OBJECTIVE: To evaluate the primary stability of different shaped miniscrews through the acquisition of data regarding maximum insertion torque, pullout force, and a radiodiagnosic evaluation of bone characteristics. MATERIALS AND METHODS: Sixty fresh porcine bone samples were scanned by computed tomography (CT) and cone-beam computed tomography (CBCT). By means of a dedicated software, CT and CBCT images were analysed to measure the insertion-site cortical thickness, cortical density, and marrow bone density. Sixty miniscrews of 12 different types were implanted with no predrilling pilot hole in the bone samples. Every device was tightened by means of a digital torque screwdriver and torque data were collected. Subsequently, pullout tests were performed. Spearman and Pearson correlations were employed to compare any relationship between continuous variables. RESULTS: Different types of miniscrews did not show statistically significant differences in their torque value (P = 0.595), instead a significant difference was revealed by considering their load measures (P = 0.039). Cortical bone thickness resulted strongly correlated both with value of load (P < 0.001), and modestly with torque measures (P = 0.004). A strong positive correlation was found between CT and CBCT both for cortical density (P < 0.001) and marrow bone density (P < 0.001). CONCLUSION: Bone characteristics play the major role in miniscrews primary stability.
Asunto(s)
Tornillos Óseos , Métodos de Anclaje en Ortodoncia/instrumentación , Diseño de Aparato Ortodóncico , Animales , Densidad Ósea/fisiología , Médula Ósea/anatomía & histología , Médula Ósea/diagnóstico por imagen , Interfase Hueso-Implante/anatomía & histología , Interfase Hueso-Implante/diagnóstico por imagen , Tomografía Computarizada de Haz Cónico/métodos , Análisis del Estrés Dental , Procesamiento de Imagen Asistido por Computador/métodos , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Miniaturización , Costillas/anatomía & histología , Costillas/diagnóstico por imagen , Estrés Mecánico , Porcinos , Tomografía Computarizada por Rayos X/métodos , TorqueRESUMEN
The concept of personalized medicine and overcoming healthcare inequalities have become extremely popular in recent decades. Polymers can support cost reductions, the simplicity of customized printing processes, and possible future wide-scale expansion. Polymers with ß-tricalcium phosphate (TCP) are well known for their synergy with oral tissues and their ability to induce osteoconductivity. However, poor information exists concerning their properties after the printing process and whether they can maintain an unaffected biological role. Poly(ε-caprolactone) (PCL) polymer and PCL compounded with TCP 20% composite were printed with a Prusa Mini-LCD-®3D printer. Samples were sterilised by immersion in a 2% peracetic acid solution. Sample analyses were performed using infrared-spectroscopy and statical mechanical tests. Biocompatibility tests, such as cell adhesion on the substrate, evaluations of the metabolic activity of viable cells on substrates, and F-actin labelling, followed by FilaQuant-Software were performed using a MC3T3-E1 pre-osteoblasts line. PCL+ß-TCP-20% composite is satisfactory for commercial 3D printing and appears suitable to sustain an ISO14937:200937 sterilization procedure. In addition, the proper actin cytoskeleton rearrangement clearly shows their biocompatibility as well as their ability to favour osteoblast adhesion, which is a pivotal condition for cell proliferation and differentiation.
RESUMEN
As highlighted by the 'Global Burden of Disease Study 2019' conducted by the World Health Organization, ensuring fair access to medical care through affordable and targeted treatments remains crucial for an ethical global healthcare system. Given the escalating demand for advanced and urgently needed solutions in regenerative bone procedures, the critical role of biopolymers emerges as a paramount necessity, offering a groundbreaking avenue to address pressing medical needs and revolutionize the landscape of bone regeneration therapies. Polymers emerge as excellent solutions due to their versatility, making them reliable materials for 3D printing. The development and widespread adoption of this technology would impact production costs and enhance access to related healthcare services. For instance, in dentistry, the use of commercial polymers blended with ß-tricalcium phosphate (TCP) is driven by the need to print a standardized product with osteoconductive features. However, modernization is required to bridge the gap between biomaterial innovation and the ability to print them through commercial printing devices. Here we showed, for the first time, the metabolic behavior and the lineage commitment of bone marrow-derived multipotent mesenchymal cells (MSCs) on the 3D-printed substrates poly(e-caprolactone) combined with 20% tricalcium phosphate (PCL + 20% ß-TCP) and L-polylactic acid (PLLA) combined with 10% hydroxyapatite (PLLA + 10% HA). Although there are limitations in printing additive-enriched polymers with a predictable and short half-life, the tested 3D-printed biomaterials were highly efficient in supporting osteoinductivity. Indeed, considering different temporal sequences, both 3D-printed biomaterials resulted as optimal scaffolds for MSCs' commitment toward mature bone cells. Of interest, PLLA + 10% HA substrates hold the confirmation as the finest material for osteoinduction of MSCs.
RESUMEN
Treatment of postsurgical infections, associated with orthopedic surgeries, has been a major concern for orthopedics. Several strategies including systematic and local administration of antibiotics have been proposed to this regard. The present work focused on fabricating alginate (Alg) modified brushite (Bru) cements, which could address osteogeneration and local antibiotic demands. To find the proper method of drug incorporation, Gentamicin sulfate (Gen) was loaded into the samples in the form of solution or powder. Several characterization tests including compression test, morphology, cytotoxicity, and cell adhesion assays were carried out to determine the proper concentration of Alg as a modifier of the Bru cement. The results indicated that addition of 1 wt% Alg led to superior mechanical and biological properties of the cement. Moreover, Alg addition changed the morphology of the cement from plate and needle-like structures to petal-like structure. Fourier transform infrared spectroscopy results confirmed the successful loading of Gen on the cements, specifically when Gen solution was used, and X-Ray Diffractometer result indicated that Gen caused a decrease in crystalline size. Furthermore, thermal analysis revealed that Gen-loaded sample had more stable structure as the transformation temperature slightly shifted to a higher one. The stability study confirmed the chemical stability and adequate mechanical performance of the cements within 1 month of soaking time. Finally, the addition of Alg has a positive impact on the release behavior at low concentration of Gen solution so that 20% decrease within 2 weeks of release experiment was remarkably detected.
Asunto(s)
Alginatos/química , Antibacterianos , Cementos para Huesos/química , Fosfatos de Calcio/química , Gentamicinas , Ensayo de Materiales , Osteoblastos/metabolismo , Antibacterianos/química , Antibacterianos/farmacocinética , Antibacterianos/farmacología , Línea Celular , Gentamicinas/química , Gentamicinas/farmacocinética , Gentamicinas/farmacología , Humanos , Osteoblastos/citologíaRESUMEN
OBJECTIVES: The aim of the present study was to investigate the mechanical characteristics of dental implant frameworks made of unidirectional carbon fiber composite (UF) and to compare them with those provided by multidirectional carbon fiber composite (IF). METHODS: 8 identical UF samples were used. The samples were initially evaluated by optical microscope and SEM then non-destructive and destructive mechanical tests were performed on 4 samples in order to evaluate dynamic, static elastic modulus, wettability and ultimate strength. The outcomes were compared with those of IF samples tested following the same protocol - data reported in a previous published paper. The remaining 4 samples were aged for 60â¯days in isotonic saline solution at 37⯰C simulating the human saliva. The same tests reported before were performed on the aged samples. RESULTS: The dynamic elastic modulus was lower for UF (78.1â¯GPa for UF vs. 92.2â¯GPa for IF) as well as the static elastic modulus (71.0â¯GPa for UF vs. 84.5â¯GPa for IF). The ultimate strength value was 582â¯MPa for the IF samples and 700â¯MPa for the UF. The aging process of the UF samples did not show any appreciable variation, with small differences that falls within the experimental error. SIGNIFICANCE: Unidirectional carbon fiber-reinforced composite appears suitable for the fabrication of frameworks for implant-supported full-arch dentures. The dynamic elastic modulus was higher for UF while the static elastic modulus was higher for IF. The aging process seems not able to significantly alter the mechanical properties of the material. Further research is needed to evaluate the clinical significance of such outcomes.
Asunto(s)
Fibra de Carbono/química , Implantes Dentales , Módulo de Elasticidad , Polímeros/química , HumectabilidadRESUMEN
PURPOSE: Torque control in lingual orthodontics is key to obtain optimal esthetic results. The aim of this in vitro experimental study was to verify the efficiency of the ligature-archwire-slot system in torque control using a customized lingual appliance. METHODS: An idealized cast with eight extracted human teeth was created and a set of customized lingual brackets was obtained. Tests were performed with the following wires: 0.016â³â¯× 0.022â³ nickel-titanium (NiTi), 0.016â³â¯× 0.024â³ stainless steel (SS), 0.017â³â¯× 0.025â³ ßIII titanium (ßIIITi), 0.0182â³â¯× 0.0182â³ ßIIITi, 0.018â³â¯× 0.025â³ SS, 0.018â³â¯× 0.025â³ NiTi, 0.018â³â¯× 0.025â³ ßIIITi, and three types of ligatures were tested using a universal testing machine to calculate the efficiency in torque control. A blind statistical analysis was performed. RESULTS: Based on post hoc multiple comparisons, differences were found for two of the three ligatures when using the 0.016â³â¯× 0.022â³ NiTi wires (pâ¯< 0.001 for both ligatures). When considering all ligatures, 0.018â³â¯× 0.025â³ SS and 0.018â³â¯× 0.025â³ ßIIITi were significantly different from all other wires (pâ¯< 0.001 in all cases). With a moment of 5â¯Nmm, the 0.016â³â¯× 0.022â³ NiTi wire developed median angles of 26.7, 29.8, and 38.7° with the three ligatures, respectively, while the 0.018â³â¯× 0.025â³ SS developed median angles of 12.9, 10.7, and 12.7°, respectively. CONCLUSIONS: The ligature type and geometry did not affect the efficiency of torque control, except for the 0.016â³â¯× 0.022â³ NiTi wire. The wires generating the greatest moments were the 0.018â³â¯× 0.025â³ SS and 0.018â³â¯× 0.025â³ ßIIITi.
Asunto(s)
Soportes Ortodóncicos , Alambres para Ortodoncia , Aleaciones Dentales , Análisis del Estrés Dental , Estética Dental , Humanos , Ensayo de Materiales , Diseño de Aparato Ortodóncico , Titanio , TorqueRESUMEN
A novel green method for graphene oxide (GO) reduction via ascorbic acid has been adopted to realize bio-friendly reduced graphene oxide (RGO)/polycaprolactone (PCL) nanofibrous meshes, as substrates for bone tissue engineering applications. PCL fibrous mats enriched with either RGO or GO (0.25â¯wt%) were fabricated to recapitulate the fibrillar structure of the bone extracellular matrix (ECM) and the effects of RGO incorporation on the structural proprieties, biomechanics and bioactivity of the nano-composites meshes were evaluated. RGO/PCL fibrous meshes displayed superior mechanical properties (i.e. Young's Modulus and ultimate tensile strength) besides supporting noticeably improved cell adhesion, spreading and proliferation of fibroblasts and osteoblast-like cell lines. Furthermore, RGO-based electrospun substrates enhanced in vitro calcium deposition in the ECM produced by osteoblast-like cells, which was paralleled, in human mesenchymal stem cells grown onto the same substrates, by an increased expression of the osteogenic markers mandatory for mineralization. In this respect, the capability of graphene-based materials to adsorb osteogenic factors cooperates synergically with the rougher surface of RGO/PCL-based materials, evidenced by AFM analysis, to ignite mineralization of the neodeposited matrix and to promote the osteogenic commitment of the cultured cell in the surrounding microenvironment.
Asunto(s)
Materiales Biomiméticos/química , Calcificación Fisiológica , Diferenciación Celular , Fibroblastos/metabolismo , Grafito/química , Nanofibras/química , Osteoblastos/metabolismo , Osteogénesis , Ingeniería de Tejidos , Animales , Huesos/citología , Huesos/metabolismo , Fibroblastos/citología , Ratones , Células 3T3 NIH , Osteoblastos/citología , Oxidación-Reducción , PoliésteresRESUMEN
BACKGROUND: The clinical success of orthodontic miniscrews is strictly related to primary stability, which depends on bone viscoelastic properties too. In this study, we evaluated the short time mechanical response of native bone to miniscrews, by a laboratory test based on dynamic loading. METHODS: Thirty-six segments of porcine ribs were first scanned by cone-beam computerized tomography to obtain insertion-site cortical thickness, cortical and marrow bone density. Twelve different types of miniscrews were implanted in the bone samples to evaluate the elastic compliance of the implants in response to a point force applied at the screw head normally to the screw axis. The compliance was measured dynamically in a Dynamic Mechanical Analysis apparatus as the Fourier Response Function between the signals of displacement and force. The measurements were repeated in five days successive to the insertion of the miniscrew. FINDINGS: The elastic compliance was positively related to observation timepoints, but it was not related neither to the screw type nor to the value of the insertion torque. INTERPRETATION: Stability behavior is significantly related to the short time response of native bone rather than to the screw design or the insertion torque values.
Asunto(s)
Huesos , Ensayo de Materiales , Fenómenos Mecánicos , Ortodoncia/instrumentación , Animales , Estrés Mecánico , Porcinos , TorqueRESUMEN
OBJECTIVES: The aim of the present study was to investigate the biocompatibility and mechanical characteristics of dental implant frameworks made of carbon fiber composite. METHODS: The biocompatibility of intact samples and fragments was evaluated by cell count and MTT test according to EN-ISO 10993-5:2009 directions. Destructive and non-destructive mechanical tests were performed in order to evaluate: porosity, static and dynamic elastic modulus of carbon fiber samples. These tests were conducted on different batches of samples manufactured by different dental technicians. The samples were evaluated by optical microscope and by SEM. A compression test was performed to compare complete implant-supported fixed dentures, provided with a metal or carbon fiber framework. RESULTS: Carbon fiber intact and fragmented samples showed optimal biocompatibility. Manufacture technique strongly influenced the mechanical characteristics of fiber-reinforced composite materials. The implant-supported full-arch fixed denture provided with a carbon fiber framework, showed a yield strength comparable to the implant-supported full-arch fixed denture, provided with a metal framework. SIGNIFICANCE: Carbon fiber-reinforced composites demonstrated optimal biocompatibility and mechanical characteristics. They appear suitable for the fabrication of frameworks for implant-supported full-arch dentures. Great attention must be paid to manufacture technique as it strongly affects the material mechanical characteristics.