Theoretical Analysis of Superior Photodegradation of Methylene Blue by Cerium Oxide/Reduced Graphene Oxide vs. Graphene.

Density functional theory and a semi-empirical quantum chemical approach were used to evaluate the photocatalytic efficiency of ceria (CeO2) combined with reduced graphene oxide (rGO) and graphene (GP) for degrading methylene blue (MB). Two main aspects were examined: the adsorption ability of rGO and GP for MB, and the separation of photogenerated electrons and holes in CeO2/rGO and CeO2/GP. Our results, based on calculations of the adsorption energy, population analysis, bond strength index, and reduced density gradient, show favorable energetics for MB adsorption on both rGO and GP surfaces. The process is driven by weak, non-covalent interactions, with rGO showing better MB adsorption. A detailed analysis involving parameters like fractional occupation density, the centroid distance between molecular orbitals, and the Lewis acid index of the catalysts highlights the effective charge separation in CeO2/rGO compared to CeO2/GP. These findings are crucial for understanding photocatalytic degradation mechanisms of organic dyes and developing efficient photocatalysts.

Graphitic carbon nitride supported silver nanoparticles (AgNPs/g-C3N4): synthesis and photocatalytic behavior in the degradation of 2,4-dichlorophenoxyacetic acid.

Graphitic carbon nitride supported silver nanoparticles (AgNPs/g-C3N4) with 1%, 3%, and 5% AgNPs were successfully synthesized by an "ex situ" method with ultrasound of a mixture of AgNP solution and g-C3N4. The AgNP solution was prepared by chemical reduction with trisodium citrate, and g-C3N4 was synthesized from the urea precursor. The supported nanoparticles were characterized by X-ray diffraction spectroscopy (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), nitrogen adsorption-desorption (BET), Fourier transformation infrared (FTIR) and Raman spectroscopy, ultraviolet-visible diffuse reflectance spectroscopy (UV-Vis DRS), photoluminescence spectroscopy (PL), electron paramagnetic resonance (EPR) and electrochemical impedance spectroscopy (EIS) Nyquist plots. The visible light-driven photocurrent measurement was performed by three on-off cycles of intermittent irradiation. The analyses show that AgNPs were evenly dispersed on g-C3N4, and have sizes ranging from 40 to 50 nm. The optical properties of the AgNPs/g-C3N4 material were significantly enhanced due to the plasmonic effect of AgNPs. The photocatalytic activity of catalysts was evaluated by 2,4-D degradation under visible light irradiation (λ > 420 nm). In the reaction conditions: pH 2.2; C o (2,4-D) 40 ppm; a m/v ratio of 0.5 g L-1, AgNPs/g-C3N4 materials exhibit superior photocatalytic activity compared to the pristine g-C3N4. The studies on the influence of free radicals and photogenerated holes, h+, show that ˙OH, O2˙-, and h+ play decisive roles in the photocatalytic activity of AgNPs/g-C3N4. The TOC result indicates the minimal toxicity of the by-products formed during the 2,4-D degradation. In addition, the AgNPs/g-C3N4 catalytic activity under direct sunlight irradiation was similar to that under artificial UV irradiation. Based on these results, a possible mechanism is proposed to explain the enhanced photocatalytic activity and stability of AgNPs/g-C3N4. Theoretical calculations on the interaction between 2,4-D and g-C3N4, Ag/g-C3N4 was also performed. The calculated results show that the adsorption of 2,4-D on Ag-modified g-C3N4 is significantly more effective compared to pristine g-C3N4.