RESUMEN
The aim of this study was to evaluate the shear bond strength of a composite resin to dental enamel, using three different surface treatments. Fifteen sound third molars were randomly assigned to three groups. The mesial and distal surfaces were flattened and covered using adhesive tape with a central orifice delimiting the adhesion area (7.07 mm2). Group I, the enamel surface was conditioned with 37% phosphoric acid for 15 s; group II, the surface was treated using air abrasion with aluminum oxide; group III, the enamel surface was treated using an association of air abrasion with aluminum oxide and 37% phosphoric acid. The Single Bond (3M) adhesive system was applied and a Teflon matrix was placed and filled with composite resin Z-100 (3M) and light-cured. The shear bond strength test was performed with a universal testing machine. The acid etching technique and air abrasion with aluminum oxide associated with acid etching had the highest shear bond strength values. Data were subjected to statistical analysis using ANOVA and the Turkey test, and no statistically significant difference in shear bond strength was observed between group I (12.49 +/- 2.85 MPa) and group III (12.59 +/- 2.68 MPa). In contrast, both groups had statistically better shear bond strengths compared to group II (0.29 +/- 0.56 MPa; p < 0.05). Air abrasion with aluminum oxide does not substitute acid etching. The association of these methods to obtain adequate adhesion to the substrate is necessary.
Asunto(s)
Abrasión Dental por Aire , Recubrimiento Dental Adhesivo/métodos , Esmalte Dental/fisiología , Grabado Ácido Dental , Óxido de Aluminio , Análisis de Varianza , Bisfenol A Glicidil Metacrilato , Resinas Compuestas , Análisis del Estrés Dental , Recubrimientos Dentinarios , Humanos , Ensayo de Materiales , Diente Molar , Ácidos Fosfóricos , Distribución Aleatoria , Cementos de Resina , Resistencia al Corte , Dióxido de Silicio , Estadísticas no Paramétricas , Propiedades de Superficie , CirconioRESUMEN
The aim of this study was to evaluate the shear bond strength of a composite resin to dental enamel, using three different surface treatments. Fifteen sound third molars were randomly assigned to three groups. The mesial and distal surfaces were flattened and covered using adhesive tape with a central orifice delimiting the adhesion area (7.07 mm²). Group I, the enamel surface was conditioned with 37 percent phosphoric acid for 15 s; group II, the surface was treated using air abrasion with aluminum oxide; group III, the enamel surface was treated using an association of air abrasion with aluminum oxide and 37 percent phosphoric acid. The Single Bond (3M) adhesive system was applied and a Teflon matrix was placed and filled with composite resin Z-100 (3M) and light-cured. The shear bond strength test was performed with a universal testing machine. The acid etching technique and air abrasion with aluminum oxide associated with acid etching had the highest shear bond strength values. Data were subjected to statistical analysis using ANOVA and the Tukey test, and no statistically significant difference in shear bond strength was observed between group I (12.49 ± 2.85 MPa) and group III (12.59 ± 2.68 MPa). In contrast, both groups had statistically better shear bond strengths compared to group II (0.29 ± 0.56 MPa; p<0.05). Air abrasion with aluminum oxide does not substitute acid etching. The association of these methods to obtain adequate adhesion to the substrate is necessary
Asunto(s)
Humanos , Grabado Ácido Dental , Abrasión Dental por Aire , Recubrimiento Dental Adhesivo/métodos , Esmalte Dental , Técnicas In Vitro , Óxido de Aluminio , Resinas Compuestas , Recubrimientos Dentinarios , Diente Molar , Ácidos Fosfóricos , Resistencia a la TracciónRESUMEN
Os autores estudaram o efeito de quatro diferentes técnicas de polimento de restauraçöes de amálgama feitas em laboratório com duas ligas convencionais e três ligas com alto teor de cobre, sendo o polimento realizado no tempo de 168 horas após a condensaçäo. A utilizaçäo de brocas multilaminadas para o acabamento superficial dos corpos-de-prova exibiu níveis de rugosidade semelhante aos corpos-de-prova näo polidos. No tocante às ligas utilizadas, a liga DFL mostrou os mais altos valores de rugosidade superficial, enquanto a liga GS 80 exibiu os melhores valores. A trituraçäo foi efetuada segundo a indicaçäo dos fabricantes e o amálgama foi condensado em uma matriz de aço fabricada especialmente para a pesquisa. A matriz tinha uma cavidade de 4,0 mm de diâmetro com 2,0 mm de profundidade. Cinco minutos após a condensaçäo, foi feita a escultura com uma lâmina de aço e em seguida a brunidura. Depois de 25 minutos, o corpo-de-prova de amálgama era retirado utilizando-se um parafuso da própria matriz. Entäo, 168 h após a condensaçäo, os corpos-de-prova eram polidos e submetidos aos testes de rugosimetria
Asunto(s)
Amalgama Dental/análisis , Aleaciones Dentales , Pulido Dental/métodos , Restauración Dental Permanente/métodosRESUMEN
Frente a evoluçäo de novos materiais restauradores estéticos adesivos, a Odontologia Restauradora tem sido cada vez mais atuante, sendo que a realizaçäo de procedimentos restauradores estéticos é crescente tanto nos dentes anteriores como nos posteriores, permitindo a realizaçäo de procedimentos mais conservadores, econômicos e com menor tempo clínico. Neste contexto, o presente trabalho relata a aplicaçäo de procedimentos clínicos estéticos em um paciente jovem, que após a perda do incisivo central superior direito optou-se pela realizaçäo de transplante do primeiro pré-molar inferior esquerdo e sua caracterizaçäo em incisivo central superior. O procedimento restaurador resumiu-se na utilizaçäo da técnica de condicionamento ácido do esmalte, aplicaçäo de sistema adesivo e inserçäo incremental de resina composta
Asunto(s)
Humanos , Masculino , Niño , Estética Dental , Incisivo , Trasplante AutólogoRESUMEN
Como tratamento restaurador estético de dentes anteriores fraturados, podemos lançar mäo de materiais de uso direto como as resinas compostas e a colagem do fragmento dental, ou indireto, como as coroas totais de porcelana. Entretanto, quando há perda do fragmento dental, pode-se optar por uma técnica conservadora e econômica, que baseia-se na utilizaçäo de fragmentos feitos de dentes armazenados em um banco de dentes. O presente trabalho propôs a realizaçäo de uma colagem homógena, em paciente de treze anos como técnica alternativa para restabelecimento da funçäo e estética do incisivo central fraturado, evitando-se desta forma, utilizar um tratamento protético mais radical e conseqüentemente de custo mais elevado
Asunto(s)
Humanos , Masculino , Adolescente , Recubrimiento Dental Adhesivo/métodos , Fracturas de los DientesRESUMEN
O preparo cavitário geralmente diminui a resistência à fratura dos dentes, principalmente quando a largura da caixa oclusal da cavidade é de um terço ou mais da distância intercuspídea. Dependendo do material restaurador empregado, esses dentes apresentam grande variaçäo na resistência à fratura. Neste trabalho, foi comparada a resistência à fratura de dentes pré-molares superiores com preparo cavitário mésio-oclusal com a cúspide vestibular socavada com a resistência à fratura de dentes com esse mesmo tipo de cavidade e restaurados com resina composta com adesivo dental, a amálgama com base de resina composta e amálgama com base de cimento ionômero de vidro. Os dentes testados foram submetidos à carga de compressäo numa máquina de ensaios Universal Kratos com velocidade controlada. Os dentes restaurados com resina composta e com amálgama mais base de resina composta apresentaram resistência à fratura semelhante entre si e estatisticamente mais elevada que a resistência à fratura dos dentes apenas preparados. Os restaurados com amálgama e com base de cimento ionômero de vidro apresentaram resistência à fratura estatisticamente semelhante à dos dentes apenas preparados
Asunto(s)
Diente Canino , Restauración Dental Permanente , Materiales Dentales/clasificación , Fracturas de los Dientes , Resinas Compuestas , Amalgama Dental , Cementos de Ionómero VítreoRESUMEN
Foram examinados 100 pacientes que possuiam dentes com 867 restaurações com amálgama, das quais 526 apresentavam defeitos. Destas, 352 restaurações exibiram defeitos que poderiam ser corrigidos com um novo acabamento e polimento. Ficou evidenciado que um número maior de restaurações não precisa ser trocado, sendo isto considerado uma atitude conservadora, pois evita um novo preparo cavitário e a perda de estrutura dental
Asunto(s)
Humanos , Masculino , Femenino , Amalgama Dental , Fracaso de la Restauración DentalRESUMEN
Os autores estudaram o efeito de duas técnicas de brunidura (brunidura pós-escultura e brunidura pré e pós-escultura) sobre a microdureza do amálgama, obtido de 3 diferentes ligas, 24 e 168 horas após a condensaçäo. Näo houve diferença estatística entre os resultados obtidos com as diferentes técnicas de brunidura em relaçäo ao grupo controle (sem brunidura). Além disso, os resultados mostraram que a microdureza é aumentada após 168 horas e que as ligas com alto teor de cobre (Dispersalloy e Sybraloy) apresentaram maiores valores de microdureza que a liga convencional (Novo True)
Asunto(s)
Amalgama Dental/análisis , Pruebas de Dureza , Aleaciones Dentales/análisis , Pulido Dental/métodosRESUMEN
Este trabalho teve como objetivo estudar "in vitro" o comportamento de diferentes amálgamas odontológicos, condensados em matrizes metálicas, que ao serem removidos eram polidos e mergulhados, separadamente, em soluçöes de Q-suco, Tang e saliva artificial, com a finalidade de se observar possíveis alteraçöes nas superfícies destes materiais restauradores. Uma análise dos resultados mostrou que as superfícies dos diferentes amálgamas utilizados, que foram submetidos a açäo dessas soluçöes artificiais apresentavam alteraçöes em forma de manchamento e ofuscamento. Estas alteraçöes foram analisadas macroscopicamente e constatadas através da análise de refletância aparente