Reliable femoral chronic total occlusion model using a thin biodegradable polymer coated copper stent in a porcine model.

Chronic total occlusions (CTOs) are common in patients with peripheral arterial disease (PAD). This study aimed to examine the feasibility and reliability of a CTO induced by a thin biodegradable polymer (polyglycolic acid) coated copper stent in a porcine femoral artery. Novel thin biodegradable polymer coated copper stents (9 mm long) were crimped on an angioplasty balloon (4.5 mm diameter × 12 mm length) and inserted into the femoral artery. Histopathologic analysis was performed 35 days after stenting. In five of six stented femoral arteries, severe in-stent restenosis and total occlusion with collateral circulation were observed without adverse effects such as acute stent thrombosis, leg necrosis, or death at 5 weeks. Fibrous tissue deposition, small vascular channels, calcification, and inflammatory cells were observed in hematoxylin-eosin, Carstair's, and von Kossa tissue stains; these characteristics were similar to pathological findings associated with CTOs in humans. The neointima volume measured by micro-computed tomography was 93.9 ± 4.04 % in the stented femoral arteries. CTOs were reliably induced by novel thin biodegradable polymer coated copper stents in porcine femoral arteries. Successful induction of CTOs may provide a practical understanding of their formation and application of an interventional device for CTO treatment.

Efficacy and Safety Evaluation of Tacrolimus-Eluting Stent in a Porcine Coronary Artery Model.

BACKGROUND: A drug-eluting stent (DES) is a highly beneficial medical device used to widen or unblock narrowed blood vessels. However, the drugs released by the implantation of DES may hinder the re-endothelialization process, increasing the risk of late thrombosis. We have developed a tacrolimus-eluting stent (TES) that as acts as a potent antiproliferative and immunosuppressive agent, enhancing endothelial regeneration. In addition, we assessed the safety and efficacy of TES through both in vitro and in vivo tests. METHODS: Tacrolimus and Poly(lactic-co-glycolic acid) (PLGA) were applied to the metal stent using electrospinning equipment. The surface morphology of the stent was examined before and after coating using a scanning electron microscope (SEM) and energy dispersive X-rays (EDX). The drug release test was conducted through high-performance liquid chromatography (HPLC). Cell proliferation and migration assays were performed using smooth muscle cells (SMC). The stent was then inserted into the porcine coronary artery and monitored for a duration of 4 weeks. RESULTS: SEM analysis confirmed that the coating surface was uniform. Furthermore, EDX analysis showed that the surface was coated with both polymer and drug components. The HPCL analysis of TCL at a wavelength of 215 nm revealed that the drug was continuously released over a period of 4 weeks. Smooth muscle cell migration was significantly decreased in the tacrolimus group (54.1% ± 11.90%) compared to the non-treated group (90.1% ± 4.86%). In animal experiments, the stenosis rate was significantly reduced in the TES group (29.6% ± 7.93%) compared to the bare metal stent group (41.3% ± 10.18%). Additionally, the fibrin score was found to be lower in the TES group compared to the group treated with a sirolimus-eluting stent (SES). CONCLUSION: Similar to SES, TES reduces neointimal proliferation in a porcine coronary artery model, specifically decreasing the fibrins score. Therefore, tacrolimus could be considered a promising drug for reducing restenosis and thrombosis.