systems presented high reliability for physiologic masticatory forces, whereas for high load-bearing applications, wide-diameter implants presented increased reliability. Failures were confined to abutment fractures.

Alumina-toughened zirconia nanocomposite: Aging effect on microstructural, optical, and mechanical properties.

OBJECTIVES: To process an alumina-toughened zirconia (ATZ) nanocomposite and to characterize its crystalline phases, microstructure, residual stress, mechanical and optical properties before and after two different artificial aging methodologies. METHODS: Disc-shaped specimens were obtained through uniaxial pressing of a commercial ATZ powder comprised of 80%ZrO2 / 20%Al2O3, with a particle size of 50 nm and 150 nm, respectively. Sintering was performed at 1500ºC for 2 h. Groups were established according to the aging protocol as immediate (ATZ-I) and aged either in autoclave (ATZ-A) or hydrothermal reactor (ATZ-R) at 134 ºC for 20 h at 2.2 bar. Crystalline phases and microstructure were assessed by X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. Residual stress was evaluated by Raman spectroscopy. Contrast Ratio (CR) and Translucency Parameter (TP) were calculated to characterize optical properties. Mechanical properties were analyzed through Vickers microhardness, fracture toughness, and biaxial flexural strength test. RESULTS: XRD spectra of both aging protocols revealed the presence of monoclinic zirconia (20-31%), where higher phase transformation was observed after aging in hydrothermal reactor. Optical properties evaluation demonstrated high opacity (CR: 0.99) and masking ability (TP: 0.26), with no significant differences after aging. Raman spectroscopy evidenced the presence of residual compressive stresses in the aged groups, being significantly higher for ATZ-R (-215.2 MPa). As-sintered specimens revealed hardness of ∼12.3 GPa and fracture toughness of ∼1.9 MPa.m1/2. Characteristic strength was 740 MPa for ATZ-I, 804 MPa for ATZ-A, and 879 MPa for ATZ-R, with significant differences between groups. Weibull modulus ranged from 16.5 to 18.8. All groups demonstrated high reliability up to 500 MPa stress missions (99-100%), with no significant differences after aging. SIGNIFICANCE: The experimental ATZ nanocomposite presented high opacity and a high Weibull modulus. While aging created internal compressive stress responsible for an increase in characteristic strength, the nanocomposite was susceptible to hydrothermal degradation. Further studies are required to evaluate its degradation kinetics at low temperatures.

In vitro assessment of the effect of luting agents, abutment height, and fatigue on the retention of zirconia crowns luted to titanium base implant abutments.

STATEMENT OF PROBLEM: The bonding of implant-supported prostheses is determined by abutment material, convergence angle, height, surface treatment, and luting agents. However, studies evaluating the bonding of luting agents to titanium base abutments with different heights under fatigue conditions are scarce. PURPOSE: The purpose of this in vitro study was to evaluate the retention of zirconia crowns bonded with different luting agents to titanium base abutments of different heights before and after fatigue testing. MATERIAL AND METHODS: Zirconia crowns were designed, milled, and distributed into 4 experimental groups according to the luting agents (G-Multi Primer/G-Cem LinkForce [MP/GC] and Scotchbond Universal/RelyX Ultimate [SU/RU]) and titanium base abutment heights (2.5 mm and 4 mm) (n=10). Pull-out testing was performed in a universal testing machine at a crosshead speed of 1 mm/min until crown displacement. Fatigue testing was performed by an electric precision fatigue simulator (1×106 cycles; 100 N; and 15 Hz), followed by pull-out testing of fatigued specimens. Collected data were statistically evaluated by using a linear mixed model after post hoc comparisons by the least significant difference test (α=.05). RESULTS: Luting agents, abutment heights, and fatigue influenced the bonding retention of zirconia crowns to titanium base abutments. SU/RU agents promoted higher pull-out compared with MP/GC for both abutment heights before and after fatigue. Higher abutment height increased pull-out regarding lower abutment height for SU/RU materials before and after fatigue testing. Although fatigue had no significant effect on the pull-out of MP/GC, lower bond retention was observed for SU/RU after fatigue, regardless of abutment height. CONCLUSIONS: Luting agent composition and the interaction with abutment height and fatigue influenced the retention of zirconia crowns to titanium base abutments.

Probability of survival and failure mode of endodontically treated incisors without ferrule restored with CAD/CAM fiber-reinforced composite (FRC) post-cores.

PURPOSE: This study evaluated the probability of survival and failure mode of endodontically treated incisors without ferrule restored with CAD/CAM FRC post-cores. METHODS: Root canals of bovine incisors were treated, leaving post preparations of ∼10 mm. Teeth were allocated into three groups: (i) cast metal post-core, (ii) FRC prefabricated post with a direct resin core build-up, and (iii) CAD/CAM FRC post-core. Posts and zirconia crowns were cemented using resin cement. Specimens were subjected to step-stress accelerated-life fatigue testing in water. Use level probability Weibull curves, probability of survival for a mission of 100,000 cycles at 25, 50, and 100 N, Weibull modulus, and characteristic strength were calculated and plotted. Failure mode was examined under a stereomicroscope. RESULTS: Restored incisors demonstrated high probability of survival (93-100%) for missions estimated at 25 and 50 N, irrespective of post-core foundation. At 100 N, incisors restored with metal posts presented significantly higher probability of survival (99%) relative to CAD/CAM posts (79%), whereas FRC groups demonstrated no significant difference. Weibull analysis indicated no significant difference on the Weibull modulus (m = 3.38-5.92). Incisors reconstructed with metal post-cores (431 N) presented significantly higher characteristic strength relative to prefabricated (200 N) and CAD/CAM (202 N) FRC post-cores. While post fracture was the chief failure mode for prefabricated and CAD/CAM FRC post-cores, post and/or root fracture were the main event for metal post-cores. CONCLUSION: Endodontically treated incisors without ferrule restored with CAD/CAM FRC post-cores presented promising probability of survival for loads compatible with anterior masticatory forces and favorable failure modes.

The Influence of Surface Treatment on Osseointegration of Endosteal Implants Presenting Decompressing Vertical Chambers: An In Vivo Study in Sheep.

PURPOSE: To qualitatively and quantitatively evaluate histologic osseointegration parameters of implants designed with decompressing vertical chambers between the threads with two different surface treatments (TiO2 blasting + maleic acid vs TiO2 blasting + maleic + HCl) in a large translational animal model at 3 and 6 weeks in vivo. MATERIALS AND METHODS: Nine female sheep were used, and 72 implants with trapezoidal threads and decompressing vertical chambers of 0.6 mm in diameter and 0.2 mm in depth were placed in the ilium crest. After 3 and 6 weeks, the animals were euthanized, and biomechanical and histomophometric analyses were performed. RESULTS: Survey histologic evaluation indicated intimate contact between the bone and the implants independent of surface treatment at both times in vivo. Bone formation at both time points depicted an intramembranous-type healing pattern between the implant threads. The mean removal torque values for all groups showed a relative increase in removal torque from 3 to 6 weeks. In terms of bone area fraction occupancy analysis, significant differences were found at 6 weeks between surface treatments (P = .046), where the experimental surface yielded higher degrees of bone area fraction occupancy. CONCLUSION: Conical implants with decompressing vertical chambers between threads presented similar osseointegration parameters regarding bone-toimplant contact and torque-out test values irrespective of surface treatment. However, shifting from a minimally rough to a moderately rough surface (experimental surface with supplemental acid-etching) resulted in significantly improved bone area fraction occupancy at 6 weeks.

Stability of fatigued and aged ZTA compared to 3Y-TZP and Al2O3 ceramic systems.

To evaluate the effect of fatigue and aging on the crystalline content and reliability of a zirconia-toughened-alumina (ZTA) composite compared to its individual counterpart materials (3Y-TZP and Al2O3). Thirty-six disc-shaped specimens per group were obtained to comply with ISO 6872:2015. Crystalline content, microstructure and reliability of experimental groups were evaluated in four stages: 1) immediate; 2) aged; 3) fatigued; 4) aged + fatigue. Aging was performed in autoclave and Step-Stress-Accelerated-Life-Testing (SSALT) was performed using three stress profiles. Weibull statistics were used to determine Weibull parameters and life-expectancy. A significant increase in monoclinic phase in 3Y-TZP was observed after aging (19.31%), fatigue (17.88%) and aging + fatigue (55.81%), while ZTA evidenced minimal variation among all conditions (<5.69%). 3Y-TZP presented higher reliability than ZTA at 300 and 500 MPa, and ZTA outperformed Al2O3 at the same stress missions. None of the ceramics yielded acceptable reliability at 800 MPa. A higher characteristic strength was observed for 3Y-TZP, followed by ZTA and Al2O3. While after aging ZTA and Al2O3 remained stable, 3Y-TZP exhibited a significant increase in the characteristic stress. Aging did not affect the reliability of ZTA and Al2O3. 3Y-TZP demonstrated an increase in monoclinic content and characteristic strength after aging.

Temporary materials used in prosthodontics: The effect of composition, fabrication mode, and aging on mechanical properties.

PURPOSE: To evaluate the effect of composition, fabrication mode, and thermal cycling on the mechanical properties of different polymeric systems used for temporary dental prostheses. MATERIALS AND METHODS: Standard bar-shaped specimens (25 × 2 × 2 mm) were fabricated of six polymeric systems of varying compositions and fabrication modes (n = 10/group): conventional PMMA (Alike, GC) - group CGC; conventional PMMA (Dêncor, Clássico) - group CD; bis-acryl (Tempsmart, GC) - group BGC; bis-acryl (Yprov, Yller) - group BY; milled PMMA (TelioCAD, Ivoclar) - group MI; 3D printed bis-acryl - (Cosmos Temp, Yller) group PY. Half of the specimens were subjected to 5000 thermal cycles (5 °C to 55 °C). Three-point bending tests were performed using a universal testing machine with a crosshead speed set to 0.5 mm/min. Flexural strength and elastic modulus were calculated from the collected data. FTIR spectra were recorded pre and post curing and after thermal cycling to evaluate material composition and degree of conversion. Energy-dispersive spectroscopy (EDS) and scanning electron microscope (SEM) were utilized to examine the composition and micromorphology of the systems, respectively. Data were analyzed using two-analysis of variance and Tukey tests (α = 0.05). RESULTS: FTIR spectra indicated that BGC, BY and PY groups corresponded to urethane dimethacrylate systems (bis-acryl), while CGC, CD, and MI groups corresponded to monomethacrylate systems, polymethyl methacrylate (PMMA). Bis-acryl BGC system yeilded the highest flexural strength (80 MPa), followed by the milled PMMA MI system (71 MPa), both statistically significant different relative to other groups. Bis-acryl BY exhibited the lowest flexural strength (27 MPa). Thermocycling significantly increased the flexural strength of all polymeric systems (∼10-15 MPa), except for the 3D-printed PY group. Bis-acryl BGC (1.89 GPa) and conventional PMMA CGC (1.66 GPa) groups exhibited the highest elastic modulus, followed by milled PMMA MI group (1.51 GPa) and conventional PMMA CD (1.45 GPa) systems, with significant difference detected between BGC group and MI and CD groups. The 3D printed PY (0.78 GPa) and bis-acryl BY (0.47 GPa) systems presented the lowest elastic modulus. Thermocycling did not have a significant influence on the elastic modulus. FTIR spectra indicate water sorption and release of unreacted monomers as well as increased degree of conversion (∼5-12%) after thermal cycling. CONCLUSION: Composition and fabrication mode and thermal cycling significantly affected the mechanical properties of polymeric systems used for temporary dental prostheses.

Laddec® versus Bio-Oss®: The effect on the healing of critical-sized defect - Calvaria rabbit model.

The aim of this study was to evaluate the in vivo performance of two different deproteinized bovine bone (DBB) grafting materials: DBBB (Bio-Oss®) and DBBL (Laddec®), for the regeneration of critically sized (8 mm) defects in rabbit's calvaria. Three round-shaped defects were surgically created in the calvaria of 13 New Zealand White rabbits proximal to the coronal suture in the parietal bone. Two of the defects were filled with one of the grafting materials while a third was left empty to serve as a negative control. Bone regeneration properties were evaluated at 4- and 8-weeks after implantation by means of histological and histomorphometrical analyses. Statistical analyses were performed through a mixed model analysis with fixed factors of time and material. Histological evaluation of the control group evidenced a lack of bridging bone formation across the defect sites at both evaluation time points. For the experimental groups, new bone formation was observed around the defect periphery and to progress radially inwards to the center of the defect site, regardless of the grafting material. Histomorphometric analyses at 4 weeks demonstrated higher amount of bone formation through the defect for DBBB group. However, at 8 weeks, DBBL and DBBB demonstrated osteoconductivity and low resorption rates with evidence of statistically similar bone regeneration through the complete boney defect. Finally, DBBB presented lower soft tissue migration within the defect when compared to DBBL at both evaluation time points. DBBB and DBBL presented similar bone regeneration performance and slow resorption rates. Although both materials promoted bone regeneration through the complete defect, DBBB presented lower soft tissue migration within the defects at 4- and 8-weeks.

Effect of leukocyte-platelet-rich fibrin in bone healing around dental implants placed in conventional and wide osteotomy sites: A pre-clinical study.

Leukocyte-platelet-rich fibrin (L-PRF) has been suggested for gap management for immediate implant placement when the distance is greater than 2 mm. However, there remains a paucity in hierarchically designed research to support this application. The present study aimed to evaluate the effect of L-PRF on the osseointegration parameters of dental implants placed after conventional osteotomy of surgically created bone defects that simulate post extraction sockets in a canine model after 3, 6, and 12 weeks in vivo. Eighty dental implants (Intra-Lock, Boca Raton, FL) were placed in the radius of 13 beagle dogs. The experiment consisted of 4 groups (n = 20 implants/group): 1) Regular osteotomy (Reg n/L-PRF); 2) Regular osteotomy and implant placement with L-PRF membrane (Reg L-PRF); 3) Wide osteotomy with no gap management performed, where an osteotomy/bony defect (6 mm of diameter and ~5 mm deep) was created to simulate immediate implant placement in post-extraction sockets, and the gap was left for spontaneous healing (Wide nL-PRF); and 4) Wide osteotomy with L-PRF gap management (Wide L-PRF). L-PRF membranes were obtained by blood drawn from each subject and centrifuged at 2700 rpm (408 RCF-clot) for 12 min. In the experimental groups where L-PRF was utilized, the membrane was inserted into the osteotomy site prior to implant placement. Six dogs had implants placed in the radius for 3 weeks; and 7 dogs had implants placed in the left radius for 6 weeks and in the right radius for 12 weeks. At the corresponding experimental time points, samples were harvested, and subjected to histological processing for qualitative and quantitative analyses, via bone-to-implant contact (BIC) and bone-area-fraction occupancy (BAFO). Qualitative analysis demonstrated increased amounts of bone formation around the implant and within the healing chambers over time for all groups. While comparable histological features were observed for both Reg groups (L-PRF and nL-PRF), the gap management performed in Wide L-PRF group resulted in effective gap filling with improved bone growth in close proximity to the implant surface. Quantitative analyses of BIC and BAFO yielded higher values for both variables at 3 weeks for Wide L-PRF (~38% and ~56% respectively) compared to Wide nL-PRF (~20% for BIC and BAFO) (p < .03). No statistical differences were detected between Wide groups at 6 and 12 weeks, neither between Reg groups, independent of the association with or without the L-PRF membrane at all healing times. L-PRF placed within wide osteotomies, prior to implant placement, resulted in increased early bone formation compared to unfilled wide osteotomies at the early healing time (3 weeks in vivo).

A Histologic and Histomorphometric Evaluation of an Allograft, Xenograft, and Alloplast Graft for Alveolar Ridge Preservation in Humans: A Randomized Controlled Clinical Trial.

The aim of this study was to clinically evaluate the guided bone regeneration (GBR) potential of allograft, xenograft, and alloplastic materials in combination with resorbable membranes in extraction sockets. The qualitative and quantitative assessments of this prospective study were accomplished through histologic and histomorphometric analysis. Three experimental groups and 1 control group for comparison (n = 8) received either an allograft (human cancellous bone, freeze dried, Deutsches Institut für Zell und Gewebeersatz, Berlin, Germany), xenograft (BioOss, Geistlich Pharma AG, Wolhusen, Switzerland), or alloplast (biphasic calcium sulphate, Bondbone, MIS Implants Technologies Ltd., Charlotte, NC). The negative control group received no regenerative material. Tissue samples were then qualitatively and quantitatively evaluated as a function of percentage of new vital bone, graft particles content, soft tissue, and bone marrow over time. All 3 study groups presented bone volume suitable for the successful placement of a dental implant. The xenograft group yielded significantly less amount of vital bone compared with the allograft and alloplast groups. When comparing the percentage of residual graft particles, there was significantly greater amounts associated with the xenograft group in contrast to the allograft and alloplast groups. Similarly, a significantly increased amount of soft tissue percentage was observed within the xenograft group relative to all other groups. No significant differences were observed in the percentage of residual graft particles between the allograft and alloplast groups. There were also no significant differences detected in vital bone percentage between the allograft, alloplast, and control groups. When evaluating the bone marrow percentage, the only significant difference detected was between the xenograft and alloplast materials. Overall, no complications (ie, fever, malaise, purulence or fistula) were observed during the entirety of clinical trial among all patients. The greatest GBR potential was associated with the allograft material because of the greater degree of vital bone and the lowest percentage of residual graft particles. All studied bone substitute materials resulted in bone apposition for efficient use in alveolar ridge preservation procedures.

Ultra-translucent zirconia processing and aging effect on microstructural, optical, and mechanical properties.

OBJECTIVES: To evaluate the effect of the ceramic processing and aging method on the microstructure, optical, and mechanical properties of a third generation ultra-translucent zirconia, yttria partially stabilized zirconia (5Y-PSZ). METHODS: In-house discs were obtained through uniaxial and isostatic pressing an ultra-translucent Y-PSZ powder and sintering at 1450 °C for 2 h. As control, a commercial disc was milled from pre-sintered blocks fabricated with the same 5Y-PSZ powder through isostatic pressing and sintered under the same protocol. Discs were allocated into three groups according to aging condition as immediate (non-aged) and aged using autoclave or hydrothermal reactor at 134ºC for 20 h at 2.2 bar. Crystalline content and microstructure were evaluated using X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. Optical properties were determined using reflectance data to calculate the contrast ratio (CR) and translucency parameter (TP). Mechanical properties were assessed by Vickers hardness, fracture toughness and biaxial flexural strength tests. RESULTS: XRD spectra revealed a prevalence of cubic (70%) and tetragonal (30%) phases, and the SEM images showed a dense fully crystalline ceramic matrix for both materials. Crystalline content and microstructure of the in-house and commercial 5Y-PSZs were not affected by aging. As-sintered 5Y-PSZs demonstrated similar CR (~0.6) and TP (~18) values, as well as Vickers hardness (~14 GPa) and fracture toughness (~3.8 Mpa.m1/2), with no significant alteration after both aging methods. In-house and commercial Y-PSZs Weibull moduli ranged from 3.0 to 5.3. 5Y-PSZ processing methods resulted in similar characteristic strength after sintering (592-618 Mpa). While commercial 5Y-PSZ showed no significant influence of aging on strength, hydrothermal reactor aging significantly decreased the in-house Y-PSZ characteristic strength (474 Mpa). Both 5Y-PSZs demonstrated high reliability up to 300-Mpa strength missions, with no detrimental effect of aging (88-100%). SIGNIFICANCE: Irrespective of the processing method, ultra-translucent 5Y-PSZ showed high aging resistance and translucency stability, as well as strength corresponding to the indication up to short-span anterior prostheses.

Effects of local single dose administration of parathormone on the early stages of osseointegration: A pre-clinical study.

The present study aimed to evaluate the effect of parathormone (PTH) administered directly to the implant's surface prior to insertion, using a large translational animal model. Sixty titanium implants were divided into four groups: (i) Collagen, control group, where implants were coated with Type-I Bovine-collagen, and three experimental groups, where implants received varying doses of PTH: (ii) 12.5, (iii) 25, and (iv) 50 µg, prior to placement. Fifteen female sheep (~2 years old, weighing ~65 kg) received four implants in an interpolated fashion in C3, C4 or C5 vertebral bodies. After 3-, 6- and 12-weeks, samples were harvested, histologically processed, qualitatively and quantitatively assessed for bone-to-implant contact (BIC) and bone area fraction occupancy (BAFO). BIC yielded lower values at 6-weeks for 50 µg relative to the control group, with no significant differences, when compared to the 12.5- and 25-µg. No significant differences were detected at 6-weeks between collagen, 12.5- and 25-µg groups. At 3- and 12-weeks, no differences were detected for BIC among PTH groups. With respect to BAFO, no significant differences were observed between the control and experimental groups independent of PTH concentration and time in vivo. Qualitative observations at 3-weeks indicated the presence of a more mature bone near the implant's surface with the application of PTH, however, no significant differences in new bone formation or healing patterns were observed at 6- and 12-weeks. Single local application of different concentrations of PTH on titanium implant's surface did not influence the osseointegration at any time-point evaluation in low-density bone.