RESUMEN
Autologous bone grafts, used mainly in extensive bone loss, are considered the gold standard treatment in regenerative medicine, but still have limitations mainly in relation to the amount of bone available, donor area, morbidity and creation of additional surgical area. This fact encourages tissue engineering in relation to the need to develop new biomaterials, from sources other than the individual himself. Therefore, the present study aimed to investigate the effects of an elastin and collagen matrix on the bone repair process in critical size defects in rat calvaria. The animals (Wistar rats, n = 30) were submitted to a surgical procedure to create the bone defect and were divided into three groups: Control Group (CG, n = 10), defects filled with blood clot; E24/37 Group (E24/37, n = 10), defects filled with bovine elastin matrix hydrolyzed for 24 h at 37 °C and C24/25 Group (C24/25, n = 10), defects filled with porcine collagen matrix hydrolyzed for 24 h at 25 °C. Macroscopic and radiographic analyses demonstrated the absence of inflammatory signs and infection. Microtomographical 2D and 3D images showed centripetal bone growth and restricted margins of the bone defect. Histologically, the images confirmed the pattern of bone deposition at the margins of the remaining bone and without complete closure by bone tissue. In the morphometric analysis, the groups E24/37 and C24/25 (13.68 ± 1.44; 53.20 ± 4.47, respectively) showed statistically significant differences in relation to the CG (5.86 ± 2.87). It was concluded that the matrices used as scaffolds are biocompatible and increase the formation of new bone in a critical size defect, with greater formation in the polymer derived from the intestinal serous layer of porcine origin (C24/25).
Asunto(s)
Biopolímeros/química , Regeneración Ósea/fisiología , Andamios del Tejido/química , Animales , Materiales Biocompatibles/química , Birrefringencia , Matriz Ósea/química , Matriz Ósea/fisiología , Remodelación Ósea/fisiología , Sustitutos de Huesos/química , Calcificación Fisiológica/fisiología , Bovinos , Colágeno/química , Colágeno/metabolismo , Elastina/química , Elastina/metabolismo , Imagenología Tridimensional , Masculino , Ensayo de Materiales , Ratas , Ratas Wistar , Cráneo/diagnóstico por imagen , Cráneo/lesiones , Cráneo/fisiología , Porcinos , Ingeniería de Tejidos/métodos , Microtomografía por Rayos XRESUMEN
The use of biomaterials in medical and dental areas has become increasingly important due to the need to restore areas with bone loss or defects. This study analyzed the use of a new elastin polymer matrix combined with Bone Morphogenetic Protein for the repair of cranial defects in rats. Thirty rats were divided into five groups: control (C) defect without graft, E24 (defect filled with elastin matrix submitted to alkaline hydrolysis at 50°C for 24 h), E24/BMP (defect filled with elastin matrix treated at 50°C for 24 h plus BMP), E96 (defect filled with elastin matrix treated at 37°C for 96 h) and E96/BMP (defect filled with elastin matrix treated at 37°C for 96 h plus BMP). The animals were killed after 6 weeks. In the histological and microtomographic analysis, all groups showed bone growth from the defect margins remaining in this region without a marked inflammatory process, but in the E96/BMP group the lamellae were thicker and the collagen fibers more organized. Histometrically, the same group presented higher percentage of new formation (43.25 ± 3.72) in relation to the other groups. It was concluded that the support and delivery system formed by the elastin matrix associated with BMPs had a positive effect on the bone repair process.
RESUMEN
Tissue engineering has special interest in bone tissue aiming at future medical applications Studies have focused on recombinant human bone morphogenetic protein-2 (rhBMP-2) and natural latex proteins due to the osteogenic properties of rhBMP-2 and the angiogenic characteristic of fraction 1 protein (P-1) extracted from the rubber tree Hevea brasiliensis. Furthermore, heterologous fibrin sealant (FS) has been shown as a promising alternative in regenerative therapies. The aim of this study was to evaluate these substances for the repair of bone defects in rats. A bone defect measuring 3mm in diameter was created in the proximal metaphysis of the left tibia of 60 rats and was implanted with rhBMP-2 or P-1 in combination with a new heterologous FS derived from snake venom. The animals were divided into six groups: control (unfilled bone defect), rhBMP-2 (defect filled with 5µg rhBMP-2), P-1 (defect filled with 5µg P-1), FS (defect filled with 8µg FS), FS/rhBMP-2 (defect filled with 8µg FS and 5µg rhBMP-2), FS/P-1 (defect filled with 8µg FS and 5µg P-1). The animals were sacrificed 2 and 6 weeks after surgery. The newly formed bone projected from the margins of the original bone and exhibited trabecular morphology and a disorganized arrangement of osteocyte lacunae. Immunohistochemical analysis showed intense expression of osteocalcin in all groups. Histometric analysis revealed a significant difference in all groups after 2 weeks (p<0.05), except for the rhBMP-2 and FS/rhBMP-2 groups (p>0.05). A statistically significant difference (p<0.05) was observed in all groups after 6 weeks in relation to the volume of newly formed bone in the surgical area. In conclusion, the new heterologous fibrin sealant was found to be biocompatible and the combination with rhBMP-2 showed the highest osteogenic and osteoconductive capacity for bone healing. These findings suggest a promising application of this combination in the regeneration surgery.