Background/purpose: The dental adhesive market is constantly evolving to meet the demands of dentists and patients, but new products and upgrades should be rigorously evaluated before being used in clinical practice. This study investigated the physicomechanical properties and dentin bonding efficacy of a newly upgraded universal adhesive compared to its predecessor. Materials and methods: Twenty-four molars were divided into four groups (n = 6/group) based on adhesive (new vs. predecessor) and application mode [self-etch (SE) vs. etch-and-rinse (ER)] for evaluating their dentin microtensile bond strength (µTBS), failure pattern, and bonding interface. Additional thirty-six molars' crowns were perpendicularly sectioned to obtain flat mid-coronal dentin discs. The opposing dentin surfaces of each disc received contrasting treatments (new/predecessor adhesive applied in SE/ER mode), resulting in six interventions. The bonded discs (n = 6/intervention) were used to assess the adhesives' survival probability employing a double-sided µTBS test. The other physicomechanical properties examined were adhesives' oxygen inhibition layer (OIL), viscosity, hardness, elastic modulus, degree of conversion (DC), and in-situ DC. Results: Both adhesive versions showed similar µTBS (P > 0.05), failure pattern (P > 0.05), and survival probability (P > 0.008). ER mode promoted resin tag formation and exhibited a slender adhesive layer for both adhesives. The newer adhesive version showed a thinner adhesive layer in general with narrower OIL (P < 0.001), less viscosity (P < 0.001), higher hardness (P < 0.05), elastic modulus (P < 0.05), DC (P < 0.001), and in-situ DC (P < 0.001). Conclusion: While the newly updated adhesive had superior physicomechanical properties with more fluidity, its dentin bonding efficacy and survival probability were comparable to its predecessor.
RESUMEN
This study evaluated the effect of simulated pulpal pressure (SPP) conditions and storage time on contemporary adhesive systems' microtensile bond strength (µTBS) to dentin. Extracted human molars were prepared and randomly divided into four groups according to the adhesives: Clearfil Megabond 2 (CSE), Beautibond Xtreme Universal (BXU), G2-Bond (G2B), and Scotchbond Universal Plus (SBP). Each adhesive group was further divided following the SPP conditions: control with no simulation (SPP-CTR), SPP with distilled water (SPP-DTW), and SPP with fetal bovine serum (SPP-FBS). Resin composite build-ups were prepared, and teeth were stored in water (37 °C) for 24 h (24 h) and 3 months (3 m). Then, teeth were sectioned to obtain resin-dentin bonded beams and tested to determine the µTBS. Data were analyzed using three-way ANOVA, Tukey post hoc tests (=0.05), and Weibull failure analysis. Failure mode was observed using scanning electron microscopy. The µTBS response was affected by adhesive systems, simulated pulpal pressure conditions, and storage time. SPP-CTR groups presented a higher overall bond strength than SPP-DTW and SPP-FBS, which were not significantly different from each other. Only for SBP, the SPP-FBS group showed higher µTBS than the SPP-DTW group. The Weibull analysis showed that the bonding reliability and durability under SPP-DTW and SPP-FBS were inferior to SPP-CTR, and the 24 h bonding quality of adhesives to dentin was superior to that of 3 m. SPP drastically reduced the µTBS of all adhesives to dentin regardless of solution (distilled water or fetal bovine serum). Storage after 3 m also decreased µTBS despite the SPP condition.
RESUMEN
[This corrects the article DOI: 10.3389/fbioe.2024.1354241.].
RESUMEN
AIM: Calcium hydroxide (CH) has been considered as a direct pulp capping materials (DPC) for the last decades despite having some limitations. Phosphorylate pullulan (PPL) incorporated with CH (CHPPL) is a novel biomaterial that was introduced as a promising DPC material. Thus, the aim of the study was to evaluate the inflammatory response and mineralized tissue formation (MTF) ability of PPL-based CH formulations on rat molars after DPC. METHODOLOGY: This study consisted of six groups: CH with 1% PPL (CHPPL-1); 3% PPL (CHPPL-3); 5% PPL (CHPPL-5); Dycal and NEX MTA Cement (N-MTA) as the positive control, and no capping materials (NC). One hundred twenty maxillary first molar cavities were prepared on Wistar rats. After capping, all the cavities were restored with 4-META/MMA-TBB resin and pulpal responses were evaluated at days 1, 7, and 28. Kruskal-Wallis followed by Mann-Whitney U-test was performed with a significance level of 0.05. Immunohistochemical expression of IL-6, Nestin, and DMP-1 was observed. RESULTS: At day 1, CHPPL-1, N-MTA, and Dycal exhibited no to mild inflammation, whilst CHPPL-3, CHPPL-5, and NC showed mild to moderate inflammation, and the results were significantly different (p < .05). At day 7, mild to moderate inflammation was observed in CHPPL-1, N-MTA, and Dycal, whereas CHPPL-3, CHPPL-5, and NC exhibited moderate to severe inflammation. Significant differences were observed between CHPPL-1 and N-MTA with NC (p < .05), CHPPL-1 and CHPPL-3 with CHPPL-5 and Dycal (p < .05), and CHPPL-3 with N-MTA (p < .05). A thin layer of mineralized tissue formation (MTF) was observed in all groups. At day 28, CHPPL-1, Dycal, and N-MTA showed no to mild inflammation, whilst CHPPL-3, CHPPL-5, and NC exhibited mild to severe inflammation, and statistically significant difference was detected (p < .05). CHPPL-1, Dycal, and N-MTA exhibited continuous MTF, whilst CHPPL-3, CHPPL-5, and NC had thicker and interrupted MTF. Significant differences were observed between CHPPL-1, CHPPL-3, and N-MTA with NC group (p < .05). Variable expressions of IL-6, Nestin, and DMP-1 indicated differences in the materials' impact on odontoblast-like cell formation and tissue mineralization. CONCLUSIONS: These findings suggest that CHPPL-1 has the potential to minimize pulpal inflammation and promote MTF and had similar efficacy as MTA cement.
Asunto(s)
Hidróxido de Calcio , Recubrimiento de la Pulpa Dental , Glucanos , Materiales de Recubrimiento Pulpar y Pulpectomía , Ratas Wistar , Animales , Glucanos/farmacología , Hidróxido de Calcio/farmacología , Ratas , Materiales de Recubrimiento Pulpar y Pulpectomía/farmacología , Recubrimiento de la Pulpa Dental/métodos , Compuestos de Calcio/farmacología , Compuestos de Aluminio , Combinación de Medicamentos , Masculino , Silicatos/farmacología , Pulpa Dental/efectos de los fármacos , Pulpa Dental/metabolismo , Fosforilación , Óxidos , Diente Molar , MineralesRESUMEN
OBJECTIVES: This study aimed to evaluate microtensile bond strength (µTBS) and ultra-morphological characteristic changes in sound dentin resulting from silver diamine fluoride (SDF) when using adhesives. METHODS: Ninety-six extracted human third molars were divided into the SDF-contaminated dentin group and the sound dentin group. In the SDF-contaminated dentin group, 38% SDF was agitated for 1 min, left undisturbed for 2 min, and rinsed with distilled water for 30 s. Then, each group was further subdivided into six subgroups (n = 8 / group) according to application modes: self-etch mode (SE) and etch-and-rinse mode (ER) followed by three adhesives: (1) Scothbond Universal Plus Adhesive (SUP); (2) G2-Bond Universal Adhesive (G2B); and (3) Clearfil Mega Bond 2 (MB2). All specimens were restored with resin composite and were stored in distilled water for 24 h before µTBS testing. Data from the µTBS test were analyzed using Three-way ANOVA and Duncan test (p < 0.05). The morphology of fractured surface and adhesive-dentin interfaces were evaluated by SEM, TEM, and STEM. Further elemental analysis was done by EDX. RESULTS: All SDF-contaminated dentin groups demonstrated significantly lower µTBS than sound dentin groups. All ER groups had higher µTBS than SE groups, except for G2B in the sound dentin group. STEM/EDX revealed an SDF-dentin-reacted layer in the SDF-contaminated dentin group. SIGNIFICANCE: SDF had an adverse effect on adhesives. Additionally, ER mode is preferable when bonded to SDF-contaminated dentin. A calcium and fluoride-contained layer was observed in all SDF-contaminated dentin.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos Dentales , Compuestos de Amonio Cuaternario , Compuestos de Plata , Humanos , Cementos Dentales/farmacología , Recubrimientos Dentinarios/química , Recubrimiento Dental Adhesivo/métodos , Dentina , Resistencia a la Tracción , Ensayo de Materiales , Agua , Cementos de Resina/química , Fluoruros TópicosRESUMEN
Objective: The present study aimed to assess the bond strength and durability of six bonding agents concerning their application to metal or ceramic brackets and zirconia. Materials and Methods: Six resin cement bonding agents (XT, XTS, RSBU, RGBU, SBPM, and GMP) were chosen for this investigation. Specimens were either stored in distilled water at 37°C for 24 h or subjected to 5,000 thermocycles before conducting a Shear Bond Strength (SBS) test. Statistical analysis of the SBS data was performed using three-way ANOVA and Games-Howell tests (α = 0.05). The Adhesive Remnant Index was examined, and the debonding surface details on brackets and zirconia were observed. Results: For metal brackets, all groups demonstrated clinically acceptable bond strength, irrespective of storage conditions, except for the XT group. Regarding ceramic brackets, all groups displayed acceptable bond strength after 24 h of water storage. However, following thermocycling, a significant decrease in SBS was noted across all groups (p < 0.05), with SBPM exhibiting a higher bond strength. Three-way ANOVA analysis indicated that SBS values were notably influenced by each factor, and an interaction among the three independent variables was observed (p = 0.000). Conclusion: The reliable bond strength between ceramic brackets and zirconia was significantly lower after thermocycling compared to that of metal brackets and zirconia. SBPM exhibited consistent and robust bond strength between ceramic/metal brackets and zirconia across various storage conditions. Furthermore, the HEMA-free adhesive demonstrated a potentially more consistent bonding performance compared to the HEMA-containing adhesive employed in this study.
RESUMEN
This study evaluated the effect of a 0.5% chloramine T solution on a chemical-cured universal adhesive by comparing the light-cured, one-step, self-etch adhesive for the bonding performance, mechanical properties, and resin-dentin interfacial characteristics. Caries-free human molars were randomly assigned into eight groups based on the bonding systems employed (Bond Force II, BF and Bondmer Lightless, BL), the immersion solutions used before bonding (0.5% chloramine T solution and distilled water), and the immersion durations (5 and 60 min). Microtensile bond strength (µTBS), nanoleakage evaluation, and nanoindentation tests were performed, and the surface morphology of the resin-dentin interface was examined using a focus ion beam/scanning ion microscopy system. Immersion in chloramine-T for 5 min significantly decreased the µTBS of Bondmer Lightless (from 22.62 to 12.87 MPa) compared with that in distilled water. Moreover, there was also a decreasing trend after immersing in chloramine-T for 60 min (from 19.11 to 13.93 MPa). Chloramine T was found to have no effect on the hardness, elastic modulus, or morphological characteristics of the ion-beam milled resin-dentin interfacial surfaces in the tested adhesives, suggesting that chloramine T might reduce the bond strength by interfering with the interaction and the sealing between the adhesive resin and dentin in the chemical-cured universal adhesive, albeit without affecting the mechanical properties.
RESUMEN
Abstract Background/purpose: The most widely utilized irrigation solution in endodontic therapy is sodium hypochlorite (NaOCl). The purpose of this study was to assess the effects of NaOCl on the bond strength of four universal adhesives and one two-step self-etch adhesive to pulp chamber dentin. Materials and methods: One hundred sixteen extracted sound human third molars were used in this study. All the teeth were divided into two groups: (1) with NaOCl treatment and (2) without NaOCl treatment. These two groups were subdivided into five bonding groups: G-Premio Bond (GP), Beautibond Xtreme (BBX), Scotchbond Universal (SBU), Clearfil Universal Bond Quick (UBQ), and Clearfil Megabond 2 (MB2). The microtensile bond strength (µTBS), the fracture mode analysis, resin-dentin interface and dentin surface were observed by SEM. Two-way ANOVA was performed to analyze the µTBS (α = 0.05). Results: The µTBS of the NaOCl group significantly decreased for GP and MB2 (P < 0.05). Significant effects of adhesive (F = 12.182, P < 0.001), and irrigation (F = 27.224, P < 0.001) on the µTBS were observed, whereas interaction between adhesive and irrigation was not significant (F = 1.761, P = 0.144). The adhesive layer with variable thickness was observed in all groups with different morphological structures. Conclusion: The effect of NaOCl treatment on the µTBS differs depending on the type of adhesives.
RESUMEN
OBJECTIVES: To determine the effect of an extra hydrophobic resin layer (EHL) on the bond strength and durability of three different pH one-step universal adhesives (UAs) utilized in self-etch (SE) mode, and to explore whether UAs can be used as a primer in two-step bonding system. METHODS: Three different pH UAs were utilized: G-Premio Bond (GPB), Scotchbond Universal (SBU), All-Bond Universal (ABU), while the bonding agent of Clearfil SE Bond 2 (SE2) was selected as the EHL. For the EHL groups, EHL was applied after the air blow of each UA and before light curing. The microtensile bond strength (µTBS), fracture modes, interfacial structures and nanoleakage (NL) were evaluated after 24 h water storage and after 15,000 thermal cycling (TC). Elastic modulus (EM) and hardness (H) was tested by a nanoindenter after 24 h. RESULTS: Significantly higher µTBS was achieved in the GPB+EHL group compared with GPB both at 24 h and after 15,000 TC, while the additional use of EHL did not improve the µTBS of SBU and ABU significantly both at 24 h and after 15,000 TC. GPB+EHL demonstrated lower NL than GPB. The mean EM and H of the adhesive layer in GPB+EHL was significantly decreased compared with GPB. CONCLUSIONS: The results indicated that the bond strength and durability of low pH one-step UA (GPB) were significantly improved by additional application of EHL both at 24 h and after 15,000 TC, while no significant improvement was observed for ultra-mild one-step UAs (SBU and ABU). CLINICAL SIGNIFICANCE: This study indicates that GPB can be used as a primer in a two-step bonding system, while SBU and ABU may not be as effective. These findings may help guide clinicians in selecting the appropriate UAs and bonding techniques for different clinical scenarios.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos Dentales , Recubrimientos Dentinarios/química , Resinas Compuestas/química , Resistencia a la Tracción , Ensayo de Materiales , Dentina , Cementos de Resina/química , AdhesivosRESUMEN
The aim of direct pulp capping (DPC) is to promote pulp healing and mineralized tissue barrier formation by placing a dental biomaterial directly over the exposed pulp. Successful application of this approach avoids the need for further and more extensive treatment. In order to ensure a complete pulp healing with the placement of restorative materials, a mineralized tissue barrier must form to protect the pulp from microbial invasion. The formation of mineralized tissue barrier can only be induced when there is a significant reduction in pulp inflammation and infection. Consequently, promoting the healing of pulp inflammation may provide a favorable therapeutic opportunity to maintain the sustainability of DPC treatment. Mineralized tissue formation was observed as the favorable reaction of exposed pulp tissue against a variety of dental biomaterials utilized for DPC. This observation reveals an intrinsic capacity of pulp tissue for healing. Therefore, this review focuses on the DPC and its healing procedure as well as the materials used for DPC treatment and their mechanisms of action to promote pulpal healing. In addition, the factors that can affect the healing process of DPC, clinical considerations and future perspective has been described.
RESUMEN
Several desensitizers routinely used clinically for dentin hypersensitivity are expected to inhibit demineralization. This study aimed to evaluate the effectiveness of sealing materials in inhibiting demineralization and increasing fluorine (F) uptake by acid-treated root surfaces. Five noncarious extracted human teeth were used to produce specimens. Three different fluoride-containing materials, namely "MS Coat F" (MS), "MS Coat Hys Block Gel" (HS), and CTX2 Varnish (FV), were used herein. Each material was applied to the demineralized root surface. Single sections were obtained from each specimen. All surfaces of each specimen, except the polished surface, were covered with wax and immersed in an automatic pH cycling system for 2 weeks. Fluorine and calcium distributions in the carious lesions of each specimen were evaluated using proton-induced gamma emission (PIGE) and X-ray (PIXE) techniques, respectively. Dentin demineralization was analyzed using transverse microradiography (TMR) before and after pH cycling. µPIXE/PIGE analysis demonstrated that all sample groups showed increased fluoride uptake on the root surface. TMR analysis revealed that both HS and FV showed significantly lower integrated mineral loss values than the control group. All three samples demonstrated a tendency towards increased fluoride uptake from fluoride-containing hypersensitivity desensitizers and a demineralization inhibition effect on root dentin.
RESUMEN
The purpose of this study was to evaluate the microtensile bond strength (µTBS) and Knoop hardness number (KHN) of a novel experimental light-cured resin cement (HL). Eighteen flat dentin surfaces of human molars were polished using #600 SiC paper and bonded to CAD/CAM resin blocks with the respective resin cements and composites: HL, Panavia V5 (PV), and Clearfil AP-X (AP). All specimens were stored in distilled water at 37 °C for 24 h and 7 days. Scanning electron microscope (SEM) and energy dispersive X-ray (EDX) observations were performed to evaluate filler morphology and to detect the elements. The resin cements had a significant effect on the immediate µTBS (F = 22.59, p < 0.05) and after water storage µTBS (F = 22.83, p < 0.05). Significant differences (p < 0.05) in the KHN between the tested materials were observed, and HL indicated the highest KHN when compared with PV. HL showed a combination of the regular-shaped filler and spherical-shaped filler within the matrix. Silicon was detected in HL from the EDX evaluation. HL exhibited better bonding performance and polymerization, which may have contributed to the improvement of the adhesive strength.
RESUMEN
This study aims to assess the color stability, water sorption, and solubility of 11 resin composites as commercially available dental products. Twenty samples (10 mm in diameter and 2 mm in thickness) of each material were fabricated using a customized silicone mold, followed by immersion in each of curry, coffee, wine, and distilled water for 28 days (n = 5). Baseline shade and color changes (ΔE) were measured using a reflection spectrophotometer. The CIE L*, a*, b* system was used to evaluate the color changes. Five samples of each resin composite were applied to test water sorption and solubility according to ISO 4049:2009. As a result, the ∆E values were significantly influenced by each of the three factors (composition of material, solution, time) and the interactions between them (p < 0.001). Highest resistance to discoloration was achieved by Ceram.X One Universal (CXU), followed by Magnafill Putty (MP). Generally, microhybrid composites showed fewer color changes than nanohybrid composites and giomers. DX. Universal and Filtek Z350 XT showed the highest ΔE values in all colorants. All materials tested in this study fulfilled the criteria of ISO 4049:2009; CXU and MP had the lowest water sorption and solubility. The Pearson test showed statistically significant positive correlations between water sorption and ΔE and between solubility and ΔE.
RESUMEN
This study aimed to evaluate the shear bond strength (SBS) of four bonding agents used to bond metal brackets to zirconia under different storage conditions. Four bonding agents were used [FLC: (Fuji ORTHO LC), XT: (TransbondTM XT), RUC-SBU: (Rely XTM Ultimate Clicker Adhesive Resin Cement+Single Bond Universal), and RUC-GBU: (Rely XTM Ultimate Clicker Adhesive Resin Cement+Gluma Bond Universal)] to bond two types of metal brackets (PT/3M) to zirconia surfaces, and they were stored in water at 37ºC for 24 h or thermocycling for 3,000 cycles. The SBS data of RUC-SBU and RUC-GBU using PT brackets were significantly higher than those of 3M brackets before and after thermocycling. It could be concluded that RUC-SBU and RUC-GBU could offer sufficient bond strength between metal brackets and zirconia for the short term compared with FLC and XT. The design of brackets can significantly affect the bond strength to zirconia.
Asunto(s)
Recubrimiento Dental Adhesivo , Soportes Ortodóncicos , Análisis del Estrés Dental , Ensayo de Materiales , Cementos de Resina/química , Resistencia al Corte , Agua/química , CirconioRESUMEN
Teledentistry is an online dental care service that allows patients and dentists to meet in real time, safely, without being at the same location. During the COVID-19 pandemic, real-time videoconferencing has gained popularity in the field of teledentistry, with numerous benefits for both patients and dentists. Online consultations can minimize costs, maximize time, and provide more convenient care options for both patients and dentists. When practicing teledentistry, a dentist must establish a good doctor-patient relationship. Dentists must ensure that the telecommunication solution that they choose meets their clinical requirements and complies with privacy laws. Dentists should provide adequate information to patients about the limitations, advantages, and disadvantages that may occur during online consultation. Dentists must follow guidelines and procedures regarding informed consent, patient details, personal communications, and consultancies' privacy and confidentiality. The patient should be aware of the limitations of teledentistry, and dentists will provide the best advice possible in the absence of a face-to-face consultation. This article discusses how teledentistry could be an effective tool for dentists and patients.
RESUMEN
PURPOSE: To evaluate whether varying thicknesses of universal adhesives utilizing the additional coating strategy would affect their microtensile bond strength (µTBS) to dentin, hardness, and elastic modulus (mechanical properties). MATERIALS AND METHODS: Ninety-nine human maxillary premolars were cut to expose coronal dentin, ground with regular-grit diamond burs, and randomly distributed into 9 groups based on 1. adhesive: Scotchbond Universal Adhesive (SB; universal), G Premio Bond (GP; universal) and Clearfil Megabond 2 (MB; two-step self-etch; control); and 2. application strategy (one, two or three coats; each coat light cured). After adhesive application and resin composite buildup, the bonded teeth were stored in distilled water (37°C; 24 h). Resin-dentin sticks from eight premolars per group (each premolar yielded 3 sticks; n = 24 sticks altogether) were prepared for the µTBS test, followed by measurement of the adhesive thicknesses at their fractured ends using SEM. The mechanical properties of the adhesive layers produced by different coats were evaluated on separate resin-dentin slices (n = 3 teeth per group). RESULTS: Two coats significantly increased the µTBS (p < 0.001) of all the adhesives. The correlation between adhesive thickness and bond strength was positive for GP but negative for SB. MB did not show any correlation. Additional coating significantly increased the mechanical properties of GP (p < 0.05) but did not affect SB and MB (p < 0.05). CONCLUSION: An additional adhesive coating over the manufacturers' recommendations improved the bond strength of all the adhesives tested. However, the increased mechanical properties of the adhesives with additional curing was material dependent.
Asunto(s)
Recubrimiento Dental Adhesivo , Recubrimientos Dentinarios , Adhesivos , Resinas Compuestas/química , Cementos Dentales , Dentina , Recubrimientos Dentinarios/química , Humanos , Ensayo de Materiales , Cementos de Resina/química , Resistencia a la TracciónRESUMEN
Cetylpyridinium chloride (CPC), a quaternary ammonium compound, which is present in mouthwash, is effective against bacteria, fungi, and enveloped viruses. This study was conducted to explore the antiviral effect of CPC on SARS-CoV-2. There are few reports on the effect of CPC against wild-type SARS-CoV-2 at low concentrations such as 0.001%-0.005% (10-50 µg/mL). Interestingly, we found that low concentrations of CPC suppressed the infectivity of human isolated SARS-CoV-2 strains (Wuhan, Alpha, Beta, and Gamma) even in saliva. Furthermore, we demonstrated that CPC shows anti-SARS-CoV-2 effects without disrupting the virus envelope, using sucrose density analysis and electron microscopic examination. In conclusion, this study provided experimental evidence that CPC may inhibit SARS-CoV-2 infection even at lower concentrations.
Asunto(s)
Tratamiento Farmacológico de COVID-19 , Cetilpiridinio , Antivirales/farmacología , Cetilpiridinio/farmacología , Humanos , Antisépticos Bucales/farmacología , SARS-CoV-2RESUMEN
OBJECTIVE: To evaluate the effect of a time delay before the light activation of resin composite on the microtensile bond strength (µTBS) of self-etch adhesives under dynamic simulated pulpal pressure. MATERIALS AND METHODS: One hundred twenty crown segments were prepared from human third molars. Dentin surfaces were prepared with coarse diamond burs and connected to a dynamic pulpal pressure device. The self-etch adhesives used were Clearfil SE Bond (CSE), G2-Bond Universal (G2B), Clearfil Universal Bond Quick (CBQ), and G-Premio Bond (GPB). Each adhesive was divided into 3 subgroups: immediate light activation of resin composite (T0), delayed light activation for 150 s (T1), and 300 s (T2). The µTBS data were obtained after 24-h water storage. Scanning electron microscopy was used to evaluate the nanoleakage at the resin-dentin surface. The µTBS data were analyzed using two-way ANOVA and Duncan's multiple comparisons. RESULTS: All adhesives demonstrated a significant reduction in µTBS at T2, except for CBQ where the bond strength was not affected by the delayed light activation times. The two-step self-etch adhesives (CSE and G2B) demonstrated higher bond strength than the one-step adhesives at all conditions. Nanoleakage was observed in all adhesives at T2; however, nanoleakage was detected only in CBQ and GPB at T1. CONCLUSIONS: Delayed light activation of resin composite adversely affected the dentin bond strength of self-etch adhesives. Two-step self-etch adhesives had better bonding performance than one-step self-etch adhesives. CLINICAL RELEVANCE: After adhesive application, resin composite should be adapted and cured as soon as possible.
Asunto(s)
Recubrimiento Dental Adhesivo , Humanos , Dentina , Resistencia a la Tracción , Cementos Dentales , Ensayo de Materiales , Recubrimientos Dentinarios/química , Cementos de Resina/química , Resinas Compuestas/química , AdhesivosRESUMEN
BACKGROUND: This study aimed to evaluate the color matching, light transmittance, and reflectance characteristics of the novel flowable resin composite OCF-001 (OCF). METHODS: Fifty-four resin composite molds were made with simulated class I cavities of A2, A3, and A4 shades by filling the rubber mold interspace with Estelite Sigma Quick (ESQ), Gracefil Putty (GP) and Filtek Supremme Ultra (FSU). After applying the adhesive, three different flowable resin composites (n = 6), OCF, Gracefil LoFlo (GLF), and Supreme Ultra Flowable (SUF), were used to fill the cavities. A colorimeter was used to measure the color parameters (CIEDE2000). The color measurements were taken immediately and after 28 days. Data were analyzed using the nonparametric Kruskal-Wallis (α = 0.05) and Wilcoxon tests. The light transmittance and reflection characteristics were measured with a black background using a spectrophotometer under D65 illumination. RESULTS: The ΔE00, and ΔC of OCF was lower than other tested materials in A2 and A3 shades both immediately and after 28 days. OCF showed the highest transmittance characteristic, and a relatively stable reflectance curve in all the wavelengths. CONCLUSIONS: OCF showed better shade matching with the surrounding shades of A2 and A3, a relative uniform reflectance and higher light transmission properties.
RESUMEN
Despite recent advances in bonding restorations, which are the basis of restorative dentistry, secondary caries are still able to form. Previously, a novel fluoride-containing zinc and copper (ZCF) nanocomposite was introduced to prevent the formation of caries due to its antibacterial activity. In this study, we studied the impact of ZCF nanoparticles on the adhesive strength of bonding restorations through micro-tensile bond strength (µTBS) testing. The impact of antibacterial and matrix metalloproteinase (MMP) inhibitors on the nanoparticles was also examined. The nanocomposites were prepared using a simple one-step homogeneous co-precipitation method at a low temperature. A self-etch adhesive was applied to 10 extracted caries-free human molars with (test group) and without (control group) the ZCF nanoparticles. This was followed by composite resin build-up and µTBS testing, MMP activity assays, and evaluation of the antibacterial effects. The results showed no significant differences in the µTBS between the ZCF and the control groups. However, the ZCF exhibited a significant inhibitory effect against MMP-2, MMP-8, and MMP-9, in addition to an antibacterial effect on Streptococcus mutans. Therefore, the present study demonstrated that the addition of ZCF nanoparticles to adhesive systems can result in MMP inhibition and antibacterial action while maintaining the mechanical properties of the bonding restorations.