Hierarchical Porous Polystyrene Monoliths from PolyHIPE.

Hierarchical porous polystyrene monoliths (HCP-PolyHIPE) are obtained by hypercrosslinking poly(styrene-divinylbenzene) monoliths prepared by polymerization of high internal phase emulsions (PolyHIPEs). The hypercrosslinking is achieved using an approach known as knitting which employs formaldehyde dimethyl acetal (FDA) as an external crosslinker. Scanning electron microscopy (SEM) confirms that the macroporous structure in the original monolith is retained during the knitting process. By increasing the amount of divinylbenzene (DVB) in PolyHIPE, the BET surface area and pore volume of the HCP-PolyHIPE decrease, while the micropore size increases. BET surface areas of 196-595 m(2) g(-1) are obtained. The presence of micropores, mesopores, and macropores is confirmed from the pore size distribution. With a hierarchical porous structure, the monoliths reveal comparable gas sorption properties and potential applications in oil spill clean-up.

Organic Microporous Nanofillers with Unique Alcohol Affinity for Superior Ethanol Recovery toward Sustainable Biofuels.

To minimize energy consumption and carbon footprints, pervaporation membranes are fast becoming the preferred technology for alcohol recovery. However, this approach is confined to small-scale operations, as the flux of standard rubbery polymer membranes remain insufficient to process large solvent volumes, whereas membrane separations that use glassy polymer membranes are prone to physical aging. This study concerns how the alcohol affinity and intrinsic porosity of networked, organic, microporous polymers can simultaneously reduce physical aging and drastically enhance both flux and selectivity of a super glassy polymer, poly-[1-(trimethylsilyl)propyne] (PTMSP). Slight loss in alcohol transportation channels in PTMSP is compensated by the alcohol affinity of the microporous polymers. Even after continuous exposure to aqueous solutions of alcohols, PTMSP pervaporation membranes loaded with the microporous polymers outperform the state-of-the-art and commercial pervaporation membranes.