RESUMEN
OBJECTIVE: this study evaluated dentin microtensile bond strength (µTBS) and failure modes (at 24 h and one year), bonding interface regarding hybridization, surface morphology regarding demineralization, in situ metalloproteinase (MMP) activity, and antibacterial effect of three dentin etchants compared to 35% phosphoric acid (PA). MATERIALS AND METHODS: The Adper Single Bond 2 adhesive (3 M Oral Care) was applied on moist dentin etched with PA (control) or on air-dried dentin etched with 3% aluminum nitrate + 2% oxalic acid (AN), 6.8% ferric oxalate + 10% citric acid (FO), or 10% citric acid (CA). The µTBS test used 40 human teeth (n = 10). Failure modes and surface morphology were analyzed by scanning electron microscopy (n = 3), while bonding interface morphology and MMP activity were evaluated by laser scanning confocal microscopy (n = 3). Antibacterial activity was evaluated against S. Mutans biofilm by means of viable cells count (CFU/mL). RESULTS: PA presented the highest bond strengths regardless of aging time. PA, AN, and CA showed stable bond strengths after one year of storage. Adhesive and mixed failures were predominant in all groups. Thin hybrid layers with short resin tags were observed for the experimental etchants. The AN-based etchant was able to inhibit MMP activity. All tested etchants presented antibacterial activity against S. Mutans biofilm. SIGNIFICANCE: This study suggests different dentin etchants capable of inhibiting MMP activity while also acting as cavity disinfectants.
Asunto(s)
Resinas Compuestas , Recubrimiento Dental Adhesivo , Compuestos Férricos , Humanos , Resinas Compuestas/química , Recubrimientos Dentinarios/farmacología , Recubrimientos Dentinarios/química , Cementos de Resina/farmacología , Cementos de Resina/química , Microscopía Electrónica de Rastreo , Dentina/química , Ácido Cítrico/farmacología , Antibacterianos/farmacología , Resistencia a la Tracción , Ensayo de MaterialesRESUMEN
BACKGROUND: To investigate the effect of 0.3 M 1-ethyl-3(3-dimethylaminopropyl) carbodiimide (EDC) aqueous solution pretreatment on push-out bond strength (PBS) and matrix-metalloproteinases (MMPs) activity within radicular dentin when different post cementation strategies were employed. METHODS: One hundred and twenty monoradicular human teeth were endodontically treated and randomly divided into six groups, depending on the cementation strategy and root dentin pretreatment (n = 20): EAR: cementation with an etch-and-rinse adhesive (LuxaBond Total Etch, DMG) and resin cement (LuxaCore Z Dual, DMG); EAR/EDC: 1 min EDC pretreatment after etching + EAR; SE: cementation with a self-etch primer (Multilink Primer, Ivoclar Vivadent) and corresponding cement (Multilink Automix, Ivoclar Vivadent); SE/EDC: self-etch primer + EDC pretreatment + SE; SA: cementation with a universal self-adhesive cement (RelyX Universal, 3 M); SA/EDC: EDC pretreatment + SA. Slices were submitted to PBS test and interfacial nanoleakage evaluation 24 h after cementation or after thermocycling (40.000 cycles, 5-55 °C). To investigate the effect of EDC on MMPs activity, 4 additional first maxillary premolars per group were processed for in situ zymography analysis. Multivariate ANOVA and post hoc Tukey tests were used to analyze PBS values. The data from in situ zymography were analyzed with Kruskal-Wallis test and Dunn's pairwise multiple comparison procedures (α = 0.05). RESULTS: The variables "EDC pretreatment", "root region" and "thermocycling" significantly influenced PBS (p < 0.05), while the variable "cementation strategy" had no influence (p > 0.05). Thermocycling significantly reduced PBS in SE and SA groups (p < 0.05). EDC was effective in preserving PBS after artificial aging. EDC pretreatment significantly reduced enzymatic activity at baseline in EAR and SE groups, and in SA group after thermocycling (p < 0.05). CONCLUSIONS: The use of EDC prevents the reduction of bond-strength values after artificial aging and silences endogenous enzymatic activity within radicular dentin when different cementation strategies were employed.
Asunto(s)
Recubrimiento Dental Adhesivo , Humanos , Carbodiimidas/química , Dentina , Cementos de Resina/uso terapéutico , Cementos de Resina/química , Metaloproteinasas de la Matriz , Ensayo de MaterialesRESUMEN
OBJECTIVES: Etching approaches [37% phosphoric acid, self-etching, 10-3 solution (3% ferric chloride dissolved in 10% citric acid), or 1.4% nitric acid] were evaluated regarding enamel shear bond strength (24 h), dentin microtensile bond strength (24 h and 2 years), failure mode, enzymatic activity of the hybrid layer, and nanoleakage (24 h and 2 years) of Prime&Bond Universal (PBU, Dentsply-Sirona) and Gluma Bond Universal (GBU, Kulzer). METHODS: Adhesives were applied on blot-dried (wet-bonding, positive control) or air-dried (remaining groups) dentin after acid-etching (15 s) or in self-etch mode. Enamel and dentin bond strength tests used 160 human teeth (n = 10). Failure mode of tested samples and nanoleakage within the dentin-adhesive interface (n = 5) were analyzed by scanning electron microscopy. Dentin enzymatic activity was investigated by in situ zymography (n = 3). RESULTS: Enamel bond strengths did not differ statistically among groups. Wet-bonding with 37% phosphoric acid showed similar dentin bond strength compared to 10-3 solution or 1.4% nitric acid at 24 h for both adhesives. None of the etchants inhibited enzymatic activity, and all groups showed dentin bond strength reduction after 2-year storage. GBU showed higher nanoleakage. Experimental etchants did not affect enamel bond strength. Dentin bond strength was not stable after 2 years, despite promising 24-hour results. SIGNIFICANCE: This study suggests multiple etching approaches to optimize and achieve stable dentin bonding, while also offering in-depth information about the performance of recently released universal adhesive systems.
Asunto(s)
Recubrimiento Dental Adhesivo , Recubrimientos Dentinarios , Recubrimiento Dental Adhesivo/métodos , Cementos Dentales , Dentina , Recubrimientos Dentinarios/química , Humanos , Ácido Nítrico , Cementos de ResinaRESUMEN
OBJECTIVE: This systematic review and meta-analyses aimed to evaluate the potential protective effect of titanium tetrafluoride (TiF4) compound compared to sodium fluoride (NaF) on eroded enamel or dentin. METHODS: Two independent reviewers searched PubMed, Scopus, Web of Science, LILACS, Cochrane, EMBASE, and Open gray Literature up to June 2020. MeSH terms, supplementary concepts, synonyms, and free terms were applied based on PICOS strategy (P- population: eroded enamel or dentin; I- intervention: eroded teeth treated with solution or varnish of TiF4; C- comparison: eroded teeth treated with a solution or varnish of NaF; O- outcome: mineral loss measurement; S- study design: in vitro studies). Seven distinct parameters evaluated the risk of bias, and all studies were submitted to 4 meta-analyses (first and second meta-analyses related to enamel loss treated with fluoride solution or varnish, respectively; third and fourth meta-analyses related to dentin loss treated with fluoride solution or varnish, respectively). A sensitivity test was performed by the RevMan software, based on standard mean difference calculation (P < .05). RESULTS: A total of 10,260 studies were retrieved, from which 22 studies were included in systematic review through eligibility criteria, of which 1 study was classified as low risk of bias, 19 as medium, and 3 as high. Seventeen studies were included in 4 different meta-analyses, presenting considerable overall heterogeneity (I2â¯=â¯95; 92; 95; and 93%, respectively) with statistical significance for TiF4 on the first meta-analysis, and no statistical significance for second, third, and fourth meta-analyses. CONCLUSIONS: Titanium tetrafluoride compound delivered as solution provided significant effective protection for erosion lesions on the enamel surface compared to sodium fluoride. However, when TiF4 or NaF were applied on enamel or dentin surfaces as varnish, both provided the same effective protection, based on in vitro studies with considerable heterogeneity.
Asunto(s)
Fluoruros , Erosión de los Dientes , Cariostáticos/farmacología , Cariostáticos/uso terapéutico , Fluoruros/farmacología , Humanos , Fluoruro de Sodio/farmacología , Titanio , Erosión de los Dientes/prevención & controlRESUMEN
OBJECTIVE: This study comprehensively reviewed clinical trials that investigated the effect of immediate dentin sealing (IDS) technique on postoperative sensitivity (POS) and clinical performance of indirect restorations. MATERIALS AND METHODS: The systematic review was conducted according to the preferred reporting items for systematic reviews and meta-analyses statement, and was guided by the PICOS strategy. Clinical trials in which adult patients received at least one indirect restoration cemented with IDS approach and one restoration cemented following the delayed dentin sealing (DDS) were considered. RESULTS: Following title screening and full-text reading, four studies met the inclusion criteria and were included for qualitative synthesis, while two studies were selected for quantitative synthesis. According to Risk of bias-2 tool, two studies were classified as "some concerns" for the outcome POS. No statistically significant differences were found between teeth restored with indirect restorations using the IDS and DDS approach for POS (p > 0.05), neither at the baseline (very low certainty of evidence according to GRADE) nor after 2 years of follow-up (low certainty of evidence according to GRADE). CONCLUSION: There is low-certainty evidence that IDS does not reduce POS in teeth restored with indirect restorations. CLINICAL SIGNIFICANCE: There is no clinical evidence to favor IDS over DDS when restoring teeth with indirect restorations.
Asunto(s)
Dentina , Diente Molar , Adulto , Resinas Compuestas , HumanosRESUMEN
OBJECTIVES: To compare the operative time and presence of air voids on Class II restorations fabricated by dental practitioners with 1 to 5 years of experience using incremental and bulk-filling techniques. METHOD AND MATERIALS: Four techniques were evaluated: incremental, bulk-filling, bulk-filling with heated composite, and snowplow technique. Standardized mandibular first molars with a MOD (mesial, occlusal, and distal) cavity were used. Voluntary operators made two restorations using each technique and the time required for each restoration was recorded. The restorations were scanned by micro-computed tomography to calculate the volume of the restoration occupied by air voids. The "operative time" and "volume of air voids" were analyzed individually by two-way ANOVA and Tukey HSD post hoc (α = .05) for the factors operator and insertion technique. A correlation between "operative time" and "volume of air voids" was evaluated using Pearson coefficient (α = .05). RESULTS: The incremental technique required significantly longer time, yet no differences were observed between the bulk-filling techniques. There were no significant differences between techniques regarding the volume of air voids. A significant, but weak, and inverse linear correlation (P = .0059; r = -.29; r2 = 8.41%) was found between the operative time and volume of air voids. CONCLUSION: There were no significant differences in the volume of air voids among the evaluated techniques, although bulk-filling techniques required a shorter operative time. Hence, implementing bulk-filling techniques by dental schools and restorative dental practitioners with different levels of expertise may reduce chair time and produce a volume of air voids similar to the incremental technique.
Asunto(s)
Resinas Compuestas , Restauración Dental Permanente , Preparación de la Cavidad Dental , Odontólogos , Humanos , Ensayo de Materiales , Tempo Operativo , Rol Profesional , Microtomografía por Rayos XRESUMEN
This in vitro study evaluated the effect of the beam homogeneity of a multiple-peak light-curing unit on the surface microhardness and the effect of toothbrushing wear on the microhardness, surface roughness, roughness profile, volume loss, and gloss retention of incremental and bulk-fill resin-based composites (RBCs). A LED light-curing unit (VALO) with four LEDs at the tip end (405, 445, 465A, and 465B nm emission peak) was used according to each manufacturer-recommended time to obtain disks (n=10) of six RBCs: Estelite Sigma Quick, Charisma Classic, Tetric EvoCeram Bulk Fill, Filtek Z250, Filtek Supreme Ultra, and Filtek Bulk Fill. Microhardness values were obtained according to each LED positioning of the light-curing unit on the top surface of the RBCs and were analyzed before and after toothbrushing regarding microhardness, surface roughness, roughness profile, volume loss, and gloss retention. Microhardness was considered homogeneous on the top surface regardless of the type of RBC or wavelength tested (p>0.05). Overall, toothbrushing did not reduce the microhardness of the RBCs but influenced the gloss values for most RBCs (p<0.001). Charisma Classic presented the greatest surface roughness and roughness profile after toothbrushing (p<0.05). Volume loss did not differ among RBCs (p>0.05). In conclusion, different wavelengths of the LED did not affect the top surface microhardness, regardless of the RBCs tested; and bulk-fill composites presented similar surface changes (microhardness, surface roughness, roughness profile, volume loss, and gloss retention) when compared to conventional composites after toothbrushing.
Asunto(s)
Resinas Compuestas , Materiales Dentales , Ensayo de Materiales , Polimerizacion , Propiedades de Superficie , Cepillado DentalRESUMEN
PURPOSES: this clinical study evaluated the accuracy and execution time of a digital imaging fiber-optic transillumination (DIFOTI) technique for the detection of approximal caries in posterior teeth compared to intra-oral examination associated with bitewing radiographs. METHODS: one hundred patients were selected and submitted to clinical inspection and bitewing radiographs. The outcomes of this process were converted into scores, according to the International Caries Detection and Assessment System (ICDAS): 0-sound tooth; 1, 2, and 3-carious lesion confined within enamel; 4, 5, and 6-dentin carious lesion. Subsequently, an independent investigator acquired digital images of the same teeth using a DIFOTI device (DIAGNOcam, Kavo Dental), which were also converted into ICDAS scores. The time required for executing diagnostic procedures was measured. The clinical sensitivity and specificity of DIFOTI were analyzed by receiver operating characteristic (ROC) curves. The time necessary to perform the diagnostic methods was evaluated by Mann-Whitney U (alfa = 0.05). RESULTS: the overall test accuracy for the DIFOTI-based device ranged from 0.717 to 0.815 (area under the ROC curve) with p < 0.0001 for all ICDAS scores. Bitewing radiographs took almost twice the time required by DIFOTI (p < 0.001). CONCLUSIONS: the DIFOTI-based device DIAGNOcam provided accurate detection of approximal caries in posterior teeth, even at early stages. The technique employed for transillumination caries diagnosis by the same device took less time than conventional bitewing radiographs. CLINICAL RELEVANCE: transillumination devices, such as DIAGNOcam, can be accurately used for caries diagnosis in approximal surfaces of posterior teeth, demanding less clinical time and without radiation-related risks.
RESUMEN
PURPOSE: This study evaluated dentin bond strength, failure mode, interface morphology, adhesive infiltration into dentin, and marginal adaptation of bulk-fill composites used with different adhesives. MATERIALS AND METHODS: Third molars received occlusal class I cavities (4 mm x 4 mm x 4 mm) that were bulk-filled with Admira Fusion x-tra (Voco) or SonicFill 2 (Kerr) using four adhesives (Scotchbond Multipurpose, 3M Oral Care; Clearfil SE Bond, Kuraray Noritake; OptiBond All-In-One, Kerr; Futurabond U, Voco). Scotchbond was used with acid-etching, while the remaining adhesives were applied in self-etch mode. Sixty-four teeth were selected for the microtensile bond strength test (n = 8). Failure modes were analyzed with scanning electron microscopy (SEM). Interface morphology and adhesive infiltration (n = 3) were investigated using confocal laser scanning microscopy (CLSM). Marginal adaptation (n = 3) was also evaluated using SEM. Bond strength, failure mode, and adhesive infiltration data were analyzed for distribution and homocedasticity, followed by appropriate statistical analyses (α = 0.05). RESULTS: Regarding bond strength, no differences were found among adhesives for SonicFill; Clearfil showed a significantly lower mean value than did Scotchbond (p ≤ 0.05) for Admira; the two composites did not differ. Adhesive and mixed failures were observed for all groups. Scotchbond led to thicker hybrid layers with deeper adhesive infiltration as opposed to Futurabond. The groups Admira+Futurabond, SonicFill+Clearfil, and SonicFill+Futurabond presented the highest marginal discontinuity. CONCLUSION: The tested bulk-fill composites did not affect dentin bonding. Scotchbond and Clearfil seem to be reliable for bonding SonicFill 2 to dentin. The performance of Futurabond was questionable, given its poor-quality interface and higher percentages of marginal gaps.
Asunto(s)
Recubrimiento Dental Adhesivo , Recubrimientos Dentinarios , Adhesivos , Resinas Compuestas , Cementos Dentales , Dentina , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Cementos de Resina , Resistencia a la TracciónRESUMEN
Abstract This in vitro study evaluated the effect of the beam homogeneity of a multiple-peak light-curing unit on the surface microhardness and the effect of toothbrushing wear on the microhardness, surface roughness, roughness profile, volume loss, and gloss retention of incremental and bulk-fill resin-based composites (RBCs). A LED light-curing unit (VALO) with four LEDs at the tip end (405, 445, 465A, and 465B nm emission peak) was used according to each manufacturer-recommended time to obtain disks (n=10) of six RBCs: Estelite Sigma Quick, Charisma Classic, Tetric EvoCeram Bulk Fill, Filtek Z250, Filtek Supreme Ultra, and Filtek Bulk Fill. Microhardness values were obtained according to each LED positioning of the light-curing unit on the top surface of the RBCs and were analyzed before and after toothbrushing regarding microhardness, surface roughness, roughness profile, volume loss, and gloss retention. Microhardness was considered homogeneous on the top surface regardless of the type of RBC or wavelength tested (p>0.05). Overall, toothbrushing did not reduce the microhardness of the RBCs but influenced the gloss values for most RBCs (p<0.001). Charisma Classic presented the greatest surface roughness and roughness profile after toothbrushing (p<0.05). Volume loss did not differ among RBCs (p>0.05). In conclusion, different wavelengths of the LED did not affect the top surface microhardness, regardless of the RBCs tested; and bulk-fill composites presented similar surface changes (microhardness, surface roughness, roughness profile, volume loss, and gloss retention) when compared to conventional composites after toothbrushing.
Resumo Este estudo in vitro avaliou a homogeneidade do feixe de um fotopolimerizador de múltiplos picos na microdureza superficial e o efeito da escovação na microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e retenção do brilho de compósitos a base de resina (RBCs) incrementais ou bulk-fill. Um fotopolimerizador LED (VALO) com quatro LEDs na ponteira (405, 445, 465A e 465B nm de pico de emissão) foi usado de acordo com o tempo recomendado por cada fabricante para obtenção de discos (n=10) de seis RBCs: Estelite Sigma Quick, Charisma Classic, Tetric EvoCeram Bulk Fill, Filtek Z250, Filtek Supreme Ultra e Filtek Bulk Fill. Os valores de microdureza foram obtidos seguindo o posicionamento de cada LED na superfície superior das amostras e foram analisados antes e após a escovação quanto a microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e retenção do brilho. A microdureza foi considerada homogênea no topo da superfície, independentemente do tipo de RBCs ou comprimento de onda testados (p>0.05). No geral, a escovação não reduziu a microdureza das RBCs, mas influenciou o brilho para a maioria das RBCs (p<0.001). Charisma Classic apresentou os maiores valores de rugosidade superficial e perfil de rugosidade após a escovação (p<0.05). A perda de volume não diferiu entre as RBCs (p>0.05). Em conclusão, os diferentes comprimentos de onda do LED não alteraram a microdureza do topo da superfície, independentemente das RBCs testadas; e as resinas bulk-fill apresentaram alterações superficiais similares (microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e manutenção do brilho) quando comparadas às resinas convencionais após a escovação.
Asunto(s)
Resinas Compuestas , Materiales Dentales , Propiedades de Superficie , Ensayo de Materiales , PolimerizacionRESUMEN
OBJECTIVE: This study evaluated physical and mechanical properties and characterized the filler particles of seven composites. MATERIALS AND METHODS: Filtek Supreme (FS, 3M Oral Care), Forma (FO, Ultradent), Charisma Diamond (CD, Kulzer), Spectra Smart (SS, Dentsply), Filtek Bulk Fill (FB, 3M Oral Care), Tetric N-Ceram Bulk Fill (TB, Ivoclar), and Cention N (Ivoclar) in self- (CNSC) or dual-curing (CNDC) were evaluated. Fillers size, shape, and content were analyzed by scanning electron microscopy (SEM) and X-ray dispersive energy spectroscopy (EDX). Disk-shaped specimens (n = 5) were prepared for sorption (SP) and solubility (SL). Flexural strength and elastic modulus were tested at 24 h and 12 months (n = 10). Degree of conversion (DC%) and maximum rate of polymerization (Rpmax) were evaluated using micro-Raman spectroscopy. SP and SL results were submitted to Kruskal-Wallis one-way ANOVA and Dunn's pairwise test (α = 0.05). Mechanical properties were analyzed by 2-way ANOVA and Tukey's test (α = 0.05). DC% of CNSC and CNDC was compared by independent t-test (α = 0.05). Rpmax results were analyzed by 1-way ANOVA and Tukey's test (α = 0.05). RESULTS: The composites differed regarding filler size, shape, and content. CD and CNSC showed lower SP than FS. SS had lower SL than CNSC and CNDC. CNDC presented higher DC% than CNSC. CD, TB, and CNDC showed the highest Rpmax. TB, CNSC, and CNDC showed the lowest 24-h flexural strengths. Mechanical properties of CD did not decrease, while FO, TB, and CNSC showed a significant reduction after storage. CONCLUSIONS: Monomer composition and fillers characteristics greatly influenced the physico-mechanical properties of the tested composites.
Asunto(s)
Resinas Compuestas , Resistencia Flexional , Módulo de Elasticidad , Ensayo de Materiales , Polimerizacion , Solubilidad , Propiedades de SuperficieRESUMEN
This article reports a comprehensive restorative treatment using bulk-fill composites and discusses their properties and clinical performance. A 20-year-old man sought dental treatment due to the dark shade of his smile and multiple old amalgam fillings. Based on clinical and radiographic findings, and the patient's demand for tooth-colored fillings, treatment comprised enamel microabrasion and in-office dental bleaching, followed by the replacement of amalgam fillings by bulk-fill composites. Bulk-fill composites exhibit modifications in the filler size and shape or in the chemistry of monomers that allow them to be applied in thicker layers (4 to 5 mm), creating opportunities for simpler, faster, and more-efficient clinical procedures, as seen in the present report.
Asunto(s)
Resinas Compuestas , Diente , Adulto , Materiales Dentales , Humanos , Ensayo de Materiales , Adulto JovenRESUMEN
The purpose of this study was to evaluate the surface roughness (Ra), and the morphology and composition of filler particles of different composites submitted to toothbrushing and water storage. Disc-shaped specimens (15 mm × 2 mm) were made from five composites: two conventional (Z100™, and Filtek™ Supreme Ultra Universal, 3M), one "quick-cure" (Estelite ∑ Quick, Tokuyama), one fluoride-releasing (Beautiful II, Shofu), and one self-adhering (Vertise Flow, Kerr) composite. Samples were finished/polished using aluminum oxide discs (Sof-Lex, 3M), and their surfaces were analyzed by profilometry (n = 5) and scanning electron microscopy (SEM; n = 3) at 1 week and after 30,000 toothbrushing cycles and 6-month water storage. Ra data were analyzed by two-way analysis of variance and Tukey's test (α = 0.05). Filler particles morphology and composition were analyzed by SEM and X-ray dispersive energy spectroscopy, respectively. Finishing/polishing resulted in similar Ra for all the composites, while toothbrushing and water storage increased the Ra of all the tested materials, also changing their surface morphology. Beautifil II and Vertise Flow presented the highest Ra after toothbrushing and water storage. Filler particles were mainly composed of silicon, zirconium, aluminum, barium, and ytterbium. Size and morphology of fillers, and composition of the tested composites influenced their Ra when samples were submitted to toothbrushing and water storage.
Asunto(s)
Resinas Acrílicas , Resinas Compuestas , Poliuretanos , Propiedades de Superficie , Imagen ÓpticaRESUMEN
OBJECTIVES: To evaluate the effect of experimental conditioners (10-3 solution - 10-3, 6.8% ferric oxalate - FOX, and 1.4% nitric acid - NI) on dentin elastic modulus, flexural strength, bond strength, failure mode, and adhesive interface morphology of two etch-and-rinse adhesives (XP Bond, Dentsply or One-Step, Bisco) applied on etched dry dentin. METHODS: Sound human third molars were used for the microtensile bond strength test (nâ¯=â¯8), performed at 24â¯h and after one year of water storage. Failure modes were evaluated by scanning electron microscopy. Dentin bonding interface was analyzed by confocal laser scanning microscopy (nâ¯=â¯3). Adhesive systems were applied on phosphoric acid-etched, wet (positive control) and dry (negative control) dentin, and on etched and dry dentin previously treated with 10-3 (15s), FOX (60s), or NI (15s). Bovine dentin bars (nâ¯=â¯15) were immersed into the conditioning solutions and subjected to a three-point bending test. RESULTS: XP Bond +â¯10-3 or NI resulted in lower bond strength than phosphoric acid. One-Step +â¯10-3 or NI resulted in bond strengths equivalent to the positive control. Experimental conditioners presented no bond strength reduction after one year, regardless of the bonding agent tested. One-Step resulted in more adhesive failures than XP Bond at 24â¯h, and mixed failures increased after storage. All experimental conditioners promoted hybridization and resin tags formation, except FOX. Dentin elastic modulus was not affected by the conditioners, whereas flexural strength was significantly reduced by FOX. CONCLUSIONS: Adequate and stable dentin bonds were achieved when the bonding agents were applied on 10-3 or NI-treated dentin. None of the experimental conditioners reduced dentin elastic modulus, but dentin flexural strength was significantly reduced by FOX-conditioning.
Asunto(s)
Dentina/química , Hierro/química , Ácido Nítrico/química , Adhesivos/química , Animales , Bovinos , Humanos , SolucionesRESUMEN
The effects of tooth brushing could affect the long-term esthetic outcome of composite restorations. This study evaluated the effect of two different emission spectrum light-curing units on the surface roughness, roughness profile, topography and microhardness of bulk-fill composites after in vitro toothbrushing. Valo (multiple-peak) and Demi Ultra (single-peak) curing lights were each used for 10s to polymerize three bulk-fill resin composites: Filtek Bulk Fill Posterior Restorative (FBF), Tetric EvoCeram Bulk Fill (TET) and Surefil SDR Flow (SDR). After 30,000 reciprocal strokes in a toothbrushing machine, the roughness profile, surface roughness, surface morphology, and microhardness were examined. Representative SEM images were also obtained. When light-cured with the Demi Ultra, SDR showed the most loss in volume compared to the other composites and higher volume loss compared to when was light-cured with Valo. The highest surface roughness and roughness profile values were found in SDR after toothbrushing, for both light-curing units tested. FBF always had the greatest microhardness values. Light-curing TET with Valo resulted in higher microhardness compared to when using the Demi Ultra. Confocal and SEM images show that toothbrushing resulted in smoother surfaces for FBF and TET. All composites exhibited surface volume loss after toothbrushing. The loss in volume of SDR depended on the light-curing unit used. Toothbrushing can alter the surface roughness and superficial aspect of some bulk-fill composites. The choice of light-curing unit did not affect the roughness profile, but, depending on the composite, it affected the microhardness.
Asunto(s)
Resinas Compuestas/efectos de la radiación , Luces de Curación Dental , Cepillado Dental/efectos adversos , Análisis de Varianza , Resinas Compuestas/química , Dureza/efectos de los fármacos , Dureza/efectos de la radiación , Curación por Luz de Adhesivos Dentales/métodos , Ensayo de Materiales , Microscopía Confocal , Microscopía Electrónica de Rastreo , Polimerizacion , Reproducibilidad de los Resultados , Propiedades de Superficie/efectos de los fármacos , Propiedades de Superficie/efectos de la radiación , Factores de TiempoRESUMEN
This study evaluated dentin bond strength (BS) and nanoleakage of non- and pre-etched dentin immediately (T0 ,), 7 days (T7 ), and 14 days (T14 ) after bleaching. Bovine incisors (150) were selected and half of them submitted to intrapulpal dentin etching (e). Non- and pre-etched dentin were subjected to the following (n = 15): no bleaching/control (C); 35% carbamide peroxide (CP); 35% hydrogen peroxide (35% HP); 25% hydrogen peroxide (25% HP); and sodium perborate (SP). Bleaching agents were applied to the pulp chamber four times within a 72-h interval. Afterwards, pulp chamber dentin was prepared for the BS test at different evaluation times (n = 5): T0 , T7 , and T14 . Composite blocks were built on pulp chamber and sectioned in slices. Slices were reduced to an hour-glass shape with a cross-sectional area of 0.8 mm2 and submitted to microtensile BS test. Two additional specimens for each group were prepared for nanoleakage evaluation by transmission electron microscopy (TEM). Results were analyzed by ANOVA (two-way) and Dunnett's test (p < .05). BS decreased immediately after intracoronal bleaching for both sound and pre-etched dentin (p < .05). At T14 , the BS of non-etched bleached dentin increased for all groups, whereas the pre-etched SPe group presented BS similar to the Ce. Nanoleakage within the hybrid layer was perceptible immediately after bleaching, although a decrease in nanoleakage was observed for all groups at T14 . Adhesive restorations should be performed 7-14 days after bleaching, according to the bleaching agent used. Intracoronal bleaching should be performed preferably with sodium perborate if previous dentin etching is applied.