Comparative in vitro analysis of the antifungal activity of different calcium silicate-based endodontic sealers
Braz. j. oral sci
; 23: e243355, 2024. ilus
Article
en En
| LILACS, BBO
| ID: biblio-1551649
Biblioteca responsable:
BR218.1
ABSTRACT
Aim:
This study aimed to perform an in vitro comparative analysis of the antifungal activity of different calcium silicate-based endodontic sealers against three fungal species.Methods:
The antifungal properties of three calcium silicate-based sealers were tested Bio-C Sealer, Cambiar a Sealer Plus BC, and MTA-Fillapex. Two commonly used sealers were used as controls AH Plus and Endomethasone. An agar diffusion test was performed to analyze the antifungal activity of the sealers against Candida albicans, Candida glabrata, Candida tropicalis, and a mixed microbial culture medium. The results were analyzed using ANOVA (p <0.05).Results:
Endomethasone exhibited the highest inhibition against all strains examined, maintaining a consistent level of inhibition throughout 7 days. MTA-Fillapex demonstrated the best performance among the calcium silicate-based sealers for the three fungal species (p < 0.05), maintaining stable values over the 7 days, surpassing that of Endomethasone. Nevertheless, MTA-Fillapex only exhibited antimicrobial effect against the mixed culture for the first 24 hours, and no antimicrobial activity was observed at 48 hours, being surpassed by all tested sealers (p < 0.05).Conclusion:
Of all silicate-based sealers tested, only MTA-Fillapex exhibited promising antifungal activity. Nevertheless, care must be taken when extrapolating these results, as MTA-Fillapex exhibited poor antimicrobial activity when tested in mixed microbial culturesAsunto(s)
Palabras clave
Texto completo:
1
Base de datos:
LILACS
Asunto principal:
Materiales de Obturación del Conducto Radicular
/
Cemento de Silicato
/
Bacterias
/
Candida albicans
/
Candida glabrata
/
Candida tropicalis
/
Endodoncia
/
Antifúngicos
Idioma:
En
Revista:
Braz. j. oral sci
Asunto de la revista:
ODONTOLOGIA
Año:
2024
Tipo del documento:
Article