Effectiveness of Concrete Reinforcement with Recycled Tyre Steel Fibres.

The role of searching for industrial waste management solutions in construction is key for environmental protection. Research in recent years has focused on solutions aimed at reducing the carbon footprint. This paper presents the results of tests conducted on concrete reinforced with treated recycled tyre steel fibres (RTSFs) compared to the same amount of manufactured steel fibres (MSFs). The effectiveness of concrete reinforcement with RTSFs was analysed using the fracture mechanics parameters of cementitious composites. Rheological tests, residual flexural tensile strength tests, work of fracture measurements, toughness indices, examinations of the fibre distribution in the concrete, and SEM observations of the concrete fractures with fibres were performed. Determining the work of fracture and toughness indices was an innovative aspect of this paper. As the amount of RTSFs increased, a decrease in the consistency was observed, although the distribution of fibres in the concrete was uniform, as proven by the results of computer tomography tests. Concrete reinforced with RTSFs that is purified and refined during the recycling process might have better properties than concrete reinforced with the same amount of MSFs. The application of RTSFs in construction has environmental and economic benefits in addition to the strengthening of cementitious composites.

Effectiveness of Curing Compounds for Concrete.

Curing compounds are widely used materials that are used in place of other methods of curing fresh concrete. The article presents an overview of the effectiveness of the concrete curing compounds widely used in Europe. Eleven different products have been tested. FTIR spectroscopy identification tests showed that all tested products might be divided into two main groups, depending on the type of their active substance. The water retention efficiency of each curing compound was examined, and the tensile strength of the cured samples was tested using the pull-off method. The dry mass content of the tested products was examined to check for a correlation between their effectiveness and active substance content. The microstructure of mortars treated with the most effective compounds and the reference mortar were examined using SEM techniques. Significant differences in microstructure were found between cured samples with different curing compounds, and also with uncured samples.

Fly Ash with Ammonia: Properties and Emission of Ammonia from Cement Composites.

The article presents the results of tests performed on fly ash with a high content of ammonium (up to 400 ppm) from the NOx reduction process. The main properties of fly ash were tested according to EN 450-1 and the results were compared with fly ash without ammonium. The comparison showed that fly ash with high concentration of ammonium suits the requirements of the European standard. Although the requirements do not limit the ammonium content, using such material as an additive for cement composites causes the emission of gaseous ammonium during mixing and from the final product. For this reason, the emission of ammonium from mortars containing fly ash were tested. The results have shown that using high ammonium fly ash might pollute indoor air and affect the health of users.

Research on the Influence of the Type of Surfactant and Concentrator in Aqueous Dispersion of Pigments.

This work reports tests performed to evaluate the stability of aqueous dispersions of inorganic oxide pigments with different specific surface areas, with the use of anionic and non-ionic surfactants and concentrators. Color mixtures of oxide compounds of blue, green, olive and brown with the unit cell spinel structure were used as pigments. The sodium salt of sulfosuccinic acid monoester, oxyethylenated nonylphenol and ethoxylated derivatives of lauryl alcohol, fatty alcohol and fatty amine were used as surfactants. The concentrators used were: poly(vinyl alcohol), the sodium salt of carboxymethyl cellulose as well as a water-based polyurethane oligomer. The highest dispersion efficiency was found for dispersed systems in which surfactant and concentrator were incorporated in the formula. The one containing the sodium salt of carboxymethyl cellulose or polyurethane oligomer with ethoxylated saturated fatty alcohol or fatty amine was found to be the most efficient. It was discovered that a higher dispersion efficiency corresponds to pigments with larger specific surface. The efficiency is also found to improve when the concentrator is an acrylic polymer or copolymer made up of two acrylic species. In this case, the concentrator interaction with the surfactant is more effective if the value of its boundary viscosity number is higher. This observation confirms the existence of interactions between macro-chains of the concentrator and surfactant molecules forming micelles with the pigment particles.

Steviamine, a new class of indolizidine alkaloid [(1R,2S,3R,5R,8aR)-3-hydroxy-meth-yl-5-methyl-octa-hydro-indolizine-1,2-diol hydro-bromide].

X-ray crystallographic analysis of the title hydro-bromide salt, C(10)H(20)N(+)·Br(-), of (1R,2S,3R,5R,8aR)-3-hydroxy-meth-yl-5-methyl-octa-hydro-indolizine-1,2-diol defines the absolute and relative stereochemistry at the five chiral centres in steviamine, a new class of polyhydroxy-lated indolizidine alkaloid isolated from Stevia rebaudiana (Asteraceae) leaves. In the crystal structure, mol-ecules are linked by inter-molecular O-H⋯Br and N-H⋯Br hydrogen bonds, forming double chains around the twofold screw axes along the b-axis direction. Intra-molecular O-H⋯O inter-actions occur.