Network confinement and heterogeneity slows nanoparticle diffusion in polymer gels.

ABSTRACT

Nanoparticle (NP) diffusion was measured in polyacrylamide gels (PAGs) with a mesh size comparable to the NP size, 21 nm. The confinement ratio (CR), NP diameter/mesh size, increased from 0.4 to 3.8 by increasing crosslinker density and from 0.4 to 2.1 by adding acetone, which collapsed the PAGs. In all gels, NPs either became localized, moving less than 200 nm, diffused microns, or exhibited a combination of these behaviors, as measured by single particle tracking. Mean squared displacements (MSDs) of mobile NPs decreased as CR increased. In collapsed gels, the localized NP population increased and MSD of mobile NPs decreased compared to crosslinked PAGs. For all CRs, van Hove distributions exhibited non-Gaussian displacements, consistent with intermittent localization of NPs. The non-Gaussian parameter increased from a maximum of 1.5 for crosslinked PAG to 5 for collapsed PAG, consistent with greater network heterogeneity in these gels. Diffusion coefficients decreased exponentially as CR increased for crosslinked gels; however, in collapsed gels, the diffusion coefficients decreased more strongly, which was attributed to network heterogeneity. Collapsing the gel resulted in an increasingly tortuous pathway for NPs, slowing diffusion at a given CR. Understanding how gel structure affects NP mobility will allow the design and enhanced performance of gels that separate and release molecules in membranes and drug delivery platforms.