RESUMEN
In this study, we fabricated Si-based heterojunction solar cells (HSCs) with an asymmetric TMO-metal-TMO (TMT) structure using both MoO3 and V2O5 as the hole-selective contacts. Our HSCs offer enhanced long-term stability and effective passivation for crystal defects on the Si sur-face. We analyzed the oxygen vacancy state and surface morphology of the MoO3- and V2O5-TMO thin films using X-ray photoelectron spectroscopy and atomic force microscopy to investigate their passivation characteristics for Si surface defects. From the measured minority carrier lifetime, V2O5 revealed a highly improved lifetime (590 µs) compared to that of MoO3 (122.3 µs). In addition, we evaluated the long-term stability of each TMO thin film to improve the operation stability of the HSCs. We deposited different types of TMOs as the top- and bottom-TMO layers and assessed the effect of the thickness of each TMO layer. The fabricated asymmetric TMT/Si HSCs showed noticeable improvements in efficiency (7.57%) compared to 6.29% for the conventional symmetric structure which used the same TMO material for both the top and bottom layers. Furthermore, in terms of long-term stability, the asymmetric TMT/Si HSCs demonstrated an efficiency that was 250% higher than that of symmetric TMT/Si HSCs, as determined via power conversion efficiency degradation over 2000 h which is mainly attributed by the lower oxygen vacancy of the top-TMO, V2O5. These results suggest that the asymmetric TMT structure is a promising approach for the fabrication of low-cost and high-efficiency Si-based HSCs with enhanced long-term stability.
RESUMEN
In recent decades, dopant-free Si-based solar cells with a transition metal oxide layer have gained noticeable research interest as promising candidates for next-generation solar cells with both low manufacturing cost and high power conversion efficiency. Here, we report the effect of the substrate temperature for the deposition of vanadium oxide (V2O5-x, 0 ≤ X ≤ 5) thin films (TFs) for enhanced Si surface passivation. The effectiveness of SiOx formation at the Si/V2O5-x interface for Si surface passivation was investigated by comparing the results of minority carrier lifetime measurements, X-ray photoelectron spectroscopy, and atomic force microscopy. We successfully demonstrated that the deposition temperature of V2O5-x has a decisive effect on the surface passivation performance. The results confirmed that the aspect ratio of the V2O5-x islands that are initially deposited is a crucial factor to facilitate the transport of oxygen atoms originating from the V2O5-x being deposited to the Si surface. In addition, the stoichiometry of V2O5-x TFs can be notably altered by substrate temperature during deposition. As a result, experimentation with the fabricated Si/V2O5-x heterojunction solar cells confirmed that the power conversion efficiency is the highest at a V2O5-x deposition temperature of 75 °C.
RESUMEN
In the last decades, the conductive polymer PEDOT:PSS has been introduced in Si-based hybrid solar cells, gaining noticeable research interest and being considered a promising candidate for next generation solar cells which can achieve both of low manufacturing cost and high power conversion efficiency. This study succeeded in improving the electrical conductivity of PEDOT:PSS to 937 S/cm through a simple process of adding hydroquinone (HQ) to the pristine PEDOT:PSS solution. The results also showed that the addition of HQ to PEDOT:PSS(HQ-PEDOT:PSS) could not only dramatically improve the conductivity but also well-sustain the work function characteristics of PEDOT:PSS by promoting the formation of more continuous conductive-PEDOT channels without removing the insulating PSS. In this report, we reveal that the application of the HQ-PEDOT:PSS to the Si/PEDOT:PSS HSC could significantly improve the short-circuit current and open-circuit voltage characteristics to increase the power conversion efficiency of the HSCs compared to the conventional approaches. Moreover, we also treated the Si surface with the organic monomer, benzoquinone (BQ) to (1) passivate the excess Si surface defect states and (2) to improve the properties of the Si/PEDOT:PSS interface. We show that BQ treatment is able to dramatically increase the minority carrier lifetime induced by effective chemical and field-effect passivation in addition to enhancing the wettability of the Si surface with the PEDOT:PSS solution. As a result, the power conversion efficiency was increased by 10.6% by introducing HQ and BQ into the fabrication process of the Si/PEDOT:PSS HSC.