RESUMEN
To evaluate the effect of fatigue and aging on the crystalline content and reliability of a zirconia-toughened-alumina (ZTA) composite compared to its individual counterpart materials (3Y-TZP and Al2O3). Thirty-six disc-shaped specimens per group were obtained to comply with ISO 6872:2015. Crystalline content, microstructure and reliability of experimental groups were evaluated in four stages: 1) immediate; 2) aged; 3) fatigued; 4) aged + fatigue. Aging was performed in autoclave and Step-Stress-Accelerated-Life-Testing (SSALT) was performed using three stress profiles. Weibull statistics were used to determine Weibull parameters and life-expectancy. A significant increase in monoclinic phase in 3Y-TZP was observed after aging (19.31%), fatigue (17.88%) and aging + fatigue (55.81%), while ZTA evidenced minimal variation among all conditions (<5.69%). 3Y-TZP presented higher reliability than ZTA at 300 and 500 MPa, and ZTA outperformed Al2O3 at the same stress missions. None of the ceramics yielded acceptable reliability at 800 MPa. A higher characteristic strength was observed for 3Y-TZP, followed by ZTA and Al2O3. While after aging ZTA and Al2O3 remained stable, 3Y-TZP exhibited a significant increase in the characteristic stress. Aging did not affect the reliability of ZTA and Al2O3. 3Y-TZP demonstrated an increase in monoclinic content and characteristic strength after aging.
Asunto(s)
Óxido de Aluminio , Itrio , Anciano , Óxido de Aluminio/química , Cerámica/química , Materiales Dentales , Humanos , Ensayo de Materiales , Reproducibilidad de los Resultados , Propiedades de Superficie , Itrio/química , Circonio/químicaRESUMEN
OBJECTIVES: To evaluate the effect of the ceramic processing and aging method on the microstructure, optical, and mechanical properties of a third generation ultra-translucent zirconia, yttria partially stabilized zirconia (5Y-PSZ). METHODS: In-house discs were obtained through uniaxial and isostatic pressing an ultra-translucent Y-PSZ powder and sintering at 1450 °C for 2 h. As control, a commercial disc was milled from pre-sintered blocks fabricated with the same 5Y-PSZ powder through isostatic pressing and sintered under the same protocol. Discs were allocated into three groups according to aging condition as immediate (non-aged) and aged using autoclave or hydrothermal reactor at 134ºC for 20 h at 2.2 bar. Crystalline content and microstructure were evaluated using X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. Optical properties were determined using reflectance data to calculate the contrast ratio (CR) and translucency parameter (TP). Mechanical properties were assessed by Vickers hardness, fracture toughness and biaxial flexural strength tests. RESULTS: XRD spectra revealed a prevalence of cubic (70%) and tetragonal (30%) phases, and the SEM images showed a dense fully crystalline ceramic matrix for both materials. Crystalline content and microstructure of the in-house and commercial 5Y-PSZs were not affected by aging. As-sintered 5Y-PSZs demonstrated similar CR (~0.6) and TP (~18) values, as well as Vickers hardness (~14 GPa) and fracture toughness (~3.8 Mpa.m1/2), with no significant alteration after both aging methods. In-house and commercial Y-PSZs Weibull moduli ranged from 3.0 to 5.3. 5Y-PSZ processing methods resulted in similar characteristic strength after sintering (592-618 Mpa). While commercial 5Y-PSZ showed no significant influence of aging on strength, hydrothermal reactor aging significantly decreased the in-house Y-PSZ characteristic strength (474 Mpa). Both 5Y-PSZs demonstrated high reliability up to 300-Mpa strength missions, with no detrimental effect of aging (88-100%). SIGNIFICANCE: Irrespective of the processing method, ultra-translucent 5Y-PSZ showed high aging resistance and translucency stability, as well as strength corresponding to the indication up to short-span anterior prostheses.
Asunto(s)
Materiales Dentales , Circonio , Cerámica , Ensayo de Materiales , Polvos , Reproducibilidad de los Resultados , Propiedades de Superficie , ItrioRESUMEN
OBJECTIVE: To characterize the biomechanical performance of fiber-reinforced composite 5-unit implant-supported fixed dental prostheses (FDPs) receiving individually milled crowns by insilico and fatigue analyses. METHODS: Eighteen implant-supported five-unit fiber-reinforced composite frameworks with an individually prepared abutment design were fabricated, and ninety resin-matrix ceramic crowns were milled to fit each abutment. FDPs were subjected to step-stress accelerated-life testing with load delivered at the center of the pontic and at 2nd molar and 1st premolar until failure. The reliability of the prostheses combining all loaded data and of each loaded tooth was estimated for a mission of 50,000 cycles at 300, 600 and 900 N. Weibull parameters were calculated and plotted. Fractographic and finite element analysis were performed. RESULTS: Fatigue analysis demonstrated high probability of survival at 300 N, with no significant differences when the set load was increased to 600 and 900 N. 1st and 2nd molar dataset showed high reliability at 300 N, which remained high for the higher load missions; whereas 1st premolar dataset showed a significant decrease when the reliability at 300 N was compared to higher load missions. The characteristic-strength of the combined dataset was 1252 N, with 1st molar dataset presenting higher values relative to 2nd molar and 1st premolar, both significantly different. Failure modes comprised chiefly cohesive fracture within the crown material originated from cracks at the occlusal area, matching the maximum principal strain location. SIGNIFICANCE: Five-unit implant-supported FDP with crowns individually cemented in a fiber-reinforced composite framework presented a high survival probability. Crown fracture comprised the main failure mode.
Asunto(s)
Implantes Dentales , Fracaso de la Restauración Dental , Cerámica , Coronas , Porcelana Dental , Prótesis Dental de Soporte Implantado , Análisis del Estrés Dental , Humanos , Ensayo de Materiales , Reproducibilidad de los ResultadosRESUMEN
OBJECTIVE: Evaluate the effect of aging using two different methods on the three-dimensional fit of zirconia abutments at the implant-abutment connection and estimate the probability of survival of anterior crowns supported by straight and 17-degree angled abutments. MATERIALS AND METHODS: Two different zirconia abutment designs, straight and 17-degree angled abutments (n = 63/group), were evaluated in the current study. The abutments were randomly allocated into three experimental groups according to laboratory aging condition (134°C, 2.2 bar, 20 h): (i) control, (ii) autoclave aging, and (iii) hydrothermal reactor aging. Crystalline content was determined by X-Ray diffraction (XRD) and Raman spectroscopy, and microstructure was analyzed using field-emission gun scanning electron microscope (FEG-SEM). Implant-abutment volume misfit was determined in the straight abutments by micro-computed tomography using the silicone replica technique. For fatigue testing, abutments were torqued to the implants and connected to standardized maxillary incisor zirconia crowns. The assemblies were subjected to step-stress accelerated life testing (SSALT) in water until fracture or suspension. The use level probability Weibull curves and probability of survival for a mission of 50,000 cycles at 50, 100, 150 and 200 N were calculated and plotted. Fractured samples were analyzed using a stereomicroscope and scanning electron microscope. RESULTS: The crystalline spectra depicted a zirconia system primarily composed of the tetragonal phase. Laboratory aging yielded a 20%- and 37%-increase in the monoclinic content for abutments aged in autoclave and hydrothermal reactor relative to control, respectively. A fully crystalline matrix with a regular grain size was observed in the FEG-SEM for control abutments, with a considerable presence of intergranular defects. While autoclave aging triggered no significant alteration to the microstructure, defect population was reduced after hydrothermal reactor aging. Control abutments presented a significantly higher volume misfit (2.128 ± 0.54 mm3) relative to aged abutments using autoclave (1.244 ± 0.48 mm3) or hydrothermal reactor (1.441 ± 0.41 mm3). The beta (ß) values indicated that failures were predominantly controlled by material strength rather than fatigue damage accumulation for all groups, except for straight control abutments. Irrespective of aging, the probability of survival of straight and angled zirconia abutments was up to 95% (95-100%) at 50 and 100 N. A 50N-increase in the load resulted in wider range of survival estimate, with straight autoclave abutments percentage significantly lower probability of survival (77%) than angled hydrothermal reactor abutments (99%). At 200N, angled hydrothermal reactor (97%) or autoclave (82%) aged abutments demonstrated the highest probability of survival, angled control (71%) and straight hydrothermal reactor (69%) abutments intermediate values, and straight autoclave (23%) and control (7%) abutments the lowest estimate. The failure mode predominantly involved abutment and/or abutment screw fracture for both straight and angled abutments. CONCLUSIONS: Hydrothermal aging significantly influenced volume misfit, as well as the probability of survival of zirconia abutments at higher loads for both angled and straight abutments.
Asunto(s)
Prótesis e Implantes , Circonio , Fracaso de la Restauración Dental , Análisis del Estrés Dental , Ensayo de Materiales , Microtomografía por Rayos XRESUMEN
OBJECTIVES: To characterize the physicochemical and mechanical properties of a milled fiber-reinforced composite (FRC) for implant-supported fixed dental prostheses (FDPs). METHODS: For FRC characterization, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X-ray diffraction, Fourier-transformed infrared spectrometry, simultaneous thermogravimetric analysis and differential scanning calorimetry were performed. For fatigue testing, 3-unit FRC frameworks were fabricated with conventional (9 mm2 connector area) and modified designs (12 mm2 connector area and 2.5 mm-height lingual extension). A hybrid resin composite was veneered onto the frameworks. FDPs were subjected to step-stress accelerated-life fatigue testing until fracture or suspension. Use level probability Weibull curves at 300 N were plotted and the reliability for 100,000 cycles at 300, 600 and 800 N was calculated. Fractographic analysis was performed by stereomicroscope and SEM. RESULTS: The FRC consisted of an epoxy resin (â¼25%) matrix reinforced with inorganic particles and glass fibers (â¼75%). Multi-layer continuous regular-geometry fibers were densely arranged in a parallel and bidirectional fashion in the resin matrix. Fatigue analysis demonstrated high probability of survival (99%) for FDPs at 300 N, irrespective of framework design. Conventional FDPs showed a progressive decrease in the reliability at 600 (84%) and 800 N (19%), whereas modified FDPs reliability significantly reduced only at 800 N (75%). The chief failure modes for FRC FDPs were cohesive fracture of the veneering composite on lower loads and adhesive fracture of the veneering composite at higher loads. SIGNIFICANCE: Milled epoxy resin matrix reinforced with glass fibers composite resulted in high probability of survival in the implant-supported prosthesis scenario.
Asunto(s)
Implantes Dentales , Prótesis Dental de Soporte Implantado , Resinas Compuestas , Diseño Asistido por Computadora , Materiales Dentales , Fracaso de la Restauración Dental , Análisis del Estrés Dental , Ensayo de Materiales , Reproducibilidad de los ResultadosRESUMEN
OBJECTIVE: To evaluate the fatigue survival, failure mode, and maximum principal stress (MP Stress) and strain (MP Strain) of resin-matrix ceramic systems used for implant-supported crowns. METHODS: Identical molar crowns were milled using four resin-matrix ceramics (n = 21/material): (i) Shofu Hard, (ii) Cerasmart (iii) Enamic, and (iv) Shofu HC. Crowns were cemented on the abutments, and the assembly underwent step-stress accelerated-life testing. Use level probability Weibull curves at 300 N were plotted and the reliability at 300, 500 and 800 N was calculated for a mission of 50,000 cycles. Fractographic analysis was performed using stereomicroscope and scanning electron microscope. MP Stress and MP Strain were determined by finite element analysis. RESULTS: While fatigue dictated failures for Cerasmart (ß > 1), material strength controlled Shofu Hard, Enamic, and Shofu HC failures (ß < 1). Shofu HC presented lower reliability at 300 N (79%) and 500 N (59%) than other systems (>90%), statistically different at 500 N. Enamic (57%) exhibited a significant reduction in the probability of survival at 800 N, significantly lower than Shofu Hard and Cerasmart; however, higher than Shofu HC (12%). Shofu Hard and Cerasmart (>93%) demonstrated no significant difference for any calculated mission (300-800 N). Failure mode predominantly involved resin-matrix ceramic fracture originated from occlusal cracks, corroborating with the MP Stress and Strain location, propagating through the proximal and cervical margins. SIGNIFICANCE: All resin-matrix ceramics crowns demonstrated high probability of survival in a physiological molar load, whereas Shofu Hard and Cerasmart outperformed Enamic and Shofu HC at higher loads. Material fracture comprised the main failure mode.
Asunto(s)
Implantes Dentales , Fracaso de la Restauración Dental , Cerámica , Simulación por Computador , Diseño Asistido por Computadora , Coronas , Porcelana Dental , Análisis del Estrés Dental , Ensayo de Materiales , Reproducibilidad de los ResultadosRESUMEN
OBJECTIVES: To characterize the optical and mechanical properties of a commercial and in-house translucent Y-TZP before and after aging in autoclave or hydrothermal reactor. METHODS: In-house experimental discs were obtained through uniaxial and isostatic pressing a translucent Y-TZP powder and sintering at 1,550 °C/1 h. Commercial discs were milled from pre-sintered blocks fabricated with the same powder through uniaxial and isostatic pressing and sintering. Discs were allocated into three groups according to aging condition: immediate, aged via autoclave, or reactor (134 °C, 20 h, 2.2 bar). Crystalline content and microstructure were evaluated using X-ray diffraction (XRD) and scanning electron microscopy (SEM). Residual compressive stress (CS) was determined by Raman spectroscopy. Optical properties were determined by the contrast ratio (CR) and translucency parameter (TP) using reflectance data. Mechanical properties were assessed by Vickers hardness, fracture toughness and biaxial flexural strength tests. RESULTS: XRD and SEM revealed a typical Y-TZP crystalline content, chiefly tetragonal phase, and a dense crystalline matrix for both processing protocols. Reactor aging triggered a more pronounced t-m transformation relative to autoclave. In-house and commercial Y-TZPs demonstrated similar CR and TP, with reactor aging significantly increasing their translucency. Similarly, reactor aging influenced Vickers hardness and fracture toughness. In-house processed Y-TZP clearly demonstrated the presence of CS, whereas commercial Y-TZP showed no presence of CS. Non-aged in-house Y-TZP resulted in significantly lower characteristic strength relative to commercial Y-TZP. While aging protocols significantly increased the characteristic strength of in-house Y-TZP, reactor significantly decreased commercial Y-TZP characteristic strength. Both Y-TZP processing protocols demonstrated high reliability at high-stress missions, with no detrimental effect of aging. CONCLUSIONS: Laboratory aging methodology significantly influenced optical and mechanical properties of a commercial and in-house translucent Y-TZP.
Asunto(s)
Cerámica , Itrio , Materiales Dentales , Ensayo de Materiales , Reproducibilidad de los Resultados , Propiedades de Superficie , CirconioRESUMEN
The reduced hardware design of narrow implants increases the risk of fracture not only of the implant itself but also of the prosthetic constituents. Hence, the current study is aimed at estimating the probability of survival of anterior crowns supported by different narrow implant systems. Three different narrow implant systems of internal conical connections were evaluated (Ø3.5 × 10 mm): (i) Active (Nobel Biocare), (ii) Epikut (S.I.N. Implant System), and (iii) BLX (Straumann). Abutments were torqued to the implants, and standardized maxillary incisor crowns were cemented. The assemblies were subjected to step-stress accelerated life testing (SSALT) in water through load application of 30 degrees off-axis lingually at the incisal edge of the crowns using a flat tungsten carbide indenter until fracture or suspension. The use level probability Weibull curves and reliability for completion of a mission of 100,000 cycles at 80 N and 120 N were calculated and plotted. Weibull modulus and characteristic strength were also calculated and plotted. Fractured samples were analyzed in a stereomicroscope. The beta (ß) values were 1.6 (0.9-3.1) and 1.4 (0.9-2.2) for BLX and Active implants, respectively, and 0.5 (0.3-0.8) for the Epikut implant, indicating that failures were mainly associated with fatigue damage accumulation in the formers, but more likely associated with material strength in the latter. All narrow implant systems showed high probability of survival (≥95%, CI: 85-100%) at 80 and 120 N, without significant difference between them. Weibull modulus ranged from 6 to 14. The characteristic strength of Active, Epikut, and BLX was 271 (260-282) N, 216 (205-228) N, and 275 (264-285) N, respectively. The failure mode predominantly involved abutment and/or abutment screw fracture, whereas no narrow implant was fractured. Therefore, all narrow implant systems exhibited a high probability of survival for anterior physiologic masticatory forces, and failures were restricted to abutment and abutment screw.