Light transmission and bond strength of glass fiber posts submitted to different surface treatments.

STATEMENT OF PROBLEM: Light transmitted deep into the root canal is an important parameter to increase bonding of the cement to the post and dentin. Glass fiber posts seem to be an option to increase transmitted light, but literature on the light transmittance profile and power transmission to deep canal regions is lacking. PURPOSE: The purpose of this in vitro study was to evaluate light delivered by 2 types of fiberglass posts submitted to different surface treatments and to evaluate the bond strength. MATERIAL AND METHODS: Whiteposts and Superposts were allocated to 4 groups: no surface treatment, surface treatment with 24% hydrogen peroxide, surface treatment with silane, and surface treatment with 24% hydrogen peroxide plus silane. The total light transmitted by the posts was measured by using an integrating sphere to collect the diffuse light. The light profile that was laterally delivered to the post was measured with a power detector equipped with an optical fiber probe. The bond strength was measured with the push-out test. Scanning electron microscopy was used to evaluate the surface treatments. The light transmission data were analyzed by using a generalized linear model and the Bonferroni test and the bond strength values were evaluated by using ANOVA and the Tukey test (α=.05). RESULTS: The cervical third presented the highest transmission (74.1% for Whiteposts and 74.6% for Superposts), followed by the middle (20.9% for Whiteposts and 20.4% for Superposts) and apical (5.0% for both Whiteposts and Superposts) thirds. Superposts led to higher bond strength than Whiteposts (9.73 ±5.89 and 8.48 ±4.99 MPa, respectively). Surface treatment with silane and hydrogen peroxide plus silane afforded similar bond strength (11.4 ±6.4 and 10.7 ±5.6 MPa, respectively), which was higher as compared with the bond strength obtained after surface treatment with hydrogen peroxide. For both post types, the bond strength decreased from the cervical (12.2 ±6.0 MPa) to the middle (9.7 ±5.0 MPa) and apical (6.5 ±3.6 MPa) thirds. CONCLUSIONS: Light transmission and bond strength decreased from the cervical to the apical third. Surface treatment impacted bond strength; light transmission through Whiteposts was slightly higher than light transmission through Superposts.

Effect of high-concentrated bleaching agents on the bond strength at dentin/resin interface and flexural strength of dentin.

This study evaluated the effect of bleaching agents on bond strength at the dentin/resin interface and the flexural strength of dentin. Forty maxillary canines were selected for the study. In the shear strength test, 40 slabs of intracoronary dentin (5 x 5 mm) obtained from buccal surfaces of the crowns were included in acrylic resin. In the flexural strength test, 40 dentin bars (8 x 2 x 2 mm) were obtained from the roots. The 40 hemi-sections of the lingual surface were prepared for scanning electron microscopy (SEM). The specimens were divided into 4 groups according to the bleaching protocol (n=10): Unbleached (control), Sodium perborate + 20% hydrogen peroxide (SP + 20% HP), 37% carbamide peroxide (37% CP) and 38% hydrogen peroxide (38% HP). After 7 days, the bond strength specimens were restored and tested. Dentin bars were bleached and subjected to a three-point bending test. Data (MPa) were analyzed by ANOVA and Tukey's test (α=0.05). In the shear test, the control group was superior (p<0.05) to the bleached groups, which, in turn, were statistically similar (p>0.05). In the flexural strength test, the control group also had the highest values and differed significantly from the other groups (p<0.05). SEM revealed smear layer in all groups, with fissures in the bleached specimens. SP + 20% HP and 38% HP showed discontinuous interfaces with few tags. In conclusion, bond strength of restorative material to dentin and flexural strength of dentin were reduced after the use of high-concentration bleaching agents.

Effect of high-concentrated bleaching agents on the bond strength at dentin/resin interface and flexural strength of dentin

This study evaluated the effect of bleaching agents on bond strength at the dentin/resin interface and the flexural strength of dentin. Forty maxillary canines were selected for the study. In the shear strength test, 40 slabs of intracoronary dentin (5 x 5 mm) obtained from buccal surfaces of the crowns were included in acrylic resin. In the flexural strength test, 40 dentin bars (8 x 2 x 2 mm) were obtained from the roots. The 40 hemi-sections of the lingual surface were prepared for scanning electron microscopy (SEM). The specimens were divided into 4 groups according to the bleaching protocol (n=10): Unbleached (control), Sodium perborate + 20 percent hydrogen peroxide (SP + 20 percent HP), 37 percent carbamide peroxide (37 percent CP) and 38 percent hydrogen peroxide (38 percent HP). After 7 days, the bond strength specimens were restored and tested. Dentin bars were bleached and subjected to a three-point bending test. Data (MPa) were analyzed by ANOVA and Tukey's test (α=0.05). In the shear test, the control group was superior (p<0.05) to the bleached groups, which, in turn, were statistically similar (p>0.05). In the flexural strength test, the control group also had the highest values and differed significantly from the other groups (p<0.05). SEM revealed smear layer in all groups, with fissures in the bleached specimens. SP + 20 percent HP and 38 percent HP showed discontinuous interfaces with few tags. In conclusion, bond strength of restorative material to dentin and flexural strength of dentin were reduced after the use of high-concentration bleaching agents.

Este estudo avaliou o efeito de agentes clareadores na resistência de união da interface dentina/resina e resistência à flexão da dentina. Quarenta caninos superiores foram selecionados para o estudo. No teste de cisalhamento, 40 fragmentos de dentina intracoronária (5 x 5 mm) obtidos a partir de superfícies vestibulares das coroas foram incluídos em resina acrílica. No teste de flexão, 40 barras de dentina (8 x 2 x 2 mm) foram obtidas a partir das raízes. As 40 hemi-seções da superfície lingual foram preparadas para microscopia eletrônica de varredura (MEV). Os espécimes foram divididos em 4 grupos de acordo com o protocolo de clareamento (n=10): Não clareados (controle), perborato de sódio + peróxido de hidrogênio 20 por cento (PS + PH 20 por cento), peróxido de carbamida 37 por cento (PC37 por cento) e peróxido de hidrogênio 38 por cento (PH 38 por cento). Após 7 dias, as amostras destinadas à resistência de união foram restauradas e submetidas ao teste. As barras de dentina foram clareadas e submetidas ao teste de flexão de 3 pontos. Os dados (MPa) foram analisados por ANOVA e teste de Tukey (α=0,05). No teste de cisalhamento, o controle foi superior (p<0,05) aos grupos clareados, que foram semelhantes entre si (p>0,05). Na resistência à flexão, o grupo controle também exibiu os maiores valores, diferente dos demais (p<0,05). SEM revelou camada de smear em todos os grupos, com fissuras nos espécimes clareados. PS + 20 por cento PH e PH 38 por cento apresentaram interfaces de descontínuas com poucos tags. A resistência de união do material restaurador à dentina e a resistência à flexão da dentina foram reduzidas após o uso de agentes clareadores de alta concentração.