Evaluation of Novel Plant-derived Monomers-based Pretreatment on Bonding to Sound and Caries-affected Dentin.

This study evaluated the influence of new monomers derived from cashew nut shell liquid (CNSL) applied for dentin biomodification on resin-dentin bond strength, nanoleakage, and micropermeability to sound and artificially-created caries-affected dentin. Human dentin specimens were assigned to five groups, according to the following dentin pretreatment solutions: Absolute ethanol (control), 2 wt% grape seed extract (Vitis vinifera), 2 wt% cardol [from cashew nut shell liquid (CNSL)], 2 wt% cardol-methacrylate or 2 wt% cardanol-methacrylate applied on sound and artificial caries-affected dentin. Specimens were analyzed after 24 hour or 1 year of water storage. Microtensile bond strength (µTBS) (n=6), interface micropermeability (n=3), and silver nanoleakage (n=6) were assessed using a universal testing machine, confocal laser scanning microscope, and scanning electron microscope, respectively. In sound dentin, no difference in bond strength was observed between the groups in either storage period. In artificial caries-affected dentin, pretreatment with cardol-methacrylate resulted in statistically higher bond strength than all the other treatments in both storage periods. Cardol-methacrylate treatment resulted in less nanoleakage, along with improved interfacial integrity, compared to further treatments in artificial caries-affected dentin. Regarding micropermeability analysis, all treatments depicted deficient sealing ability when applied on artificial caries-affected dentin, with the presence of gaps in the control group. In conclusion, cardol-methacrylate is a promising plant-derived monomer to reinforce the hybrid layer, since it preserved resin-dentin bond strength and improved dentin bonding, especially to caries-affected dentin, a well-known harsh substrate for adhesion longevity.

Effect of Polymeric Microparticles Loaded With Catechin on the Physicochemical Properties of an Adhesive System.

The objective of this study was to synthesize and characterize epigallocatechin-3-gallate (EGCG)-loaded/poly(D-L lactide-co-glycolide) acid (PLGA) microparticles, evaluate their effects on degree of conversion and release assay of adhesives, and subsequently to examine the resin-dentin bond strength of two EGCG formulations (free EGCG or loaded into PLGA microparticles) applied as a pretreatment or incorporated into an adhesive system. The formulations were prepared according to a PLGA:EGCG ratio of 16:1 using the spray-drying technique. The size and polydispersity index were determined by light scattering in aqueous dispersion. The degree of conversion (%DC) and release assay were assessed by Fourier transform infrared spectroscopy and ultraviolet-visible spectrophotometer, respectively. Subsequently, 45 third molars were divided into five groups (n=9) according to the different EGCG application modes and prepared for bond strength testing in a universal testing machine. Results demonstrated no statistically significant difference among the DC means after the PLGA microparticles were loaded with EGCG. For the release assay, the 1.0% PLGA/EGCG group presented better results after being elected for use in the bond strength test. The resin-dentin bond strengths of the experimental groups after 12 months of water storage were significantly higher than in the control group. EGCG could improve the durability of the resin-dentin bond over time and promote a new era for adhesive dentistry with the concept of controlled release.