1.
Int J Biol Macromol ; 217: 792-802, 2022 Sep 30.
Artículo en Inglés | MEDLINE | ID: mdl-35902018

RESUMEN

The high density and poor thermal insulation of traditional wood-plastic composites limited the application in the field of building materials. In this paper, wood fiber (WF) and PLA were used as raw materials and azodicarbonamide was used as the foaming agent. Lightweight WF/PLA composites were prepared by the hot-pressing foaming method, aiming to obtain renewable, low-density material with high strength-to-weight ratio and thermal insulation performance. The results showed that after adding 20 % WF into PLA, the cell morphology was excellent and the cell size was uniform. The magnification reached the minimum value of 0.36 g/cm3 and the foaming magnification was 3.42 times. The impact strength and compressive strength were 3.16 kJ/m3 and 4.12 MPa, its comprehensive mechanical properties were outstanding. The thermal conductivity of foamed materials was 0.110-0.148 (W/m·K), which was significantly lower than that of unfoamed materials and common wood. Its excellent mechanical properties and thermal insulation can be suitable for application in the construction field to replace traditional wood.


Asunto(s)
Poliésteres , Madera , Materiales de Construcción , Temperatura
SELECCIÓN DE REFERENCIAS
DETALLE DE LA BÚSQUEDA