RESUMEN
Most medium entropy alloys (MEAs) exhibit excellent mechanical properties, but their applications are limited because of their high density. This study explores a series of lightweight nonequiatomic Ti65(AlCrNbV)35-xZrx (x = 3, 5, 7, and 10) MEAs with a low density, high strength, and high ductility. To achieve solid solution strengthening, Zr with a large atomic radius was used. In addition, various thermomechanical treatment parameters were adopted to further improve the MEAs' mechanical properties. The density of the MEAs was revealed to be approximately 5 g/cm3, indicating that they were lightweight. Through an X-ray diffraction analysis, the MEAs were revealed to have a single body-centered cubic structure not only in the as-cast state but also after thermomechanical treatment. In terms of mechanical properties, all the as-cast MEAs with Zr additions achieved excellent performance (>1000 MPa tensile yield strength and 20% tensile ductility). In addition, hot rolling effectively eliminated the defects of the MEAs; under a given yield strength, hot-rolled MEAs exhibited superior ductility relative to non-hot-rolled MEAs. Overall, the Ti65(AlCrNbV)28Zr7 MEAs exhibited an optimum combination of mechanical properties (yield strength > 1200 MPa, plastic strain > 15%) after undergoing hot rolling 50%, cold rolling 70%, and rapid annealing for 30 to 50 s (at a temperature of approximately 850 °C) with a heating rate of 15 K/s. With their extremely high specific yield strength (264 MPa·g/cm3) and high ductility (22%), the Ti65(AlCrNbV)28Zr7 MEAs demonstrate considerable potential for energy and transportation applications.