RESUMEN
The nonlinear optical response of graphene oxide quantum dots (GOQDs) fabricated by the carbonization and exfoliation of electrospun polyacrylonitrile (PAN) fibers is reported. Electrospun and carbonized fibers were characterized by SEM and XPS. SEM micrograph confirmed the formation of PAN fibers of 153.44 ± 6.44 nm, while by XPS the binding energies associated with sp2 and sp3 carbon hybridizations were found, after the carbonization process. On the other hand, the GOQDs obtained were characterized by photoluminescence (PL), UV-Vis, Raman spectroscopy, and High-Resolution Transmission Electron Microscopy (HRTEM). The GOQDs size of 10 nm was estimated by HRTEM. Raman spectroscopy showed the D and G bands associated with the sp2 and sp3 hybridizations of the GOQDs, by PL two energy values of 2.67 and 2.97 eV were calculated. The UV-Vis spectrum showed two absorption bands confirming the presence of GOQDs. The nonlinear characterization was carried out using the P-scan technique, previously photodepositing GOQDs onto an optical fiber, using a coherent radiation source at a wavelength of 1550 nm. The results obtained showed a saturable absorption behavior with a value of ß = - 2.474 × 10 - 4 m / W and a nonlinear susceptibility of χ ( 3 ) ≈ - 7.749 × 10 - 4 ( e s u ) . The results of this work showed that GOQDs obtained can be used for optical switching applications.
RESUMEN
The absorption of pesticide endosulfan on the surface of gold nanoparticles results from the formation of micrometric structures (1-10 µm) with irregular shape because of the aggregation of individual particles. Such aggregation of gold nanoparticles after absorption of pesticide shows a surface-enhanced Raman scattering (SERS) spectrum, whose intensity depends on the concentration of endosulfan. In addition, the discoloration of the colloidal solution and a diminishing of the intensity of the surface plasmon resonance absorption from individual particles were observed by UV-visible spectroscopy. At the same time, a second band between 638 and 700 nm confirms the formation of aggregates of gold nanoparticles as the concentration of endosulfan increases. Finally, we used the SERS intensity of the S-O stretching vibration at 1239 cm(-1) from the SO3 group as a measure of concentration of pesticide endosulfan. This method could be used to estimate the level of pollution in water by endosulfan in a simple and practical form.