Selective Growth of Stacking Fault Free ⟨100⟩ Nanowires on a Polycrystalline Substrate for Energy Conversion Application.

Cubic semiconductor nanowires grown along ⟨100⟩ directions have been reported to be promising for optoelectronics and energy conversion applications, owing to their pure zinc-blende structure without any stacking fault. But, until date, only limited success has been achieved in growing ⟨100⟩ oriented nanowires. Here we report the selective growth of stacking fault free ⟨100⟩ nanowires on a commercial transparent conductive polycrystalline fluorine-doped SnO2 (FTO) glass substrate via a simple and cost-effective chemical vapor deposition (CVD) method. By means of crystallographic analysis and density functional theory calculation, we prove that the orientation relationship between the Au catalyst and the FTO substrate play a vital role in inducing the selective growth of ⟨100⟩ nanowires, which opens a new pathway for controlling the growth directions of nanowires via the elaborate selection of the catalyst and substrate couples during the vapor-solid-liquid (VLS) growth process. The ZnSe nanowires grown on the FTO substrate are further applied as a photoanode in photoelectrochemical (PEC) water splitting. It exhibits a higher photocurrent than the ZnSe nanowires do without preferential orientations on a Sn-doped In2O3 (ITO) glass substrate, which we believe to be correlated with the smooth transport of charge carriers in ZnSe ⟨100⟩ nanowires with pure zinc-blende structures, in distinct contrast with the severe electron scattering happened at the stacking faults in ZnSe nanowires on the ITO substrate, as well as the efficient charge transfer across the intensively interacting nanowire-substrate interfaces.

Interaction-Dependent Interfacial Charge-Transfer Behavior in Solar Water-Splitting Systems.

Dual-band-gap systems are promising for solar water splitting due to their excellent light-harvesting capability and high charge-separation efficiency. However, a fundamental understanding of interfacial charge-transfer behavior in the dual-band-gap configuration is still incomplete. Taking CdS/reduced graphene oxide (CdS/RGO) nanoheterojunctions as a model solar water splitting system, we attempt here to highlight the interaction-dependent interfacial charge-transfer behavior based on both experimental observations and theoretical calculations. Experimental evidence points to charge transfer at the CdS-RGO interface playing a dominant role in the photocatalytic hydrogen production activity. By tuning the degree of reduction of RGO, the interfacial interaction, and, thereby, the charge transfer can be controlled at the CdS-RGO interface. This observation is supported by theoretical analysis, where we find that the interfacial charge transfer is a balance between the effective single-electron- and hole-transfer probability and the surface free electron and hole concentration, both of which are related to the surface potential and tailored by interfacial interaction. This mechanism is applicable to all systems for solar water splitting, providing a useful guidance for the design and study of heterointerfaces for high-efficiency energy conversion.

Antibacterial Carbon-Based Nanomaterials.

The emergence and global spread of bacterial resistance to currently available antibiotics underscore the urgent need for new alternative antibacterial agents. Recent studies on the application of nanomaterials as antibacterial agents have demonstrated their great potential for management of infectious diseases. Among these antibacterial nanomaterials, carbon-based nanomaterials (CNMs) have attracted much attention due to their unique physicochemical properties and relatively higher biosafety. Here, a comprehensive review of the recent research progress on antibacterial CNMs is provided, starting with a brief description of the different kinds of CNMs with respect to their physicochemical characteristics. Then, a detailed introduction to the various mechanisms underlying antibacterial activity in these materials is given, including physical/mechanical damage, oxidative stress, photothermal/photocatalytic effect, lipid extraction, inhibition of bacterial metabolism, isolation by wrapping, and the synergistic effect when CNMs are used in combination with other antibacterial materials, followed by a summary of the influence of the physicochemical properties of CNMs on their antibacterial activity. Finally, the current challenges and an outlook for the development of more effective and safer antibacterial CNMs are discussed.

Vertically Aligned Porous Organic Semiconductor Nanorod Array Photoanodes for Efficient Charge Utilization.

Because of inefficient charge utilization caused by localized π-electron conjugation and large exciton binding energy, the photoelectrochemical water-splitting efficiency of organic polymers is seriously limited. Taking the graphitic carbon nitride (g-CN) polymer as an example, we report a novel photoanode based on a vertically aligned g-CN porous nanorod (PNR) array prepared in situ, using a thermal polycondensation approach, with anodic aluminum oxide as the template. The g-CN PNR array exhibits an excellent photocurrent density of 120.5 µA cm-2 at 1.23 VRHE under one sun illumination, the highest reported incident photon-to-current efficiency of ∼15% at 360 nm, and an outstanding oxygen evolution reaction stability in 0.1 M Na2SO4 aqueous solution, which constitutes a benchmark performance among the reported g-CN-based polymer photoanodes without any sacrificial reagents. When compared with its planar counterpart, the enhanced performance of the PNR array results principally from its unique structure that enables a high degree of aromatic ring π-electron conjugation for higher mobility of charge carriers, provides a direct pathway for the electron transport to the substrate, produces a large portion of hole-accepting defect sites and space charge region to promote exciton dissociation, and also withstands more strain at the interface to ensure intimate contact with the substrate. This work opens a new avenue to develop nanostructured organic semiconductors for large-scale application of solar energy conversion devices.

Facile Integration between Si and Catalyst for High-Performance Photoanodes by a Multifunctional Bridging Layer.

Designing high-quality interfaces is crucial for high-performance photoelectrochemical (PEC) water-splitting devices. Here, we demonstrate a facile integration between polycrystalline n+p-Si and NiFe-layered double hydroxide (LDH) nanosheet array by a partially activated Ni (Ni/NiOx) bridging layer for the excellent PEC water oxidation. In this model system, the thermally deposited Ni interlayer protects Si against corrosion and makes good contact with Si, and NiOx has a high capacity of hole accumulation and strong bonding with the electrodeposited NiFe-LDH due to the similarity in material composition and structure, facilitating transfer of accumulated holes to the catalyst. In addition, the back illumination configuration makes NiFe-LDH sufficiently thick for more catalytically active sites without compromising Si light absorption. This earth-abundant multicomponent photoanode affords the PEC performance with an onset potential of ∼0.78 V versus reversible hydrogen electrode (RHE), a photocurrent density of ∼37 mA cm-2 at 1.23 V versus RHE, and retains good stability in 1.0 M KOH, the highest water oxidation activity so far reported for the crystalline Si-based photoanodes. This bridging layer strategy is efficient and simple to smooth charge transfer and make robust contact at the semiconductor/electrocatalyst interface in the solar water-splitting systems.

Sacrificial Interlayer for Promoting Charge Transport in Hematite Photoanode.

The semiconductor/electrolyte interface plays a crucial role in photoelectrochemical (PEC) water-splitting devices as it determines both thermodynamic and kinetic properties of the photoelectrode. Interfacial engineering is central for the device performance improvement. Taking the cheap and stable hematite (α-Fe2O3) wormlike nanostructure photoanode as a model system, we design a facile sacrificial interlayer approach to suppress the crystal overgrowth and realize Ti doping into the crystal lattice of α-Fe2O3 in one annealing step as well as to avoid the consequent anodic shift of the photocurrent onset potential, ultimately achieving five times increase in its water oxidation photocurrent compared to the bare hematite by promoting the transport of charge carriers, including both separation of photogenerated charge carriers within the bulk semiconductor and transfer of holes across the semiconductor-electrolyte interface. Our research indicates that understanding the semiconductor/electrolyte interfacial engineering mechanism is pivotal for reconciling various strategies in a beneficial way, and this simple and cost-effective method can be generalized into other systems aiming for efficient and scalable solar energy conversion.