RESUMEN
CaCO3 nanoparticles of around 60 nm were obtained by a co-precipitation method and used as filler to prepare low-density polyethylene (LDPE) composites by melt blending. The nanoparticles were also organically modified with oleic acid (O-CaCO3) in order to improve their interaction with the LDPE matrix. By adding 3 and 5 wt% of nanofillers, the mechanical properties under tensile conditions of the polymer matrix improved around 29%. The pure LDPE sample and the nanocomposites with 5 wt% CaCO3 were photoaged by ultraviolet (UV) irradiation during 35 days and the carbonyl index (CI), degree of crystallinity (χc), and Young's modulus were measured at different times. After photoaging, the LDPE/CaCO3 nanocomposites increased the percent crystallinity (χc), the CI, and Young's modulus as compared to the pure polymer. Moreover, the viscosity of the photoaged nanocomposite was lower than that of photoaged pure LDPE, while scanning electron microscopy (SEM) analysis showed that after photoaging the nanocomposites presented cavities around the nanoparticles. These difference showed that the presence of CaCO3 nanoparticles accelerate the photo-degradation of the polymer matrix. Our results show that the addition of CaCO3 nanoparticles into an LDPE polymer matrix allows future developments of more sustainable polyethylene materials that could be applied as films in agriculture. These LDPE-CaCO3 nanocomposites open the opportunity to improve the low degradation of the LDPE without sacrificing the polymer's behavior, allowing future development of novel eco-friendly polymers.
Asunto(s)
Carbonato de Calcio/química , Ácido Oléico/química , Polietileno/química , Módulo de Elasticidad , Nanocompuestos/química , Nanopartículas/química , FotólisisRESUMEN
Metals, such as copper and silver, can be extremely toxic to bacteria at exceptionally low concentrations. Because of this biocidal activity, metals have been widely used as antimicrobial agents in a multitude of applications related with agriculture, healthcare, and the industry in general. Unlike other antimicrobial agents, metals are stable under conditions currently found in the industry allowing their use as additives. Today these metal based additives are found as: particles, ions absorbed/exchanged in different carriers, salts, hybrid structures, etc. One recent route to further extend the antimicrobial applications of these metals is by their incorporation as nanoparticles into polymer matrices. These polymer/metal nanocomposites can be prepared by several routes such as in situ synthesis of the nanoparticle within a hydrogel or direct addition of the metal nanofiller into a thermoplastic matrix. The objective of the present review is to show examples of polymer/metal composites designed to have antimicrobial activities, with a special focus on copper and silver metal nanoparticles and their mechanisms.
Asunto(s)
Antiinfecciosos/farmacología , Nanopartículas del Metal/química , Polímeros/farmacología , Pruebas de Sensibilidad Microbiana , Nanocompuestos/químicaRESUMEN
Electrospun scaffolds based on poly(l-lactic acid) (PLLA) with bioglass (n-BG) and zinc oxide (n-ZnO), and mixture of both, were developed to design bifunctional biomaterials with enhanced bioactive and biocidal properties. The presence of n-BG increased the fiber diameter of the pure PLA from 1.5 ± 0.3 µm to 3.0 ± 0.8 µm for 20 wt%. ZnO and the mixed nanoparticles did not significantly affect the morphology. The mechanical properties decreased with the presence of nanoparticles. Scaffolds based on PLA/n-BG promoted hydroxyapatite (HA) formation in simulated body fluid (SBF) that was inhibited with the presence of ZnO. Notably, mixed particles produced bioactivity although at longer times. The incorporation of n-ZnO produced a biocidal capacity against S. aureus in the polymeric scaffold, reaching a viability reduction of 60 % after 6 h of exposure. When both types of nanoparticles were combined, the bacterial viability reduction was 30 %. Pure PLA scaffolds and the composites with n-BG showed good ST-2 bone marrow-derived cell line viability, scaffolds with n-BG (pure or mixture) presented lower viability. Results validated the use of both n-BG and n-ZnO fillers for the development of novel bifunctional PLA-based scaffolds with both bioactive and biocidal properties for bone tissue engineering applications.
Asunto(s)
Nanopartículas , Óxido de Zinc , Ingeniería de Tejidos/métodos , Andamios del Tejido , Staphylococcus aureus , PoliésteresRESUMEN
Over the last three decades but more particularly during the last 5 years, auxetic mechanical metamaterials constructed from precisely architected polymer-based materials have attracted considerable attention due to their fascinating mechanical properties. These materials present a negative Poisson's ratio and therefore unusual mechanical behavior, which has resulted in enhanced static modulus, energy adsorption, and shear resistance, as compared with the bulk properties of polymers. Novel advanced polymer processing and fabrication techniques, and in particular additive manufacturing, allow one to design complex and customizable polymer architectures that are particularly relevant to fabricate auxetic mechanical metamaterials. Although these metamaterials exhibit exotic mechanical properties with potential applications in several engineering fields, biomedical applications seem to be one of the most relevant with a growing number of articles published over recent years. As a result, special focus is needed to understand the potential of these structures and foster theoretical and experimental investigations on the potential benefits of the unusual mechanical properties of these materials on the way to high performance biomedical applications. The present Review provides up to date information on the recent progress of polymer-based auxetic mechanical metamaterials mainly fabricated using additive manufacturing methods with a special focus toward biomedical applications including tissue engineering as well as medical devices including stents and sensors.
Asunto(s)
Fenómenos Biomecánicos , Ingeniería Biomédica , Polímeros , Animales , Ingeniería Biomédica/métodos , Materiales Biomiméticos , Equipos y Suministros , Humanos , Polímeros/química , Ingeniería de TejidosRESUMEN
Electrospun fibers of poly (lactic acid) (PLA) containing 10 and 20 wt% of bioactive glass (n-BG) and magnesium oxide (n-MgO) nanoparticles of ca. 27 and 23 nm respectively, were prepared toward to application in bone tissue engineering. The addition of both nanoparticles into the PLA will produce a synergic effect increasing its bioactivity and antimicrobial behavior. Neat PLA scaffold and the composites with MgO showed an average fiber diameter of 1.7 ± 0.6 µm, PLA/n-BG and PLA/n-BG/n-MgO fibers presented a significant diameter increase reaching values of ca. 3.1 ± 0.8 µm. Young's modulus of the electrospun scaffolds was affected by the direct presence of the particle and scaffold morphologies. All the composites having n-BG presented bioactivity through the precipitation of hydroxyapatite structures on the surface. Although n-MgO did not add bioactivity to the PLA fibers, they were able to render antimicrobial characteristics reducing the S. aureus viability around 30%, although an effect on E. coli strain was not observed. PLA/n-BG nanocomposites did not display any significant antimicrobial behavior. The different composites increased the alkaline phosphatase (ALP) expression as compared with pure PLA barely affecting the cell viability, meaning a good osteoblastic phenotype expression capacity, with PLA/n-BG presenting the highest osteoblastic expression.
Asunto(s)
Óxido de Magnesio , Nanopartículas , Materiales Biocompatibles/química , Materiales Biocompatibles/farmacología , Regeneración Ósea , Escherichia coli/metabolismo , Vidrio/química , Ácido Láctico/química , Óxido de Magnesio/farmacología , Nanopartículas/química , Poliésteres/química , Staphylococcus aureus/metabolismo , Ingeniería de Tejidos , Andamios del Tejido/químicaRESUMEN
Direct ink writing (DIW) is a promising extrusion-based 3D printing technology, which employs an ink-deposition nozzle to fabricate 3D scaffold structures with customizable ink formulations for tissue engineering applications. However, determining the optimal DIW process parameters such as temperature, pressure, and speed for the specific ink is essential to achieve high reproducibility of the designed geometry and subsequent mechano-biological performance for different applications, particularly for porous scaffolds of finite sizes (total volume > 1000 mm3) and controlled pore size and porosity. The goal of this study was to evaluate the feasibility of fabricating Polycaprolactone (PCL) and bio-active glass (BG) composite-based 3D scaffolds of finite size using DIW. 3D-scaffolds were fabricated either as cylinders (10 mm diameter; 15 mm height) or cubes (5 × 5 × 5 mm3) with height/width aspect ratios of 1.5 and 1, respectively. A rheological characterization of the PCL-BG inks was performed before printing to determine the optimal printing parameters such as pressure and speed for printing at 110 °C. Microstructural properties of the scaffolds were analyzed in terms of overall scaffold porosity, and in situ pore size assessments in each layer (36 pores/layer; 1764 pores per specimen) during their fabrication. Measured porosity of the fabricated specimens-PCL: x¯ =46.94%, SD = 1.61; PCL-10 wt%BG: x¯ = 48.29%, SD = 5.95; and PCL-20 wt% BG: x¯=50.87%, SD = 2.45-matched well with the designed porosity of 50%. Mean pore sizes-PCL [x¯ = 0.37 mm (SD = 0.03)], PCL-10%BG [x¯ = 0.38 mm (SD = 0.07)] and PCL-20% BG [x¯ = 0.37 mm (SD = 0.04)]-were slightly fairly close to the designed pore size of 0.4 mm. Nevertheless there was a small but consistent, statistically significant (p < 0.0001) decrease in pore size from the first printed layer (PCL: 0.39 mm; PCL-10%BG: 0.4 mm; PCL-20%BG: 0.41 mm) to the last. SEM and micro-CT imaging revealed consistent BG particle distribution across the layers and throughout the specimens. Cell adhesion experiments revealed similar cell adhesion of PCL-20 wt% BG to pure PCL, but significantly better cell proliferation - as inferred from metabolic activity - after 7 days, although a decrease after 14 days was noted. Quasi-static compression tests showed a decrease in compressive yield strength and apparent elastic modulus with increasing BG fraction, which could be attributed to a lack of adequate mechanical bonding between the BG particles and the PCL matrix. The results show that the inks were successfully generated, and the scaffolds were fabricated with high resolution and fidelity despite their relatively large size (>1000 mm3). However, further work is required to understand the mechano-biological interaction between the BG particle additives and the PCL matrix to improve the mechanical and biological properties of the printed structures.
Asunto(s)
Poliésteres , Andamios del Tejido , Poliésteres/química , Impresión Tridimensional , Reproducibilidad de los Resultados , Andamios del Tejido/químicaRESUMEN
Bioglass nanoparticles (n-BGs, 54SiO2 :40CaO:6P2 O5 mol %) with about 27 nm diameter were synthesized by the sol-gel method and incorporated into a poly(lactic acid) (PLA) matrix by the melting process in order to obtain nanocomposites with filler contents of 5, 10, and 25 wt %. Our results showed that during the cooling scan, the crystallization temperature (Tc ) of the PLA/n-BG nanocomposites decreased 13°C as compared to neat PLA. The presence of nanoparticles also decreased the thermal stability of the PLA matrix, as nanocomposites presented up to about 20°C lower degradation temperatures in a nitrogen atmosphere. The presence of n-BG increased the stiffness of the polymer matrix, and for instance the composite with 25 wt % of filler presented about 52.6% higher Young's modulus than neat PLA. n-BG incorporation into PLA increased also the hydrolytic degradation of the polymer over time. When the PLA composites were immersed in simulated body fluid, an apatite layer was formed on their surface, as verified by Fourier transform infrared, X-Ray Diffraction (XRD), and scanning electron microscopy-EDS, showing that the presence of n-BG induced bioactivity on the PLA matrix. Moreover, the viability of cervical uterine adenocarcinoma cells was higher on PLA/n-BG nanocomposite with 25 wt % of filler. The presence of n-BG barely gave an antibacterial effect on the polymer matrix, despite the well-known biocidal properties of these nanoparticles. Our results show that the presence of n-BGs is a proper route for improving the bioactivity of PLA with potential application in tissue engineering.
Asunto(s)
Materiales Biocompatibles/química , Cerámica/química , Nanopartículas/química , Poliésteres/química , Materiales Biocompatibles/farmacología , Supervivencia Celular/efectos de los fármacos , Cerámica/farmacología , Cristalización , Módulo de Elasticidad , Células HeLa , Humanos , Nanocompuestos/química , Poliésteres/farmacologíaRESUMEN
Copper and its alloys are effective antimicrobial surface materials in the laboratory and in clinical trials. Copper has been used in the healthcare setting to reduce environmental contamination, and thus prevent healthcare-associated infections, complementing traditional protocols. The addition of copper nanoparticles to polymer/plastic matrices can also produce antimicrobial materials, as confirmed under laboratory conditions. However, there is a lack of studies validating the antimicrobial effects of these nanocomposite materials in clinical trials. To satisfy this issue, plastic waiting room chairs with embedded metal copper nanoparticles, and metal hospital IV pools coated with an organic paint with nanostructured zeolite/copper particles were produced and tested in a hospital environment. These prototypes were sampled once weekly for 10 weeks and the viable microorganisms were analysed and compared with the copper-free materials. In the waiting rooms, chairs with copper reduced by around 73% the total viable microorganisms present, showing activity regardless of the microorganism tested. Although there were only low levels of microorganisms in the IV pools installed in operating rooms because of rigorous hygiene protocols, samples with copper presented lower total viable microorganisms than unfilled materials. Some results did not have statistical significance because of the low load of microorganisms; however, during at least three weeks the IV pools with copper had reduced levels of microorganisms by a statistically significant 50%. These findings show for the first time the feasibility of utilizing the antimicrobial property of copper by adding nanosized fillers to other materials in a hospital environment.
Asunto(s)
Aleaciones/farmacología , Antibacterianos/farmacología , Cobre/farmacología , Infección Hospitalaria/prevención & control , Control de Infecciones/métodos , Nanopartículas del Metal , Nanocompuestos , Infección Hospitalaria/tratamiento farmacológico , Infección Hospitalaria/microbiología , Equipos y Suministros de Hospitales/microbiología , Hospitales , HumanosRESUMEN
Poly(lactic acid) (PLA) is a biodegradable and biocompatible polyester widely used in biomedical applications. Unfortunately, this biomaterial suffers from some shortcomings related with the absence of both bioactivity and antibacterial capacity. In this work, composites of PLA with either graphene oxide (GO) or thermally reduced graphene oxide (TrGO) were prepared by melt mixing to overcome these limitations. PLA composites with both GO and TrGO inhibited the attachment and proliferation of Escherichia coli and Staphylococcus aureus bacteria depending on the kind and amount of filler. Noteworthy, it is shown that by applying an electrical stimulus to the percolated PLA/TrGO, the antibacterial behavior can be dramatically increased. MTT analysis showed that while all the PLA/GO composites were more cytocompatible to osteoblast-like cells (SaOS-2) than pure PLA, only low content of TrGO was able to increase this property. These tendencies were related with changes in the surface properties of the resulting polymer composites, such as polarity and roughness. In this way, the addition of GO and TrGO into a PLA matrix allows the development of multifunctional composites for potential applications in biomedicine. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 106A: 1051-1060, 2018.
Asunto(s)
Antibacterianos/farmacología , Materiales Biocompatibles/farmacología , Grafito/química , Poliésteres/química , Línea Celular Tumoral , Módulo de Elasticidad , Conductividad Eléctrica , Estimulación Eléctrica , Escherichia coli/efectos de los fármacos , Humanos , Pruebas de Sensibilidad Microbiana , Nanocompuestos/química , Oxidación-Reducción , Staphylococcus aureus/efectos de los fármacos , Temperatura , Agua/químicaRESUMEN
Novel multifunctional scaffolds for bone regeneration can be developed by incorporation of bioactive glasses (BG) doped with therapeutic and antibacterial metal ions, such as copper (Cu) and zinc (Zn), into a biodegradable polymer. In this context, porous composite materials of biodegradable poly(d, l-lactide) (PDLLA) mixed with sol-gel BG of chemical composition 60SiO2 ; 25CaO; 11Na2 O; and 4P2 O5 (mol %) doped with either 1 mol % of CuO or ZnO, and with both metals, were prepared. The cytocompatibility of the scaffolds on bone marrow stromal cells (ST-2) depended on both, the amount of glass filler and the concentration of metal ion, as evaluated by lactate dehydrogenase (LDH) activity, cell viability (water-soluble tetrazolium salt [WST-8]), and by cell morphology (scanning electron microscopy [SEM]) tests. In particular, scaffolds having a filler content of 10 wt % showed the highest cytocompatibility. In addition, compared to the neat polymer, the scaffolds containing Cu promoted the angiogenesis marker (Vascular endothelial growth factor concentration) to a larger extent while scaffolds containing Zn increased the osteogenesis marker (specific alkaline phosphatase-activity). Noteworthy, the scaffolds with both metal ions showed a combined effect on both properties. Cu- and Zn-doped glasses also provided higher antibacterial capacity to PDLLA-based scaffolds against methicillin-resistant S. aureus bacteria than undoped glass. In combination, our results showed that by a proper addition of Cu- and Zn-doped BG to a PDLLA matrix, multifunctional composite scaffolds with enhanced biological activity can be designed for bone tissue regeneration. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 746-756, 2017.
Asunto(s)
Regeneración Ósea , Cobre/química , Vidrio/química , Poliésteres/química , Polietilenglicoles/química , Andamios del Tejido/química , Zinc/química , Animales , Antibacterianos/química , Línea Celular , Staphylococcus aureus Resistente a Meticilina/crecimiento & desarrollo , RatonesRESUMEN
Metal doping of bioactive glasses based on ternary 60SiO2-36CaO-4P2O5 (58S) and quaternary 60SiO2-25CaO-11Na2O-4P2O5 (NaBG) mol% compositions synthesized using a sol-gel process was analyzed. In particular, the effect of incorporating 1, 5 and 10 mol% of CuO and ZnO (replacing equivalent quantities of CaO) on the texture, in vitro bioactivity, and cytocompatibility of these materials was evaluated. Our results showed that the addition of metal ions can modulate the textural property of the matrix and its crystal structure. Regarding the bioactivity, after soaking in simulated body fluid (SBF) undoped 58S and NaBG glasses developed an apatite surface layer that was reduced in the doped glasses depending on the type of metal and its concentration with Zn displaying the largest inhibitions. Both the ion release from samples and the ion adsorption from the medium depended on the type of matrix with 58S glasses showing the highest values. Pure NaBG glass was more cytocompatible to osteoblast-like cells (SaOS-2) than pure 58S glass as tested by 3-(4, 5-dimethylthiazol-2-yl)-2, 5-diphenyltetrazolium bromide (MTT) assay. The incorporation of metal ions decreased the cytocompatibility of the glasses depending on their concentration and on the glass matrix doped. Our results show that by changing the glass composition and by adding Cu or Zn, bioactive materials with different textures, bioactivity and cytocompatibility can be synthesized.
Asunto(s)
Materiales Biocompatibles/química , Materiales Biocompatibles/síntesis química , Cerámica/química , Cerámica/síntesis química , Vidrio/química , Materiales Biocompatibles/toxicidad , Líquidos Corporales , Línea Celular , Supervivencia Celular/efectos de los fármacos , Cobre/química , Humanos , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Osteoblastos/citología , Osteoblastos/efectos de los fármacos , Transición de Fase , Silicatos/síntesis química , Silicatos/química , Propiedades de Superficie , Zinc/químicaRESUMEN
Background: Bacteriophages have been proposed as an alternative to control pathogenic bacteria resistant to antibiotics. However, they are not extensively used due to different factors such as vulnerability under environmental conditions and the lack of efficient administration methods. A potential solution is the encapsulation of bacteriophages in hydrogel polymers to increase their viability and as a controlled release method. This work describes the use of alginate-Ca+2 matrixes as mechanisms for protection and dosification of the phage f3αSE which has been successfully used to prevent infections produced by Salmonella Enteritidis. Results: The viability of the pure phage is reduced in near 100% after 1-h incubation at pH 2 or 3. However, the encapsulated phage remains active in 80, 6% at pH 3, while no differences were observed at pH 2, 4 or 7. Exposition of f3αSE to different T° showed that the viability of this phage decreased with increased T° to near 15% at 60°C, while the encapsulated phage remains with 50% viability at same temperature. Finally, the encapsulation of phages showed to extend their presence for 100 h in the medium compared to non-encapsulated phages in a water flow system, which simulate automatic birdbath used in poultry industry, maintaining the phage concentration between 102 and 104 PFU/mL during 250 h. Conclusions: Encapsulation in alginate-Ca+2 spheres can be a good alternative to extend viability of phages and can be used as a phage method dosification method in water flow systems.
Asunto(s)
Salmonella enteritidis/patogenicidad , Infecciones por Salmonella/terapia , Bacteriófagos/fisiología , Alginatos/química , Polímeros , Temperatura , Cápsulas , Hidrogel de Polietilenoglicol-Dimetacrilato , Viabilidad Microbiana , Concentración de Iones de HidrógenoRESUMEN
Bioactive glasses (SiO2-P2O5-CaO) having tailored concentrations of different biocide metal ions (copper or silver) were produced by the sol-gel method. All the particles release phosphorous ions when immersed in water and simulated body fluid (SBF). Moreover, a surface layer of polycrystalline hydroxy-carbonate apatite was formed on the particle surfaces after 10 day immersion in SBF as confirmed by X-ray diffraction and scanning electron microscopy (SEM) showing the bioactive materials. Samples with embedded either copper or silver ions were able to further release the biocide ions with a release rate that depends on the metal embedded and the dissolution medium: water or SBF. This biocide ion release from the samples explains the antimicrobial effect of our active particles against Escherichia coli DH5α ampicillin-resistant (Gram-negative) and Streptococcus mutans (Gram-positive) as determined by the Minimum Bactericidal Concentration (MBC) method. The antimicrobial behavior of the particles depends on the bacteria and the biocide ion used. Noteworthy, although samples with copper are able to release more metal ion than samples with silver, they present higher MBC showing the high effect of silver against these bacteria.