Nanoindentation creep: The impact of water and artificial saliva storage on milled and 3D-printed resin composites.

PURPOSE: This study evaluated the effects of artificial saliva and distilled water on the nanoindentation creep of different 3D-printed and milled CAD-CAM resin composites. MATERIAL AND METHODS: Disk-shaped specimens were subtractively fabricated from polymer-infiltrated ceramic network (EN) and reinforced resin composite (B) and additively from resin composite (C) and hybrid resin composite (VS) using digital light processing (DLP). Specimens from each material were divided into two groups according to their storage conditions (artificial saliva or distilled water for 3 months). Creep was analyzed by nanoindentation testing. Statistical analysis was done using two-way ANOVA, one-way ANOVA, Bonferroni post hoc tests, and independent t-test (α = 0.05). RESULTS: The main effects of material and storage conditions, and their interaction were statistically significant on nanoindentation (p < 0.001). Storage condition had the greatest influence (partial eta squared ηP 2 = 0.370), followed by the material (ηP 2 = 0.359), and the interaction (ηP 2 = 0.329). The nanoindentation creep depths after artificial saliva storage ranged from 0.34 to 0.51 µm and from 0.50 to 0.87 µm after distilled water storage. One of the additively manufactured groups had higher nanoindentation creep depths in both storage conditions. CONCLUSIONS: All specimens showed comparable performance after artificial saliva storage, but increased nanoindentation creep after distilled water storage for 3 months. The subtractive CAD-CAM blocks showed superior dimensional stability in terms of nanoindentation creep depths in both storage conditions. Additively manufactured composite resins had lower dimensional stability than one of the subtractively manufactured composites, which was demonstrated as having higher creep deformation and maximum recovery. However, after artificial saliva storage, one of the additively manufactured resins had dimensional stability similar to that of subtractively manufactured.

Effect of Printing Layer Thickness on Optical Properties and Surface Roughness of 3D-Printed Resins: An In Vitro Study.

PURPOSE: To investigate the impact of printing layer thickness on the optical properties and surface roughness of various 3D-printed resins manufactured by digital light processing (DLP) and indicated for provisional and definitive restorations. MATERIALS AND METHODS: A total of 240 specimens from four different 3D-printing resins-VarseoSmile Crown Plus (Bego; VS), Crowntec (Saremco Dental; CR), GC Temp PRINT (GC Dental; TG), and NextDent C&B MFH (NextDent; ND)-were divided into four groups (n = 60 per group). Each group was further divided into three subgroups (n = 20) according to printing layer thickness (25, 50, and 100 µm). All specimens were subjected to thermocycling with coffee before measurements were taken with a spectroradiometer to calculate color differences. The Kubelka-Munk (K-M) absorption (K) and scattering coefficients (S), translucency parameters (TP), and surface roughness (Ra) values were calculated for each printing layer thickness and compared with those of the 2M2 shade tab (target). The data were analyzed using Mann-Whitney U test, the variance accounted for (VAF) coefficient by Cauchy-Schwarz, and post hoc comparisons using Tukey test (α ≤ .05). RESULTS: S (79% ≤ VAF ≤ 100%) and K (40.45% ≤ VAF ≤ 100%) spectral distribution depended on the wavelength. A 25-µm layer thickness resulted in no significant differences from the 2M2 shade for S (P > .230) and K (P > .200). VS showed significantly different S (P = .004) and K (P = .003) values from those of the shade tab with 50-µm layering thickness, whereas other materials did not show significant differences from the 2M2 shade for S (P > .280) and K (P > .301). The 100-µm layer thickness specimens had significantly different S and K values compared to the 2M2 shade tab (P < .004). TP values of resins with 100-µm layer thickness were significantly lower than resins in 25- and 50-µm layer thicknesses (P < .001). The Ra values of resins increased significantly with 100-µm layer thickness (P ≤ .001). CONCLUSIONS: All tested materials, except for VS, showed color properties similar to the target shade when 25- and 50-µm printing layer thicknesses were used. The translucency of resins tended toward an inverse relationship with printing layer thickness. The surface roughness of resins increased significantly with 100-µm layer thickness. However, all resins with a printing thickness of 25 µm showed better color properties and surface roughness.

Investigation of color and physicomechanical properties of peek and pekk after storage in a different medium.

The aim of this study is to assess color stability, solubility, and water sorption on polyether ether ketone (PEEK) and polyether ketone ketone (PEKK) after immersion in different storage conditions. Material and Methods Ninety disc-shaped specimens (8 × 2) were obtained from CAD/CAM blocks [PEEK (n = 45) and PEKK (n = 45)]. Before immersion, baseline color value data were recorded with a spectrophotometer. The specimens were soaked in three solutions red wine, coffee, and distilled water at 37 °C for 28 days. Following immersion, color values were remeasured, and color-change values (ΔE) were calculated. Water sorption and solubility were assessed by mass gain or loss after storage in water for 28 days. The Kruskal-Wallis and the Mann-Whitney U test were used for analysis (P = 0.05). Results ΔE00 between PEEK and PEKK was significantly different statistically (P < 0.001). PEEK presented higher water sorption than PEKK (P = 0.005). The difference in solubility between PEEK and PEKK was not statistically significant (P = 0.163). The materials and storage medium types had a statistically significant impact (P = 0.100). In terms of staining potential, the solutions tested in this experiment were ranked as: coffee > red wine > distilled water. The results of this study demonstrated that PEKK was more successful in polymer-containing CAD/CAM materials as it exhibited less color change and water absorption.

Stainability and translucency of potassium aluminum sulfate applied computer-aided design and computer-aided manufacturing materials after coffee thermocycling.

OBJECTIVE: The purpose of this in vitro study was to evaluate the effect of potassium aluminum sulfate (alum) application on the stainability and translucency of computer-aided design and computer-aided manufacturing (CAD-CAM) materials after coffee thermocycling (CTC). MATERIALS AND METHODS: Disk-shaped specimens (Ø10 × 1 mm; N = 200) were fabricated by using additively (Crowntec [CT] and Varseo Smile Crown Plus [VS]) and subtractively manufactured (Brilliant Crios [RCR], CEREC Block [FC], and Vita Enamic [VE]) CAD-CAM materials and polished. All specimens were randomly divided into two groups as alum applied and control (n = 10). All specimens were then subjected to CTC (10,000 cycles at 5-55°C) and color coordinates were measured at each time interval. Color differences (ΔE00 ) and relative translucency parameters (RTPs) were calculated and the data were statistically analyzed (a = 0.05). RESULTS: Among tested time intervals, alum applied specimens had their lowest ΔE00 after alum application (p ≤ 0.006), except for FC (p = 0.177). In addition, alum applied RCR had lower ΔE00 values than its control specimens (p = 0.029). Alum applied specimens had their lowest RTP after CTC (p < 0.001) and alum application decreased the RTP of CT (p = 0.010). CTC reduced the RTP of all materials in control groups (p < 0.001). Alum applied CT had higher RTP than its control specimens (p = 0.049). CONCLUSIONS: Alum application's effect on color change varied depending on the material and alum mostly resulted in clinically acceptable changes in translucency. CTC led to unacceptable color and translucency changes based on previously reported threshold values. CLINICAL SIGNIFICANCE: Optical properties of CAD-CAM materials and the sustainability of these properties over time is critical for longevity. Alum may improve the color stability of reinforced composite resin when subjected to long-term coffee consumption.

Marginal discrepancy and fracture load of thermomechanically fatigued crowns fabricated with different CAD-CAM techniques.

PURPOSE: To assess the effect of CAD-CAM technique (monolithic, CAD-on, or CAD-on cemented) and thermomechanical fatigue on the marginal discrepancy and fracture load of ceramic crowns. MATERIAL AND METHODS: A total of 90 brass master dies were fabricated to investigate marginal adaptation and fracture load. A mandibular first molar crown's median measurements were loaded into CAD software and divided into 2 crown design groups: Monolithic (M)(IPS e.max zirCAD)(n = 30) or CAD-on core (IPS e.max zirCAD) and lithium disilicate veneer (IPS e.max CAD) (n = 60). The crowns and cores were milled, seated on their respective dies, and marginal discrepancy values were measured by using microcomputed tomography. After veneers were milled, the cores in the veneer groups were divided into 2 groups; veneers bonded with fusion glass-ceramic (IPS e.max CAD Crystal) in CAD-on group (CO) and CAD-on cemented group (CO-C) where veneers were cemented (RelyX U200) onto cores (CO-C). The marginal discrepancy measurements were remade and the crowns were subjected to thermomechanical fatigue (TMF) by using a chewing simulator and thermocycling (5-55°C, 1,200,000 cycles). Marginal discrepancy measurements were repeated and the crowns were subjected to fracture load test by using a universal test device. Data were analyzed statistically by analysis of variance (ANOVA) and Tukey's honestly significant difference test (α = 0.05). RESULTS: All crown groups had similar marginal discrepancy before veneering. Veneering and cementation on die increased the marginal discrepancy of crowns in cemented CAD-on group. Thermomechanical fatigue increased the marginal discrepancy of both CAD-on groups. Monolithic crown group had the lowest marginal discrepancy after thermomechanical fatigue (p < 0.001), and the highest fracture load (p < 0.001) CONCLUSIONS: Fabrication technique affected the marginal fit and fracture load of CAD-CAM crowns after thermomechanical fatigue. All crowns survived the thermomechanical fatigue test without dislodgement or fracture. Monolithic crowns had the best fit and highest fracture load after fatigue testing. The CAD-on systems had similar marginal discrepancies, and static loading reproduced veneer chipping.

Effect of Potassium Aluminum Sulfate Application on the Viability of Fibroblasts on a CAD-CAM Feldspathic Ceramic before and after Thermocycling.

Potassium aluminum sulfate (alum) is a known adjuvant, which has been used as a mordant in textile industry for color fixation. This material has potential to be incorporated into dentistry for color stability, yet its toxicity first needs to be evaluated. The present study aimed to evaluate the cytotoxic potential of potassium aluminum sulfate (alum) on fibroblasts when applied onto feldspathic ceramic before and after thermocycling. Forty-eight feldspathic ceramic specimens were divided into four groups (FC: no alum application or thermocycling; FCT: thermocycling without alum application; FA: alum application without thermocycling; FAT: alum application and thermocycling) (n = 12). Cell viability was assessed by using a tetrazolium salt 3-[4,5-dimethylthiazol-2-yl]-2,5-diphnyltetrazolium bromide assay at 24 and 72 h, and cell cultures without any ceramic specimens served as control (C). One sample from each material group was further analyzed with energy dispersive X-ray spectroscopy (EDX). Cell viability at different time intervals within each group was analyzed with Friedman tests, while Kruskal−Wallis tests were used to compare the test groups within each time interval. Pairwise comparisons were further resolved by using Wilcoxon tests (a = 0.05). C had lower (p = 0.01) and FA had higher (p = 0.019) cell viability after 72 h. After 24 h, the highest cell viability was observed in C (p ≤ 0.036). After 72 h, the differences between C and FA, C and FAT, FC and FA, and FCT and FAT were nonsignificant (p > 0.05). Cell viability was not affected by alum application or thermocycling at any time interval (p ≥ 0.631). EDX analysis showed an increase in potassium concentration in FA and FAT when compared with FC and FCT. Regardless of the time interval, alum application onto feldspathic ceramic and thermocycling did not influence the cell viability.

Influence different polishing systems on roughness and colour stability of chairside CAD/CAM blocks with laminate veneer thickness.

OBJECTIVE: The aim of this study was to evaluate the effect of different polishing systems on the colour stability of different laminate veneer blocks for chair-side CAD-CAM after ultraviolet (UV) ageing. METHODS: About 240 sample (13 × 13 × 0.7) were prepared from four different CAD-CAM blocks IPS e.max CAD (IP), IPS Empress CAD (IE), Mark II (M) and Lava Ultimate (LU)) with A1 shade. Each group was divided into five subgroups (n = 12) according to the control (C) and four different polishing system: Sof-Lex (S), Edenta (E), Identoflex (I) and Zircon Brite (Z). Surface roughnesses (Ra) were measured by a profilometer before and after polishing. The baseline colour values were recorded according to the CIELab system. The colour coordinates (L*, a* and b*) of the samples were measured before and after UV ageing, and colour differences (ΔE00) were calculated by using the CIEDE2000 colour difference formula. A two-way ANOVA and Tukey test methods were used to analyse the data (α = 0.05). RESULTS: A significant interaction was observed between CAD-CAM blocks and polishing system (p < 0.001). The higher Ra and colour difference was calculated in LU in the Z group after polished and the lower Ra and colour difference was calculated in the IP in the S group after polished. For the IP group, the glazing procedure showed higher Ra and ΔE values with Z group than polished S system, whereas there is no statistical differences. CONCLUSION: It is concluded that polishing with the Sof-Lex system improves significantly smoothness and colour stability. However, there is no success in using the Zircon Brite polishing system.

Effect of stain brand and shade on color stability of stains applied on a CAD-CAM feldspathic ceramic.

The aim of this study was to investigate the effect of stain brand and color on color stability of stains on a CAD-CAM ceramic after aging. Specimens (15 × 8 × 1.5 mm) were fabricated from A2-shade ceramic blocks (Mark II; Vita Zahnfabrik) (N = 120). Specimens were divided into two groups (n = 10) to be stained with six different stains (yellow, orange, blue, gray, violet, and brown) from two manufacturers (GC initial spectrum (GC) and IPS e.max Ceram (IPS)). Aging was performed for 5 h at 134 °C. Color coordinates before and after aging were measured to calculate color differences (ΔE00). Kubelka-Munk absorption (K) and scattering coefficients (S) of stains were compared with those of A2 shade tab. Two-way ANOVA was used to analyze the ΔE00 values and Tamhane T2 was used to analyze the K and S coefficients (alpha = 0.05). A significant interaction was found between stain color and brand (p < 0.001). Color changes with IPS stains were higher than those with GC stains except for brown. The highest color difference was with orange stain of IPS (p < 0.001). Absorption and scattering coefficients of different stains on CAD-CAM ceramic were different from those of A2 shade tab except for brown stain (p < 0.001). Tested stains on CAD-CAM ceramic had varying color changes after aging. Color of gray, violet and brown of both stains was stable. Yellow, orange, and blue GC stains were more color stable compared with IPS. Absorption and scattering coefficients of stains in different colors varied.

Comparison of Silane Heat Treatment by Laser and Various Surface Treatments on Microtensile Bond Strength of Composite Resin/Lithium Disilicate.

In the current study, we evaluated the effects of heat treatment (by Er:YAG or furnace) and various surface treatments on the microtensile bond strength (µTBS) of silanized lithium disilicate ceramic. Seventy lithium disilicate (IPS e. max Press; Ivoclar Vivadent) and composite resin (Tetric N-Ceram; Ivoclar Vivadent) blocks were made and distributed into seven groups (n = 10) at random: S: silanization alone; ALS: airborne particle abrasion (APA) and silanization; SC: APA modified with silica and silanization; SHT1: silanization and heat treatment by Er:YAG; SHT2: silanization and heat treatment performed in the furnace (100 °C, 1 min); HF: etching with HF; and HFS: etching with HF and silanization. Every ceramic specimen was cemented to a composite resin block after surface treatment. Cemented specimens were embedded into acrylic resin and were tested with the µTBS test. Data were analyzed using one-way ANOVA and Tamhane T2 tests (α = 0.05). The SHT1 group had the highest bond of strength compared to the other groups (27.46 MPa). The ALS group had the lowest strength of the groups (15.56 MPa). Between SHT2 and HFS (p = 1), the comparison of the mean µTBS values showed no significant differences. It was concluded that silane heat treatment increased the resin composite-ceramic bond strength; however, within the terms of µTBS, the Er:YAG laser treatment was more successful than other surface treatment applications.

Effect of mouth rinses on optical properties of CAD-CAM materials used for laminate veneers and crowns.

OBJECTIVE: The purpose of this study was to investigate the effect of mouth rinses on the color and translucency of three computer-aided design and computer-aided manufacturing (CAD-CAM) restorative materials in laminate veneer and crown thicknesses. METHODS: Specimens from two different 5Y-TZP zirconia (InCoris TZI (IT), and Zirkonzahn (ZH)) and lithium disilicate (IPS e.max CAD [IC]) in two different thicknesses (0.7 mm for laminate veneer, and 1.5 mm for crown) were sectioned. All specimens were colored with an A2-shade liquid, and the baseline color values were recorded according to the CIELab system with a spectrophotometer. Each group was divided into two subgroups (n = 15) according to the immersion solution: two different mouth rinses, KL (Klorhex), and LI (Listerine, cool mint) for 180 hours. The color coordinates (L*, a*, b*) of the specimens were measured before and after immersion in a mouth rinse, and TP and ΔE00 color differences were calculated by using the CIEDE2000 color difference formula. A 3-way ANOVA, Bonferroni test, and 1-sample t tests were used to analyze the data (α = 0.05). RESULTS: The 3-way ANOVA revealed a significant interaction of material, thickness, and mouth rinse for translucency parameter and color difference (ΔE00 ) data (p < 0.001). TP decreased for both zirconia materials in laminate veneer thickness when immersed in LI mouth rinse (p < 0.05). No difference was found among the TP mean values of three materials in crown thickness after immersed in mouth rinses (p > 0.826). Both zirconia materials immersed in LI showed greater discoloration than after immersed in KL (p < 0.05). A significant difference was found in color change values among three materials for the laminate veneer thickness after immersed in LI (p < 0.001). However, all color difference values were within the clinical acceptability threshold, except for when ZH in laminate veneer thickness was immersed in LI. CONCLUSIONS: The color change of ZH zirconia with LI mouth rinse in laminate veneer thickness was high. For both zirconia ceramics, translucency decreased and the color was less stable in laminate veneer thickness after immersed in LI compared to the crown thickness. CLINICAL SIGNIFICANCE: The results of this in vitro study suggest that long-term use of alcohol-containing mouth rinse may alter the optical properties of tested CAD-CAM materials in tested laminate veneer thickness. For color stability with the long term use of tested mouth rinses, lithium disilicate may be preferred for both types of restorations.