Effects of Er:YAG laser irradiation and manipulation treatments on dentin components, part 2: energy-dispersive X-ray fluorescence spectrometry study.

The effects of laser etching, decontamination, and storage treatments on dentin components were studied by energy-dispersive X-ray fluorescence spectrometry (EDXRF). Thirty bovine incisors were prepared to expose the dentin surface and then divided into two main groups based upon the decontamination process and storage procedure: autoclaved (group A, n=15) or stored in aqueous thymol solution (group B, n=15). The surfaces of the dentin slices were schematically divided into four areas, with each one corresponding to a treatment subgroup. The specimens were either etched with phosphoric acid (control subgroup) or irradiated with erbium-doped yttrium-aluminum-garnet (Er:YAG) laser (subgroups: I-80 mJ, II-120 mJ, and III-180 mJ). Samples were analyzed by micro-EDXRF, yielding three spectra for each area (before and after treatment). Surface mappings covering an area of 80x60 points with steps of 20 mum were also performed on selected specimens. The amount of Ca and P in group A specimens decreased significantly (P<0.05) after the acid etching and the CaP ratio increased (P<0.001). Er:YAG laser-etching using lower laser energies did not produce significant changes in dentin components. The mapping data support the hypothesis that acid etching on dentin produced a more chemically homogeneous surface and thus a more favorable surface for the diffusion of adhesive monomers.

Effects of Er:YAG laser irradiation and manipulation treatments on dentin components, part 1: Fourier transform-Raman study.

The effects of laser etching, decontamination, and storage treatments on dentin components were studied using Fourier transform (FT)-Raman spectroscopy. Thirty bovine incisors were prepared to expose the dentin surface and then divided in two main groups based upon the decontamination process and storage procedure: autoclaved (group A, n=15) or stored in thymol aqueous solution (group B, n=15). The surfaces of the dentin slices were schematically divided into four areas, with each one corresponding to a treatment subgroup. The specimens were either etched with phosphoric acid (control subgroup) or irradiated with erbium-doped yttrium-aluminum-garnet (Er:YAG) laser (subgroups: I-80 mJ, II-120 mJ, and III-180 mJ, and total energy of 12 J). Samples were analyzed by FT-Raman spectroscopy; we collected three spectra for each area (before and after treatment). The integrated areas of five Raman peaks were calculated to yield average spectra. The areas of the peaks associated with phosphate content (P<0.001), type I collagen, and organic C-H bonds (P<0.05) were reduced significantly in group A (control). Analyses of samples irradiated with reduced laser energies did not show significant changes in the dentin components. These results suggest that thymol storage treatment is advised for in vitro study; furthermore, 12 J of Er:YAG laser energy does not affect dentin components.