Strong and ultrafast stimulus-healable lignin-based composite elastomers with excellent adhesion properties.

With the increased environmental issues, advanced high-performance and multifunctional polymeric materials derived from biomass have tremendous attention due to the great potential to replace their traditional petroleum-based counterparts. In this work, a series of lignin graft copolymers, lignin-graft-poly(n-butyl acrylate-co-acrylic acid) (Lig-g-P(BA-co-AA)), were rationally prepared via reversible addition-fragmentation chain transfer (RAFT) polymerization. These lignin-based copolymers demonstrate good thermal stability and tunable glass transition temperature (Tg) values. The mechanical performance, including tensile strength, extensibility, Young's modulus, and toughness can be facilely adjusted by the BA/AA feed ratio and lignin content during polymerization. Owing to the extraordinary photothermal conversion ability of lignin, the Lig-B550 copolymer, containing 11.8 wt% lignin content, shows excellent stimulus-healing behavior within 1 min with a 97.1 % healing efficiency under near-infrared (NIR) laser irradiation. Moreover, the Lig-g-P(BA-co-AA) copolymers exhibit remarkable adhesion property, broadening their potential applications in the adhesive area. This grafting strategy is versatile and efficient, conferring the resultant lignin-based composite elastomers with dramatically enhanced mechanical properties and unprecedented photothermal behavior, which can inspire the further development of strong lignin-based sustainable elastomers.

Poly(2-hydroxyethyl methacrylate-co-quaternary ammonium salt chitosan) hydrogel: A potential contact lens material with tear protein deposition resistance and antimicrobial activity.

Tear protein deposition resistance and antimicrobial property are two challenges of conventional poly(2-hydroxyethyl methacrylate) (pHEMA) contact lenses. In this work, we developed a poly(2-hydroxyethyl methacrylate-co-quaternary ammonium salt chitosan) hydrogel, named as p(HEMA-co-mHACC) hydrogel, using acryloyl HACC (mHACC) as a macromolecular crosslinker. With increasing the acryloyl substitution degree (14-29%) or mHACC content (2-11%), the hydrogel showed an enhanced tensile strength (432-986 kPa) and Young's modulus (360-1158 kPa), a decreased elongation at break (242-84%), and an increased visible light transmittance (0-95%). At an optimal acryloyl substitution degree of 26%, with the increase of mHACC content from 2% to 11%, p(HEMA-co-mHACC) hydrogel presented a decreased water contact angle from 84.6 to 55.3 degree, an increased equilibrium water content from 38% to 45%, and an enhanced oxygen permeability from 8.5 to 13.5 barrer. Due to the enhancement in surface hydrophilicity and electropositivity, p(HEMA-co-mHACC) hydrogel remarkably reduced the deposition of lysozyme, but little affected the adsorption of BSA, depending on the hydrophilic/hydrophobic and electrostatic interactions. The antimicrobial test against Staphylococcus aureus and Escherichia coli showed that p(HEMA-co-mHACC) hydrogel presented an 8-32 times higher germicidal ability than pHEMA hydrogel, indicative of a better antimicrobial activity. The in vitro cell culture of mouse NIH3T3 fibroblasts and immortalized human keratinocytes showed that p(HEMA-co-mHACC) hydrogel was non-toxic. Thus, p(HEMA-co-mHACC) hydrogel with tear protein deposition resistance and antimicrobial activity is a potential candidate for contact lenses.