A compact evanescent wave detection platform (EWDP) is developed for the detection of fluorescence gold nanoclusters. The EWDP employs a simple optical system and a Si-based photodetector SOP-1000 assembly to improve the optical efficiency and detection sensitivity. A microfluidic sample cell is also used to decrease the amount of analyte to 200 µL (The volume of sample cell is really about 30 µL). On this basis, we design a strategy for detecting dopamine (DA) based on the photoinduced electron transfer (PET) quenching mechanism. By introduction of tyrosinase (TYR) during the detection, the testing time is shortened to 1 min. The fluorescence emission signal decreased dramatically and the quenching ratio (F0-F)/F0 is linearly related to the concentration of DA in the range of 0.03-60 µM with a detection limit of 0.03 µM. Additionally, this detection platform has potential applications for DA fast detection in the microsamples.

Tailoring NiCoAl layered double hydroxide nanosheets for assembly of high-performance asymmetric supercapacitors.

NiCoAl layered double hydroxide nanosheets (NiCoAl-LDHNs) were prepared by a one-step solvothermal method. The shape and size of the obtained nanosheets are optimized by adjusting the solvothermal time and the molar concentration ratio of Ni2+/Co2+ to obtain the electrode material with the best performance. When the solvothermal time is 9 h and the molar concentration ratio of Ni2+/Co2+ is 1:1, NiCoAl-LDHNs has the best morphology and electrochemical performance. When assembled into a supercapacitor, NiCoAl-LDHN-9 has a high specific capacitance of 1228.5 F g-1 at 1 A g-1. As the current density is increased to 20 A g-1, the specific capacitance is 1001.8 F g-1, which still has a high capacitance retention of 81.6%. When NiCoAl-LDHN-9 was assembled into an asymmetric supercapacitor, NiCoAl-LDHN-9//AC has a specific capacitance of 102.1 F g-1 at 0.5 A g-1. The asymmetric supercapacitor devices also show excellent electrochemical performance in terms of energy density (35.9 Wh kg-1 at 225.8 W kg-1), power density (4.8 kW kg-1 at 22.2 Wh kg-1) and cycle life (capacitance retention rate after 10,000 cycles is 87.1%). Those results indicate that NiCoAl-LDHN have the potential to be promising electrode materials for high performance supercapacitors.