PBAT/PLA humic acid biodegradable film applied on solar greenhouse tomato plants increased lycopene and decreased total acid contents.

This work aims to resolve residual film pollution in farmlands and improve tomato quality. The mechanical properties and degradation of PBAT/PLA lignin (MZS) and PBAT/PLA humic acid (FZS) composite biodegradable film were analyzed, and its effect on soil temperature and humidity, soil microorganisms, soil physical and chemical properties, tomato yield, and quality was studied. Polyethylene film (PE) was used as a control. The results demonstrate a higher degradation degree of FZS film than of MZS film. The degradation degree of FZS and MZS films reached level 2 and level 1, respectively, after 131 days of film covering. The weight loss rate of FZS and MZS films reached 52.74 % and 57.82 %, respectively, when buried for 160 days. Compared to the coverings of PE and MZS films, FZS film could significantly increase the soil's electric conductivity and organic matter content (p < 0.05). The relative abundance of soil fungi Chaetomium also increased. The yield, soluble solids, vitamin C (Vc), soluble sugar, and lycopene of tomato plants covered with FZS film significantly increased by 6.74 %, 8.75 %, 15.41 %, 8.30 %, and 27.27 % compared to plants covered with PE film, and the total acid and hardness significantly decreased by 24.95 % and 8.46 %, respectively (p < 0.05). Using 10 µm PBAT/PLA humic acid biodegradable film for tomato cultivation in autumn and winter increased the lycopene and decreased the total acid content by changing the soil's physical and chemical characteristics and increasing the content of Chaetomium soil.

Effects of biodegradable films on melon quality and substrate environment in solar greenhouse.

With the increase in plastic pollution of farmland substrate, biodegradable mulch film research has become a hotspot. However, the degradation rate of biodegradable plastic film over the entire crop growth period is still unclear, as well as its impact on crop growth and product quality. Here, several properties of two kinds of composite biodegradable mulch films, PBAT/PLA-[S1] and PBAT/lignin-[S2], are studied with polyethylene-[PE] and uncovered substrate (CK) as controls. We tested the differences in morphological characterization, physical properties, and weight loss rate of the plastic films, as well as the effects of the different plastic films on melon yield and quality, substrate temperature and humidity, physical and chemical properties of the substrate, and substrate fungal species composition. Compared to PE, biodegradable plastic films S1 and S2 increased substrate temperature and the net photosynthetic rate of leaves. The results of substrate 18 s rDNA assay of CK, PE, S1, and S2 after 80 days of treatment and pre-treatment showed that a total of 12 fungal phylum, with 317 fungal genera were found, in which Ascomycota as the main phyla and Penicillium as the main genera. Compared with PE, the S2 treatment significantly increased the single fruit weight, central sugar content and soluble sugar of melon by 225.35 g, 1.26%, and 0.68%, respectively (p < 0.05). When buried for 240 d, the weight loss rate of S2 was significantly increased by 86.08% compared with PE (p < 0.05). From these results, we extrapolated that covering the substrate with the most biodegradable film, PBAT/lignin composite (10 µm), improved the yield and fruit quality of the melon in winter greenhouse production.