More lipophilic dialkyldiamine-based diazeniumdiolates: synthesis, characterization, and application in preparing thromboresistant nitric oxide release polymeric coatings.

The synthesis, characterization, and biomedical application in preparing more thromboresistant polymeric coatings for a series of lipophilic dialkyldiamine-based diazeniumdiolatesare described. Dialkylhexamethylenediamine diazeniumdiolates of the form RN[N(O)NO](-)(CH(2))(6)NH(2)(+)R, where R = CH(3), CH(2)CH(3), (CH(2))(2)CH(3), (CH(2))(3)CH(3), (CH(2))(4)CH(3,) (CH(2))(5)CH(3), and (CH(2))(11)CH(3), are prepared via reaction of the corresponding diamine with NO. The more lipophilic diazeniumdiolates [e.g., R = (CH(2))(3)CH(3)] can be incorporated into hydrophobic polymeric films (e.g., plasticized PVC), and the resulting materials release NO for extended periods of time upon exposure to PBS buffer. The mechanism of NO release from these films is examined in detail. More stable initial NO release can be achieved by adding lipophilic anionic species (e.g., tetraphenylborate derivative) to the polymeric material to buffer the activity of protons within the organic phase. It is shown that the use of these new lipophilic NO-donors in polymers provides the ability to tailor NO release rates for a variety of medical applications. As an example, polymers doped with N,N'-dibutylhexamethylenediamine diazeniumdiolate and a tetraphenylborate derivative are employed as coatings for vascular grafts in sheep. The NO release grafts exhibited enhanced performance and had an average 95% thrombus-free surface area compared to 42% for the corresponding control grafts when examined after 21d of implantation.

Nitric oxide releasing silicone rubbers with improved blood compatibility: preparation, characterization, and in vivo evaluation.

Nitric oxide (NO) releasing silicone rubbers (SR) are prepared via a three-step reaction scheme. A diamino triaminoalkyltrimethoxysilane crosslinker is used to vulcanize hydroxyl terminated polydimethylsiloxane (PDMS) in the presence of ambient moisture and a dibutyltin dilaurate catalyst so that the respective diamine triamine groups are covalently linked to the cured SR structure. These amine sites are then diazeniumdiolated, in situ, when the cured SR is reacted with NO at elevated pressure (80 psi). Although nitrite species are also formed during the NO addition reaction, in most cases the diazeniumdiolated polymer is the major product within the final SR matrix. Temperature appears to be the major driving force for the dissociation of the attached diazeniumdiolate moieties, whereas the presence of bulk water bathing the SR materials has only minimal effect on the observed NO release rate owing to the low water uptake of the SR matrices. The resulting SR films/coatings release NO at ambient or physiological temperature for up to 20 d with average fluxes of at least 4 x 10(10) mol x cm(-2) x min(-1) (coating thickness > or = 600 microm) over first 4 h, comparable to the NO fluxes observed from stimulated human endothelial cells. The NO loading and concomitant NO release flux of the SR material are readily adjustable by altering the diamine triamine loading and film/coating thickness. The new NO releasing SR materials are shown to exhibit improved thromboresistance in vivo, as demonstrated via reduced platelet activation on the surface of these polymers when used to coat the inner walls of SR tubings employed for extracorporeal circulation in a rabbit model.

Nitric oxide-releasing fumed silica particles: synthesis, characterization, and biomedical application.

The preparation, characterization, and preliminary biomedical application of various nitric oxide (NO)-releasing fumed silica particles (0.2-0.3 microm) are reported. The tiny NO-releasing particles are synthesized by first tethering alkylamines onto the surface of the silica using amine-containing silylation reagents. These amine groups are then converted to corresponding N-diazeniumdiolate groups via reaction with NO(g) at high pressure in the presence of methoxide bases (e.g., NaOMe). N-Diazeniumdiolate groups were found to form more readily with secondary amino nitrogens than primary amino nitrogens tethered to the silica. Different alkali metal cations of the methoxide bases, however, have little effect on the degree of N-diazeniumdiolate formation. The N-diazeniumdiolate moieties attached on the silica surface undergo a primarily proton-driven dissociation to NO under physiological conditions, with an "apparent" reaction order somewhat greater than 1 owing to local increases in pH at the surface of the particles as free amine groups are generated. The rates of N-diazeniumdiolate dissociation are further related to the parent amine structures and the pH of the soaking buffer. The N-diazeniumdiolate groups also undergo slow thermal dissociation to NO, with zero-order dissociation observed at both -15 and 23 degrees C. It is further shown that the resulting NO-releasing fumed silica particles can be embedded into polymer films to create coatings that are thromboresistant, via the release of NO at fluxes that mimic healthy endothelial cells (EC). For example a polyurethane coating containing 20 wt % of NO-releasing particles prepared with pendant hexane diamine structure (i.e., Sil-2N[6]-N(2)O(2)Na) is shown to exhibit improved surface thromboresistivity (compared to controls) when used to coat the inner walls of extracorporeal circuits (ECC) employed in a rabbit model for extracorporeal blood circulation.

Nitric oxide-releasing biopolymers inhibit thrombus formation in a sheep model of arteriovenous bridge grafts.

OBJECTIVES: Nitric oxide (NO), produced by normal vascular endothelial cells, reduces platelet aggregation and thrombus formation. NO-releasing biopolymers have the potential to prolong vascular graft and stent patency without adverse systemic vasodilation. METHODS: 5-mm polyurethane vascular grafts coated with a polymer containing the NO-donor dialkylhexanediamine diazeniumdiolate were implanted for 21 days in a sheep arteriovenous bridge-graft model. RESULTS: Eighty percent (4/5) of grafts coated with the NO-releasing polymer remained patent through the 21 day implantation period, compared to fifty percent (2/4) of sham-coated grafts and no (0/3) uncoated grafts. Thrombus-free surface area (+/-SEM) of explanted grafts was significantly increased in NO-donor coated grafts (98.2% +/- 0.9%) compared with sham-coated (79.2% +/- 8.6%) and uncoated (47.2% +/- 5.4%) grafts ( P = .00046). Examination of the graft surface showed no adherent thrombus or platelets and no inflammatory cell infiltration in NO-donor coated grafts, while control grafts showed adherent complex surface thrombus consisting of red blood cells in an amorphous fibrin matrix, as well as significant red blood cell and inflammatory cell infiltration into the graft wall. CONCLUSION: In this study we determined that local NO release from the luminal surface of prosthetic vascular grafts can reduce thrombus formation and prolong patency in a model of prosthetic arteriovenous bridge grafts in adult sheep. These findings may translate into improved function and improved primary patency rates in small-diameter prosthetic vascular grafts.