RESUMEN
This study describes the valorization of a pine wood by-product (Pinus pinaster) in the form of individualized fibers to a complex copper or more broadly metals present in an aqueous solution using a batch process. The adsorption results show that pine fibres activated by sodium carbonate are effective in recovering copper ions from monocontaminated or polycontaminated solutions of varying concentrations in a few minutes. One gram of material captures 2.5 mg of copper present in 100 mL of solution at pH 5 in less than 10 min. The results are perfectly reproducible and independent of pH between 3 and 5. The presence of the Na+ cation at concentrations of 0.1 M has no impact on material performance, unlike that of Ca2+ ions, which competes with Cu2+ ions for active sites. The adsorption process can be considered as rapid, as most of the copper is adsorbed within the first 10 min of exposure. Investigation of modeling possibilities shows some limitations. Indeed, the Weber and Morris and Elovich models show poor possibilities to describe all the kinetic data for copper adsorption on fibres. This may prove that the mechanism is far more complex than simple physisorption, chemisorption and/or diffusion. Complexation by wood fibers can be extended to solutions containing several types of metals. The results of this study show that the field of selective metal recovery could be a new way of valorizing by-products from the wood industry.
Asunto(s)
Pinus , Contaminantes Químicos del Agua , Cobre/química , Difusión , Cationes , Adsorción , Concentración de Iones de Hidrógeno , Cinética , Soluciones , MaderaRESUMEN
FINEAU (2021-2024) is a trans-disciplinary research project involving French, Serbian, Italian, Portuguese and Romanian colleagues, a French agricultural cooperative and two surface-treatment industries, intending to propose chènevotte, a co-product of the hemp industry, as an adsorbent for the removal of pollutants from polycontaminated wastewater. The first objective of FINEAU was to prepare and characterize chènevotte-based materials. In this study, the impact of water washing and treatments (KOH, Na2CO3 and H3PO4) on the composition and structure of chènevotte (also called hemp shives) was evaluated using chemical analysis, X-ray diffraction (XRD) analysis, scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) spectroscopy, X-ray computed nanotomography (nano-CT), attenuated total reflectance-Fourier transform infrared (ATR-FTIR) spectroscopy, solid state NMR spectroscopy and thermogravimetric analysis. The results showed that all these techniques are complementary and useful to characterize the structure and morphology of the samples. Before any chemical treatment, the presence of impurities with a compact unfibrillated structure on the surfaces of chènevotte samples was found. Data indicated an increase in the crystallinity index and significant changes in the chemical composition of each sample after treatment as well as in surface morphology and roughness. The most significant changes were observed in alkaline-treated samples, especially those treated with KOH.
Asunto(s)
Cannabis/química , Productos Agrícolas/química , Residuos/análisis , Aguas Residuales/química , Contaminantes Químicos del Agua/aislamiento & purificación , Adsorción , Europa (Continente) , Humanos , Cinética , Ensayo de Materiales , TermogravimetríaRESUMEN
Lignocellulosic fibers extracted from plants are considered an interesting raw material for environmentally friendly products with multiple applications. This work investigated the feasibility of using hemp- and flax-based materials in the form of felts as biosorbents for the removal of metals present in aqueous solutions. Biosorption of Al, Cd, Co, Cu, Mn, Ni and Zn from a single solution by the two lignocellulosic-based felts was examined using a batch mode. The parameters studied were initial metal concentration, adsorbent dosage, contact time, and pH. In controlled conditions, the results showed that: (i) the flax-based felt had higher biosorption capacities with respect to the metals studied than the hemp-based felt; (ii) the highest removal efficiency was always obtained for Cu ions, and the following order of Cu > Cd > Zn > Ni > Co > Al > Mn was found for both examined biosorbents; (iii) the process was rapid and 10 min were sufficient to attain the equilibrium; (iv) the efficiency improved with the increase of the adsorbent dosage; and (v) the biosorption capacities were independent of pH between 4 and 6. Based on the obtained results, it can be considered that plant-based felts are new, efficient materials for metal removal.
Asunto(s)
Cannabis/química , Lino/química , Metales Pesados/análisis , Metales Pesados/aislamiento & purificación , Contaminantes Químicos del Agua/análisis , Contaminantes Químicos del Agua/aislamiento & purificación , Purificación del Agua/métodos , Adsorción , Lignina/química , Metales Pesados/metabolismo , Contaminantes Químicos del Agua/metabolismoRESUMEN
This paper focuses on the removal of tetracycline from polluted water by chitosan-olive pomace adsorbing films. More specifically, both raw olive solid wastes (olive pomace) and the olive solid wastes/chitosan composite were compared and used for this purpose. Adsorption capacities values of 16â¯mgâ¯×â¯g-1 and 1.6â¯mgâ¯×â¯g-1 were obtained for the two adsorbents respectively. However, chitosan/olive pomace is proposed as suitable for environmental applications avoiding the dispersion of the pomace blocked inside the chitosan film. To detail the adsorption process, the effect of several experimental parameters such as the pH values, ionic strength, amount of adsorbent and pollutant and temperature values was investigated. The results showed that the adsorption process improved increasing the pH values, with a maximum at pHâ¯8, and it was negatively affected by the presence of salts that retarded the adsorption. Indeed, the desorption of tetracycline was obtained in a MgCl2 2â¯M solution. So, a low-cost and cleaner approach, fundamental for the pollutant recovery and for an adsorbent safe reuse, for several cycles of adsorption/desorption, transforming a waste in resource is presented. The kinetics, isotherms models of adsorption and the thermodynamic parameters (ΔG°, ΔH° and ΔS°) were also evaluated observing that the physisorption of the pollutant occurred with and an endothermic character (ΔH°â¯>â¯0) with ΔG°â¯<â¯0 and ΔS°â¯>â¯0. The use of Advanced Oxidation Processes was proposed as possible alternative to the tetracycline recovery, obtaining its degradation after the desorption. With the present paper, the alternative reuse of olive pomace is reported avoiding its disposal in the environment claiming its potential in the removal/recover of emerging contaminants from water.