3D-printed chitosan scaffolds modified with D-(+) raffinose and enriched with type IV collagen to improve epithelial cell colonization.

Tissue regeneration often requires the use of biocompatible resorbable scaffolds to support the ingrowth of cells from neighboring tissues into a localized tissue defect. Such scaffolds must possess surface molecular cues that stimulate cells to populate the device, the first necessary condition for the formation of a healthy tissue. Chitosan is a natural polymer that has long been tested in biomedical applications because of its high biocompatibility, which can be further increased by modifying its formulation, e.g. adding D-(+) raffinose. We used this formulation in an ad hoc designed 3D printer to create regularly ordered scaffolds, which we then enriched with type IV collagen, an isoform of collagen that is exclusively found in basement membranes. Human epithelial A549 cells were then seeded on control scaffolds or on scaffolds coated with collagen, which was precipitated, or on scaffolds first collagenized and then exposed to either UVB or UVC radiation. Observations by the transmission light microscope, confocal microscope after staining with calcein-AM/propidium iodide, and by environmental scanning electron microscope revealed that collagen-enriched UV-treated scaffolds promoted the attachment of a higher number of cells, which covered a more extensive area of the scaffold, as also confirmed by alamar blue viability assay. Together these data confirm that coating 3D-printed scaffolds made of D-(+) raffinose-modified chitosan with type IV collagen and exposing them to UV light sensibly increases the cell compatibility of scaffolds, making them a better candidate to serve as a tool for the regeneration of epithelia.

The Use of Pulsed Electromagnetic Fields to Promote Bone Responses to Biomaterials In Vitro and In Vivo.

Implantable biomaterials are extensively used to promote bone regeneration or support endosseous prosthesis in orthopedics and dentistry. Their use, however, would benefit from additional strategies to improve bone responses. Pulsed Electromagnetic Fields (PEMFs) have long been known to act on osteoblasts and bone, affecting their metabolism, in spite of our poor understanding of the underlying mechanisms. Hence, we have the hypothesis that PEMFs may also ameliorate cell responses to biomaterials, improving their growth, differentiation, and the expression of a mature phenotype and therefore increasing the tissue integration of the implanted devices and their clinical success. A broad range of settings used for PEMFs stimulation still represents a hurdle to better define treatment protocols and extensive research is needed to overcome this issue. The present review includes studies that investigated the effects of PEMFs on the response of bone cells to different classes of biomaterials and the reports that focused on in vivo investigations of biomaterials implanted in bone.

Osteoprotegerin and receptor activator of nuclear factor-kappa B ligand modulation by enamel matrix derivative in human alveolar osteoblasts.

BACKGROUND: Bone regeneration techniques increasingly rely on the use of exogenous molecules able to enhance tissue formation in pathologic and traumatic defects. An enamel matrix derivative (EMD) has been largely used to promote tooth ligament regeneration within periodontal pockets. Recent evidence suggests that EMD may contribute to inducing osteoblast growth and differentiation. We investigated the effects of EMD on growth and osteogenic marker modulation in human mandibular osteoblasts. METHODS: We focused our attention on cell growth by 3-(4,5-dimethyl[thiazol-2-yl]-3,5-diphery)tetradium bromide (MTT) assay, cell differentiation, mineralized nodule formation, and, in particular, the expression of receptor activator of nuclear factor-kappa B ligand (RANKL), the main osteoclast differentiation factor, and its decoy receptor, osteoprotegerin (OPG), by enzyme-linked immunosorbent assay. RESULTS: Cell growth was significantly increased by EMD. Similarly, a significantly higher quantity of OPG and a lower amount of RANKL were detectable in groups treated with 50 and 100 microg/ml at weeks 1, 2, and 3, and alkaline phosphatase activity and osteocalcin production were enhanced in cultures treated with 50 and 100 microg/ml at weeks 2 and 3. Mineralized nodules appeared bigger and more numerous in cultures treated with 50 and 100 microg/ml EMD. CONCLUSIONS: EMD was able to enhance osteoblast cell growth and the expression of markers of osteoblastic phenotype and differentiation. EMD also seemed able to create a favorable osteogenic microenvironment by reducing RANKL release and enhancing osteoblastic OPG production.

Comparison of human mandibular osteoblasts grown on two commercially available titanium implant surfaces.

BACKGROUND: Surface characteristics play a major role in determining tissue response to implants and therefore their clinical outcome. The aim of the present study was to compare two commercially available titanium surfaces: plasma sprayed (TPS) and sand-blasted, acid-etched surface (SLA). METHODS: The surfaces were characterized by roughness testing, scanning electronic microscopy (SEM), Raman spectroscopy, and protein adsorption to determine their microtopographic and chemical properties. The effect of the surfaces on human mandibular osteoblasts was then studied in terms of cell morphology, adhesion, proliferation, and differentiation. Human osteoblasts from the mandible were cultured on these two surfaces and evaluated at 3, 6, 24, and 48 hours to determine cell attachment and morphology. Growth and differentiation kinetics were subsequently investigated by evaluating cell growth, alkaline phosphatase activity, osteocalcin and osteoprotegerin production at 7, 14, and 21 days. RESULTS: Although roughness was quite similar, the two surfaces presented strong differences in their topography, and cell morphology varied as a consequence. Osteoblasts on SLA appeared more elongated and spindle shaped than those on TPS, and their adhesion at 3 and 6 hours was weaker, but reached that of cells on TPS at hour 24. Cell proliferation was greater on SLA surfaces but differentiation parameters; i.e., alkaline phosphatase and osteocalcin, provided better results on TPS surfaces. Osteoprotegerin production was enhanced on TPS surfaces at days 14 and 21. CONCLUSION: Although cells grown on both surfaces exhibited good adhesion capabilities, a well-differentiated osteoblastic phenotype, and maintained a clear proliferation potential, our study suggests that plasma-sprayed treatment offers a better performance than SLA by creating, at least in the early phases, better conditions for tissue healing.

Different titanium surface treatment influences human mandibular osteoblast response.

BACKGROUND: Six titanium disks with six different surface treatments were examined: SS: smooth (polished) surface; TPS: plasma spray; C100: sand blasting by aluminum oxide (Al2O3) diameter 100 microm and acid etching; C150: sand blasting by Al2O3 diameter 150 microm and acid etching; B60: sand blasting by zirconium oxide (ZrO2) diameter 60 microm and acid etching; and B120: sand blasting by ZrO2 diameter 120 microm and acid etching. METHODS: The surface characteristics were determined by scanning electron microscopy (SEM) observation and a roughness tester. Raman spectroscopy was used to determine the presence of residual substances on the samples. Cells were seeded onto the disk and after 24 hours, 6 days, and 12 days were observed under SEM and growth curves generated with a cell counter. Some samples were used to determine alkaline phosphatase activity (ALP), using a colorimetric assay. RESULTS: SEM observation revealed drastic differences in surface microtopography, with a higher cell density on sand-blasted and acid-etched (SLA) samples than SS and TPS, and more regularly aligned cells on B60 and B120 surfaces than on the others. The growth curves showed a greater adhesion of cells on the etched/blasted surfaces compared to the SS and TPS surfaces. The number of cells increased on all the SLA samples, especially B60, throughout the experiment. At the same time, there was considerable ALP activity on the B60 sample, while it remained at extremely low levels on SS and TPS surfaces. Raman analyses revealed Al2O3 debris on C100 and C150, partly explaining the poorer performances of these two surface treatments, since this substance was shown to be toxic for cultured osteoblasts. CONCLUSIONS: Surface treatments influence the growth and the metabolic activity of cultured osteoblasts, and B60 seems to be the most favorable surface inducing a more pronounced proliferation of cells together with a high differentiation degree.

Sr, Mg cosubstituted HA porous macro-granules: potentialities as resorbable bone filler with antiosteoporotic functions.

Porous macro-granules of nanostructured apatite with Ca ions partially cosubstituted with Mg and Sr ions in different ratios (SrMgHAs), were synthesized at 37°C and compared with Mg and/or Sr free apatites (MgHAs and HA). Strontium improved the Mg substitution extent in the apatite and the chemical-physical and thermal stability of the resulting cosubstituted apatite. Porous macro-granules of 400-600 micron with selected composition were tested for the ionic release in synthetic body fluid and the data were related with the results of preliminary cell investigation in vitro. As compared to the corresponding Sr-free granulate, the SrMgHA could be exploited to prolong the beneficial Mg release during the bone regeneration process. In addition the contemporary in situ supply of Sr, an antiosteoporotic and anticarie ion, could influence the quality of new hard tissues. The ionic multirelease created a more favorable environment for human osteoblasts, demonstrated by a proliferative effect for each dose tested in the range 0.1-10 mg/mL.

Human osteoblast behavior on as-synthesized SiO(4) and B-CO(3) co-substituted apatite.

The functional behavior of synthetic apatite, commonly used as fillers or scaffolds, depends on physical and chemical parameters, which vary in response to chemical substitutions and to thermal treatments. The effect of silicon co-substituting with carbonate ions in the apatite lattice on the properties of the as-synthesized powder and finally on human osteoblast in vitro behavior was investigated. Dose-response curves of Si-free and Si-substituted carbonated apatites (namely CHA and SiCHA-1 and SiCHA-2 with 0.88 and 0.55 wt % of Si, respectively) showed that SiCHA-1 had toxic effect, whereas CHA and SiCHA-2, at worst, hindered osteoblast proliferation, but no toxicity occurred. Subsequent experiments compared the effects of CHA and SiCHA-2 used at the doses of 0.3 and 1 mg/mL. After 7 days of treatment, both the powders stimulated cell proliferation and protein content and inhibited alkaline phosphatase activity. However, SiCHA-2 slightly stimulated osteoblast differentiation, as shown by higher calcium deposition, compared with CHA. The cell behaviors were linked to the peculiar powder characteristics. The as-synthesized powder represents the most critical system in terms of reactivity toward cells and can inform on the limits for positively exploiting the characteristics of SiCHA powders in making bone fillers or scaffolds, using no thermal treatments. (c) 2010 Wiley Periodicals, Inc. J Biomed Mater Res, 2010.