In Vitro Evaluation of Color and Surface Roughness Changes of Polyetheretherketone, Monolithic Zirconia, and Resin Nanoceramics Exposed to Staining Liquids.

BACKGROUND: This study aims to investigate color stability and surface roughness of polyetheretherketone (PEEK), zirconia, and hybrid ceramics while stored in different liquids. METHODS: A total of 240 specimens were prepared from monolithic zirconia, PEEK, and hybrid ceramics. All specimens were polished using rubber sets with different grain sizes. Color parameters (L*, a*, b*) were measured three times using a dental spectrophotometer in standard D65 lightning. Each group was divided into eight different groups to be kept in eight different solutions as distilled water, cola, red wine, tea, coffee, heptane, citric acid, and 50% ethanol. Specimens were held in solutions at 37°C for 12 days. Color measurements were repeated, and color change (ΔE) was calculated using the CIE Lab formula. RESULTS: The color difference of PEEK specimens was found above the clinically acceptable limit; however, color differences for monolithic zirconia produced by coffee were found within the clinically acceptable limits. ZR and HC specimens' color change values were found between threshold values (1<ΔE < 3.3). The differences observed in surface roughness levels amongst the ZR specimens could be caused by the polishing instrument and procedure. CONCLUSION: The color change of the materials was within acceptable limits, whereas the surface roughness increased more than 0.2 µm. Especially cola, heptane, and red wine significantly increased the mean surface roughness.

Effects of Coloring Liquid Dipping Time and Surface Finishing Procedures on the Optical Properties of Monolithic Zirconia.

BACKGROUND: Monolithic zirconia restorations can be produced from self-colored or uncolored blocks. The coloring procedure of uncolored blocks and surface treatments may affect the appearance of the restoration. AIM: The purpose of this study is to evaluate the effect of liquid coloring and surface treatments on optical properties of translucent monolithic zirconia. METHODS: All specimens were cut from zirconia blocks with a thickness of 1 mm. Specimens were dipped in the coloring liquids for 3 min, 5 min, and 7 min and then divided into groups of 10 specimens for surface treatments. Glaze and mechanical polishing were applied, and the color of the specimens was measured under the D65 lighting condition with a spectrophotometer device. Color values obtained from the CIE Lab formula and the translucency parameter (TP), opalescence parameter (OP), and contrast ratio (CR) were calculated. The normality of the data was confirmed with the Shapiro-Wilk test. A three-way analysis of variance (ANOVA) was used to assess the effect of dipping time, liquid shade, and surface treatments. RESULTS: The effect of liquid shade and dipping time on the TP, OP, and CR parameters were statistically significant, and the TP values were reduced with the application of coloring liquid. Mechanical polishing groups had higher OP values and lower TP values than glazed groups. CONCLUSION: In cases where high translucency is required, it may be advisable to use self-colored blocks and apply glaze as a surface treatment to achieve the desired optical properties.