RESUMEN
Two-dimensional (2D) lead halide perovskites are excellent candidates for X-ray detection due to their high resistivity, high ion migration barrier, and large X-ray absorption coefficients. However, the high toxicity and long interlamellar distance of the 2D perovskites limit their wide application in high sensitivity X-ray detection. Herein, we demonstrate stable and toxicity-reduced 2D perovskite single crystals (SCs) realized by interlamellar-spacing engineering via a distortion self-balancing strategy. The engineered low-toxicity 2D SC detectors achieve high stability, large mobility-lifetime product, and therefore high-performance X-ray detection. Specifically, the detectors exhibit a record high sensitivity of 13488 µC Gy1- cm-2, a low detection limit of 8.23 nGy s-1, as well as a high spatial resolution of 8.56 lp mm-1 in X-ray imaging, all of which are far better than those of the high-toxicity 2D lead-based perovskite detectors. These advances provide a new technical solution for the low-cost fabrication of low-toxicity, scalable X-ray detectors.
RESUMEN
0D Bi-based 329-type halide perovskite is demonstrated as a promising semiconductor for X-ray detection due to its strong X-ray absorption, superior stability, availability of large single crystals (SCs) and solution processibility at low temperature. However, its low mobility-lifetime product (µτ) limits its further improvement in detection sensitivity. Based on the first-principles calculations, this work designs a new 2D Bi-based 329-type halide perovskite using a mixed-halide-induced structural dimension regulation strategy. By using a continuous supply of a precursor solution, this work successfully grows inch-sized high-quality SCs. These SCs exhibit large µτ product, high resistivity, and low ion migration. The detectors fabricated using the SCs show X-ray detection sensitivity as high as 24,509 µC Gyair -1 cm-2, short response time of 315 µs, low detection limit of 4.3 nGy s-1, and superior stability. These properties are the best among all lead-free perovskite detectors and are comparable to those of the best lead-based perovskite detectors. The linear array detector assembled on the SCs for the first time also shows a high spatial resolution of 10.6 lp mm-1 during X-ray imaging. The high performance combined with superior stability of these new 329-type lead-free halide perovskite SCs is expected to promote a new generation of X-ray detection technologies.
RESUMEN
Metal halide perovskite single crystals (MHP-SCs) are known for their facile fabrication into large sizes using inexpensive solution methods. Owing to their combination of large mobility-lifetime products and strong X-ray absorption, they are considered promising materials for efficient X-ray detection. However, they suffer from large dark currents and severe ion migration, which limit their sensitivity and stability in critical X-ray detection applications. Herein, a heterointerface design is proposed to reduce both the dark current and ion migration by forming a heterojunction. In addition, the carrier transport performance is significantly improved using heterointerface engineering by designing a gradient band structure in the SCs. The SC heterojunction detectors exhibit a high sensitivity of 3.98 × 105 µC Gyair -1 cm-2 with a low detection limit of 12.2 nGyair s-1 and a high spatial resolution of 10.2 lp mm-1 during imaging. These values are among the highest reported for state-of-the-art MHP X-ray detectors. Moreover, the detectors show excellent stability under continuous X-ray irradiation and maintainclear X-ray imaging after 240 d. This study provides novel insights into the design and fabrication of X-ray detectors with high detection efficiency and stability, which are beneficial for developing inexpensive, high-resolution X-ray imaging equipment.
RESUMEN
Lead-free A3 Bi2 I9 -type perovskites are demonstrated as a class of promising semiconductors for high-performance X-ray detection due to their high bulk resistivity and strong X-ray absorption, as well as reduced ion migration. However, due to their long interlamellar distance along their c-axis, their limited carrier transport along the vertical direction is a bottleneck for their detection sensitivity. Herein, a new A-site cation of aminoguanidinium (AG) with all-NH2 terminals is designed to shorten the interlayer spacing by forming more and stronger NH···I hydrogen bonds. The prepared large AG3 Bi2 I9 single crystals (SCs) render shorter interlamellar distance for a larger mobility-lifetime product of 7.94 × 10-3 cm2 V-1 , which is three times higher than the value measured on the best MA3 Bi2 I9 SC (2.87 × 10-3 cm2 V-1 ). Therefore, the X-ray detectors fabricated on the AG3 Bi2 I9 SC exhibit high sensitivity of 5791 uC Gy-1 cm-2 , a low detection limit of 2.6 nGy s-1, and a short response time of 690 µs, all of which are far better than those of the state-of-the-art MA3 Bi2 I9 SC detectors. The combination of high sensitivity and high stability enables astonishingly high spatial resolution (8.7 lp mm-1 ) X-ray imaging. This work will facilitate the development of low-cost and high-performance lead-free X-ray detectors.