The shell-ferromagnetic effect originates from the segregation process in off-stoichiometric Ni-Mn-based Heusler alloys. In this work, we investigate the precipitation process of L21-ordered Ni2MnSn and L10-ordered NiMn in off-stoichiometric Ni50Mn45Sn5 during temper annealing, by X-ray diffraction (XRD) and 119Sn Mössbauer spectroscopy. While XRD probes long-range ordering of the lattice structure, Mössbauer spectroscopy probes nearest-neighbour interactions, reflected in the induced Sn magnetic moment. As shown in this work, the induced magnetic Sn moment can be used as a detector for microscopic structural changes and is, therefore, a powerful tool for investigating the formation of nano-precipitates. Similar research can be performed in the future, for example, on different pinning type magnets like Sm-Co or Nd-Fe-B.
RESUMEN
Strong unidirectional anisotropy in bulk polycrystalline B20 FeGe has been measured by ferromagnetic resonance spectroscopy. Such anisotropy is not present in static magnetometry measurements. B20 FeGe exhibits inherent Dzyaloshinskii-Moriya interaction, resulting in a nonreciprocal spin-wave dispersion. Bulk and micron sized samples were produced and characterized. By X-band ferromagnetic resonance spectroscopy at 276 K ± 1 K, near the Curie temperature, a distribution of resonance modes was observed in accordance with the cubic anisotropy of FeGe. This distribution exhibits a unidirectional anisotropy, i.e. shift of the resonance field under field inversion, of KUD = 960 J/m3 ± 10 J/m3, previously unknown in bulk ferromagnets. Additionally, more than 25 small amplitude standing spin wave modes were observed inside a micron sized FeGe wedge, measured at 293 K ± 2 K. These modes also exhibit unidirectional anisotropy. This effect, only dynamically measurable and not detectable in static magnetometry measurements, may open new possibilities for directed spin transport in chiral magnetic systems.