RESUMEN
OBJECTIVE: Remineralising composites with antibacterial properties may seal the cavity and prevent secondary caries. This study aimed at developing experimental flowable composites containing different concentrations of fluoride-doped calcium phosphate fillers and evaluating their remineralising and antibacterial properties. METHODS: Experimental resin-based composites containing different concentrations (0-20 %) of fluoride-doped calcium phosphate fillers (VS10/VS20) were formulated. The release of calcium (Ca), phosphate (PO) and fluoride (F) ions was assessed for 30 days. Remineralisation properties were evaluated through ATR-FTIR and SEM/EDX after storage in simulated body fluid (SBF). The metabolic activity and viability of Streptococcus gordonii was also evaluated through ATP, CFU and live/dead confocal microscopy. The evaluation of specific monomer elution from the experimental composites was conducted using high-performance liquid chromatography (HPLC). RESULTS: The composites containing VS10 showed the highest release of Ca, those containing VS20 released more F over time (p < 0.05), while there was no significant difference in terms of PO ions release between the groups (p > 0.05). A quick 7-day mineral precipitation was observed in the tested composites containing VS10 or VS20 at 10 %; these materials also showed the greatest antibacterial activity (p < 0.05). Moreover, the tested composites containing VS10 presented the lowest elution of monomers (p < 0.05). CONCLUSIONS: Innovative composites were developed with low monomers elution, evident antibacterial activity against S. gordonii and important remineralisation properties due to specific ions release. CLINICAL SIGNIFICANCE: Novel composites containing fluoride-doped calcium phosphates may be promising to modulate bacteria growth, promote remineralisation and reduce the risk of cytotoxicity related to monomers' elution.
Asunto(s)
Fluoruros , Fosfatos , Fosfatos/farmacología , Fosfatos/química , Fluoruros/farmacología , Fluoruros/química , Ensayo de Materiales , Resinas Compuestas/farmacología , Resinas Compuestas/química , Fosfatos de Calcio/farmacología , Fosfatos de Calcio/química , Fluoruro de Calcio , Antibacterianos/farmacologíaRESUMEN
OBJECTIVES: To examine whether dentin-etching extension and/or the hydrophobic-rich content of hybrid layers would affect fatigue strengths of a mild universal adhesive after long-term aging. METHODS: Twin-bonded resin-dentin interfaces were produced by etching sound midcoronal dentin beams with 32 % ortho-phosphoric acid for 15 s (OPA15s), 3 s (OPA3s) or 10 % meta-phosphoric acid for 15 s (MPA15s). Samples were bonded with a mild universal adhesive with or without additional coating using a solvent-free bisGMA-based bonding resin. Self-etch application served as control. Composite buildups were made with a nanofilled composite. Bar-shaped twin-bonded interfaces (0.9 × 0.9 × 12 mm) were aged for two years in artificial saliva at 37 â and tested under 4-point flexure at quasi-static (n = 16) and cyclic loads (n = 35) until failure. The stress-life fatigue behavior was evaluated using the staircase method at 4 Hz. Crack initiation and fracture patterns were evaluated by SEM. Cyclic-loaded data was analyzed by Kruskal-Wallis on Ranks (α = 0.05). RESULTS: Significantly higher fatigue life distributions and higher endurance limits were observed for less aggressive etch-and-rinse protocols (OPA3s and MPA15s) after long-term ageing. Hydrophobic-rich coating produced 20-32 % higher endurance limits, prevented micrometer-sized porosities at bonded interfaces, reduced etching-associated variability and lowered crack formation. Significance Long-term hydrolysis produces detrimental effects on the fatigue strength of resin-dentin interfaces. The bond-promotion effect of less aggressive etch-and-rinse protocols and the creation of hybrid layers with higher hydrophobic-rich content are critical to extend the durability of mild universal adhesives. Therefore, current oversimplification trends in adhesive dentistry may limit resin-dentin bonding performance.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos Dentales , Recubrimientos Dentinarios , Cementos de Resina , Grabado Ácido Dental/métodos , Recubrimiento Dental Adhesivo/métodos , Dentina , Ensayo de Materiales , Resistencia a la Tracción , AdhesivosRESUMEN
OBJECTIVE: To evaluate the effect of dimethyl sulfoxide (DMSO) on the microtensile bond strength (µTBS) and nanoleakage (NL) of universal adhesives on eroded dentine, immediately and after four years of water storage. METHODS: Sixty-four sound human molars were distributed into 16 groups according to (1) Dentine surface (sound and eroded dentine); (2) dimethyl sulfoxide application (with or without); (3) Application mode (etch-and-rinse or self-etch) and (4) Storage time (immediate and four years). One mild universal adhesive was used (Scotchbond Universal). The restoration was then performed with a composite resin and the specimens were sectioned into resin-dentine bonded sticks. Resin-dentine bonded sticks were tested (immediately and after four years of water storage) for µTBS (0.5 mm/min) or used to assess NL. Data on µTBS and NL were analyzed using four-way ANOVA and Tukey's test (α = 0.05). RESULTS: Only the 3-way cross-product interaction 'substrate vs DMSO vs time' was statistically significant (p = 0.007). Eroded dentine showed a lower mean of µTBS and a higher mean of NL values than sound dentine. However, when DMSO was applied, no significant decrease of µTBS or NL values was observed after four years of water storage, regardless of adhesive strategies, or dentine evaluated, when compared to immediate results. SIGNIFICANCE: Water-based DMSO pre-treatments not only prevent degradation of MDP-containing simplified adhesives but also serve as a potential alternative to improve long-term bonding properties to eroded dentine. The versatility of using a single pre-treatment for both self-etch or etch-and-rinse bonding to eroded dentin may facilitate future clinical applications.
Asunto(s)
Recubrimiento Dental Adhesivo , Dimetilsulfóxido , Humanos , Cementos Dentales , Recubrimiento Dental Adhesivo/métodos , Recubrimientos Dentinarios/química , Grabado Ácido Dental/métodos , Cementos de Resina/química , Dentina , Agua/química , Resistencia a la Tracción , Ensayo de MaterialesRESUMEN
OBJECTIVES: To examine whether lower dimethyl sulfoxide (DMSO) concentrations would affect long-term bond stability of simplified or multistep water-based adhesives to dry-etched dentin. METHODS: H3PO4-etched mid-coronal dentin surfaces from human molars were randomly blot- or air-dried for 30 s and pretreated or not with 5 or 50 % (v/v) ethanolic DMSO solutions. Untreated samples served as control. Samples were bonded with a two-step or a three-step etch-and-rinse adhesive. Restored crown segments (n = 5/group) were stored in distilled water for 24 h and sectioned for microtensile bond strength testing. Resin-dentin beams (0.8 mm2) were tested under tension until fracture (0.5 mm/min) after 24 h and one year of storage in artificial saliva at 37 °C. Nanoleakage evaluation and hybrid layer characterization were performed by SEM. Bond strength data was examined by three-way ANOVA followed by the Tukey test (α = 0.05). RESULTS: Dry bonding produced significantly lower bond strengths than conventional wet bonding for both water-based adhesive systems (p < 0.05). DMSO-dry bonding restored bond strengths and reduced nanoleakage levels, regardless of adhesive type or DMSO concentration (p < 0.05). Bond strengths of DMSO-dry bonded samples were not significantly affected by long-term ageing regardless of adhesive type or DMSO concentration (p < 0.05). SIGNIFICANCE: Although bonding methacrylate-based resins to etched dentin is normally performed under wet conditions, hybridization of air-dried collagen can outperform conventional wet bonding by employing water-free DMSO solutions with concentrations as low as 5 %. Reduced moisture-related technique sensitivity, higher bonding performance and improved hybrid layer stability may contribute to extend the service life of resin-dentin bonding.
Asunto(s)
Recubrimiento Dental Adhesivo , Dimetilsulfóxido , Humanos , Recubrimiento Dental Adhesivo/métodos , Cementos Dentales , Dentina/química , Recubrimientos Dentinarios/química , Dimetilsulfóxido/química , Ensayo de Materiales , Cementos de Resina/química , Resistencia a la Tracción , AguaRESUMEN
The aim of this study was to determine whether erbium laser irradiation emitted by modified glass-fiber tips would improve the intraradicular bonding of fiber posts. Forty human canines were endodontically treated and prepared for fiber-post placement. Roots were divided into five groups (n=8); according to the laser-tip combinations (2,940 nm Er:YAG and 2,780 nm Er,Cr:YSGG). Non-irradiated root canals served as control. Posts were cemented with self-adhesive resin cement and subjected to push-out test. Failure modes were characterized, and intraradicular bonded interfaces were analyzed by SEM and submitted to nanoleakage evaluation. Data were analyzed by two-way ANOVA and Tukey test (α=0.05). No significant differences were observed in cervical and middle sections (p>0.05), while significantly higher bond strengths were observed in apical sections (p<0.05). Laser irradiation reduced adhesive failures, cement-dentin gap formation, and nanoleakage apically. Laser-irradiation protocols employing end- or radial-firing tips improved bonding to apical intraradicular dentin contributing to more uniform bonded interfaces.
Asunto(s)
Recubrimiento Dental Adhesivo , Láseres de Estado Sólido , Técnica de Perno Muñón , Humanos , Cementos de Resina/química , Cementos Dentales , Vidrio/química , Recubrimiento Dental Adhesivo/métodos , Dentina , Ensayo de MaterialesRESUMEN
OBJECTIVE: This study aimed to clarify the perceptibility of periapical foreign materials in imaging compared with histopathology. We hypothesized that dentoalveolar imaging is sufficient to detect periapical foreign bodies. MATERIAL AND METHODS: Radiological and histopathological records of patients diagnosed with periapical granuloma or radicular cyst from 2000 to 2013 were evaluated retrospectively. Patients with histologically verified foreign bodies were included in the study and their pathological samples and radiological images were reviewed. The outcome variable was radiologically detectable foreign material. The predictor variables were histopathological diagnosis, type of inflammation, type and number of foreign bodies, imaging modality, and site of foreign material. RESULTS: Compared to the histopathological diagnosis of foreign bodies as the gold standard, the level of radiologic detectability was mild. Histologically verified foreign material could be detected by imaging in 32/59 (53.5%) patients. Histological diagnosis, type of inflammation, type or number of foreign bodies, imaging modality or site of foreign material had no association with radiological detectability (p > 0.05). CONCLUSIONS: According to our results, histopathology is a more accurate diagnostic tool than radiology in periapical foreign bodies or foreign body reactions. Clinicians should keep in mind the limitations of imaging when setting the diagnosis and planning treatment.
RESUMEN
OBJECTIVES: To study phytic acid (IP6) effect on collagen solubilization by assessing hydroxyproline (HYP) release, evaluate its binding to demineralized (DD) and mineralized dentin (MD) and determine the effect of different media on debinding of IP6. METHODS: Demineralized dentin beams were incubated in 1%, 2% or 3% IP6 and HYP release was evaluated at 1 or 3 weeks and compared to those obtained in untreated control or phosphoric acid (PA)-treated beams. DD or MD powder was treated with 1%, 2% or 3% IP6 and the decrease in IP6 amount was quantitated by ultraviolet-visible spectroscopy. IP6-treated samples were re-suspended in distilled water, ethanol, urea or sodium chloride and the amount of IP6 displaced was determined. RESULTS: At 1 week, the control group and IP6 showed lower HYP release when compared to PA (P < 0.05). There was no difference among PA, IP6 and control at 3 weeks (P = 0.22). IP6 binding was concentration dependent. 1% IP6 had higher binding potential with MD compared to DD while 2% IP6 showed the opposite result (P<0.05). 3% IP6 had similar binding values between DD and MD (P = 0.53). The highest debinding in MD occurred with urea for 2%, 3% and 1% IP6 in descending manner. Within each concentration of IP6 in DD, the highest debinding effect was reported with ethanol. CONCLUSIONS: IP6 bound to DD and MD in a concentration-dependent manner. IP6 was debound from DD mostly by the action of ethanol, while in MD, urea caused the most displacement. Collagen solubilization of IP6-treated DD was comparable to untreated DD. CLINICAL SIGNIFICANCE: These findings add to the potential use of IP6 as an alternative to PA for dentin etching which possibly results in long-term stability of resin-dentin adhesion.
Asunto(s)
Dentina , Ácido Fítico , Ácido Fítico/farmacología , Etanol/farmacología , Colágeno/químicaRESUMEN
This study investigates the effect of ions released from S-PRG fillers on host-derived enzymatic degradation of dentin collagen matrices. Dentin beams (n=80) were demineralized and distributed to eight groups following baseline dry mass and total MMP activity assessments. Each group treated with boron, fluoride, sodium, silicone, strontium, aluminium, or S-PRG eluate solutions for 5 min. Untreated beams served as control. After pre-treatment, MMP activity was reassessed, beams were incubated in complete medium for 1 week, dry mass was reassessed. Incubation media were analyzed for MMP and cathepsin-K-mediated degradation fragments. Data were analyzed with ANOVA and Tukey's test. All pretreatment groups showed significant reduction in total MMP activity (p<0.05) that was sustainable after incubation in all groups except for boron and silicone groups (p<0.05). Cathepsin-K activity did not differ between control or treatment groups. The results indicated that ions released from S-PRG fillers have the potential to partly inhibit MMP-mediated endogenous enzymatic activity.
Asunto(s)
Boro , Colágeno , Dentina , Cementos de Ionómero Vítreo , Metaloproteinasas de la Matriz , Siliconas , Catepsina K , Colágeno/metabolismo , Dentina/enzimología , Dentina/metabolismo , Fluoruros , Cementos de Ionómero Vítreo/farmacología , Iones , Metaloproteinasas de la Matriz/metabolismo , Péptido HidrolasasRESUMEN
OBJECTIVE: To determine whether smear layer management, via conservative etching protocols, and the hydrophobic-rich content of hybrid layers would affect the fatigue strength of resin-dentin interfaces. METHODS: Bar-shaped dentin beams obtained from sound third molars were wet-polished for 30 s. Dentin was etched with 32 % ortho-phosphoric acid for 3 or 15 s, 10 % meta-phosphoric acid for 15 s or by a prime-and-rinse application using a mild universal adhesive (Scotchbond Universal, 3M ESPE). Self-etch application served as control. Coating was performed with a solvent-free bisGMA-based resin. Composite buildups were made with a nanofilled composite. Resin-dentin beams with twin-bonded interfaces were sectioned and stored in deionized water for 24 h at 37 â before 4-point flexural quasi-static monotonic testing (n = 16). Stress-life fatigue behavior was evaluated under cyclic loading (n = 35) by the staircase method at 4 Hz. The tension side of cyclic-loaded unfractured beams were evaluated under SEM, along with the micro-morphology of etched dentin surfaces. Monotonic data was analyzed by two-way ANOVA followed by the Tukey Test and cyclic-loaded data by Kruskal-Wallis on Ranks (α = 0.05). RESULTS: Etching protocols and higher hydrophobic-rich content produced significantly higher fatigue life distributions (p < 0.05). Dentin demineralization was ranked as OPA 15 s > MPA 15 s > OPA 3 s > P + R > SE. Less aggressive etching and coating reduced crack formation at hybrid layers. SIGNIFICANCE: Current oversimplification trends in resin-dentin bonding constitute a trade-off between hybridization quality and easier adhesive handling. Controlled dentin etching and increasing the hydrophobic-rich content of hybrid layers may be necessary to extend the longevity of mild universal adhesives.
Asunto(s)
Recubrimiento Dental Adhesivo , Recubrimientos Dentinarios , Grabado Ácido Dental/métodos , Recubrimiento Dental Adhesivo/métodos , Cementos Dentales , Dentina , Recubrimientos Dentinarios/química , Ensayo de Materiales , Cementos de Resina/química , Propiedades de Superficie , Resistencia a la TracciónRESUMEN
OBJECTIVES: To determine whether the composition of universal adhesives and the use of silane coupling agents could affect the fatigue strength of composite repair. METHODS: Composite samples were aged in water at 37 °C for 90 days and bonded to fresh composite to produce twin-bonded bar-shaped composite specimens (2 × 2 × 12 mm). Five universal adhesives, a multistep composite repair system and a hydrophobic solvent-free resin associated to a separate silane coupling agent application were used for bonding. Composite samples were tested under 4-pointflexure initially at quasi-static loading (n = 12) followed by cyclic loading (n = 25). The stress-life fatigue behavior was evaluated following the staircase method at 4 Hz. The unfractured side of cyclic loaded beams were evaluated under SEM to determine crack initiation sites. Fatigue data was analyzed by ANOVA and Tukey test and Wilcoxon Rank Sum Test (α = 0.05). RESULTS: Bonding protocols were unable to restore the cohesive strength of the nanofilled composite (p < 0.05). Fatigue testing was more discriminative to reveal discrepancies in composite repair than conventional quasi-static loading. While the composition of universal adhesives affected composite repair potential, the highest endurance limits occurred for the separate silane coupling agent application. Crack propagation sites were mostly located on the aged composite surface. SIGNIFICANCE: Although a trend for simplification invariably overruns current adhesive dentistry, composite repair using solely universal adhesives may result in inferior repair potential. The additonal use of silane coupling agents remains as an important procedure in composite repairs.
Asunto(s)
Recubrimiento Dental Adhesivo , Adhesivos , Resinas Compuestas/química , Recubrimiento Dental Adhesivo/métodos , Cementos Dentales/química , Ensayo de Materiales , Cementos de Resina/química , Resistencia al Corte , Silanos/química , Propiedades de SuperficieRESUMEN
Endogenous dentin proteases contribute to the degradation of collagen fibrils in the hybrid layer. Recently, inhibition of host-derived proteases by curcuminoids has shown promising results. The aim of this study was to evaluate the effect of curcuminoid treatment on the microtensile bond strength (µTBS) after 24 h or 12 months of storage. Fifty-four extracted sound human molars were flattened to mid-coronal dentin and divided into nine groups. After phosphoric acid-etching for 15 s, the dentin was experimentally treated for 60 s using 100 µM or 200 µM of curcumin, diflourobenzocurcumin, or demethoxycurcumin dissolved in 1% and 2% dimethyl sulfoxide (DMSO)/water solutions. Untreated and DMSO-treated groups served as controls. After bonding agent application, each tooth was restored with dental composite. The molars were sectioned into 0.9 × 0.9 × 6 mm beams. The µTBS testing was performed after 24 h and 12 months of storage in artificial saliva. Data were analyzed using regression analyses. Failure patterns were evaluated using scanning electron microscopy. Dentin treatment with curcuminoids did not adversely affect 24-h µTBS compared to controls. After 12 months, the µTBS of curcuminoid groups was statistically significantly higher than the controls. This study indicates the feasibility of using curcuminoids as protease inhibitors.
Asunto(s)
Recubrimiento Dental Adhesivo , Resinas Compuestas/química , Dentina/química , Recubrimientos Dentinarios/química , Diarilheptanoides , Humanos , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Cementos de Resina/química , Resistencia a la TracciónRESUMEN
OBJECTIVES: The objective of this study was to determine the effects of antimicrobial photodynamic therapy (aPDT) with indocyanine green (ICG) and toluidine blue (TB) on protease activity (matrix-bound cathepsin K and matrix metalloproteinase (MMP) and dentin bond strength. METHODS: Caries-free human third molars were assigned to five groups: 1-control group, 2-application of ICG with activation using an 810 nm diode (aPDT), 3-application of ICG, 4-application of TB with activation using a 660 nm diode (aPDT), and 5-application of TB. For the enzymatic investigation, dentin beams were incubated for either 3 days or 3 weeks. Aliquots of the incubation media were analyzed by ELISA for CTX (C-terminal cross-linked telopeptide of type I Collagen) and ICTP (cross-linked carboxy-terminal telopeptide of type I collagen). For microtensile bond strength testing (µTBS), composite resins were layered onto the tooth surface; the samples were then subjected to µTBS. Kruskall-Wallis and Mann-Whitney U tests were applied for statistical analysis of CTX and ICTP, one way-ANOVA and Tukey's test were applied for statistical analysis of µTBS. RESULTS: Pretreating the dentin matrices with aPDT decreased the endogenous protease activity. ICG with laser activation resulted in the highest µTBS. Therefore, aPDT should be considered as a treatment method because it can reduce MMP-mediated dentin degradation and increase the µTBS. SIGNIFICANCE: Inhibiting endogenous protease activity improves the stability of the dentin-adhesive bond and the durability of the bond strength.
Asunto(s)
Recubrimiento Dental Adhesivo , Fotoquimioterapia , Catepsina K , Resinas Compuestas , Dentina , Recubrimientos Dentinarios , Humanos , Ensayo de Materiales , Metaloproteinasas de la Matriz , Cementos de Resina , Resistencia a la TracciónRESUMEN
OBJECTIVE: To determine whether the effect of dentin moisture on the etch-and-rinse bonding may be minimized by dry-bonding protocols utilizing aqueous or ethanolic dimethyl sulfoxide (DMSO) pretreatments. METHODS: H3PO4-etched mid-coronal dentin surfaces from human molars were randomly blot- or air-dried for 30 s and pretreated with DMSO/H2O or DMSO/EtOH solutions. Untreated samples served as control. Moisture control was performed by either blot- or air-drying. Samples were bonded with a multistep etch-and-rinse adhesive. Restored crown segments (n = 8/group) were stored in distilled water for 24 h and sectioned for microtensile bond strength testing. Resin-dentin beams (0.8 mm2) were tested under tension until fracture (0.5 mm/min) after 24 h and two years of storage in artificial saliva at 37 °C. SEM nanoleakage evaluation was performed on aged samples. Collagen wettability was also measured by sessile drops of the hydrophilic and hydrophobic bonding resins (n = 8/group). Data were examined by factorial ANOVA followed by the Tukey test (α = 0.05). RESULTS: Dry bonding to untreated collagen produced inferior immediate and long-term bond strengths than wet bonding (p < 0.05). Regardless of initial hydration and moisture control, DMSO-dry bonding produced initially higher and stable bond strengths after aging (p < 0.05). DMSO-pretreated groups presented improved collagen wettability with lower silver uptake (p < 0.05). SIGNIFICANCE: Despite the common belief that etch-and-rinse adhesives must be applied onto moist collagen, DMSO-dry bonding protocols not only improved bonding performance and hybrid layer integrity, but also brought more versatility to collagen hybridization by reducing overdrying-related issues.
Asunto(s)
Recubrimiento Dental Adhesivo , Recubrimientos Dentinarios , Adhesivos , Anciano , Cementos Dentales , Dentina , Humanos , Ensayo de Materiales , Cementos de Resina , Resistencia a la Tracción , HumectabilidadRESUMEN
OBJECTIVE: Imperfect polymer formation as well as collagen's susceptibility to enzymatic degradation increase the vulnerability of hybrid layers over time. This study investigated the effect of new dimethyl sulfoxide (DMSO)-containing pretreatments on long-term bond strength, hybrid layer quality, monomer conversion and collagen structure. METHODS: H3PO4-etched mid-coronal dentin surfaces from extracted human molars (n = 8) were randomly treated with aqueous and ethanolic DMSO solutions or following the ethanol-wet bonding technique. Dentin bonding was performed with a three-step etch-and-rinse adhesive. Resin-dentin beams (0.8 mm2) were stored in artificial saliva at 37 °C for 24 h and 2.5 years, submitted to microtensile bond strength testing at 0.5 mm/min and semi-quantitative SEM nanoleakage analysis (n = 8). Micro-Raman spectroscopy was used to determine the degree of conversion at different depths in the hybrid layer (n = 6). Changes in the apparent modulus of elasticity of demineralized collagen beams measuring 0.5 × 1.7 × 7 mm (n = 10) and loss of dry mass (n = 10) after 30 days were calculated via three-point bending and precision weighing, respectively. RESULTS: DMSO-containing pretreatments produced higher bond strengths, which did not change significantly over time presenting lower incidence of water-filled zones. Higher uniformity in monomer conversion across the hybrid layer occurred for all pretreatments. DMSO-induced collagen stiffening was reversible in water, but with lower peptide solubilization. SIGNIFICANCE: Improved polymer formation and higher stability of the collagen-structure can be attributed to DMSO's unique ability to simultaneously modify both biological and resin components within the hybrid layer. Pretreatments composed of DMSO/ethanol may be a viable-effective alternative to extend the longevity of resin-dentin bonds.
Asunto(s)
Colágeno , Recubrimiento Dental Adhesivo , Recubrimientos Dentinarios , Cementos de Resina , Dentina , Humanos , Técnicas In Vitro , Ensayo de Materiales , Polímeros , Distribución Aleatoria , Resistencia a la TracciónRESUMEN
OBJECTIVE: To characterize whether the bonding performance and fatigue strength of resin-dentin interfaces created by a universal adhesive would be affected by different H3PO4-application times to more accurately assess long-term durability. METHODS: Mid-coronal flat dentin surfaces with standardized smear-layers were produced on sound third molars, etched with 32% H3PO4 for 0, 3 and 15 s, bonded with a mild universal adhesive (3M-ESPE) and restored with a nanofilled composite. Bonded specimens (0.9 × 0.9 mm) were stored in deionized water for 24 h and sectioned into beams for microtensile testing (n = 10). Resin-dentin beams were tested under tension until failure (0.5 mm/min) after 24 h or 6 month storage in artificial saliva at 37 ÌC. Bar-shaped resin-dentin beams (0.9 × 0.9 × 12 mm) were tested under 4-point-flexure initially at quasi-static loads (n = 22) and then under cyclic loads (n > 50). The stress-life fatigue behavior was evaluated using the twin-bonded interface approach by the staircase method at 4 Hz. Fractured interfaces and the tension side of unfractured beams were evaluated under SEM, along with the micro-morphology of the etched dentin surfaces and hybrid layers. Data were analyzed by ANOVA and Tukey test and Wilcoxon Rank Sum Test (α = 0.05). RESULTS: Quasi-static loads were limited to discriminate the bonding performance of resin-dentin interfaces. Application modes significantly affected etching patterns, fatigue strength, endurance limits and hybrid layer morphology (p < 0.001). SIGNIFICANCE: Reductions in fatigue strength of self-etched bonded interfaces raise concerns about the true ability of universal adhesives to properly bond to dentin.
Asunto(s)
Recubrimiento Dental Adhesivo , Recubrimientos Dentinarios , Adhesivos , Resinas Compuestas , Cementos Dentales , Dentina , Ensayo de Materiales , Cementos de Resina , Resistencia a la TracciónRESUMEN
We evaluated the effect of phytic acid on matrix metalloproteinase (MMP)- or cysteine cathepsin (CC)-mediated dentin degradation. Demineralized dentin beams were divided into five groups (n = 12) and treated with 1%, 2%, or 3% phytic acid or with 37% phosphoric acid. Untreated demineralized beams served as controls. After incubation for 1 or 3 wk, dry mass loss was determined and aliquots of incubation media were analysed for cross-linked telopeptide of type I collagen (ICTP) fragments for MMP-mediated and c-terminal telopeptide of type I collagen (CTX) for cathepsin-k-mediated degradation. The direct effect of phytic acid was evaluated using MMP activity assay. Data were analysed using repeated-measures anova. ICTP releases with 1% and 2% phytic acid treatment were statistically significantly lower than those following phosphoric acid treatment at 3 wk. The CTX release for phytic acid-treated beams at 3 wk was not significantly different from that of untreated control beams, but it was significantly lower than that of phosphoric acid-treated beams. Their MMP activities at 3 wk were not significantly different from those of the controls but they were significantly lower than those seen for phosphoric acid-treated beams. Compared to phosphoric acid, phytic acid treatment resulted in a reduced dentinal host-derived endogenous enzymatic activity and collagen degradation.
Asunto(s)
Dentina , Ácido Fítico , Colágeno Tipo I , Metaloproteinasas de la Matriz , Ácido Fítico/farmacologíaRESUMEN
This study evaluated the cytotoxicity of methacrylate-based resins containing dimethyl sulfoxide (DMSO). DMSO was incorporated into hydrophobic (R2) and hydrophilic (R5) resins at weight concentrations of 0, 0.01, 0.1, 1, 5, or 10 w/w %. Resin discs (n = 10/group) were prepared. Human gingival fibroblasts (HGF-1) were exposed to resin eluates for 24 h. Furthermore, dentin barrier test was performed using 3-D cultures of odontoblast-like cells (SV40 transfected pulp derived cells) with dentin slices of 400 µm thickness (n = 8). After acid etching of dentin, DMSO-modified resins were applied into the cavity part of the device and light-cured for 20 s. Cell viability (%) was assessed by MTT and analyzed spectrometrically. Data were analyzed by ANOVA and Tukey test (α = 0.05). Resin eluates showed statistically significantly lower % cell viability for all neat and DMSO-modified resins than seen for the negative control. Moreover, DMSO-R5 eluates resulted in significantly lower % cell viability than DMSO-R2 emulates. The dentin barrier test showed that DMSO-R2 did not result in significantly lower % cell viability, whereas incorporation of 1-10 w/w % DMSO into R5 resulted in significantly lower % of cell viability. Incorporating DMSO into hydrophilic self-etching resins may increase cytotoxicity. The biocompatibility is not influenced by the addition of DMSO into hydrophobic resin.
Asunto(s)
Recubrimiento Dental Adhesivo , Dimetilsulfóxido , Resinas Compuestas , Cementos Dentales , Dentina , Recubrimientos Dentinarios , Dimetilsulfóxido/toxicidad , Humanos , Interacciones Hidrofóbicas e Hidrofílicas , Ensayo de Materiales , Metacrilatos/toxicidad , Cementos de Resina/toxicidadRESUMEN
Silver diamine fluoride (SDF) was developed in Japan in the 1960s. It is a clear solution containing silver and fluoride ions. Because of its anti-bacterial and remineralizing effect, silver diamine fluoride has been used in managing dental caries for decades worldwide. This paper aims to summarize and discuss the global policies, guidelines, and relevant information on utilizing SDF for caries management. SDF can be used for treating dental caries in most countries. However, it is not permitted to be used in mainland China. Several manufacturers, mainly in Australia, Brazil, India, Japan, and the United States, produce SDF at different concentrations that are commercially available around the world. The prices differ between contents and brands. Different government organizations and dental associations have developed guidelines for clinical use of SDF. Dental professionals can refer to the specific guidelines in their own countries or territories. Training for using SDF is part of undergraduate and/or postgraduate curriculums in almost all countries. However, real utilization of SDF of dentists, especially in the private sector, remains unclear in most places because little research has been conducted. There are at least two ongoing regional-wide large-scale oral health programs, using SDF as one of the components to manage dental caries in young children (one in Hong Kong and one in Mongolia). Because SDF treatment does not require caries removal, and it is simple, non-invasive, and inexpensive, SDF is a valuable strategy for caries management in young children, elderly people, and patients with special needs. In addition, to reduce the risk of bacteria or virus transmission in dental settings, using SDF as a non-aerosol producing procedure should be emphasized under the COVID-19 outbreak.
RESUMEN
The study evaluated changes in total enzymatic activity and degradation of demineralized dentin following the application of universal or self-etch adhesives. The universal adhesives -Scotchbond Universal (SU) and All-Bond Universal (ABU) and self-etch adhesives -Adper Easy Bond (EB) and G-aenial Bond (GB) were used for 2 min pretreatment of the dentin beams. Phosphoric acid (PA) treatment as well as no treatment served as controls. Total enzymatic activity was analyzed before and after treatment, collagen degradation was assessed using mass loss, C-terminal telopeptide (CTX) and C-terminal-telopeptide of type I collagen (ICTP) release (24 h, 3-day, 3-week). Over three weeks of incubation, ICTP release of ABU treated beams was significantly higher than other groups (p<0.05), except for SU treated beams (p>0.05) and CTX release of GB treated beams was the highest among the groups with statistically significant difference (p<0.05). The results confirm that the universal adhesives tested have also potential to increase the enzymatic activity in dentin.