RESUMEN
A reversible photo-, thermal-, and pH-responsive high-performance functional wood with fluorescence has been prepared. The properties, structure, multi-response, fluorescence, water resistance, and corrosion resistance of original wood (ORW) and functional wood (FUW) were investigated with an X-ray photoelectron spectroscopy (XPS) spectrometer, a Fourier-transform infrared (FTIR) spectrometer, a N2 adsorption-desorption analyzer, an atomic force microscope (AFM), tensile tests, a scanning electron microscope (SEM), an ultraviolet-visible (UV-Vis) spectrophotometer, a fluorescence spectrometer, the equilibrium swelling ratio (ESR), and corrosion tests. The results of XPS, FTIR, N2 adsorption-desorption, and AFM exhibited that FUW was successfully prepared. Additionally, the results of the tensile test and SEM revealed that FUW had better mechanical properties than ORW, due to the filling of epoxy resin in the pores of the wood. Moreover, the UV-Vis and fluorescence spectra demonstrated that the introduction of epoxy resin induced multi-response and fluorescence functions to FUW. Furthermore, the data of ESR and corrosion test showed that the introduction of epoxy resin greatly improved the water and corrosion resistance of wood. This study provides ideas and methods for preparing novel high-performance multi-response FUW.
RESUMEN
Maleic anhydride (MAH) grafting to different polyolefins with similar grafting degree can have different effects on crystallization, crystal structure, and mechanical and thermal properties. The grafting leads to a smaller crystal size, less ordered lamellar structure, and a shorter long period for HDPE, LLDPE, and PP. The grafting makes PP lamellar packing less ordered the most and almost no effect to LLDPE. The grafting does not have that much impact on the crystallization ability of the HDPE, LLDPE, and HDPE/PP blend, but appreciably reduces the crystalline ability of PP-g-MAH, due to a dramatical drop in its molecular weight during the grafting process. As a result, the grafting makes PP a very brittle material with a lowered average melting point than the corresponding neat PP, but the grafting has almost no effect on elongation at break for LLDPE and some effect on HDPE (decreased by one-third). However, the PP degradation due to MAH grafting can be avoided in the presence of PE component, i.e., making the grafting of PP and PE at the same time with HDPE/PP blend. The grafted HDPE/PP blend shows a significantly improved compatibility, which leads to overall appreciably better mechanical properties than the neat HDPE/PP blend.