RESUMEN
In this study, Kraft lignin was modified by ammonium dihydrogen phosphate (ADP) and urea for achieving phosphorylation and carbamylation, aiming to protect wood against biological and fire attack. Scots pine (Pinus sylvestris L.) sapwood was impregnated with a water solution containing Kraft lignin, ADP, and urea, followed by heat treatment at 150 °C, resulting in changes in the properties of the Kraft lignin as well as the wood matrix. Infrared spectroscopy, 13C cross-polarisation magic-angle-spinning (MAS) nuclear magnetic resonance (NMR), and direct excitation single-pulse 31P MAS NMR analyses suggested the grafting reaction of phosphate and carbamylate groups onto the hydroxyl groups of Kraft lignin. Scanning electron microscopy with energy dispersive X-ray spectroscopy indicated that the condensed Kraft lignin filled the lumen as well as partially penetrating the wood cell wall. The modified Kraft lignin imparted fire-retardancy and increased char residue to the wood at elevated temperature, as confirmed by limiting oxygen index, microscale combustion calorimetry, and thermogravimetric analysis. The modified wood exhibited superior resistance against mold and decay fungi attack under laboratory conditions. The modified wood had a similar modulus of elasticity to the unmodified wood, while experiencing a reduction in the modulus of rupture.
RESUMEN
The exterior application of fire-retardant (FR) timber necessitates it to have high durability because of the possibility to be exposed to rainfall. In this study, water-leaching resistance of FR wood has been imparted by grafting phosphate and carbamate groups of the water-soluble FR additives ammonium dihydrogen phosphate (ADP)/urea onto the hydroxyl groups of wood polymers via vacuum-pressure impregnation, followed by drying/heating in hot air. A darker and more reddish wood surface was observed after the modification. Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, solid-state 13C cross-polarization magic-angle-spinning nuclear magnetic resonance (13C CP-MAS NMR), and direct-excitation 31P MAS NMR suggested the formation of C-O-P covalent bonds and urethane chemical bridges. Scanning electron microscopy/energy-dispersive X-ray spectrometry suggested the diffusion of ADP/urea into the cell wall. The gas evolution analyzed by thermogravimetric analysis coupled with quadrupole mass spectrometry revealed a potential grafting reaction mechanism starting with the thermal decomposition of urea. Thermal behavior showed that the FR-modified wood lowered the main decomposition temperature and promoted the formation of char residues at elevated temperatures. The FR activity was preserved even after an extensive water-leaching test, confirmed by the limiting oxygen index (LOI) and cone calorimetry. The reduction of fire hazards was achieved through the increase of the LOI to above 80%, reduction of 30% of the peak heat release rate (pHRR2), reduction of smoke production, and a longer ignition time. The modulus of elasticity of FR-modified wood increased by 40% without significantly decreasing the modulus of rupture.
RESUMEN
Guanyl-urea phosphate (GUP) was introduced into furfurylated wood in order to improve fire retardancy. Modified wood was produced via vacuum-pressure impregnation of the GUP-furfuryl alcohol (FA) aqueous solution, which was then polymerized at elevated temperature. The water leaching resistance of the treated wood was tested according to European standard EN 84, while the leached water was analyzed using ultra-performance liquid chromatography (UPLC) and inductively coupled plasma-sector field mass spectrometry (ICP-SFMS). This new type of furfurylated wood was further characterized in the laboratory by evaluating its morphology and elemental composition using optical microscopy and electron microscopy coupled with energy-dispersive X-ray spectrometry (SEM-EDX). The chemical functionality was detected using infrared spectroscopy (FTIR), and the fire resistance was tested using cone calorimetry. The dimensional stability was evaluated in wet-dry soaking cycle tests, along with the mechanical properties, such as the Brinell hardness and bending strength. The fire retardancy of the modified furfurylated wood indicated that the flammability of wood can be depressed to some extent by introducing GUP. This was reflected in an observed reduction in heat release rate (HRR2) from 454.8 to 264.9 kW/m2, without a reduction in the material properties. In addition, this leaching-resistant furfurylated wood exhibited higher fire retardancy compared to conventional furfurylated wood. A potential method for producing fire-retardant treated furfurylated wood stable to water exposure has been suggested.
RESUMEN
The objective of the work was to improve the leaching resistance of fire-retardant (FR) modified wood by the incorporation of a thermoset resin. Here, Scots pine (Pinus sylvestris L.) sapwood was impregnated with melamine formaldehyde (MF) resin and hydrophilic FRs guanyl-urea phosphate/boric acid by a vacuum-pressure treatment. Resistance to leaching of FR-modified wood was evaluated, after conducting an accelerated aging test according to European standard EN 84. Inductively coupled plasma analysis showed that the incorporation of MF resin significantly reduced the leachability of FRs. Scanning electron microscopy/energy-dispersive X-ray spectrometry revealed that the mechanism of water resistance was by doping the FRs into MF resin microspheres. Fourier transform infrared spectra showed the chemical functionality changes of FR-modified wood such as the formation of methylene bridges by drying the modified wood specimens. An increase in the thermal stability of FR-modified wood was confirmed by thermal gravimetric analysis. Excellent fire performance of FR-modified wood after leaching was affirmed by the limiting oxygen index and cone calorimeter tests.
RESUMEN
The potential of producing eco-friendly, formaldehyde-free, high-density fiberboard (HDF) panels from hardwood fibers bonded with urea-formaldehyde (UF) resin and a novel ammonium lignosulfonate (ALS) is investigated in this paper. HDF panels were fabricated in the laboratory by applying a very low UF gluing factor (3%) and ALS content varying from 6% to 10% (based on the dry fibers). The physical and mechanical properties of the fiberboards, such as water absorption (WA), thickness swelling (TS), modulus of elasticity (MOE), bending strength (MOR), internal bond strength (IB), as well as formaldehyde content, were determined in accordance with the corresponding European standards. Overall, the HDF panels exhibited very satisfactory physical and mechanical properties, fully complying with the standard requirements of HDF for use in load-bearing applications in humid conditions. Markedly, the formaldehyde content of the laboratory fabricated panels was extremely low, ranging between 0.7-1.0 mg/100 g, which is, in fact, equivalent to the formaldehyde release of natural wood.
RESUMEN
In this research, acetylated wood (Accoya) was tested in ground contact in central Greece. After ten years of exposure during a ground stake test, acetylated pine wood (Pinus radiata) stakes, with a 20% acetyl weight gain, were completely intact and showed no visual decay (decay rating: 0). However, the key mechanical properties of Accoya wood, that is, modulus of elasticity (MOE) and modulus of rupture (MOR) after 10 years of ground contact, were significantly reduced by 32.8% and 29.6%, respectively, despite an excellent visual result since no evidence of fungal attack was identified. This contradiction could possibly indicate that the hallmarks of decay, i.e., brown-rot decay of acetylated wood can be the significant loss of mechanical properties before decay is actually visible.