RESUMEN
Aqueous zinc-ion batteries hold promise for sustainable energy storage, yet challenges in finding high-performance cathode materials persist. Polyoxovanadates (POVs) are emerging as potential candidates due to their structural diversity and robust redox activity. Despite their potential, issues like dissolution in electrolytes, structural degradation, and byproduct accumulation persist. This work introduces a POV-based hydrophobic two-dimensional (2D) layered superstructure that addresses these challenges. The hydrophobic nature minimizes POV dissolution, enhancing structural stability and inhibiting phase transitions during cycling. The 2D arrangement ensures a larger surface area and improved electronic conductivity, resulting in faster kinetics and higher specific capacity. The superstructure demonstrates improved cycle life and an increased operating voltage, marking a significant advancement in POV-based cathode materials for aqueous zinc-ion batteries.
RESUMEN
Aqueous zinc metal batteries with mild acidic electrolytes are considered promising candidates for large-scale energy storage. However, the Zn anode suffers from severe Zn dendrite growth and side reactions due to the unstable interfacial pH and the absence of a solid electrolyte interphase (SEI) protective layer. Herein, a novel and simple mixed electrolyte strategy is proposed to address these problems. The mixed electrolytes of 2 M ZnSO4 and 2 M Zn (CF3 SO3 )2 can efficiently buffer the interfacial pH and induce the in situ formation of the organic-inorganic SEI layer, which eliminates dendrite growth and prevents side reactions. As a result, Zn anodes in mixed electrolyte exhibit a lifespan enhancement over 400 times, endure stable cycling over 270 h at a high DOD of 62% and achieve high Zn plating/stripping reversibility with an average CE of 99.5% for 1000 cycles at 1 mA cm-2 . The findings pave the way for developing practical electrolyte systems for Zn batteries.