Corrosion of three experimental AgMn-based casting alloys.
Dent Mater
; 14(6): 448-52, 1998 Nov.
Article
en En
| MEDLINE
| ID: mdl-10483408
ABSTRACT
OBJECTIVE:
Alloys based on AgMn are being evaluated in our laboratory for their possible use as an alternative to Type III dental alloys. They respond to heat treatment and develop hardness values comparable to that of Type III alloys. The objective of the present research was to evaluate their corrosion characteristics.METHODS:
The three experimental silver-based alloys of the following composition (at%) (1) 63Ag37Mn, (2) 60Ag35Mn5Au and (3) 60Ag35Mn5Pd, were tested in their peak-hardened condition. Following 0.5 h open-circuit potential (OCP) measurement of each alloy in a phosphated buffer saline (PBS) solution, its current-potential profile was generated by the cyclic voltammetry technique within -1300 and +200 mV (SCE) at 1 mV s-1. In a separate test, the OCP of each alloy was monitored over a 24 h period.RESULTS:
Each of the three alloys showed ennoblement of their OCP over time due to dissolution of Mn and consequent enrichment with Ag (Au or Pd). At 24 h, the two ternary alloys were the most noble followed by the binary alloy. With respect to the cyclic voltammetry, oxidation of Ag was noted during forward scans at around 0 mV. The reverse scan was associated with a reduction current peak between -37 and -128 mV. The values for this peak, which is a measure of Ag oxidation, were highest (11.5 mA cm-2) for the binary alloy followed by the Au- (2.9 mA cm-2) and Pd-containing (0.04 mA cm-2) alloys, respectively. This indicates that, for equivalent concentration, Pd is more effective in reducing Ag corrosion than Au.SIGNIFICANCE:
Alloys based on the AgMn system are as hard as Type III dental alloys. Information on the corrosion characteristics of the AgMn-based alloys presented here is of value in further development of this alloy system.
Buscar en Google
Base de datos:
MEDLINE
Asunto principal:
Aleaciones Dentales
Idioma:
En
Revista:
Dent Mater
Asunto de la revista:
ODONTOLOGIA
Año:
1998
Tipo del documento:
Article