Multiple/Two-Way Shape Memory Poly(urethane-urea-amide) Elastomers.

Multiple and two-way reversible shape memory polymers (M/2W-SMPs) are highly promising for many fields due to large deformation, lightweight, strong recovery stress, and fast response rates. Herein, a semi-crystalline block poly(urethane-urea-amide) elastomers (PUUAs) are prepared by the copolymerization of isocyanate-terminated polyurethane (OPU) and amino-terminated oligomeric polyamide-1212 (OPA). PUUAs, composed of OPA as stationary phase and PTMEG as reversible phase, exhibit excellent rigidity, flexibility, and resilience, and cPUUA-C7 -S25 exhibits the best tensile property with strength of 10.3 MPa and elongation at break of 360.2%. Besides, all the PUUAs possess two crystallization/melting temperatures and a glass transition temperature, which endow PUUAs with multiple and reversible two-way shape memory effect (M/2W-SME). Physically crosslinked PUUA-C0 -S25 exhibits excellent dual and triple shape memory, and micro chemically crosslinked cPUUA-C7 -S25 further shows quadruple shape memory behavior. Additionally, both PUUA-C0 -S25 and cPUUA-C7 -S25 have 2W-SME. Intriguingly, cPUUA-C7 -S25 can achieve a higher temperature (up to 165 °C) SME, which makes it suitable for more complex and changeable applications. Based on the advantages of M/2W-SME, a temperature-responsive application scenario where PUUAs can transform spontaneously among different shapes is designed. These unique M/2W-SME and high-temperature SME will enable the applications of high-temperature sensors, actuators, and aerospace equipment.

Precisely Size-Tunable Monodisperse Hairy Plasmonic Nanoparticles via Amphiphilic Star-Like Block Copolymers.

In situ precision synthesis of monodisperse hairy plasmonic nanoparticles with tailored dimensions and compositions by capitalizing on amphiphilic star-like diblock copolymers as nanoreactors are reported. Such hairy plasmonic nanoparticles comprise uniform noble metal nanoparticles intimately and perpetually capped by hydrophobic polymer chains (i.e., "hairs") with even length. Interestingly, amphiphilic star-like diblock copolymer nanoreactors retain the spherical shape under reaction conditions, and the diameter of the resulting plasmonic nanoparticles and the thickness of polymer chains situated on the surface of the nanoparticle can be readily and precisely tailored. These hairy nanoparticles can be regarded as hard/soft core/shell nanoparticles. Notably, the polymer "hairs" are directly and permanently tethered to the noble metal nanoparticle surface, thereby preventing the aggregation of nanoparticles and rendering their dissolution in nonpolar solvents and the homogeneous distribution in polymer matrices with long-term stability. This amphiphilic star-like block copolymer nanoreactor-based strategy is viable and robust and conceptually enables the design and synthesis of a rich variety of hairy functional nanoparticles with new horizons for fundamental research on self-assembly and technological applications in plasmonics, catalysis, energy conversion and storage, bioimaging, and biosensors.

A simple route to hierarchically assembled micelles and inorganic nanoparticles.

Earning their stripes: A hierarchical assembly of micelles composed of an amphiphilic diblock copolymer, poly(styrene)-block-poly(4-vinylpyridine) (PS-b-P4VP), were made by combining controlled evaporative self-assembly of the confined PS-b-P4VP toluene solution in a cylinder-on-Si geometry with spontaneous self-assembly of micelles. This method gave microscopic stripes of nanometer-sized PS-b-P4VP micelles within the stripes (see pictures).

From Unimolecular Template to Silver Nanocrystal Clusters: An Effective Strategy to Balance Antibacterial Activity and Cytotoxicity.

Silver nanomaterials have attracted a great deal of interest due to their broad-spectrum antimicrobial activity. However, it is still challenging to balance the high antibacterial efficiency with low damage to biological cells of silver nanostructures, especially when the diameter decreases to less than 10 nm. Here, we developed a new type of Ag nanohybrid material via a unimolecular micelle template method, which presents amazing antibacterial activities and almost noncytotoxicity. First, water-soluble multiarm star-shaped brushlike copolymer α-CD-g-[(PEO40-g-PAA50)-b-PEO5]18 was precisely synthesized and its micelle behavior in different solvents was revealed. Then, nanocrystal clusters assembled by Ag grains (Ag@Template NCs) were prepared through an in situ redox route using the unimolecular micelle of α-CD-g-[(PEO40-g-PAA50)-b-PEO5]18 as the soft template, AgNO3 as a precursor, and tetrabutylammonium borohydride (TBAB) as the reducing agent. The overall size of the achieved Ag@Template NCs is controlled by the template structure at around 40 nm (Dh in DMF), and the size of the Ag grain can be easily regulated from ∼1 to ∼5 nm by adjusting the feeding ratio of AgNO3/acrylic acid (AA) units in the template from 1:10 to 1:1. Benefitting from the structural design of the template, all Ag@Template NCs prepared here exhibit excellent dispersibility and chemical stability in different aqueous environments (neutral, pH = 5.5, and 0.9% NaCl physiological saline solution), which play a crucial role in the long-term storage and potential application in a complex physiological environment. The antibacterial and cytotoxicity tests indicate that Ag@Template NCs display much better performance than Ag nanoparticles (Ag NPs), which have a comparable overall size of ∼25 nm. The inhibitory capability of Ag@Template NCs to bacteria strongly depends on the grain size. Specifically, the Ag@Template-1 NC assembled by the smallest grains (1.6 ± 0.3 nm) presents the best antibacterial activity. For E. coli (-), the MIC value is as low as 5 µg/mL (0.36 µg/mL of Ag), while for S. aureus (+), the value is around 10 µg/mL (0.72 µg/mL of Ag). The survival rate of L02 cells and lactate dehydrogenase assay together illustrate the low cytotoxicity possessed by the prepared Ag@Template NCs. Therefore, the proposed Ag@Template NC structure successfully resolves the high reactivity, instability, and fast oxidation issues of the ultrasmall Ag nanoparticles, and integrates high antibacterial efficiency and nontoxicity to biological cells into one platform, which implies its broad potential application in biomedicine.

Preparation of highly colloidal stable Yolk-Shell nanocomposite and its multi-stimuli responsive based on surface aggregation-induced emission (S-AIE).

Multi-stimuli responsive fluorescence probe could pave the way for monitoring more complex environmental changes. Here we prepared multifunctional nanoparticle Fe3O4@SiO2@P(DMAEMA-co-TPEE), which displayed yolk-shell morphology with well-defined polymer brush. With superparamagnetic Fe3O4 component and pH/temperature dual sensitive PDMAEMA polymer brush, the as prepared nanoparticles (YS-NPs) exhibited as multi-stimuli responsive fluorescence probe for real-time visual monitoring of environmental changes such as magnetic field, temperature and pH. Such YS-NPs could also be applied as a sensitive detector for CO2 in aqueous solution. Notably, the solution of YS-NPs showed high colloidal stability during the environmental changes, and surface aggregation-induced emission (S-AIE) was proposed for the aggregation of TPE residue on the surface of YS-NPs.

A general and robust strategy for the synthesis of nearly monodisperse colloidal nanocrystals.

Colloidal nanocrystals exhibit a wide range of size- and shape-dependent properties and have found application in myriad fields, incuding optics, electronics, mechanics, drug delivery and catalysis, to name but a few. Synthetic protocols that enable the simple and convenient production of colloidal nanocrystals with controlled size, shape and composition are therefore of key general importance. Current strategies include organic solution-phase synthesis, thermolysis of organometallic precursors, sol-gel processes, hydrothermal reactions and biomimetic and dendrimer templating. Often, however, these procedures require stringent experimental conditions, are difficult to generalize, or necessitate tedious multistep reactions and purification. Recently, linear amphiphilic block co-polymer micelles have been used as templates to synthesize functional nanocrystals, but the thermodynamic instability of these micelles limits the scope of this approach. Here, we report a general strategy for crafting a large variety of functional nanocrystals with precisely controlled dimensions, compositions and architectures by using star-like block co-polymers as nanoreactors. This new class of co-polymers forms unimolecular micelles that are structurally stable, therefore overcoming the intrinsic instability of linear block co-polymer micelles. Our approach enables the facile synthesis of organic solvent- and water-soluble nearly monodisperse nanocrystals with desired composition and architecture, including core-shell and hollow nanostructures. We demonstrate the generality of our approach by describing, as examples, the synthesis of various sizes and architectures of metallic, ferroelectric, magnetic, semiconductor and luminescent colloidal nanocrystals.