Evaluation of calcium hydroxide root canal filling materials by cone beam computed tomography and three-dimensional modeling.

AIM: The aim of this study was to compare the effectiveness of filling pastes in resin prototype primary molars by cone beam computed tomography (CBCT) and 3D modeling.

Evaluation of various obturation techniques with bioceramic sealers in 3D-printed C-shaped canals.

This in vitro study compared various obturation techniques with bioceramic sealers for filling C-shaped 3D-printed replicas. A mandibular molar with a C-shaped root canal with a C1 configuration was obtained. After instrumenting with M3 Pro Gold files (United Dental, Shanghai, China) up to size #30/0.04, a CBCT scan of the tooth was taken. Sixty 3D-printed replicas of the tooth were created. The samples were obturated with EndoSeal TCS sealer (E. TCS; Maruchi, Wonju, Korea) or EndoSeal MTA (E. MTA; Maruchi, Wonju, Korea) (n = 30). The samples in each group were obturated with the following techniques (n = 10): (1) single-cone technique (SC), (2) SC with ultrasonic activation (UA), and (3) cold hydraulic compaction (CHC). Following incubation, the replicas' apical, middle, and coronal thirds were inspected under a digital microscope, and the proportion of filling material and void were calculated. Also, the obturation time and sealer extrusion were recorded. Data were analyzed using ANOVA, LSD post-hoc, and the chi-square tests (α = 0.05). The results indicated that in the apical third, E. TCS-SC, E. TCS-UA, and E. MTA-UA had the lowest void percentage among groups (p < 0.05). In the middle thirds, samples obturated with E. TCS-UA showed a significantly lower void percentage among all groups (p < 0.05). However, in the coronal third, E. TCS-CHC showed the least void percentage (p < 0.05), followed by E. TCS-UA and E. MTA-CHC. The E. TCS-SC and E. TCS-UA were the least time-consuming methods (p < 0.05). Sealer extrusion significantly differed among the groups, with E. MTA-UA and E. TCS-UA showing higher incidence (p = 0.019). It was concluded that E. TCS-UA was the most convenient obturation technique. However, care must be taken when obturating the canals with high flow and ultrasonic activation near the vital anatomical landmarks.

Assessment of sealing efficacy, radiopacity, and surface topography of a bioinspired polymer for perforation repair.

Background: Root perforation repair presents a significant challenge in dentistry due to inherent limitations of existing materials. This study explored the potential of a novel polydopamine-based composite as a root repair material by evaluating its sealing efficacy, radiopacity, and surface topography. Methods: Confocal microscopy assessed sealing ability, comparing the polydopamine-based composite to the gold standard, mineral trioxide aggregate (MTA). Radiopacity was evaluated using the aluminium step wedge technique conforming to ISO standards. Surface roughness analysis utilized atomic force microscopy (AFM), while field emission scanning electron microscopy (FESEM) visualized morphology. Results: The polydopamine-based composite exhibited significantly superior sealing efficacy compared to MTA (P < 0.001). Radiopacity reached 3 mm aluminium equivalent, exceeding minimum clinical requirements. AFM analysis revealed a smooth surface topography, and FESEM confirmed successful composite synthesis. Conclusion: This study demonstrates promising properties of the polydopamine-based composite for root perforation repair, including superior sealing efficacy, clinically relevant radiopacity, and smooth surface topography. Further investigation is warranted to assess its clinical viability and potential translation to endodontic practice.

The Effect of Adding Various Antibiotics on the Push-out Bond Strength of a Resin-based Sealer: An In Vitro Study.

AIM: This study aimed to compare the bond strength of AH Plus sealer to root canal dentin when used with or without various antibiotics including amoxicillin, clindamycin, and triple antibiotic mixture (TAM). MATERIALS AND METHODS: A total of 80 single-rooted extracted human teeth were instrumented and obturated with gutta-percha and four different sealer-antibiotic combinations (n = 20). Group I: AH Plus without any antibiotics, Group II: AH Plus with amoxicillin, Group III: AH Plus with clindamycin, and Group IV: AH Plus with TAM. After seven days, the roots were sectioned perpendicular to their long axis and 1 mm thick slices were obtained from the midroots. The specimens were subjected to a push-out bond strength test and failure modes were also evaluated. Data was analyzed using Kruskal-Wallis and Dunn's post hoc tests. RESULTS: Group IV had significantly higher bond strength compared to other groups (p ≤ 0.05). No significant differences were found between other groups. While the sealer-antibiotic groups predominantly showed cohesive failure modes, the control group displayed both cohesive and mixed failure modes. CONCLUSION: Within the limitations of this study, the addition of TAM increased the push-out bond strength of AH Plus. CLINICAL SIGNIFICANCE: Amoxicillin, clindamycin, or TAM can be added to AH Plus for increased antibacterial efficacy without concern about their effects on the bond strength of the sealer. How to cite this article: Adl A, Shojaei NS, Ranjbar N. The Effect of Adding Various Antibiotics on the Push-out Bond Strength of a Resin-based Sealer: An In Vitro Study. J Contemp Dent Pract 2024;25(3):231-235.

Volumetric Analysis of Hand and Rotary Instrumentation, Root Canal Filling Techniques, and Obturation Materials in Primary Teeth Using Spiral CT.

AIM AND BACKGROUND: To compare the root canal volume in primary teeth using hand and rotary instruments and to evaluate root canal filling techniques and flow of root canal obturation materials in the postinstrumented root canal volume using spiral computed tomography (SCT). MATERIALS AND METHODS: Freshly extracted 16 primary molars were randomly divided into two groups and subjected to SCT analysis before and after instrumentation. For the manual technique (group I) with eight teeth were prepared using K files, and rotary (group II) eight teeth preparation was performed with ProTaper files. The filled volume in each canal was measured using SCT, and the percentage of obturated volume was calculated. The data were statistically analyzed using the Mann-Whitney U test. RESULTS: There was a statistically significant difference in both groups' volume of root canals enlarged. Even though both K files and the ProTaper system brought about enlarged canals after instrumentation, there was a statistically significant increase in volume after using K files in two canals. In three canals, there was a statistically significant increase in volume after using ProTaper. Irrespective of the obturation technique and materials used, there is no statistically significant difference in the volume after obturation. CONCLUSION: From the results of this study, the ProTaper file system shows suitable volumetric enlargement up to an optimum level, which is needed in primary root canal walls, and is better in canal shaping, as evidenced by good postobturation volume. CLINICAL SIGNIFICANCE: The traditional method of cleaning and shaping the root canals in permanent teeth using manual stainless-steel files can lead to undesirable curvatures in root canal morphology, making correctly filling the root canals difficult. It is also time-consuming and sometimes leads to iatrogenic errors. Rotary nickel-titanium (Ni-Ti) instrumentation techniques have been developed to overcome these problems. How to cite this article: Yadav DBUC, Varma RB, Kumar JS, et al. Volumetric Analysis of Hand and Rotary Instrumentation, Root Canal Filling Techniques, and Obturation Materials in Primary Teeth Using Spiral CT. J Contemp Dent Pract 2024;25(3):250-259.

Comparative evaluation of resin-based sealers and bioceramic sealers for postoperative pain after endodontic treatment: A systematic review.

The systematic review aimed to compare and evaluate the effect of resin-based sealers and bioceramic sealers on postoperative pain after endodontic treatment. Two reviewers independently conducted electronic search in PubMed, the Web of Science, ScienceDirect, the Wiley Online Library, SpringerLink, Google Scholar, and the Cochrane Library, employing a complete dual-review process to ensure the inclusion of all relevant studies in the review. The search was carried out until November 2021. After selecting eligible studies, the risk of bias assessment was carried out using the revised Cochrane risk-ofbias tool for randomized trials (RoB 2). A total of 1,931 studies were identified from the electronic search, and finally 10 studies were included after full-text assessment. In all our included studies, the visual analog scale (VAS) was used for recording pain scores. Most of the studies recorded pain intensity starting from 6 h to 7 days. The results showed that there was no significant difference between resin-based sealers and bioceramic sealers in terms of incidence or intensity of postoperative pain at any point in time.

Epoxy resin-based root canal sealers: An integrative literature review.

The correct obturation of the root canal system achieved by means of a core and a cement is essential for the success of endodontic treatment. There are several root canal cements (RCCs) on the market; however, because of their excellent characteristics, epoxy resin-based sealers (ERBSs) have been widely used. The main aim of this review was to analyze and integrate the available information on different ERBSs. An electronic search was performed in the PubMed and Scopus databases, using "epoxy resin" AND "root canal treatment", and "epoxy resin" AND "endodontics" as search terms. In general, ERBSs have good flow properties, film thickness, solubility, dimensional stability, sealing capacity, and radiopacity. They are also able to adhere to dentin while exhibiting low toxicity and some antibacterial effects. However, their main disadvantage is the lack of bioactivity and biomineralization capability. A large number of ERBSs are available on the market, and AH Plus keeps being the gold standard RCC. Yet, information on many of them is limited or non-existent, which could be due to the fact that some of them are relatively new. The latter emphasizes the need for relevant research on the physicochemical and biological properties of some ERBSs, with the aim of supporting their clinical use with sufficient evidence via prospective and long-term studies.

Micro-computed tomographic evaluation on the quality of single-cone obturation using a modified passive-deflation sealer injection needle: an in vitro study.

OBJECTIVES: This study aimed to design a modified passive-deflation sealer injection needle and investigate its ability to improve obturation quality of single-cone technique through assessing the distribution of voids in root canals using micro-computed tomography (micro-CT). MATERIALS AND METHODS: Forty-eight mandibular incisors were divided into eight groups (n = 6), according to the taper of root canal preparation (0.06 or 0.04), the needle used for sealer injection (modified or commercial iRoot SP injection needle), and the obturation method (iRoot SP sealer-only or single-cone obturation). After obturation, each specimen was scanned by micro-CT. The volumetric percentage and distribution of all voids were first analyzed and compared among groups, then the open and closed voids were separately analyzed and compared among single-cone obturation groups. RESULTS: Compared to commercial needle groups, modified needle groups showed much less voids, especially in the apical root canal part (P < 0.05). Besides, the modified needle groups produced much less open voids than commercial needle groups despite the root canal taper (P < 0.05). CONCLUSIONS: The modified passive deflation sealer injection needle could effectively improve the quality of single-cone obturation through reducing intra-canal voids, especially open voids throughout the root canal, thus might possibly be developed as an effective intra-canal sealer delivering instrument.

Assessment of Drying Protocol on the Bond Strength and Tag Penetration of Two Different Sealers to the Root Dentin: An In Vitro Study.

Accomplishment of an ideal root canal treatment is attributed to various essential factors such as proper instrumentation, chemomechanical preparation, obturation and post endodontic restoration. The main aim of this study is to test the null hypothesis that is the moisture condition of root dentin would not affect the bond strength and sealer penetration. This is an in vitro study conducted in Department of Conservative Dentistry and Endodontics, M A Rangoonwala Dental College, Pune, India over a period of two years (from 2021 to 2023). One hundred and twenty single-rooted Premolars with fully formed apices and similar root morphology were obtained and stored in 0.1% thymol solution. The specimens were randomly assigned to 3 broad experimental groups (n=40) according to the drying protocol such as Group A- Paper points (P), Group B- diode laser (L) and Group C- isopropyl alcohol (A). For each drying protocol, the specimens were further assigned to 2 subgroups (n=20) with respect to the sealers used: AH Plus (AH) and Apexit Plus sealers (APx). The effect of drying protocol using paper points, isopropyl alcohol and diode-lasers on the bond strength and tag penetration of two different sealers to the root dentin was evaluated. Maximum overall push-out Bond strength was seen in group AH+L and least in group APx+ L. Inter-site push-out bond Strength was highest in the coronal third followed by the middle and least in the apical third of all the groups. Maximum over all depth of penetration was seen in group AH+L and minimum in group APx+L. AH plus sealer showed better bond strength, sealer penetration and adaptation to the dentinal walls compared to Apexit plus sealer, irrespective of the drying protocol followed. All the drying protocols used did not show statistically significant results in the apical thirds of root canals of all the groups.

Effect of pH on the solubility and volumetric change of ready-to-use Bio-C Repair bioceramic material.

Acidic pH can modify the properties of repair cements. In this study, volumetric change and solubility of the ready-to-use bioceramic repair cement Bio-C Repair (BCR, Angelus, Londrina, PR, Brazil) were evaluated after immersion in phosphate-buffered saline (PBS) (pH 7.0) or butyric acid (pH 4.5). Solubility was determined by the difference in initial and final mass using polyethylene tubes measuring 4 mm high and 6.70 mm in internal diameter that were filled with BCR and immersed in 7.5 mL of PBS or butyric acid for 7 days. The volumetric change was established by using bovine dentin tubes measuring 4 mm long with an internal diameter of 1.5 mm. The dentin tubes were filled with BCR at 37°C for 24 hours. Scanning was performed with micro-computed tomography (micro-CT; SkyScan 1176, Bruker, Kontich, Belgium) with a voxel size of 8.74 µm. Then, the specimens were immersed in 1.5 mL of PBS or butyric acid at and 37 °C for 7 days. After this period, a new micro-CT scan was performed. Bio-C Repair showed greater mass loss after immersion in butyric acid when compared with immersion in PBS (p<0.05). Bio-C Repair showed volumetric loss after immersion in butyric acid and increase in volume after immersion in PBS (p<0.05). The acidic pH influenced the solubility and dimensional stability of the Bio-C Repair bioceramic cement, promoting a higher percentage of solubility and decrease in volumetric values.

Assessment of dental students' knowledge and performance of master gutta-percha cone selection and fitting during root canal treatment: a pilot study.

BACKGROUND: Misconceptions should be detected early in dental students' training to improve their clinical performance. Accordingly, this study aimed to assess undergraduate dental students' knowledge and performance of master gutta-percha (GP) cone selection and fitting during clinical endodontic courses at the College of Dentistry, King Saud University. METHODS: Ninety-nine undergraduate dental students completed an online survey about their knowledge of master GP cone selection. Forty-five of these students were observed by faculty members in clinical endodontic courses while they fitted master GP cones during root canal treatments. The observers recorded the details of each student's cone-fitting techniques. The data were analysed using t-tests, one-way analysis of variance, and chi-square tests (p < 0.05). Inter- and intra-observer reliability were tested using Fliess' Kappa. RESULTS SURVEY: All participants had good knowledge of over-extended cone management, while 80.8% knew how to properly manage a short cone. The proper flaring assessment method was selected by 86.9% of the female and 34.2% of the male students, and this difference was statistically significant (p = 0.0001). OBSERVATION: The students labelled the working length on the master GP cone with an indentation in 64.4% of the cases and by bending the cone 35.6% of the time. Of all students, 84.4% encountered an apical stop, and this rate correlated significantly with the length of the cone on the master apical cone radiograph (p = 0.001). Improper shaping of the canal was the most common cause of ill-fitting cones (83.3%), while 16.7% of the students chose the wrong cone size. The final obturation length was adequate in 80% of the cases; 57.8% of the students were helped by instructors. CONCLUSIONS: Most students had the basic knowledge required to solve problems related to the selection of master GP cones. However, in the clinical setting, more than half of the students required the assistance of an instructor to adjust their cone's fit. The presence of an apical stop had the most significant effect on the length of the fitted master GP cone on radiography. The most common cause of ill-fitting master cones was improper shaping of the canal.

Comparative bioactivity and immunomodulatory potential of the new Bioroot Flow and AH Plus Bioceramic sealer: An in vitro study on hPDLSCs.

OBJECTIVES: To evaluate the cytocompatibility, bioactivity, and anti-inflammatory potential of the new pre-mixed calcium silicate cement-based sealers Bioroot Flow (BrF) and AH Plus Bioceramic Sealer (AHPbcs) on human periodontal ligament stem cells (hPDLSCs) compared to the epoxy resin-based sealer AH Plus (AHP). MATERIALS AND METHODS: Standardized discs and 1:1, 1:2, and 1:4 eluates of BrF, AHPbcs and AHP after setting were prepared. The following assays were performed: cell attachment and morphology via SEM, cell viability via a MTT assay, cell migration/proliferation via a wound-healing assay, cytoskeleton organization via immunofluorescence staining; cytokine release via ELISA; osteo/cemento/odontogenic marker expression via RT-qPCR, and cell mineralized nodule formation via Alizarin Red S staining. HPDLSCs were isolated from extracted third molars from healthy patients. Comparisons were made with hPDLSCs cultured in unconditioned (negative control) or osteogenic (positive control) culture media. Statistical significance was established at p < 0.05. RESULTS: Both BrF and AHPbcs showed significantly positive results in the cytocompatibility assays (cell metabolic activity, migration, attachment, morphology, and cytoskeleton organization) compared with a negative control group, while AHP showed significant negative results. BrF exhibited an upregulation of at least one osteo/cementogenic marker compared to the negative and positive control groups. BrF showed a significantly higher calcified nodule formation than AHPbcs, the negative and positive control groups, while AHPbcs was higher than the negative control group. Both were also significantly higher than AHP group. CONCLUSION: BrF and AHPbcs exhibit adequate and comparable cytocompatibility on hPDLSCs. BrF also promoted the osteo/cementogenic differentiation of hPDLSCs. Both calcium silicate-based sealers favored the downregulation of the inflammatory cytokine IL-6 and the calcified nodule formation from hPDLSCs. BrF exerted a significantly higher influence on cell mineralization than AHPbcs. CLINICAL RELEVANCE: This is the first study to elucidate the biological properties and immunomodulatory potential of Bioroot Flow and AH Plus Bioceramic Sealer. The results act as supporting evidence for their use in root canal treatment.

Characterisation and evaluation of physical properties of AH-Plus sealer with and without the incorporation of petasin, pachymic acid, curcumin and shilajit-an invitro study.

BACKGROUND: AH Plus, an epoxy resin-based sealer, is widely used in endodontic practice, owing to its good physical properties that confers longstanding dimensional stability and good adhesion to dentin. Nevertheless, its propensity to trigger inflammation, especially in its freshly mixed state, has been extensively documented. Phytochemicals such as Petasin, Pachymic acid, Curcumin, and Shilajit are known for their anti-inflammatory and analgesic effects. This study aimed to analyze and determine the effect of these natural products on the physical properties of AH Plus sealer when incorporated with the sealer. METHODS: AH Plus (AHR) sealer was mixed with 10% petasin, 0.75% pachymic, 0.5% and 6%shilajit to obtain AHP, AHA, AHC and AHS in the ratio of 10:1 and 5:1 respectively. Five samples of each material were assessed for setting time, solubility, flow, and dimensional stability in accordance with the ISO 6876:2012 standardization. Sealers were characterized through scanning electron microscopy (SEM), X-ray energy dispersive spectroscopy, X-ray diffraction (XRD), and Fourier transform infrared (FTIR) spectroscopy. Statistical evaluation involved the Kolmogorov-Smirnov and Shapiro-Wilks tests for normality and the one-way ANOVA test for analysis. RESULTS: In this investigation, the characterisation analysis revealed a relatively similar microstructure in all the experimental root canal sealers. All experimental groups, excluding the control group, exhibited an increase in flow ranging from 11.9 to 31.4% at a 10:1 ratio. Similarly, for the 5:1 ratio, the increase ranged from 12.02 to 31.83%. In terms of dimensional stability, all groups at the 10:1 ratio showed a decrease compared to the control group. The addition of natural agents to AHR in 10:1 ratio led to a reduction in setting time by 8.9-31.6%, and at a 5:1 ratio, the reduction ranged from 8.1 to 31.5%. However, regarding solubility, the addition of natural agents did not induce any significant alterations. CONCLUSION: Based on the results of this study, it can be concluded that all tested root canal sealers exhibited properties that met the acceptable criteria outlined in the ISO 6876:2012 standardization.

Comparative Evaluation of Push-out Bond Strength of Conventional Mineral Trioxide Aggregate, Biodentine, and Two Novel Antibacterial-enhanced Mineral Trioxide Aggregates.

AIM: To evaluate the push-out bond strength of two newly modified mineral trioxide aggregates (MTAs) with conventional MTA and biodentine. MATERIALS AND METHODS: Material preparation: Two commercially available bioactive bioceramics: Group I: Mineral trioxide aggregate; Group II: Biodentine; and two newly formulated modified MTAs: Group III: Doxycycline incorporated MTA formulation; Group IV: Metronidazole incorporated MTA formulation was used in the present study. All the test materials were then carried using a plastic instrument to the desired experimental design. Teeth sample preparation: A total of 120 teeth samples were collected and divided into four groups of test materials with 30 teeth samples per group. Single-rooted permanent teeth, that is, incisors were collected and stored in saline until the study was performed. Sectioning of the teeth into 2.0 ± 0.05-mm thick slices was performed perpendicular to the long axis of the tooth. The canal space was instrumented using Gates Glidden burs to achieve a diameter of 1.5 mm. All four prepared materials were mixed and placed in the lumen of the slices and placed in an incubator at 37°C for 72 hours. Push-out test and bond failure pattern evaluation: The push-out test was performed using a universal testing machine. The slices were examined under a scanning electron microscope (SEM) at 40× magnification to determine the nature of bond failure. All the collected data were recorded and statistically analyzed. RESULTS: The mean push-out bond strength was found to be the highest for group II (37.38 ± 1.94 MPa) followed by group III (28.04 ± 2.22 MPa) and group IV (27.83 ± 1.34 MPa). The lowest mean push-out bond strength was noticed with group I (22.89 ± 2.49 MPa). This difference was found to be statistically significant (p = 0.000). Group I samples had the predominantly adhesive type of failure (86.4%), while group II samples showed the cohesive type of failure (94.2%). Both the modified MTAs (groups III and IV) primarily showed mixed types of failures. CONCLUSION: Both the antibacterial-enhanced MTAs had better pushout bond strength compared to conventional MTA but did not outperform biodentine. Hence, it could serve as a substitute for conventional MTA due to its augmented physical properties. CLINICAL SIGNIFICANCE: Carious pulp exposure and nonvital open apices pose a critical challenge to pediatric dental practitioners. In such circumstances, maintaining the vitality of pulp and faster healing would help in a better prognosis. Novel MTAs without any cytotoxic components, and enhanced antibacterial contents with augmented physical properties can help in treating such clinical conditions. How to cite this article: Merlin ARS, Ravindran V, Jeevanandan G, et al. Comparative Evaluation of Push-out Bond Strength of Conventional Mineral Trioxide Aggregate, Biodentine, and Two Novel Antibacterial-enhanced Mineral Trioxide Aggregates. J Contemp Dent Pract 2024;25(2):168-173.

Comparative Evaluation of Shear Bond Strength of Resin-modified Glass Ionomer Cement with ProRoot MTA and MTA Angelus.

AIM: The aim of the present study was to evaluate the shear bond strength of resin-modified glass ionomer cement with two different types of mineral trioxide aggregate at different time intervals. MATERIALS AND METHODS: A total of 80 cylindrical blocks were prepared using a self-cure acrylic resin with a central cavity of 4 mm internal diameter and 2 mm height. The prepared samples were randomly divided into two groups (n = 40 each) according to the type of MTA cements used (ProRoot MTA and MTA Angelus). Two groups were further sub-divided into four sub-groups of 10 samples each according to the different time intervals. ProRoot MTA and MTA Angelus were placed in the prepared cavity and a wet cotton pellet was placed over the filled cavity. A hollow plastic tube was placed over the MTA surface and resin-modified glass ionomer cement (RMGIC) was placed into the hollow plastic tube and light-cured (Spectrum 800, Dentsply Caulk Milford, DE, USA) according to the time intervals decided. After light curing the plastic tubes were removed carefully and the specimens were stored at 37°C and 100% humidity for 24 hours to encourage setting of MTA. The specimens were mounted in a universal testing machine (ADMET) and a crosshead speed of 0.5 mm/min was applied to each specimen by using a knife-edge blade until the bond between the MTA and RMGIC failed. The data were statistically analyzed using ANOVA, post hoc Tukey's t-test and Fisher's t-test and p-value ≤ 0.5 was considered significant. RESULTS: For both ProRoot MTA and MTA Angelus there was no statistically significant difference between 45 minutes and 24 hours (p-value ≥ 0.8). For ProRoot MTA, shear bond strength value at 10 minutes were significantly lower than 45 minutes and 24 hours group. However, for MTA Angelus, shear bond strength value at 10 minute was not significantly different from 45 minutes group (p-value ≥ 0.3). For both ProRoot MTA and MTA Angelus shear bond strength value at 0 minute were the least and were significantly lower than 10 minutes, 45 minutes, and 24 hours, respectively (p-value ≥ 0.000). CONCLUSION: Resin-modified glass ionomer cement can be layered over MTA Angelus after it is allowed to set for 10 minutes. However, ProRoot MTA should be allowed to set for at least 45 minutes before the placement of RMGIC to achieve better shear bond strength. CLINICAL SIGNIFICANCE: Due to the variety of types of mineral trioxide aggregate cements available in dentistry, it is justifiable to emphasize on different time intervals as it may affect the shear bond strength of restorative cements. Such information is pivotal for the clinicians while using mineral aggregate-based cements that receive forces from the condensation of restorative materials or occlusion, as the compressive strength may be affected due to different time intervals. How to cite this article: Tyagi N, Chaman C, Anand S, et al. Comparative Evaluation of Shear Bond Strength of Resin-modified Glass Ionomer Cement with ProRoot MTA and MTA Angelus. J Contemp Dent Pract 2024;25(1):35-40.

Comparative Evaluation of Push-out Bond Strength of Three Different Root Canal Sealers: An In Vitro Study.

AIM: The aim of this present study was to compare the dislodgement resistance of calcium silicate-based sealer, zinc oxide sealer, and a new sealer combining both zinc oxide and calcium silicate-based sealer in vitro. MATERIALS AND METHODS: 60 single-rooted human teeth were instrumented with F3 Protaper Gold. All endodontic canals were filled using gutta percha cones using the cold lateral condensation technique in combination using one of the mentioned sealers (n = 20 per group). The teeth were divided into three groups: group A consisted of Sealite® Ultra, group B consisted of K-Sealer®, and group C consisted of BioRoot® RC. After 2 months of incubation (37°C, 100% humidity) and after cutting out 2 mm from the most apical portion of the root apex, six slices of 1 mm thickness were generated. Mechanical dislodgement resistance was examined using a universal pressure-testing machine and the push-out bond strength (POBS) was calculated. Specimens were examined under 20× magnification to define the bond failure mode. Statistical analysis was executed using ANOVA, post hoc Turkey test for pairwise comparisons and Kruskal-Wallis tests. RESULTS: The POBS of BioRoot® was significantly higher than the POBS of the two other sealers with a mean of 10.54 MPa ± 2.10 and 5.73 MPa ± 2.34, respectively (p < 0.001). Sealite® and K-Sealer® showed similar results in the median and coronal part. K-Sealer® revealed highest POBS compared with Sealite® in the apical part (p < 0.05). CONCLUSION: The POBS of the zinc oxide and calcium silicate-based sealer was significantly lower compared with calcium silicate. Sealite® and K-Sealer® exhibited almost same results. BioRoot showed the highest POBS of all sealers. CLINICAL SIGNIFICANCE: The current study was needed to evaluate the bond strength of three different cements to dentinal walls, by evaluating their respective POBS in vitro. The findings of this study may provide guidance for the clinician in the selection of an adequate endodontic sealer that guarantees an enhanced adhesive seal between the Gutta-percha and the dentinal canal walls. How to cite this article: Makhlouf MP, El Helou JD, Zogheib CE, et al. Comparative Evaluation of Push-out Bond Strength of Three Different Root Canal Sealers: An In Vitro Study. J Contemp Dent Pract 2024;25(1):15-19.

Failed Regenerative Endodontic Case Treated by Modified Aspiration-irrigation Technique and Apexification.

AIM: This report addresses the management of a large persistent discharging lesion in an 11-year-old boy. The report describes the use of aspiration-irrigation technique for the management of immature necrotic tooth with persistent discharge after a failed regenerative procedure. BACKGROUND: Regenerative endodontics aim to provide an increase in root canal width, length, and in apical closure. Alternative procedures, such as apexification, should be attempted when regeneration fails. If the canal cannot be dried to persistent discharge, the aspiration-irrigation technique can be used. The technique relies on using aspiration along with irrigation to remove pus from the periapical area. CASE DESCRIPTION: This is a case for an 11-year-old patient who had trauma to tooth #11, which resulted in the complicated crown fracture. He had an emergency management that included pulpectomy and intracanal medication at another clinic. Two years later, the patient was presented to our clinic. Upon examination, the diagnosis was previously initiated therapy with asymptomatic apical periodontitis in immature tooth #11. Regeneration was attempted first but failed. The mineral trioxide aggregate (MTA) plug was removed, and the canal had persistent pus discharge. The canal was filled with intracanal medication, and then 2 weeks later, the canal was filled with triple antibiotic paste (TAP). Next visit, and due to continuous discharge, tooth #11 was treated conservatively with an intracanal aspiration-irrigation technique. An IrriFlex needle attached to a high-volume suction was used to aspirate the cystic fluid. Mineral trioxide aggregate plug apexification was performed in a later visit and the tooth was restored. CONCLUSION: During the 3-month and 16-month follow-up, there was resolution of the symptoms, a decrease in the periapical lesion size, and soft tissues appeared within normal limits. CLINICAL SIGNIFICANCE: Regenerative procedures are a good option for immature necrotic teeth. These procedures may fail due to persistent pus discharge from the root canals. The aspiration-irrigation technique is a good treatment option in cases of consciously discharging canals. How to cite this article: Alsofi L, Almarzouki S. Failed Regenerative Endodontic Case Treated by Modified Aspiration-irrigation Technique and Apexification. J Contemp Dent Pract 2024;25(1):92-97.

Evaluation of stress distributions of calcium silicate-based root canal sealer in bulk or with main core material: A finite element analysis study.

This research aimed to assess the stress distribution in lower premolars that were obturated with BioRoot RCS or AH Plus, with or without gutta percha (GP), and subjected to vertical and oblique forces. One 3D geometric model of a mandibular second premolar was created using SolidWorks software. Eight different scenarios representing different root canal filling techniques, single cone technique with GP and bulk technique with sealer only with occlusal load directions were simulated as follows: Model 1 (BioRoot RCS sealer and GP under vertical load [VL]), Model 2 (BioRoot RCS sealer and GP under oblique load [OL]), Model 3 (AH Plus sealer with GP under VL), Model 4 (AH Plus sealer with GP under OL), Model 5 (BioRoot RCS sealer in bulk under VL), Model 6 (BioRoot RCS in bulk under OL), Model 7 (AH Plus sealer in bulk under VL), and Model 8 (AH Plus sealer in bulk under OL). A static load of 200 N was applied at three occlusal contact points, with a 45° angle from lingual to buccal. The von Mises stresses in root dentin were higher in cases where AH Plus was used compared to BioRoot RCS. Furthermore, shifting the load to an oblique direction resulted in increased stress levels. Replacing GP with sealer material had no effect on the dentin maximum von Mises stress in BioRoot RCS cases. Presence of a core material resulted in lower stress in dentin for AH Plus cases, however, it did not affect the stress levels in dentin for cases filled with BioRoot RCS. Stress distribution in the dentin under oblique direction was higher regardless of sealer or technique used.

The outcome of combined use of iRoot BP Plus and iRoot SP for root-end filling in endodontic microsurgery: a randomized controlled trial.

OBJECTIVES: Root-end filling is important for the clinical outcome of endodontic microsurgery. Our previous study showed that combined application of iRoot BP Plus Root Repair Material (BP-RRM) and iRoot SP Injectable Root Canal Sealer (SP-RCS) in root-end filling exhibited better apical sealing as compared to the application of BP-RRM alone. The aim of this randomized controlled clinical trial was to evaluate the effect of the combined use of BP-RRM and SP-RCS on the prognosis of teeth with refractory periapical diseases after endodontic microsurgery. MATERIALS AND METHODS: 240 teeth with refractory periapical diseases scheduled for endodontic microsurgery were randomly divided into BP-RRM/SP-RCS group (n = 120) and BP-RRM group (n = 120). The patients were followed up at 3 months, 6 months, and 12 months after endodontic microsurgery. Pre- and post-operative clinical and radiographic examinations were performed to evaluate the treatment outcome. The 1-year success rate of endodontic microsurgery in BP-RRM/SP-RCS and BP-RRM groups was compared by Chi-square test. Factors that might impact the prognosis were further analyzed using Chi-square test or Fisher's exact test. RESULTS: A total of 221 teeth completed the 12-month follow-up. The 1-year success rates of the BP-RRM/SP-RCS and BP-RRM groups were 94.5% (104/110) and 92.8% (103/111), respectively. The combined use of BP-RRM and SP-RCS achieved a clinical outcome comparable to BP-RRM alone (P = 0.784). Tooth type (P = 0.002), through-and-through/apico-marginal lesion (P = 0.049), periodontal status (P < 0.0001), and Kim's lesion classification (P < 0.0001) were critical factors associated with the 1-year success of endodontic microsurgery. CONCLUSIONS: The combined use of BP-RRM and SP-RCS is a practicable method for root-end filling in endodontic microsurgery with a satisfactory 1-year clinical outcome. CLINICAL RELEVANCE: The combined application of BP-RRM and SP-RCS in EMS is an effective root-end filling method with a satisfactory 1-year clinical outcome. TRIAL REGISTRATION: This study was registered in the Chinese Clinical Trial Registry (ChiCTR2100052174).

Effect of gutta-percha solvents on the push-out bond strength to root dentin of a syringe-mixed resin sealer and premixed bioceramic sealer.

PURPOSE: To assess the push out bond strength (POBS) of a syringe-mixed resin sealer and a premixed bioceramic sealer to root dentin exposed to different gutta-percha (GP) solvents and to determine the mode of failure. METHODS: A total of 200 horizontal root slices (1 mm thickness) were prepared up to size 40, 0.04 taper and randomly divided into four main groups based on solvent (Endosolv, orange oil, chloroform) and control (saline), then subdivided into two subgroups based on sealer type (AH Plus Jet and iRoot SP). Samples were exposed to respective solvents for 5 minutes and after the final rinsing, canal spaces were filled with either AH Plus Jet or iRoot SP. POBS test was performed 2 weeks after incubation and mode of failure following POBS test was evaluated. Data were analyzed using two-way ANOVA and Dunnett post hoc analysis (P< 0.05). Failure mode patterns were categorized as adhesive, cohesive and mixed failures. RESULTS: There was no significant difference (P> 0.05) in POBS between all solvent groups against the control in both AH Plus Jet and iRoot SP groups. Regardless of the use of solvents, AH Plus Jet group had significantly higher bond strength (P< 0.001) compared to iRoot SP group. The predominant mode of failure was mixed failure in all groups irrespective of type of sealer and exposure to solvents. CLINICAL SIGNIFICANCE: This study showed that exposure to gutta-percha solvents (chloroform, orange oil and Endosolv) for 5 minutes did not affect the bond strengths of both iRoot SP (bioceramic sealer) and AH Plus (resin sealer) to root dentin.