Short-term Results of the Masking Effect of an Infiltrant Resin on Mild Molar Incisor Hypomineralization Lesions in Anterior Teeth.

This non-controlled clinical study evaluated the masking effect of an infiltrant resin on mild molar incisor hypomineralization (MIH) lesions. Thirty MIH-affected anterior teeth with creamy/ white opacities from 12 children aged 6-15 years received the application of an infiltrant resin (Icon- DMG). Standard photographs were taken before (T1), immediately after (T2), and 1 week after (T3) resin infiltration. Two calibrated examiners qualitatively analyzed the color match using the Fédération Dentaire Internationale (FDI) scale. The binomial distribution test analyzed the scores of the color match at T1 with T2 and T3, and McNemar's test analyzed the scores of the color match between T2 and T3 (α=0.05). There was a significant increase in color match between T1 and T2 (p=0.0005), between T1 and T3 (p=0.0005), and between T2 and T3 (p=0.0019). It was concluded that infiltrant resin was effective in improving the esthetic appearance of creamy/white opacities on MIH-affected anterior teeth.

Effect of Different Computer-aided Design/Computer-aided Manufacturing (CAD/CAM) Materials and Thicknesses on the Fracture Resistance of Occlusal Veneers.

The aim was to evaluate, in vitro, the influence of different computer-aided design/computer-aided manufacturing (CAD/CAM) materials (IPS e.max CAD, Vita Enamic, and Lava Ultimate) and thicknesses (0.6 mm and 1.5 mm) on the fracture resistance of occlusal veneers. Sixty human third molars were prepared to simulate advanced erosion of the occlusal surface, and the teeth were randomly divided into six experimental groups (n=10) according to the material and thickness used to build the veneers. Ten sound teeth formed the control group. The veneers were adhesively luted and submitted to mechanical cyclic loading (1 million cycles at 200-N load). The fracture resistance test was performed in a universal testing machine. The failures were classified as "reparable" and "irreparable." According to two-way analysis of variance and the Tukey test, the interaction (material × thickness) was significant ( p=0.013). The highest fracture resistance was obtained for IPS e.max CAD at a 1.5-mm thickness (4995 N) and was significantly higher compared to the other experimental groups ( p<0.05). The lowest fracture resistance was obtained for Vita Enamic at 0.6 mm (2973 N), although this resistance was not significantly different from those for IPS e.max CAD at 0.6 mm (3067 N), Lava Ultimate at 0.6 mm (3384 N), Vita Enamic at 1.5 mm (3540 N), and Lava Ultimate at 1.5 mm (3584 N) ( p>0.05). The experimental groups did not differ significantly from the sound teeth (3991 N) ( p>0.05). The failures were predominantly repairable. The occlusal veneers of IPS e.max CAD, Vita Enamic, and Lava Ultimate, with thicknesses of 0.6 mm and 1.5 mm, obtained fracture resistances similar to those associated with sound teeth.

Influence of immediate dentin sealing techniques on cuspal deflection and fracture resistance of teeth restored with composite resin inlays.

SUMMARY This research evaluated the influence of immediate dentin sealing (IDS) techniques on cuspal deflection and fracture resistance of teeth restored with composite resin inlays. Forty-eight maxillary premolars were divided into four groups: G1, sound teeth (control); G2, without IDS; G3, IDS with Clearfil SE Bond (CSE); and G4, IDS with CSE and Protect Liner F. The teeth from groups 2, 3, and 4 received mesio-distal-occlusal preparations. The impressions were made with vinyl polysiloxane, followed by provisional restoration and storage in water for seven days. The impressions were poured using type IV die stone, and inlays with Filtek Z250 composite resin were built over each cast. The inlays were luted with Panavia F. After storage in water for 72 hours, a 200-N load was applied on the occlusal surface using a metal sphere connected to a universal testing machine, and the cuspal deflection was measured with a micrometer. The specimens were then submitted to an axial load until failure. The following mean cuspal deflection (µm) and mean fracture resistance (N) followed by the same lowercase letter represent no statistical difference by analysis of variance and Tukey (p<0.05): cuspal deflection: G1, 3.1 ± 1.5(a); G2, 10.3 ± 4.6(b); G3, 5.5 ± 1.8(ac); and G4, 7.7 ± 5.1(bc); fracture resistance: G1, 1974 ± 708(a); G2, 1162 ± 474(b); G3, 700 ± 280(b); and G4, 810 ± 343(b). IDS with CSE allowed cuspal deflection comparable with that associated with sound teeth. The application of Protect Liner F did not contribute to a decrease in cuspal deflection. The IDS techniques did not influence the fracture resistance of teeth.

Fracture resistance of root filled molar teeth restored with glass fibre bundles.

AIM: To evaluate the effect of unidirectional or woven glass fibre tapes inserted into MOD cavity preparations on the fracture resistance of root filled molar teeth. METHODOLOGY: Extracted human molar teeth were randomly divided into six groups (n = 15) : G1 - sound teeth, control; G2 - MOD cavity preparation; G3 - MOD + root canal treatment (Endo); G4 - MOD + Endo + composite resin restoration (Resin); G5 - MOD + Endo + unidirectional fibre (UF) + Resin; G6 - MOD + ;Endo + woven fibre (WF) + Resin. The teeth were subjected to a compressive fracture test in a universal testing machine. After testing, two failure modes were classified: pulp chamber floor or cusp. RESULTS: The highest and the lowest mean fracture strengths were found in sound teeth (G1) (4960N) and MOD + root canal treatment (G3) (612.84N), respectively, with significant differences from the other groups (P < 0.05). The remaining groups had statistically similar means. In G5 and G6, there was a tendency for fracture to occur in the pulp chamber floor compromising tooth integrity. CONCLUSIONS: The insertion of glass fibres into MOD cavity preparations and restoring them with composite resin was not different than molar teeth filled with composite resin only in terms of fracture resistance. Fibres placed into MOD cavities do not reinforce teeth.

Comparative study of influence on tensile bond strength of a composite to dentin using Er:YAG laser, air abrasion, or air turbine for preparation of cavities.

OBJECTIVES: The purpose of this study was to evaluate, in vitro, the tensile bond strength of the Single Bond (3M) adhesive system placed over dentin surfaces treated with air turbine, Er:YAG laser without contact and in focused or air abrasion. SUMMARY BACKGROUND DATA: The use of dentin adhesives is a well-established clinical routine among the dentists. However, there have been few reports comparing the influence of the Er:YAG laser, air abrasion, and air turbine on the Single Bond tensile bond strength of adhesives systems to dentin fact that could influence which tools dentists select for use in cavity preparations. METHODS: Twenty-three extracted retained human molars were used in this study. The coronal portion was divided in two parts and fixed in acrylic resin; the occlusal surface was abraded to a 2-mm width with a mechanic lathe until the dentin surface was completely exposed. The dental portions were divided into three groups of 15 each and treated with Er:YAG laser, air abrasion, or air turbine. A 3 mm hole in the center of each tooth was marked off using contact paper. Single Bond (3M) adhesive system was applied after acid phosphoric at 35% application for 15 sec over dentin surfaces. A resin composite cone was built into the delimited area to accomplish the tensile bond strength test on the EMIC universal test machine. The specimens were then evaluated by stereoscopy to determine the type of failures into the dentin-adhesive-resin composite surface. RESULTS: The tensile test was performed using the universal testing machine EMIC DL-2000 at a cross-head speed of 0.5 mm/min. The average results were: air turbine (17.52 MPa), Er:YAG laser (16.65 MPa) and air abrasion (15.83 MPa). Statistical treatment by ANOVA and Tukey's test (p < 0.01) showed no significant differences between the groups tested. The tensile bond strength test to the dentin showed no significant difference among the three groups when the Single Bond was used after the 35% phosphoric-acid conditioning. The stereoscopy showed a predominant adhesive failure in all groups. CONCLUSION: These results suggest that Single Bond tensile bond strength is the same as dentin prepared by Er:YAG laser, air abrasion, or air turbine.