Physical and structural characterization of bis-acryl composite resin.

During the preparation of fixed prosthesis (including individual bridges and crowns) it is important to select the materials that have the best features and properties to predict a successful clinical treatment. The objective of this study was to determine if the chemical and structural characteristics could cause to increase the fracture resistance, we used four bis-acryl resins Luxatemp, Protemp, Structur and Telio. Three-points bending by Flexural test were performed in ten bars and they were carried out to compare with Anova test. In addition, the bis-acryl resins were analyzed by scanning electron microscopy, to analyze microstructure and morphology and the molecular structure were performed by Infrared Spectroscopy through Attenuated Total Reflectance. A higher flexural strength was found in Luxatemp and Structur with, no significant differences between this study groups. Regarding Protemp and Telio, these study groups showed a lower flexural strength when were compared with Luxatemp and Structur. These results corroborate SEM and ATR analysis because Luxatemp sample showed a regular size particle on the surface and chemically presents a long cross-linkage polymer chain. The presence of CO3, SiO2 and N-H groups as a fillers particle interacting with OH groups cause a higher flexural strength compared with another groups.

Enhancement of fluoride release in glass ionomer cements modified with titanium dioxide nanoparticles.

BACKGROUND: Several efforts have been made to improve the glass ionomer cements (GICs) properties with nanotechnology. Fluoride release in once of most beneficial properties of GICs. The purpose of this study was to evaluate the fluoride release, recharge, and cytotoxicity in GICs reinforced with titanium dioxide nanoparticles (TiO2N). OBJECTIVE: Evaluate the fluoride release, recharge, and cytotoxicity in GICs reinforced with TiO2N. METHODS: Four GICs, FUJI IX EXTRA (G1c), KETAC MOLAR (G2c), IONOFILL MOLAR (G3c), and FUJI IX (G4c) were combined with TiO2N (G1e, G2e, G3e, and G4e) and divided into blocks of 5-mm width and 1-mm thickness 10 each. A total of 80 samples were arranged as follows: GICs alone as negative control (n = 40) and GICs + TiO2N as experimental groups (n = 40). The fluoride release was determined for periods of 1, 2, 6, 10, 31, 90, 180, 240, and 300 days. On days 30 and 179, samples were recharged by submerging in 1 mL of 20,000 ppm sodium fluoride gel. Cytotoxic activity was carried out with gingival fibroblasts, using 3-[4,5-dimethylthiazol-2-yl]-2,5-diphenyltetrazolium bromide cell viability assay. RESULTS: The experimental groups obtained the highest and more constant fluoride released when compared to control groups. After the first recharge, experimental groups (G1e, G3e, and G4e) showed statistically significant results (P = .001, 0.010, and 0.001 respectively) enhancing their recharge ability regarding control groups. The second recharge showed better results in G1e concerning the rest of the groups. No cytotoxic activity was observed in all experimental groups, although significant differences were observed in G3e and G4e regarding control group. CONCLUSION: The incorporation of TiO2N enhance the fluoride release in glass ionomers with a noncytotoxic effect on human gingival fibroblasts.

Mechanical Properties and Antibacterial Effect on Mono-Strain of Streptococcus mutans of Orthodontic Cements Reinforced with Chlorhexidine-Modified Nanotubes.

Recently, several studies have introduced nanotechnology into the area of dental materials with the aim of improving their properties. The objective of this study is to determine the antibacterial and mechanical properties of type I glass ionomers reinforced with halloysite nanotubes modified with 2% chlorhexidine at concentrations of 5% and 10% relative to the total weight of the powder used to construct each sample. Regarding antibacterial effect, 200 samples were established and distributed into four experimental groups and six control groups (4 +ve and 2 -ve), with 20 samples each. The mechanical properties were evaluated in 270 samples, assessing microhardness (30 samples), compressive strength (120 samples), and setting time (120 samples). The groups were characterized by scanning electron microscopy and Fourier transform infrared spectroscopy, and the antibacterial activity of the ionomers was evaluated on Streptococcus mutans for 24 h. The control and positive control groups showed no antibacterial effect, while the experimental group with 5% concentration showed a zone of growth inhibition between 11.35 mm and 11.45 mm, and the group with 10% concentration showed a zone of growth inhibition between 12.50 mm and 13.20 mm. Statistical differences were observed between the experimental groups with 5% and 10% nanotubes. Regarding the mechanical properties, microhardness, and setting time, no statistical difference was found when compared with control groups, while compressive strength showed higher significant values, with ionomers modified with 10% concentration of nanotubes resulting in better compressive strength values. The incorporation of nanotubes at concentrations of 5% and 10% effectively inhibited the presence of S. mutans, particularly when the dose-response relationship was taken into account, with the advantage of maintaining and improving their mechanical properties.

Antimicrobial Activity of Biogenic Silver Nanoparticles from Syzygium aromaticum against the Five Most Common Microorganisms in the Oral Cavity.

Syzygium aromaticum (clove) has been used as a dental analgesic, an anesthetic, and a bioreducing and capping agent in the formation of metallic nanoparticles. The main objective of this study was to evaluate the antimicrobial effect in oral microorganisms of biogenic silver nanoparticles (AgNPs) formed with aqueous extract of clove through an ecofriendly method "green synthesis". The obtained AgNPs were characterized by UV-Vis (ultraviolet-visible spectroscopy), SEM-EDS (scanning electron microscopy-energy dispersive X-ray spectroscopy), TEM (transmission electron microscopy), and ζ potential, while its antimicrobial effect was corroborated against oral Gram-positive and Gram-negative microorganisms, as well as yeast that is commonly present in the oral cavity. The AgNPs showed absorption at 400-500 nm in the UV-Vis spectrum, had an average size of 4-16 nm as observed by the high-resolution transmission electron microscopy (HR-TEM), and were of a crystalline nature and quasi-spherical form. The antimicrobial susceptibility test showed inhibition zones of 2-4 mm in diameter. Our results suggest that AgNPs synthesized with clove can be used as effective growth inhibitors in several oral microorganisms.

Tooth demineralization and associated factors in patients on fixed orthodontic treatment.

Dental demineralization was determined in patients at three time points during fixed orthodontic treatment. A multiple cross-sectional study included 108 patients divided into three different groups: (1) beginning of orthodontic treatment; (2) one year into treatment; and (3) two years into treatment. Demineralization was estimated using a DIAGNOdent pen. We obtained data from multiple tooth-by-tooth demineralization readings combined with salivary pH and patients' oral hygienic and dietary behaviors. A t-test for independent samples and Spearman´s correlation were performed. No demineralizations differences were found between the initial stage and one year into treatment. Between one and two years small differences were observed, but demineralization increased between the initial stage and second treatment year, predominating in upper right central incisors (p = 0.056), upper left lateral incisors (p = 0.040), both upper canines (p = 0.055 and p = 0.040, respectively) and first left premolars (p = 0.034 and p = 0.053, respectively). We did not find associations between oral hygiene and dietary behaviours or salivary pH. In conclusion, demineralization occurred in first year of treatment and increased during second year, predominating in the upper arch and the left side mainly in upper right central incisors, upper left lateral incisors, both upper canines, and first left premolars.

Comparative study of fluoride released and recharged from conventional pit and fissure sealants versus surface prereacted glass ionomer technology.

CONTEXT: The fluoride release of sealants in vitro shows a marked decrease. Giomers are distinguishable from manufactured resin-based sealants and contain prereacted glass-ionomer particles (PRG). AIMS: To compare the amounts of fluoride released from the main pit and fissure of a resin-based sealant with that from a Giomer and to assess the abilities of the sealant and the Giomer to recharge when exposed to regular use of fluoride rinse. MATERIALS AND METHODS: The readings for the fluoride concentration were carried out for 60 days using a fluoride ion-specific electrode. After this period, the samples were recharged using a fluoride mouth rinse. The amount of fluoride released after this recharge was determined for 5 days. The data were analyzed using Student's t- and analysis of variance tests. RESULTS: In general, all materials presented higher fluoride release in the first 24 h; G1 and G4 showed a higher fluoride release in this period. On the other hand, G3 and G1 presented the most constant fluoride release until the 8(th) day, wherein all the sealants considerably decreased in the amount of fluoride released. CONCLUSION: G1 and G3 released higher concentrations of fluoride, although no significant differences were found. Giomers recharged in the first 24 h after polymerization presented an improved and sustained fluoride release.