Evaluating flexure properties, hardness, roughness and microleakage of high-strength injectable dental composite: an in vitro study.

BACKGROUND: Recently, a new generation of high-strength flowable dental composites has been introduced by manufacturers. The manufacturers claim that these materials have enhanced mechanical and physical properties and are suitable for use in a wide range of direct anterior and posterior restorations, even in high-stress bearing areas. AIM: The objective of this study was to assess certain physical and mechanical properties of these recently introduced high-strength flowable composites in comparison to conventional multipurpose dental composites. METHODS: Four types of high-strength flowable composites (Genial Universal FLO, Gaenial Universal Injectable, Beautifil Injectable, and Beautifil Flow Plus) were tested in experimental groups, while a nanohybrid conventional composite (Filtek Z350 XT) was used as the control. For flexure properties, ten rectangular samples (2 × 2 × 25 mm) were prepared from each composite material and subjected to 5000 cycles of thermocycling. Samples were then subjected to flexural strength testing using the universal testing machine. Another twenty disc-shaped specimens of dimensions (5 mm diameter × 2 mm thickness) were fabricated from each composite material for surface roughness (Ra) (n = 10) and hardness (VHN) test (n = 10). All samples underwent 5000 cycles of thermocycling before testing. Additionally, microleakage testing was conducted on 60 standardized class V cavities prepared on molar teeth and divided randomly into five groups (n = 12). Cavities were then filled with composite according to the manufacturer's instructions and subjected to thermocycling for 1000 cycles before testing using methylene blue solution and a stereomicroscope. RESULTS: All tested materials were comparable to the control group in terms of flexural strength and surface roughness (p > 0.05), with Gaenial Universal FLO exhibiting significantly higher flexural strength compared to the other flowable composite materials tested. However, all tested materials demonstrated significantly lower elastic modulus and surface hardness than the control group (p < 0.05). The control group exhibited higher microleakage scores, while the lowest scores were observed in the Gaenial Universal FLO material (p < 0.05) CONCLUSION: The physical and mechanical behaviors of the different high-strength flowable composites investigated in this study varied. Some of these materials may serve as suitable alternatives to conventional composites in specific applications, emphasizing the importance of dentists being familiar with material properties before making material selections.

Insertion torque, flexural strength and surface alterations of stainless steel and titanium alloy orthodontic mini-implants: an in vitro study.

OBJECTIVE: This study aimed to compare the insertion torque (IT), flexural strength (FS) and surface alterations between stainless steel (SS-MIs) and titanium alloy (Ti-MIs) orthodontic mini-implants. METHODS: Twenty-four MIs (2 x 10 mm; SS-MIs, n = 12; Ti-MIs, n = 12) were inserted on artificial bone blocks of 20 lb/ft3 (20 PCF) and 40 lb/ft3 (40 PCF) density. The maximum IT was recorded using a digital torque meter. FS was evaluated at 2, 3 and 4 mm-deflection. Surface topography and chemical composition of MIs were assessed by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). General linear and mixed models were used to assess the effect of the MI type, bone density and deflection on the evaluated outcomes. RESULTS: The IT of Ti-MIs was 1.1 Ncm greater than that obtained for the SS-MIs (p= 0.018). The IT for MIs inserted in 40 PCF test blocks was 5.4 Ncm greater than that for those inserted in 20 PCF test blocks (p < 0.001). SS-MIs inserted in higher density bone (40 PCF) had significantly higher flexural strength than the other groups, at 2 mm (98.7 ± 5.1 Ncm), 3 mm (112.0 ± 3.9 Ncm) and 4 mm (120.0 ± 3.4 Ncm) of deflection (p< 0.001). SEM evidenced fractures in the Ti-MIs. EDS revealed incorporation of 18% of C and 2.06% of O in the loaded SS-MIs, and 3.91% of C in the loaded Ti-MIs. CONCLUSIONS: Based on the findings of this in vitro study, it seems that SS-MIs offer sufficient stability and exhibit greater mechanical strength, compared to Ti-MIs when inserted into higher density bone.

[Effect of printing orientation on physical and mechanical properties of 3D printing prosthodontic base resin materials].

OBJECTIVE: To analyze the influence of forming direction on the surface characteristics, elastic modulus, bending strength and fracture toughness of printed parts and the relationship between forming direction and force direction, and to provide scientific basis and guidance for the clinical application of oral denture base resin materials. METHODS: The 3D printing technology was used to print denture base resin samples. The shape and size of the samples referred to the current standard for testing conventional denture base materials. The samples used for physical performance testing were cylindrical (with a diameter of 15 mm and a thickness of 1 mm) and printed at different angles along the Z axis (0°, 45°, 90°). Scanning electron microscope was used to observe the microscopic topography of the different samples. The color stability of different samples was observed by color stabilizer. The surface roughness of the samples was analyzed by using surface roughness tester. The Vickers hardness was measured to analyze the hardness of the samples. The samples used for mechanical performance testing were rectangular (elastic modulus and bending strength: A length of 64 mm, a width of 10 mm, and a height of 3.3 mm; fracture toughness: A length of 39 mm, a width of 8 mm, and a height of 4 mm), divided into two groups: W group and H group. The W group was printed from the bottom up along the Z axis with the length × width as the bottom surface parallel to the X, Y axis plane, while the H group printed from the bottom up along the Z axis with the length × height as the bottom surface parallel to the X, Y axis plane. The forming angles of both groups were equally divided into 0°, 45°, and 90°. The elastic modulus, bending strength and fracture toughness of different samples were studied through universal mechanical testing machine. SPSS 22.0 software was used for statistical analysis. RESULTS: The microscopic topography and roughness of different samples were closely related to the printing direction, with significant differences between the 0°, 45°, and 90° specimens. The 0° specimens had the smoothest surface (roughness < 1 µm). The surface of the 45° specimen was the roughest (roughness>3 µm). The microhardness of the 0° sample was the best [(196.13±0.20) MPa], with a significant difference compared with the 90° sample [(186.62±4.81) MPa, P < 0.05]. The mechanical properties of different samples were also closely related to the printing direction. The elastic modulus, bending strength, and fracture toughness of the 45° samples in the W group were the highest compared with the other groups. The results of elastic modulus showed that in the H group, the 45° specimens had the highest elastic mo-dulus, which was significantly different from the 0° and 90° specimens (P < 0.05). The elastic modulus of 0° and 45° specimens in the W group were higher than those in 90° specimens (P < 0.05). The bending strength results showed that there was no significant difference between the specimens from dif-ferent angles in the H group. The bending strength of the 90° specimens in the W group was the smallest, and there was a significant difference between 90° and the 0° and 45° specimens (P < 0.05); And the bendind strength of the 0° and 45° specimens in the W group was significantly higher than that of the 0° and 45° specimens in the H group (P < 0.05). The fracture toughness results showed that the fracture toughness of the H group specimens was lower than 1.9 MPa m1/2, which was specified in the denture base standard. The 45° samples in the W group were the highest, with significant differences compared with the 0° and 90° samples (P < 0.05). And the 90° samples of the W group specimens were lower than 1.9 MPa m1/2. And the fracture toughness of the 45° specimen in the W group was significantly higher than that of all the specimens in the H group (P < 0.05). CONCLUSION: The 0° samples had relatively better physical properties. The 45° samples had the best mechanical properties. But the fracture toughness of specimens (H group and 90° samples of W group) did not yet meet clinical requirements. That indicated that the characteristics of the 3D printing denture base resin were affected by the printing direction. Only when the performance of the printed samples in all directions met the minimum requirements of the standard, they could be used in clinical practice.

Denture base materials: An in vitro evaluation of the mechanical and color properties.

OBJECTIVES: This study aimed to compare the physical and mechanical properties of four denture base materials: Polyan IC (PA), milled polymethylmethacrylate (PMMA), three-dimensional (3D)-printed resin (3DP), and SR Ivocap (SR). METHODS: Ninety-six samples were prepared and divided into four groups as follows. Group A consisted of 3DP (Asiga DentaBASE, Asiga) fabricated using a manufacturer-recommended 3D printer (Asiga Pro 4k, Asiga). Group B comprised milled PMMA (MP) (Ivotion Base, Ivoclar Vivadent). Group C included PA (BredentSenden), meanwhile, group D involved SR (Ivoclar VivadentSchaan). Cuboid samples (65 mm x 10 mm x 2.5 mm) were used for biaxial flexure strength testing in a universal testing machine (UTM). Cylindrical samples of 20 mm x 40 mm were used for compressive strength testing in a UTM. Additionally, cuboid samples (65 mm x 10 mm x 2.5 mm) were used for Vickers surface hardness testing in a microhardness tester. disk samples (10 mm x 2.5 mm) were employed for color stability testing both in a coffee solution and Coca-Cola, using a digital spectrophotometer. Statistical analyses were performed using one-way analysis of variance and Tukey's post hoc analysis (α=0.05). RESULTS: MP demonstrated superior compressive strength (p = 0.002) and color stability compared to that exhibited by 3DP (p < 0.001) while displaying similar flexure strength (p = 0.336) and hardness (p = 0.708). MP and PA displayed similar compressive strength (p = 0.081), flexure strength (p = 0.159), and color stability in coke (p = 0.071). However, MP had reduced hardness (p < 0.001) and color stability in coffee (p < 0.001). Moreover, MP demonstrated a higher compressive strength (p < 0.001) than that displayed by SR. However, the flexure strength, hardness, and color stability were similar (p > 0.05). Furthermore, 3DP exhibited comparable compressive strength (p = 0.334) to that of PA but demonstrated significantly lower flexure strength (p = 0.005), hardness (p < 0.001), and color stability (p < 0.001) compared to PA. In comparison to SR, PA had a higher compressive strength (p < 0.001), hardness (p = 0.001), and color stability in coffee (p < 0.001), although they demonstrated similar (p > 0.05) flexure strength and color stability in coke. CONCLUSIONS: The MP and PA demonstrated superior compressive strength than that exhibited by the other materials tested. The tested materials had similar flexure strengths, except for PA which demonstrated superiority over the 3DP. Among all tested materials, PA exhibited the highest hardness, while the 3DP was the least color-stable. CLINICAL SIGNIFICANCE: Considering the mechanical properties and color stability, Polyan and milled polymethylmethacrylate are preferred for complete denture fabrication. However, the limited repairability and complex handling of Polyan should be considered.

Evaluating the antifungal effectiveness, leaching characteristics, flexural strength, and impact strength of polymethyl methacrylate added with small-scale silver nanoparticles - An in vitro study.

AIM: (1) To assess the release of stable silver nanoparticles (AgNPs) of small scale dimension added to heat polymerized polymethyl methacrylate (PMMA) in 6 months. (2) Assessing the influence of incorporating minimal concentrations of stable AgNPs with nanoscale dimensions into heat polymerized PMMA over a 6 month period on its antifungal efficacy (AF), flexural strength (FS), and impact strength (IS). SETTINGS AND DESIGN: Incorporating nanoparticles with a very small scale may have minimal impact on mechanical properties due to their diminutive size. However, the influence of these small scaled nanoparticles on antimicrobial efficacy and potential escalation in toxicity to host cells through leaching remains unexplored. AgNPs were prepared using an Ultrasonic Probe sonicator and the addition of ammonia to obtain stabilized AgNPs (< 0.01 nm) of small scale dimension. The characterization of these AgNPs involved ultraviolet visible spectroscopy, X ray diffraction, Zetasizer, and transmission electron microscopy with energy dispersive spectroscopy (TEM). MATERIALS AND METHODS: The prepared AgNPs were then added in various percentages by weight (0%-0.5%) to fabricate 252 modified PMMA samples of sizes 10 mm × 3 mm (AF, n = 108), 65 mm × 10 mm × 3 mm (FS, n = 72), and 65 mm × 10 mm × 2.5 mm (IS, n = 72) as per ADA specification no. 12. These samples underwent testing for leaching out of AgNPs and efficacy against Candida albicans for 6 months. The effect on FS and IS was evaluated using the three point bending test and Charpy's Impact Tester, respectively. STATISTICAL ANALYSIS USED: Intergroup comparison of CFU between various concentrations of AgNP was done using the Kruskal-Wallis ANOVA test succeeded by Mann-Whitney test for pair wise comparisons. Difference in CFU of various concentrations over 6 months was seen using one way ANOVA test. Intergroup comparison of FS and IS was performed using a one way ANOVA test, followed by a post hoc Tukey's test for pair wise comparisons. RESULTS: Repeated tests showed no leaching out of AgNPs from the denture base resin into the storage medium. All concentrations of AgNPs incorporated in resin showed inhibition of Candida growth. Intergroup comparison of FS and IS revealed highly statistically significant differences (F = 15.076, P < 0.01 and F = 28.266, P < 0.01) between the groups showing a reduction in strength. CONCLUSION: The AgNPs of small scale dimension incorporated into the denture base resin imparted a strong antifungal effectiveness against C. albicans, which did not decline during the study period and did not cause any release of nanoparticles. 0.5% showed the best antifungal efficacy. This may prove to be a viable and highly effective treatment for the prevention of Candida associated denture stomatitis. However, the inclusion of these particles resulted in a decrease in both FS and IS, and this reduction was directly proportional to the percentage of added AgNPs, with 0.5% demonstrating the least IS and FS.

Comparative study of physical-chemical properties of bioactive glass ionomer cement.

This study analyzed the physical-chemical properties of bioactive ionomer materials. Cention N bioactive materials were evaluated chemically activated (CN) and light-cured (CN-LC), Equia Forte Fill (EQUI); conventional resin composite Filtek Z350 XT (Z350); resin glass ionomer cement Riva light Cure (RIVA) and flowable resin composite Filtek Bulk Fill Flow (BULK-F) were evaluated. Sixty specimens (n=10) were prepared for sorption (SR), solubility (SL), flexural strength (FS), shrinkage stress (SS), conversion degree (CD), microhardness (MI), and surface roughness (SR) tests. Non-cured and light-cured materials were assessed on FTIR. 30 human molar teeth were used in the bond strength test (BS). Data were subjected to ANOVA and post-hoc Tukey's test (5% of significance). EQUI showed more sorption in SR and no statistical difference from RIVA and CN-LC. CN group showed more solubility and EQUI presented less (p<0.05). BULK-F showed higher FS (MPa), without differences from CN and Z350, whereas EQUI presented the lowest FS not differing from RIVA. BULK-F and CN-LC showed more shrinkage stress differing from EQUI. CN-LC and CN showed higher CD differing from the other which showed no differences (p>0.05) between them. EQUI showed the highest hardness (p<0.05) in MI. There were no differences (p>0.05) in SR (µm). Z350 and BULK-F presented higher BS, whereas CN-LC showed the lowest, although not differing from EQUI and RIVA. Equia Forte's solubility and microhardness make it a good alternative as a restorative material. Cention N degree of conversion and flexural strength making it an esthetic option to amalgam.

Effects of multiple firings on the translucency, crystalline phase, and mechanical strength of highly translucent zirconia.

This study aimed to clarify the effects of multiple firings on the translucency, crystal structure, and mechanical strength of highly translucent zirconia. Four types of highly translucent zirconia (LAVA Esthetic, LAVA Plus, KATANA Zirconia STML, and KATANA Zirconia HTML) were fired three times at three different temperatures, and the translucency, crystal structure, and flexural strength were evaluated before and after firing. The translucency was statistically compared using repeated-measures analysis of variance; the zirconia phase composition was assessed using X-ray diffraction followed by Rietveld analysis; and the biaxial flexural strength was assessed using Weibull analysis. The translucency of LAVA Esthetic and KATANA Zirconia HTML decreased significantly after firing, and the crystal composition of LAVA Plus and KATANA Zirconia HTML changed after multiple firings, whereas multiple firings did not affect the biaxial flexural strength of any samples. Thus, multiple firings may affect the optical properties of highly translucent zirconia.

Flexural strength of repaired denture base materials manufactured for the CAD-CAM technique.

PURPOSE: To evaluate the flexural properties of repaired poly(methylmethacrylate) (PMMA) denture base materials for computer-aided design/computer-aided manufacturing (CAD-CAM) and to compare them with heat-activated polymerized PMMA. METHODS: A total of 288 specimens (65 × 10 × 2.5 mm) were prepared using both CAD-CAM and conventional blocks and repaired using autopolymerizing and visible-light polymerizing (VLC) materials. Microwave energy, water storage and hydroflask polymerization were applied as additional post-polymerization cycles after the repair process. The flexural strength (FS) of the specimens was evaluated using the three-point bending test. Data were evaluated statistically using 2-way ANOVA followed by Bonferroni's correction to determine the significance of differences between the groups (P ≤ 0.05). RESULTS: The FS of the denture base materials for CAD-CAM was significantly higher than that for the heat-activated group (P ≤ 0.05). The FS was significantly highest when microwave energy was used for the post-polymerization cycle. The FS values for all groups repaired with VLC resin were significantly lower than for the autopolymerization group (P ≤ 0.05). CONCLUSION: The flexural properties of denture base materials for CAD-CAM repaired using autopolymerizing acrylic resins can recover by 50-70%. Additional post-polymerization cycles for autopolymerizing repair resin can be suggested to improve the clinical service properties of repaired dentures.

Influence of printing orientation on mechanical properties of aged 3D-printed restorative resins.

OBJECTIVE: To evaluate the influence of printing orientation on flexural strength (σf) and elastic modulus (E) of different 3D printing dental restorative resins. METHODS: Bar-shaped specimens (n = 20) were fabricated from two SLA-printed resins (FT- Formlabs Temporary, and FP- Formlabs Permanent) and two DLP-printed resins (DFT- Detax Freeprint Temp, and GCT- GC Temporary) using two building orientations (0º and 90º). The 3D-printed structures were aged (14 d) before submitted to three-point bending in 37ºC distilled water at a crosshead speed of 1.0 ± 0.3 mm/min until fracture to calculate the σf and the E values. The fractured surfaces were evaluated using stereomicroscopy and scanning electron microscopy (SEM) following fractography principles. Data were statistically analyzed using two-way ANOVA and Tukey post-hoc (α = 0.001). RESULTS: FP and FT showed significantly higher E values than DFT and GCT, irrespectively of printing orientation (p < 0.001). There was no statistical difference between the building orientations (0º and 90º) for the mean σf and E values for the resin materials evaluated. Fractographic characteristics were similar for the surface fracture from all the materials evaluated, showing typical brittle fracture behavior. SIGNIFICANCE: Printing orientation did not influence of flexural strength and elastic modulus values for the 3D-printed resin structures evaluated. Surface topography was mostly governed by the 3D printer type.

Methodological approaches in graded dental ceramics.

BACKGROUND: Functionally graded materials (FGM) with indistinct boundaries potentially eliminate the damaging stresses occurring at the interfaces. FGM applications in dental ceramics have enhanced their fatigue resistance and interfacial toughness. OBJECTIVES: This scoping review aims to map graded designs in dental ceramics, distinguish their methodological approaches with their material characteristics and properties, and understand the factors affecting the outcomes of each of the graded approaches. METHODS: A systematic electronic search was performed with the databases MEDLINE (PubMed), Scopus, Cochrane Library, EBSCO, and Google Scholar along with a manual search. RESULTS: About 2675 articles were initially found from all the searches with no date restriction till July 2023. After rejecting duplicates and based on exclusion criteria, about 52 articles were included. SIGNIFICANCE: Methodological approaches in grading such as glass-infiltration and silica-infiltration have been investigated on pre-sintered zirconia. The type of infiltration and the method of infiltrate application significantly influenced the phase transformation of zirconia, its microstructure, surface hardness, fracture toughness, flexural strength, wear, and fatigue strength of graded dental zirconia. Interlayers were accommodated between metal-ceramic and veneer-core all-ceramic layers. Fractions of zirconia-porcelain and alumina-porcelain showed high bending strength and better stress distribution. The results of finite element analysis studies predicted that using 10-layered graded layers reduced the stresses at the crown-cement-dentin interface.

High-Performance Dental Resins Containing a Starburst Monomer.

Dimethacrylate-based chemistries feature extensively as resin monomers in dental resin-based materials due to their distinguished overall performance. However, challenges endure, encompassing inadequate mechanical attributes, volumetric shrinkage, and estrogenicity. Herein, we first synthesized a novel resin monomer, 9-armed starburst polyurethane acrylate (NPUA), via the grafting-onto approach. Compared to the primary commercial dental monomer 2,2-bis [p-(2'-hydroxy-3'-methacryloxypropoxy) phenyl] propane (Bis-GMA) (with a viscosity of 1,174 ± 3 Pa·s and volumetric shrinkage of 4.7% ± 0.1%), the NPUA monomer achieves the lower viscosity (158 ± 1 Pa·s), volumetric shrinkage (2.5% ± 0.1%), and cytotoxicity (P < 0.05). The NPUA-based resins exhibit the higher flexural strength, flexural modulus, hardness, and hydrophobicity and lower volumetric shrinkage, water absorption, and solubility compared to the Bis-GMA (70 wt%)/TEGDMA (30 wt%) resins. The NPUA-based composites exhibit significantly higher flexural strength, flexural modulus, and hardness and lower volumetric shrinkage (171.4 ± 3.0 MPa, 12.6 ± 0.5 GPa, 2.0 ± 0.2 GPa, and 3.4% ± 0.2%, respectively) compared to the Bis-GMA group (120.3 ± 4.7 MPa, 9.4 ± 0.7 GPa, 1.5 ± 0.1 GPa, and 4.7% ± 0.2%, respectively; P < 0.05). This work presents a viable avenue for augmenting the physicochemical attributes of dental resins.

Effect of Hydrothermal Aging on the Flexural Strength and Microhardness of Materials Used for Additive or Subtractive Manufacturing of Definitive Restorations.

PURPOSE: To evaluate the flexural strength (FS) and microhardness of various CAD/CAM restorative materials intended for definitive use. The effect of hydrothermal aging on the mechanical properties of these materials was also investigated. MATERIALS AND METHODS: A total of 210 bar-shaped specimens (17 × 4 × 1.5 mm ± 0.02 mm) were fabricated via either subtractive manufacturing (SM) methods-reinforced composite resin (SM-CR), polymer-infiltrated ceramic network (SM-PICN), fine-structured feldspathic ceramic (SMFC), nanographene-reinforced polymethyl methacrylate (PMMA; SM-GPMMA), PMMAbased resin (SM-PMMA)-or additive manufacturing (AM) methods with urethane acrylate-based resins (AM-UA1 and AM-UA2). Specimens were then divided into two subgroups (nonaged or hydrothermal aging; n = 15). A three-point flexural strength test was performed, and five specimens from the nonaged group were submitted to microhardness testing. Specimens were subjected to 10,000 thermal cycles, and the measurements were repeated. RESULTS: Regardless of aging, SM-CR had the highest FS (P < .001), followed by SM-GPMMA (P ≤ .042). In nonaged groups, AM-UA2 had a lower FS than all other materials except SM-FC (P = 1.000). In hydrothermal aging groups, AM specimens had lower FS values than other materials, except SM-PMMA. With regard to microhardness, there was no significant difference found between any of the tested materials (P ≥ .945) in the nonaged and hydrothermal aging groups. CONCLUSIONS: The effect of hydrothermal aging on FS varied depending on the type of restorative material. Regardless of aging condition, SM-CR showed the highest FS values, whereas SM-FC had the highest microhardness. Hydrothermal aging had no significant influence on the microhardness of the tested materials.

Effect of thermal cycling on the flexural strength of 3-D printed, CAD/CAM milled and heat-polymerized denture base materials.

BACKGROUND: This study compared the impact of thermal cycling on the flexural strength of denture-base materials produced through conventional and digital methods, using both subtractive and additive approaches. METHODS: In total, 60 rectangular specimens were fabricated with specific dimensions for flexural strength tests. The dimensions were set according to the International Organization for Standardization (ISO) guideline 20795-1:2013 as 64 × 10 × 3.3 ± 0.2 mm. Specimens from each material group were divided into two subgroups (thermal cycled or nonthermal cycled, n = 10/group). We used distinct methods to produce three different denture-base materials: Ivobase (IB), which is a computer-aided-design/computer-aided-manufacturing-type milled pre-polymerized polymethyl methacrylate resin disc; Formlabs (FL), a 3D-printed denture-base resin; and Meliodent (MD), a conventional heat-polymerized acrylic. Flexural strength tests were performed on half of the samples without a thermal-cycle procedure, and the other half were tested after a thermal cycle. The data were analyzed using a two-way analysis of variance and a post hoc Tukey test (α = 0.05). RESULTS: Based on the results of flexural-strength testing, the ranking was as follows: FL > IB > MD. The effect of thermal aging was statistically significant for the FL and IB bases, but not for the MD base. CONCLUSIONS: Digitally produced denture bases exhibited superior flexural strength compared with conventionally manufactured bases. Although thermal cycling reduced flexural strength in all groups, the decrease was not statistically significant in the heat-polymerized acrylic group.

Fabrication of green anti-microbial and anti-static cement building bricks.

The design cement mix of grade 350 was created in accordance with Egyptian Standards by partially substituting the fine aggregate with WPVC waste in various weight percentages (10, 20, 30, 40, 50, 75, and 100%). A control mix with 0% replacement was also prepared. The W/C ratio was about 0.5 for all mixes. Compressive, flexure strength, bulk density, and absorption tests were studied. For WPVC replacement, until 30%, compressive strength and flexure strength are acceptable with respect to standerds. Thermal treatment at 200 °C improves the compressive strength, flexure strength and water absorption for 20% WPVC only. The dielectric properties of all cement paste mixes before and after heat treatment, over a frequency range (0.1-106 Hz), were measured as a function of frequency. For dielectric properties and conductivity, an improvement was obtained until 30% WPVC. After this percentage, the dielectric properties and the conductivity got worse. So, cement paste with 30% WPVC as replacement of sand is the optimum ratio with conductivity in range of 10-12 S/cm, which is a good choice for antistatic cement paste applications (10-10-10-12 S/cm). The antimicrobial efficacy of the prepared cement samples of WPVC concentrations (0, 20 and 30) % were studied, the number of grown microbial colonies decreased for all the samples compared to control tap water and decreased by introducing WPVC into the cement paste sample. So, it is recommended to use these samples in places that should be carefully shielded from bacterial infections and static electric charge dangers.

Fracture Strength of Six-Unit Anterior Fixed Provisional Restorations Fabricated Using Various Dental CAD/CAM Systems.

PURPOSE: This study compares the fracture strengths of long-span fixed provisional restorations fabricated via digital additive and subtractive methods to those fabricated via conventional heat-processing techniques. MATERIALS AND METHODS: A six-unit anterior partial restoration was designed as an anatomical and morphologic structure using a dental CAD/CAM system. The provisional restorations (N = 40) of four different fabrication methods (n = 10 per group) were used for the failure loading test: stereolithography apparatus (SLA), liquid crystal display (LCD), milling (MIL), and heat-processed temporary (HPT). The specimens were subjected to a maximum load-to-fracture test using a universal testing machine, and the representative fracture patterns were observed. Statistical analysis was performed using Shapiro-Wilk, Kruskal-Wallis, Mann-Whitney U, and Bonferroni post hoc tests (P < .05). RESULTS: The four groups showed significant differences in fracture strength according to the materials and manufacturing methods used (P < .001, except between SLA and HPT groups). The fracture strengths of MIL and LCD digitally fabricated groups were significantly higher than that of the HPT group (P < .001). CONCLUSIONS: The subtractive method is ideal for fabricating long-span fixed provisional restorations for long-term use. Additionally, LCD additive manufacturing technology could soon be a good alternative for restorations.

Comparative Evaluation of Fracture Toughness and Flexural Strength of Four Different Core Build-up Materials: An In Vitro Study.

AIM: To evaluate and compare the fracture toughness and flexural strength of four different core build-up materials. MATERIALS AND METHODS: A total of 60 samples were divided into four groups (n = 15) group I: dual cure composite resin reinforced with zirconia particles (Luxacore Z), group II: light cure composite resin (Lumiglass DeepCure), group III: zirconia reinforced glass ionomer cement (GIC) (Zirconomer Improved), and group IV: chemically cure composite resin (Self Comp) respectively. All the core build-up materials were manipulated according to the manufacturer's instructions and poured into the mold. A universal testing machine applied a central load to the specimen in a 3-point bending mode. Fracture of the specimen was identified and the reading was recorded by the universal testing machine. The data were analyzed statistically using one-way analysis of variance (ANOVA) and then compared. RESULTS: Group I showed the highest flexural strength (48.65 MPa) among all the groups while group IV showed the lowest flexural strength (17.90 MPa). Group I showed the highest fracture toughness (99.12 MPa) among all the groups while group IV showed the lowest fracture toughness (36.41 MPa.cm-0.5). When mean flexural strength and fracture toughness values of all four groups were compared by using one-way ANOVA, the compared data was highly significant. CONCLUSION: Based on the findings of this study, dual cure composite resin was the material of choice in terms of flexural strength and fracture toughness for core build-up material followed by light cure composite resin. CLINICAL SIGNIFICANCE: The core buildup material serves to strengthen the tooth structure, allowing it to withstand the forces of chewing and preventing the risk of tooth fractures. This material is essential in restoring damaged or decayed teeth, as it provides a stable foundation for further dental work. By reinforcing the tooth structure, the core buildup material ensures that the tooth can function properly and remain healthy for years to come. How to cite this article: Nakade P, Thaore S, Bangar B, et al. Comparative Evaluation of Fracture Toughness and Flexural Strength of Four Different Core Build-up Materials: An In Vitro Study. J Contemp Dent Pract 2024;25(2):191-195.

Fracture strength of porcelain veneer on surface-treated zirconia.

In this study, we investigated the effects of surface treatment on the fracture strength of porcelain-veneered zirconia. Highly translucent 4 mol% yttria-stabilized zirconia disks (KATANA HT, Kuraray Noritake Dental) were divided into three surface-treatment groups: 1)as-sintered, 2) alumina sandblasted, and 3) ground. Crystallographic and surface-roughness analyses were conducted for each group. Veneering ceramics (Cerabien ZR, Kuraray Noritake Dental) were applied to the zirconia surfaces. The fracture strengths of the porcelain-veneered zirconia disks were measured using biaxial flexural-strength tests. Crystallographic analysis revealed that grinding and sandblasting increased the fractions of the monoclinic and rhombohedral zirconia phases. The ground specimens had a higher surface roughness than the sandblasted specimens. Weibull analysis showed no significant differences in biaxial flexural strength among the three groups. The results suggest that these surface treatments do not affect the fracture strength of porcelain-veneered zirconia.

Comparison of subcritical growth parameters of a Y-TZP obtained via cyclic or dynamic fatigue tests.

OBJECTIVE: The objective of this study was to 1) compare the stress corrosion coefficient (n) of a Y-TZP obtained by two fatigue tests: cyclic and dynamic and 2) evaluate the effect of frequency in the characteristic lifetime and the existence of interaction between the cyclic fatigue and slow crack growth. METHODS: A total of 145 Y-TZP specimens were produced in accordance with the manufacturer's instructions. These specimens, measuring 4.0 × 3.0 × 25.0 mm, were used for dynamic (n = 70) and cyclic fatigue tests (n = 75). The specimens were obtained from CAD/CAM blocks, sectioned, and sintered in a furnace at 1530 °C with a heating rate of 25 °C/min. They were tested in their "as-sintered" form without any additional surface treatment. The fatigue tests were conducted using a four-point bending to obtain the slow crack growth parameters (n). The cyclic fatigue test was also conducted in two frequencies (2 and 10 Hz), using stress levels between 350 and 600 MPa. Data from these tests were analyzed using ASTM C 1368-00 formulas and Weibull statistics. Scanning electron microscope (SEM) was used for fracture surface analysis to identify the origin of the fracture. Critical defect size was measured and used, along with flexural strength values, to estimate fracture toughness. Dynamic fatigue test data were used to obtain subcritical crack growth (SCG) parameters and perform Weibull statistical analysis. The cyclic fatigue data were used in the General Log-linear Model equation using the ALTA PRO software. Data were analyzed using one-way ANOVA followed by Tukey post-hoc tests and Student's t-test at a significance level of p ≤ 0.05. RESULTS: In the dynamic fatigue test, the values obtained for σfo and n were 667 and 54, respectively. This parameter indicates how the strength of the material diminishes over time due to internal cracks. The Weibull parameters obtained from the same test results were m = 7.9, σ0 = 968, 9 and σ5% = 767, which indicates the reliability of the material. The Weibull parameters obtained by cyclic fatigue were statistically similar for the two frequencies used, the m* was 0.17 (2 Hz) and 0.21 (10 Hz); characteristic lifetimes (η) were 1.93 × 106 and 40,768, respectively. The n values obtained by cyclic fatigue were 48 and 40 at frequencies of 2 and 10 Hz, respectively. There was no effect of the frequency, the stress level or the interaction of the two in the Y-TZP lifetime, when analysed by General Log Linear Model. SIGNIFICANCE: the n values obtained by cyclic and dynamic fatigue tests showed no statistically significant difference and the effect of frequency in the characteristic lifetime and the existence of interaction between the cyclic fatigue and subcritical growth were not observed in the tested specimens.

Fracture strength of 3-units fixed partial dentures fabricated with metal-ceramic, graphene doped PMMA and PMMA before and after ageing: An in-vitro study.

OBJECTIVES: To evaluate the fracture strength and linear elongation at break of three-units fixed partial dentures (FPDs) fabricated with traditional and new materials for fixed prosthodontics before and after ageing. METHODS: Sixty models of three-units FPDs were fabricated and cemented onto a Co-Cr model simulating the replacement of a maxillary second premolar. The samples were randomly divided into 3 groups: metal-ceramic (MCR), graphene-doped polymethylmethacrylate (PMMA-GR) and polymethylmethacrylate (PMMA). Half of the samples were directly subjected to fracture test, while the remaining half underwent an ageing process and then a fracture loading test using an electrodynamic testing machine. Fracture load and elongation at break values were taken and statistically analysed. RESULTS: Significant differences were detected between the different materials (p<0.05). All groups showed a reduction of the fracture load and elongation at break values after ageing, but not statistically significant, except for PMMA group (p = 2.012e-19) (p = 3.8e-11). CONCLUSIONS: MCR and PMMA-GR three-units FPDs showed higher fracture strength and lower elongation at break compared to PMMA. MCR and PMMA-GR had higher resistance to ageing processes compared to PMMA. CLINICAL SIGNIFICANCE: PMMA-GR could be considered a material for long-term provisional restorations as its mechanical behaviour and ageing resistance are more like MCR than PMMA.

Wear resistance and flexural properties of low force SLA- and DLP-printed splint materials in different printing orientations: An in vitro study.

OBJECTIVES: To investigate the influence of material and printing orientation on wear resistance and flexural properties of one low force SLA- and two DLP-printed splint materials and to compare these 3D-printed splints to a subtractively manufactured splint material. METHODS: Two DLP-printed (V-Print splint, LuxaPrint Ortho Plus) and one low force SLA-printed (Dental LT Clear) material, where specimens were printed in three printing orientations (0°, 45°, 90°), were investigated. In addition, one milled splint material (Zirlux Splint Transparent) was examined. A total of 160 specimens were produced for both test series. The two-body wear test was performed in a chewing simulator (80'000 cycles at 50 N with 5-55 °C thermocycling). Steatite balls were used as antagonists. The wear pattern was analyzed with a 3D digital microscope in terms of maximum vertical intrusion depth (mm) and total volume loss (mm³). The flexural properties were investigated by three-point bending in accordance with ISO 20795-1: 2013 (denture base polymers). The flexural strength (MPa) and the flexural modulus (MPa) were measured. Two-way ANOVA was performed to investigate the effects of the two independent variables material and printing orientation for the three 3D-printed materials. The comparison of the printing orientations within one material was carried out with one-way ANOVA with post-hoc Tukey tests. RESULTS: Two-way ANOVA revealed that wear and flexural properties are highly dependent on the 3D-printed material (p < 0.001). Across groups, a significant effect was observed for wear depth (p = 0.031) and wear volume (p = 0.044) with regard to printing orientation but this was not found for flexural strength (p = 0.080) and flexural modulus (p = 0.136). One-way ANOVA showed that both DLP-printed groups showed no significant differences within the printing orientations in terms of wear and flexural properties. Dental LT Clear showed that 90° oriented specimens had higher flexural strength than 0° oriented ones (p < 0.001) and 45° oriented specimens also showed higher values than 0° ones (p = 0.038). No significant differences were observed within the printing orientations for flexural modulus and wear behaviour within this group. T-tests showed that the milled splints exhibited statistically higher wear resistance and flexural properties compared to all three 3D-printed splint materials (p < 0.001) and that highly significant differences were found between the 3D-printed splint materials for both test series. CONCLUSION: Within the limitations of this in vitro study, it can be stated that wear behaviour and flexural properties are highly dependent on the 3D-printed material itself. Currently, milled splints exhibit higher wear resistance and flexural properties compared to 3D-printed splint materials. The printing orientation has a minor influence on the properties investigated. Nevertheless, two-way ANOVA also showed a significant influence of printing orientation in the wear test across groups and one-way ANOVA detected significant effects for SLA material in terms of flexural strength, with printing in 90° showing the highest flexural strength. Therefore, anisotropy was found in SLA material, but it can be limited with the employed printing parameters. Both DLP-printed materials showed no significant difference within the printing orientation.