Effect of Reaction Temperature on the Microstructure and Properties of Magnesium Phosphate Chemical Conversion Coatings on Titanium.

Magnesium phosphate (MgP) has garnered growing interest in hard tissue replacement processes due to having similar biological characteristics to calcium phosphate (CaP). In this study, an MgP coating with the newberyite (MgHPO4·3H2O) was prepared on the surface of pure titanium (Ti) using the phosphate chemical conversion (PCC) method. The influence of reaction temperature on the phase composition, microstructure, and properties of coatings was systematically researched with the use of an X-ray diffractometer (XRD), a scanning electron microscope (SEM), a laser scanning confocal microscope (LSCM), a contact angle goniometer, and a tensile testing machine. The formation mechanism of MgP coating on Ti was also explored. In addition, the corrosion resistance of the coatings on Ti was researched by assessing the electrochemical behavior in 0.9% NaCl solution using an electrochemical workstation. The results showed that temperature did not obviously affect the phase composition of the MgP coatings, but affected the growth and nucleation of newberyite crystals. In addition, an increase in reaction temperature had a great impact on properties including surface roughness, thickness, bonding strength, and corrosion resistance. Higher reaction temperatures resulted in more continuous MgP, larger grain size, higher density, and better corrosion resistance.

Preparation of well-distributed titania nanopillar arrays on Ti6Al4V surface by induction heating for enhancing osteogenic differentiation of stem cells.

Great effort has recently been devoted to the preparation of nanoscale surfaces on titanium-based implants to achieve clinically fast osteoinduction and osseointegration, which relies on the unique characteristics of the nanostructure. In this work, we used induction heating treatment (IHT) as a rapid oxidation method to fabricate a porous nanoscale oxide layer on the Ti6Al4V surface for better medical application. Well-distributed vertical nanopillars were yielded by IHT for 20-35 s on the alloy surface. The composition of the oxides contained rutile/anatase TiO2 and a small amount of Al2O3 between the TiO2 grain boundaries (GBs). This technology resulted in a reduction and subsequent increase of surface roughness of 26-32 nm when upregulating the heating time, followed by the successive enhancement of the thickness, wettability and adhesion strength of the oxidation layer to the matrix. The surface hardness also distinctly rose to 554 HV in the IHT-35 s group compared with the 350 HV of bare Ti6Al4V. The massive small-angle GBs in the bare alloy promoted the formation of nanosized oxide crystallites. The grain refinement and deformation texture reduction further improved the mechanical properties of the matrix after IHT. Moreover, in vitro experiments on a mesenchymal stem cell (BMSC) culture derived from human bone marrow for 1-7 days indicated that the nanoscale layers did not cause cytotoxicity, and facilitated cell differentiation in osteoblasts by enhancing the gene and osteogenesis-related protein expressions after 1-3 weeks of culturing. The increase of the IHT time slightly advanced the BMSC proliferation and differentiation, especially during long-term culture. Our findings provide strong evidence that IHT oxidation technology is a novel nanosurface modification technology, which is potentially promising for further clinical development.

Construction of Magnesium Phosphate Chemical Conversion Coatings with Different Microstructures on Titanium to Enhance Osteogenesis and Angiogenesis.

Titanium (Ti) and its alloys are widely used as hard tissue substitutes in dentistry and orthopedics, but their low bioactivity leads to undesirable osseointegration defects in the early osteogenic phase. Surface modification is an important approach to overcome these problems. In the present study, novel magnesium phosphate (MgP) coatings with controllable structures were fabricated on the surface of Ti using the phosphate chemical conversion (PCC) method. The effects of the microstructure on the physicochemical and biological properties of the coatings on Ti were researched. The results indicated that accelerators in PCC solution were important factors affecting the microstructure and properties of the MgP coatings. In addition, the coated Ti exhibited excellent hydrophilicity, high bonding strength, and good corrosion resistance. Moreover, the biological results showed that the MgP coatings could improve the spread, proliferation, and osteogenic differentiation of mouse osteoblast cells (MC3T3-E1) and vascular differentiation of human umbilical vein endothelial cells (HUVECs), indicating that the coated Ti samples had a great effect on promoting osteogenesis and angiogenesis. Overall, this study provided a new research idea for the surface modification of conventional Ti to enhance osteogenesis and angiogenesis in different bone types for potential biomedical applications.

Calcium-Zinc Phosphate Chemical Conversion Coating Facilitates the Osteointegration of Biodegradable Zinc Alloy Implants by Orchestrating Macrophage Phenotype.

Zinc (Zn) alloys provide a new generation for orthopedic applications due to their essential physiological effects and promising degradation properties. However, excessive release of Zn ions (Zn2+ ) during degradation and the severe inflammatory microenvironment are not conducive to osseointegration, which is determined by the characteristics of the implant surface. Therefore, it is essential to modulate the release rate of Zn alloys by surface modification technology and endow them with anti-inflammatory and osteogenic effects. In this study, two kinds of phosphate chemical conversion (PCC) coatings with different compositions and morphological structures are prepared, namely Zn-P (with disk-like crystals) and Ca-Zn-P (with lamellar crystals). Although all the PCC-coated Zn implants have low cytotoxicity, Ca-Zn-P show better osteoimmunomodulation effects in several aspects: the induction of the M2-phenotype macrophage polarization and thus promotion of osteogenesis in vitro; the regulation of the bone immune microenvironment which is conducive to tissue regeneration and osseointegration in vivo; and the release of ions (through PI3K/AKT and Wnt signaling pathways) and the morphological structures (through RhoGTPase signaling pathways) act as possible mechanisms of M2 polarization. The Ca-Zn-P coating can be considered to provide new insights into bone immunomodulation and osseointegration.

Interleukin-4 assisted calcium-strontium-zinc-phosphate coating induces controllable macrophage polarization and promotes osseointegration on titanium implant.

Titanium (Ti) and its alloys are believed to be promising scaffold materials for dental and orthopedic implantation due to their ideal mechanical properties and biocompatibility. However, the host immune response always causes implant failures in the clinic. Surface modification of the Ti scaffold is an important factor in this process and has been widely studied to regulate the host immune response and to further promote bone regeneration. In this study, a calcium-strontium-zinc-phosphate (CSZP) coating was fabricated on a Ti implant surface by phosphate chemical conversion (PCC) technique, which modified the surface topography and element constituents. Here, we envisioned an accurate immunomodulation strategy via delivery of interleukin (IL)-4 to promote CSZP-mediated bone regeneration. IL-4 (0 and 40 ng/mL) was used to regulate immune response of macrophages. The mechanical properties, biocompatibility, osteogenesis, and anti-inflammatory properties were evaluated. The results showed that the CSZP coating exhibited a significant enhancement in surface roughness and hydrophilicity, but no obvious changes in proliferation or apoptosis of bone marrow mesenchymal stem cells (BMMSCs) and macrophages. In vitro, the mRNA and protein expression of osteogenic related factors in BMMSCs cultured on a CSZP coating, such as ALP and OCN, were significantly higher than those on bare Ti. In vivo, there was no enhanced bone formation but increased macrophage type 1 (M1) polarization on the CSZP coating. IL-4 could induce M2 polarization and promote osteogenesis of BMMSCs on CSZP in vivo and in vitro. In conclusion, the CSZP coating is an effective scaffold for BMMSCs osteogenesis, and IL-4 presents the additional advantage of modulating the immune response for bone regeneration on the CSZP coating in vivo.

In-situ preparation of scholzite conversion coatings on titanium and Ti-6Al-4V for biomedical applications.

A scholzite (CaZn2(PO4)2·2H2O) coating was prepared in situ on commercially pure titanium (cpTi) and Ti-6Al-4V (Ti64) substrates using the chemical conversion technology, and its phase composition and microstructure, as well as mechanical, chemical and biological properties were investigated to explore potential applications as a bioactive coating on bone implants. It is indicated that the coating consists mainly of monoclinic scholzite crystals with nano-thick laminar morphology. The crystals on cpTi aggregate to flower-like particles with the diameter of 5-10µm, while form a network structure homogeneously on Ti64. The scratch test shows that the interfacial bonding strength between the coatings and substrates is higher than 40N. Electrochemical measurements indicate that the corrosion behavior of the coatings is not inferior compared with that of oxide film on substrates. MG63 osteoblast-like cells show good adherence and significantly proliferation and differentiation characteristics on the scholzite coated cpTi and Ti64 (p<0.05) in in-vitro cell tests, demonstrating the cytocompatibility of Ti is significantly improved by the scholzite coating. It is suggested that the scholzite coating might be a promising option in hard tissue replacements for early osteogenesis.

A bioactive coating with submicron-sized titania crystallites fabricated by induction heating of titanium after tensile deformations.

Thermal oxidation technology was widely investigated as one of effective surface modification method for improving the bioactivity and biocompatibility of titanium and its alloys. In this work, the induction heat oxidization method, a fast, efficient, economical and environmental protective technology, was applied to prepare the submicron-morphological oxide coating with variable rutile TiO2 equiaxed crystallites on the surface of pure Ti substrates after cold-drawing with 10-20% deformations. The results showed the plastic-deformed Ti cylinders recrystallized during induction heating treatment (IHT) for 10-20s which resulted in evolution of microstructures as well as slight improvement of microhardness. The surface characteristics of TiO2 crystallites in oxidation layers were determined by the microstructural evolutions of Ti substrate in terms of the nucleation and growth of TiO2 crystallites. Specially, the oxidized surface with 50-75nm roughness and more uniform and finer equiaxed oxide grains remarkablely improved the apatite deposition after bioactive evaluation in 1.5 × SBF for 7 days. This work provided a potential method to create controlled bioactive oxide coatings with submicro-/nano-scaled TiO2 crystallites on titanium substrate in terms of the role of metallographic microstructure in the formation process of titanium oxides.

In vitro and in vivo evaluation of calcium phosphate composite scaffolds containing BMP-VEGF loaded PLGA microspheres for the treatment of avascular necrosis of the femoral head.

Avascular necrosis of the femoral head (ANFH) is difficult to treat due to high pressure and hypoxia, and reduced levels of growth factors such as bone morphogenetic protein (BMP), and vascular endothelial growth factor (VEGF). We generated a novel calcium phosphate (CPC) composite scaffold, which contains BMP-VEGF-loaded poly-lactic-co-glycolic acid (PLGA) microspheres (BMP-VEGF-PLGA-CPC). The BMP-VEGF-loaded microspheres have an encapsulation efficiency of 89.15% for BMP, and 78.55% for VEGF. The BMP-VEGF-PLGA-CPC scaffold also demonstrated a porosity of 62% with interconnected porous structures, and pore sizes of 219 µm and compressive strength of 6.60 MPa. Additionally, bone marrow mesenchymal stem cells (BMSCs) were seeded on scaffolds in vitro. Further characterization showed that the BMP-VEGF-PLGA-CPC scaffolds were biocompatible and enhanced osteogenesis and angiogenesis in vitro. Using a rabbit model of ANFH, BMP-VEGF-PLGA-CPC scaffolds were implanted into the bone tunnels of core decompression in the femoral head for 6 and 12 weeks. Radiographic and histological analysis demonstrated that the BMP-VEGF-PLGA-CPC scaffolds exhibited good biocompatibility, and osteogenic and angiogenic activity in vivo. These results indicate that the BMP-VEGF-PLGA-CPC scaffold may improve the therapeutic effect of core decompression surgery and be used as a treatment for ANFH.

Phosphate chemical conversion coatings on metallic substrates for biomedical application: a review.

Phosphate chemical conversion (PCC) technology has been investigated for improving the surface performance of metallic implants in the biomedical field over the last decade. The metallic materials, such as magnesium and its alloys, titanium, pure iron and stainless steel are widely used as orthopedic devices for immobilization of bone fractures in clinic. They were previously studied as metal substrates for PCC coating aiming to modify their biocompatibility and osteoconductivity. Zinc, calcium and zinc-calcium PCC coatings are frequently utilized considering their nature and the end-use. Although PCC coating has been confirmed to potentially improve the bio-performance of metallic implants in vitro and in vivo by many researchers, there are no unified standards or regulations to give quantitative appraisal of its quality and property. As such, an overview of several main phosphate phases together with their properties and behaviors in vitro and in vivo was conducted. The mechanism of phosphating was also briefly discussed. Critical qualities of PCC coating used for biomedical application including corrosion resistance, wettability and bonding strength were analyzed separately. Biological response including in vitro cell investigations and in vivo tissue response were discussed in terms of the cytocompatibility and bioactivity of PCC coating. Further investigations are proposed to develop appropriate performance evaluation measurements by combining conventional technologies and biomedical procedures.

Biocompatibility and osteogenesis of calcium phosphate composite scaffolds containing simvastatin-loaded PLGA microspheres for bone tissue engineering.

By utilizing a modified solid/oil/water (s/o/w) emulsion solvent evaporation technique, calcium phosphate composite scaffolds containing simvastatin-loaded PLGA microspheres (SIM-PLGA-CPC) were prepared in this study. We characterized the morphology, encapsulation efficiency and in vitro drug release of SIM-loaded PLGA microspheres as well as the macrostructure, pore size, porosity and mechanical strength of the scaffolds. Rabbit bone mesenchymal stem cells (BMSCs) were seeded onto SIM-PLGA-CPC scaffolds, and the proliferation, morphology, cell cycle and differentiation of BMSCs were investigated using the cell counting kit-8 (CCK-8) assay, scanning electron microscopy (SEM), flow cytometry, alkaline phosphatase (ALP) activity and alizarin red S staining, respectively. The results revealed that SIM-PLGA-CPC scaffolds were biocompatible and osteogenic in vitro. To determine the in vivo biocompatibility and osteogenesis of the scaffolds, both pure PLGA-CPC scaffolds and SIM-PLGA-CPC scaffolds were implanted in rabbit femoral condyles and microradiographically and histologically investigated. SIM-PLGA-CPC scaffolds exhibited good biocompatibility and could improve the efficiency of new bone formation. All these results suggested that the SIM-PLGA-CPC scaffolds fulfilled the basic requirements of bone tissue engineering scaffold and possessed application potentials in orthopedic surgery.

Preparation and properties of plasma electrolytic oxidation coating on sandblasted pure titanium by a combination treatment.

Plasma electrolytic oxidation (PEO) is one of the most applicable methods to produce bioceramic coating on a dental implant and sandblasting is a primary technique to modify metal surface properties. This study aims to deposit bioceramic Ca- and P-containing coatings on sandblasted commercially pure titanium by PEO technique to improve its bioactive performance. The time-dependent modified surfaces are characterized in terms of their microstructure, phase, chemical composition, mechanical properties and bioactivities. The results show that the combination-treated coating exhibits better properties than the PEO-treated one, especially in bioactivities, as evidenced by the HA formation after immersion in simulated body fluid (SBF) for 5 days and the cell viability after seeding for 1 or 3 days. The enhancement of the modified surface is attributed to a combination of the mechanical sandblasting and the microplasma oxidation.

Factors influencing the deposition of hydroxyapatite coating onto hollow glass microspheres.

Hydroxyapatite (HA) and HA coated microcarriers for cell culture and delivery have attracted more attention recently, owing to the rapid progress in the field of tissue engineering. In this research, a dense and uniform HA coating with the thickness of about 2 µm was successfully deposited on hollow glass microspheres (HGM) by biomimetic process. The influences of SBF concentration, immersion time, solid/liquid ratio and activation of HGM on the deposition rate and coating characteristics were discussed. X-ray diffraction (XRD) and Fourier transform infrared spectrum (FTIR) analyses revealed that the deposited HA is poorly crystalline. The thickness of HA coating showed almost no increase after immersion in 1.5SBF for more than 15 days with the solid/liquid ratio of 1:150. At the same time, SBF concentration, solid/liquid ratio and activation treatment played vital roles in the formation of HA coating on HGM. This poorly crystallized HA coated HGM could have potential use as microcarrier for cell culture.