Endoscopic submucosal dissection (ESD) is a challenging procedure. The use of biomaterials to improve the operator's convenience (operating affinity) has received little attention. We prepared two thermosensitive hydrogels, lactobionic acid-modified chitosan/chitosan/ß-glycerophosphate thermosensitive hydrogel (hydrogel 1) and its lyophilized powders (hydrogel 2), characterized their physicochemical properties and evaluated their performance in ESD experiments on large animals, by comparing with the commonly used normal saline (NS) and glycerin fructose (GF). These hydrogels showed good low-temperature fluidity; their viscosities at 4 °C were 92.2 mPa.s and 26.9 mPa.s, respectively. The hydrogels provided significantly better viscoelastic properties than NS and GF. The relaxation moduli of hydrogels were higher than those of NS and GF when the strains were 1 %, 5 %, and 10 %. The hydrogels can be maintained for seven days, even at pH 1, after which they degrade entirely. In pig model experiments, we performed submucosal injection and ESD procedures in the stomach and esophagus. The cushion height produced by the hydrogels was higher than those of NS and GF 30 min after injection. The ESD operation time for hydrogels was significantly shorter. Postoperative wound observation and histological analysis showed that the hydrogels promoted wound healing. The two hydrogels differed in fluidity, viscoelasticity, and other properties, which makes it possible to select the hydrogels according to the size and location of the lesion during ESD operation, and hydrogel 2 may be more suitable for use in lengthier procedures. In general, the hydrogels showed good performance, facilitated the intraoperative operation of ESD, shorten the operation time and promoted wound healing, which is of great significance for reducing the complications and reducing the threshold of ESD operation and further promoting the popularity of ESD.