Settleability and dewaterability of sewage sludge with modified diatomite.

In this study, cationic polyacrylamide (CPAM)-modified diatomite and cetyl trimethyl ammonium bromide (CTAB)-modified diatomite were synthesized and used as conditioners for sewage sludge dewatering. The effects of these two types of modified diatomite on the dewaterability and settling performance of the activated sludge were studied. The mechanisms of the two modified diatomite types in the activated sludge system were elucidated. The efficiency of the CPAM-modified diatomite was better than that of the CTAB-modified diatomite in improving the settleability and dewaterability of sludge. The results indicated that specific resistance to filtration (SRF) was decreased from 8.52 × 1012 to 0.92 × 1012 m/Kg, and the water content in the remaining sludge cake after pumping filtration was decreased from 92.2 to 68.1% by adding 0.4% of CPAM-modified diatomite and pH = 3.5, which resulted in excellent sludge settling of activated sludge. Further studies showed that the polymer/surfactant adsorbed in diatomite increased sludge dewaterability and improved the sedimentation rate owing to stripping extracellular polymeric substances (EPS) and damaging the internal structure of the sludge, leading to sludge conduce bound water release. According to scanning electron microscope (SEM) images, the two types of modified diatomite powder maintained the porous structure and showed a more complete and uniform structure compared to natural diatomite.

Synthesis and Characterization of g-C3N4/Ag3PO4/TiO2/PVDF Membrane with Remarkable Self-Cleaning Properties for Rhodamine B Removal.

g-C3N4/Ag3PO4/TiO2 nanocomposite materials were loaded onto a polyvinylidene fluoride (PVDF) membrane using a phase inversion method to obtain a photocatalytic flat membrane for dye removal. The morphology, structure, and photocatalytic activity of the g-C3N4/Ag3PO4/TiO2 nanoparticles and composite membrane were evaluated. The g-C3N4/Ag3PO4/TiO2/PVDF membrane exhibited superior morphology, hydrophilic properties, and antifouling performance compared with the raw PVDF membrane. Four-stage filtration was performed to evaluate the self-cleaning and antifouling capacity of the g-C3N4/Ag3PO4/TiO2/PVDF membrane. Upon irradiating the composite membrane with visible light for 30 min, its irreversible fouling resistance (Rir) was low (9%), and its flux recovery rate (FRR) was high (71.0%) after five filtration cycles. The removal rate of rhodamine B (RhB) from the composite membrane under visible light irradiation reached 98.1% owing to the high photocatalytic activity of the membrane, which was superior to that of raw PVDF membrane (42.5%). A mechanism of photocatalytic composite membranes for RhB degradation was proposed. Therefore, this study is expected to broaden prospects in the field of membrane filtration technology.